CN1834191A - 松香-氯化钙相变蓄能材料的制作方法 - Google Patents
松香-氯化钙相变蓄能材料的制作方法 Download PDFInfo
- Publication number
- CN1834191A CN1834191A CN 200610046376 CN200610046376A CN1834191A CN 1834191 A CN1834191 A CN 1834191A CN 200610046376 CN200610046376 CN 200610046376 CN 200610046376 A CN200610046376 A CN 200610046376A CN 1834191 A CN1834191 A CN 1834191A
- Authority
- CN
- China
- Prior art keywords
- rosin
- calcium chloride
- cacl
- chloride phase
- energy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
松香-氯化钙相变蓄能材料的制作方法,涉及一种建筑节能材料的制作方法,该方法为先将松香加热至熔化,再将一定比例的CaCl2粉末倒入熔化的松香中,对混合物搅拌,直至CaCl2完全熔解于松香之中,最终形成的稳定的复合材料。所述的松香、CaCl2为工业级松香、CaCl2。本发明的松香-CaCl2复合相变蓄能材料可添加到墙体、地板中使用,用于建筑室内的蓄能节能。本发明具有材料易获得,成本较低廉的优点。
Description
技术领域
本发明涉及一种建筑节能材料的制作方法,特别是涉及一种松香-CaCl2复合相变蓄能材料的制作方法。
背景技术
相变蓄能建筑材料是通过对传统建筑材料的改良而形成的一种新型的建筑节能材料,它能够在环境温度超过材料的相变温度时利用材料本身的相变进行蓄能,在温度低于材料的相变温度时发生反向的相变放出热量,实现能量的自我调节,达到降低室内温度波动,从而达到节能和提高环境舒适度的作用。相变材料(PCM)是利用相变过程中吸收或释放的热量来进行潜热蓄能的物质,具有在一定温度范围内改变其物理状态的能力。相变蓄能建筑材料是通过向传统的建筑材料中加入相变材料研制而成的。通常情况下相变蓄能材料可以添加到墙体、地板中使用,用于建筑室内的蓄能节能。但现有相变蓄能材料存在价格普遍偏高的缺点,不能被广泛的应用与推广。
发明内容
本发明的目的在于提供一种材料易得、成本较低的松香—氯化钙复合相变蓄能材料的制作方法。该方法以松香和CaCl2为原料,通过加热后的搅拌使二者分散均匀成为一种新的复合材料。这种复合材料的固—液相变温度在20℃~35℃之间,是一种非常理想的建筑用相变蓄能材料。
本发明的目的是通过以下技术方案实现的:
松香—氯化钙相变蓄能材料的制作方法:先将松香加热至熔化,再将一定比例的CaCl2粉末倒入熔化的松香中,对混合物搅拌,直至CaCl2完全熔解于松香之中。
所述的松香-CaCl2相变蓄能材料的制作方法,其松香、CaCl2为工业级松香、CaCl2。
本发明的优点与效果是:
本发明是一种材料易得、成本较低的松香—氯化钙复合相变蓄能材料的制作方法,以松香和CaCl2为原料为主要原料,原料容易获得且成本低廉。
具体实施方式
实施例1
首先将一定量的松香加热至熔化,然后将CaCl2与松香质量比为1∶50的CaCl2粉末倒入熔化的松香中,对混合物搅拌,直至CaCl2完全熔解于松香之中。最终形成的新的复合材料,固-液相变转化温度为21℃。
实施例2
首先将一定量的松香加热至熔化,然后将CaCl2与松香质量比为1∶45的CaCl2粉末倒入熔化的松香中,对混合物搅拌,直至CaCl2完全熔解于松香之中。最终形成的新的复合材料,固—液相变转化温度为23℃。
实施例3
首先将一定量的松香加热至熔化,然后将CaCl2与松香质量比为1∶30的CaCl2粉末倒入熔化的松香中,对混合物搅拌,直至CaCl2完全熔解于松香之中。最终形成的新的复合材料,固—液相变转化温度为29℃。
在应用时,生产温度应低于材料的相变温度,将固态的松香-CaCl2复合相变蓄能材料加工成颗粒,添加于墙体材料或复合地板中即可。松香-CaCl2复合相变蓄能材料能够在环境温度超过材料的相变温度时利用材料本身的相变进行蓄能,在温度低于材料的相变温度时发生反向的相变放出热量,从而达到节能和提高环境舒适度的作用。
Claims (2)
1.松香—氯化钙相变蓄能材料的制作方法,其特征在于先将松香加热至熔化,再将一定比例的CaCl2粉末倒入熔化的松香中,对混合物搅拌,直至CaCl2完全熔解于松香之中。
2.据权利要求1所述的松香—氯化钙相变蓄能材料的制作方法,其特征在于所述的松香、CaCl2为工业级松香、CaCl2。