CN1869269A - 稀土高锌铜合金材料及其制备方法 - Google Patents

稀土高锌铜合金材料及其制备方法 Download PDF

Info

Publication number
CN1869269A
CN1869269A CN 200610041986 CN200610041986A CN1869269A CN 1869269 A CN1869269 A CN 1869269A CN 200610041986 CN200610041986 CN 200610041986 CN 200610041986 A CN200610041986 A CN 200610041986A CN 1869269 A CN1869269 A CN 1869269A
Authority
CN
China
Prior art keywords
alloy
copper alloy
high zinc
earth high
rear earth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200610041986
Other languages
English (en)
Inventor
苏义祥
门志慧
张国祥
路阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lanzhou University of Technology
Original Assignee
Lanzhou University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lanzhou University of Technology filed Critical Lanzhou University of Technology
Priority to CN 200610041986 priority Critical patent/CN1869269A/zh
Publication of CN1869269A publication Critical patent/CN1869269A/zh
Pending legal-status Critical Current

Abstract

稀土高锌铜合金材料及其制备方法,按重量百分比计量其成分为:RE0.05~3.50%,Cu 43.00~48.00%,Mn 1.50~3.50%,Pb 1.50~3.50%,Fe0.50~2.50%,Al 0.10~2.00%,余量为Zn,其它杂质≤1%。其制备方法为:其特征在于按权利要求1所述的合金成分进行配料,将配好的原材料预热后装入电炉或者火焰反射炉中熔化,待温度升至1150~1350℃时加入合金净化剂,排气、清渣,然后用钟罩压入混合RE,充分搅拌合金液,然后静置3~8分钟,最后耙去合金液表面的熔渣,出炉浇注成铸件或者挤压型材用的棒料。

Description

稀土高锌铜合金材料及其制备方法
技术领域
本发明涉及锌铜合金材料,具体是稀土锌铜合金材料及其制备的方法。
背景技术
目前对于不承受高温重载荷的耐磨蚀铜合金零配件如:仪器、仪表壳体、支架、散热器管、螺母、螺杆、工艺美术装饰制品、建筑装潢制品或者在冷却介质条件下工作的蜗轮、轴瓦、衬套、摩擦圈、挤压工件用材料,普遍采用黄铜和青铜材料,由于黄铜和青铜材料中纯铜含量大于60%,大部分材料中含有一定量的锡、镍、铬、钴等昂贵的元素,使得零配件的制造成本较高。
发明内容
本发明的目的是降低铜元素含量,提高铜合金零配件的机械性能和耐腐蚀、耐磨性能。
稀土高锌铜合金材料,按重量百分比计量其成分为:RE 0.05~3.50%,Cu43.00~48.00%,Mn 1.50~3.50%,Pb 1.50~3.50%,Fe 0.50~2.50%,Al0.10~2.00%,余量为Zn,其它杂质≤1%。
稀土高锌铜合金材料的制备方法,按上述的合金成分进行配料,将配好的原材料预热后装入电炉或者火焰反射炉中熔化,待温度升至1150~1350℃时加入合金净化剂,排气、清渣,然后用钟罩压入混合RE,充分搅拌合金液,然后静置3~8分钟,最后耙去合金液表面的熔渣,出炉浇注成铸件或者挤压型材用的棒料。
本发明的有益效果为:其成分中的Zn、Cu是材料的基本元素与Mn、Fe、Al、RE等元素形成含Zn和Cu等元素的固溶体,提高材料的综合性能;Mn能固溶于Cu中起到强化作用,并显著提高材料的机械性能和对海水、氯化物的耐腐蚀能力;Fe元素与Zn化合生成FeZn7颗粒,使液态合金凝固时析出而成为晶核,细化合金晶粒组织;Pb几乎不熔于铜合金中,是以点状形式分布在晶界上,当材料工作时起到自润滑性能,提高铜合金材料的耐磨性能;Al在熔炼过程中可以减少Zn的蒸发,降低Zn在熔炼过程中的烧损,并能在工件表面形成具有很强的抗氧化能力的Al2O3薄膜,提高材料的耐腐蚀性能和表面光洁度,还能使工件表面泛金黄色;混合稀土可净化合金、细化晶粒、强化固溶体和提高材料的抗氧化性能,还能提高材料在型材挤压过程中的高温抗裂性能和塑性成型能力;稀土高锌铜合金材料的铸态硬度HB≥80,性能稳定。
具体实施方式
按重量百分比计算,本发明的成分为:RE 0.05~3.50%,Cu 43.00~48.00%,Mn 1.50~3.50%,Pb 1.50~3.50%,Fe 0.50~2.50%,Al 0.10~2.00%,余量为Zn,其它杂质≤1%。按上述的合金成分进行配料,将配好的原材料预热后装入电炉或者火焰反射炉中熔化,待温度升至1150~1350℃时加入合金净化剂,排气、清渣,然后用钟罩压入混合RE,充分搅拌合金液,然后静置3~8分钟,最后耙去合金液表面的熔渣,取样做炉前检查和分析,调整合金成分,合格后出炉浇注成铸件或者挤压型材用的棒料。
或者按上述合金成分配料,将配好的原材料纯Fe屑加入到坩埚底部、金属Mn或者65%Mn-Fe和纯Cu等一次性装入电炉或者火焰反射炉中熔化,待合金化清后加入Pb锭,温度升至1150~1350℃时加入Al锭后再加入Zn锭,然后加入合金净化剂,排气、清渣,最后用钟罩压入混合RE,充分搅拌合金液之后静置3~8分钟后耙去合金液表面的熔渣,取样做炉前检查和分析,调整合金成分,合格后出炉浇注;炉前检查试样为120mm×10mm×10mm条状,折断弯角15度左右,断口表面平整,组织细密,无偏析和氧化夹渣,颜色呈灰白色为合格,然后将合格的液态合金浇注铸件或者挤压型材用的棒料,经过机械加工后完成低成本的新型稀土高锌铜合金材料零配件。

Claims (3)

1、稀土高锌铜合金材料,其特征在于按重量百分比计量其成分为:RE 0.05~3.50%,Cu 43.00~48.00%,Mn 1.50~3.50%,Pb 1.50~3.50%,Fe 0.50~2.50%,Al 0.10~2.00%,余量为Zn,其它杂质≤1%。
2、稀土高锌铜合金材料制备方法,其特征在于按权利要求1所述的合金成分进行配料,将配好的原材料预热后装入电炉或者火焰反射炉中熔化,待温度升至1150~1350℃时加入合金净化剂,排气、清渣,然后用钟罩压入混合RE,充分搅拌合金液,然后静置3~8分钟,最后耙去合金液表面的熔渣,出炉浇注成铸件或者挤压型材用的棒料。
3、根据权利要求2所述的稀土高锌铜合金制备方法,其特征在于将配好的原材料纯Fe屑加入到坩埚底部、Mn或者65%Mn-Fe和纯Cu等一次性装入电炉或者火焰反射炉中熔化,待合金化清后加入Pb锭,温度升至1150~1350℃时加入Al锭后再加入Zn锭,然后加入合金净化剂,排气、清渣,最后用钟罩压入混合RE,充分搅拌合金液之后静置3~8分钟后耙去合金液表面的熔渣,出炉浇注成铸件或者挤压型材用的棒料。
CN 200610041986 2006-03-22 2006-03-22 稀土高锌铜合金材料及其制备方法 Pending CN1869269A (zh)