CN1844293B - Eva高分子防水卷材的制作工艺 - Google Patents
Eva高分子防水卷材的制作工艺 Download PDFInfo
- Publication number
- CN1844293B CN1844293B CN200610020781A CN200610020781A CN1844293B CN 1844293 B CN1844293 B CN 1844293B CN 200610020781 A CN200610020781 A CN 200610020781A CN 200610020781 A CN200610020781 A CN 200610020781A CN 1844293 B CN1844293 B CN 1844293B
- Authority
- CN
- China
- Prior art keywords
- eva
- temperature
- manufacture craft
- polymer membranes
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种EVA高分子防水卷材的制作工艺,它由以下原料制成:EVA、抗氧剂CA、防老剂2246、硬脂酸、ZnO、DCP、二丁酯,还包括天然橡胶、填料和颜料,其中填料由超细活性碳酸钙和绢白粉组成。EVA高分子防水卷材制作工艺包括以下步骤:配料、捏合、造粒、挤出定型、冷却、收卷。本发明具有耐腐蚀、耐老化、耐酸碱、抗拉强度高、抗渗力强、易粘结、变形适应力强、适应温度范围广、无毒无味、调色性强,可做透明制品等特点,适用于桥梁、地铁、公路等工程防水防渗。
Description
技术领域
本发明涉及防水卷材及其制作工艺,特别是EVA高分子防水卷材的制作工艺。
技术背景
防水材料主要包括防水涂料和防水卷材,防水卷材可分为沥青卷材、PVC、三元乙丙、三元乙丁、再生胶等防水卷材,沥青类卷材具有受温度影响能发生较大形变的缺点;PVC等防水卷材无弹性,弯折性差,低温变硬、变脆;三元乙丙、三元乙丁防水片材,成本较高,加工成型性和施工粘结性等各项性能都不甚理想;再生橡胶防水片材,虽然成本略低,但其强力、伸长率、耐老化性,耐折性、耐蠕变性等各项指标较差,在许多领域均显示出其缺陷。在桥梁、地铁等场合,对防水卷材的强度、伸缩性要求高,一般防水卷材难以满足其性能要求。
发明内容
本发明针对现有防水卷材易变形、易老化等不足,提供一种EVA高分子防水卷材的制作工艺,该防水卷材具有耐腐蚀、耐老化、耐酸碱、抗拉强度高、抗渗力强、易粘结、变形适应力强、适应温度范围广、无毒无味并可根据需要着色,甚至可作透明产品等特点,适用于桥梁、地铁、公路、洞体、隧道、水池、人工湖、地下室等工程防水防渗,特别适用于拱顶内面的防水工程。
本发明的发明目的是通过以下技术方案实现的:EVA高分子防水卷材,它由以下重量份数比的原料制成:
EVA 90~100
天然橡胶 10~0
抗氧剂CA 01~0.3
防老剂2246 1~2
硬脂酸 0.2~1
ZnO 0.2~3
DCP 0.2~1
二丁酯 5~30
填料 0~100。
天然橡胶的作用是提高产品的耐低温性。
所述的填料由超细活性碳酸钙和绢白粉组成,它们的重量比为3∶7。
过氧化异丙苯(DCP)的重量比影响所述的防水卷材的交联性。
为了制得多彩的防水卷材,所述的原料中还包括颜料,颜料的用量根据需要调制。
填料和颜料的搭配使用,还可制得透明的防水卷材。
所述EVA高分子防水卷材制作工艺包括以下步骤:
(1)配料:按配方分别称取原料组份;
(2)捏合:将原料加入捏合机内捏合,捏合机上顶栓压力为0.3~0.4M Pa,温度为80~100℃,时间8~10分钟;混合用高速混合机,温度为80~100℃;
(3)造粒:使用双螺杆挤出机造粒,双螺杆挤出机的三个温区的温度为110℃、130℃、140℃;
(4)挤出定型:挤出采用单螺杆挤出机,挤出机温区为:100℃、105℃、120℃、125℃、130℃、140℃、150℃,定型采用三滚压延机生产线;
(5)冷却:常温水冷;
(6)收卷。
本发明所述的EVA高分子防水卷材,具有类似橡胶弹性的热塑性,耐腐蚀,耐老化,耐酸碱,抗拉强度高,抗渗力强,易粘结,变形适应力强,适应温度范围广,无毒无味,适用于桥梁、地铁、公路、洞体、隧道、水池、人工湖、地下室等工程防水防渗,特别适用于拱顶内面的防水工程。
本发明所述的EVA高分子防水卷材的主要性能指标及检测结果如下表:
具体实施方式
以下结合具体实施例对本发明作进一步说明。
实施例1:非交联型EVA高分子防水卷材
一种EVA高分子防水卷材,它由以下重量份数比的原料制成:
EVA 100
抗氧剂CA 0.1
防老剂2246 1
硬脂酸 0.2
ZnO 0.2
DCP 0.2
二丁酯 5
所述EVA高分子防水卷材制作工艺,包括以下步骤:
(1)配料:按配方分别称取原料组份;
(2)捏合:将原料加入捏合机内捏合,捏合机上顶栓压力为0.3M Pa,温度为80℃,时间8分钟;混合用高速混合机,温度为80℃;
(3)造粒:使用双螺杆挤出机造粒,双螺杆挤出机的三个温区的温度为110℃、130℃、140℃;
(4)挤出定型:挤出采用单螺杆挤出机,挤出机温区为:100℃、105℃、120℃、125℃、130℃、140℃、150℃,定型采用三滚压延机生产线;
(5)冷却:常温水冷;
(6)收卷。
实施例2:交联型EVA高分子防水卷材
一种EVA高分子防水卷材,它由以下重量份数比的原料制成:
EVA 90
天然橡胶 10
抗氧剂CA 0.3
防老剂2246 2
硬脂酸 1
ZnO 3
DCP 1
二丁酯 25~30
填料 100
其中,填料由超细活性碳酸钙和绢白粉组成,它们的重量比为3∶7。为了制得多彩的防水卷材,所述的原料中还包括颜料,颜料的用量根据需要调制。
所述EVA高分子防水卷材制作工艺,包括以下步骤:
(1)配料:按配方分别称取原料组份;
(2)捏合:将原料加入捏合机内捏合,捏合机上顶栓压力为0.3M Pa,温度为90℃,时间9钟;混合用高速混合机,温度为90℃;
(3)造粒:使用双螺杆挤出机造粒,双螺杆挤出机的三个温区的温度为110℃、130℃、140℃;
(4)挤出定型:挤出采用单螺杆挤出机,挤出机温区为:100℃、105℃、120℃、125℃、130℃、140℃、150℃,定型采用三滚压延机生产线;
(5)冷却:常温水冷;
(6)收卷。
实施例3:透明型EVA高分子防水卷材
一种EVA高分子防水卷材,它由以下重量份数比的原料制成:
EVA 90
天然橡胶 7
抗氧剂CA 0.2
防老剂2246 1.5
硬脂酸 0.7
ZnO 2
DCP 0.5
二丁酯 15~20
填料 60~70
其中,填料由超细活性碳酸钙和绢白粉组成,它们的重量比为3∶7。
所述的原料中还包括颜料,颜料的用量根据需要调制。
所述EVA高分子防水卷材制作工艺,包括以下步骤:
(1)配料:按配方分别称取原料组份;
(2)捏合:将原料加入捏合机内捏合,捏合机上顶栓压力为0.4M Pa,温度为100℃,时间10分钟;混合用高速混合机,温度为100℃;
(3)造粒:使用双螺杆挤出机造粒,双螺杆挤出机的三个温区的温度为110℃、130℃、140℃;
(4)挤出定型:挤出采用单螺杆挤出机,挤出机温区为:100℃、105℃、120℃、125℃、130℃、140℃、150℃,定型采用三滚压延机生产线;
(5)冷却:常温水冷;
(6)收卷。
Claims (2)
1.EVA高分子防水卷材的制作工艺,其特征在于,它由以下重量份数比的原料组成:
EVA 90~100
天然橡胶 10~0
抗氧剂CA 0.1~0.3
防老剂2246 1~2
硬脂酸 0.2~1
ZnO 0.2~3
DCP 0.2~1
二丁酯 5~30
填料 0~100
制作工艺如下:
1)、配料:按上述配比分别称取原料组份;
2)、捏合:将原料加入捏合机内捏合,捏合机上顶栓压力为0.3~0.4MPa,温度为80~100℃,捏炼时间8~10分钟;混合用高速混合机,温度为80~100℃;
3)、造粒:使用双螺杆挤出机造粒,双螺杆挤出机的三个温区的温度为110℃、130℃、140℃;
4)、挤出定型:挤出采用单螺杆挤出机,挤出机温区为:100℃、105℃、120℃、125℃、130℃、140℃、150℃,定型采用三滚压延机生产线;
5)、冷却:常温水冷;
6)、收卷。
2.根据权利要求1所述的EVA高分子防水卷材的制作工艺,其特征在于,填料由超细活性碳酸钙和绢白粉组成,它们的重量比为3∶7。