CN1827179A - Post-surgery functional barrier film and method for preparing the same - Google Patents
Post-surgery functional barrier film and method for preparing the same Download PDFInfo
- Publication number
- CN1827179A CN1827179A CN 200510020451 CN200510020451A CN1827179A CN 1827179 A CN1827179 A CN 1827179A CN 200510020451 CN200510020451 CN 200510020451 CN 200510020451 A CN200510020451 A CN 200510020451A CN 1827179 A CN1827179 A CN 1827179A
- Authority
- CN
- China
- Prior art keywords
- medicine
- post
- barrier film
- week
- functional barrier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention is about a functional after-operation isolation membrane and method for making same. The functional after-operation isolation membrane is composed of the drugs taken by biodegradable isolation membrane host material, and the drugs contain antiphlogiston drugs, fibrin inhibitor drugs, calcium channel inhibitor drugs, anticoagulant drugs and antibiotics drugs or one or several kinds of Chinese patent drugs; while the isolation membrane host material is made of one or several kinds degradation rate differed materials, whose half-decay times are 1 week to 6 months. Alerting membrane materials kinds and charging amount, drugs kinds and charging amount and isolation membrane layers can make multifunctional, degradation rate different and drug-release characteristic different functional after-operation isolation membrane products, so as to adapt to different using demands. Experiments prove that this functional after-operation isolation membrane can effectively accelerate tissue healing after operation, diminish infection and prevent after-operation adhesions.
Description
Technical field
The invention belongs to the postoperative isolating membrane, especially for the Biodegradable high-molecular Antiadhesive film that prevents tissue adhesion.
Background technology
The exploitation of functional post-operation adhesion preventing film results from the concern of medical profession to the surgery postoperative intestinal adhesion.Surgical operation being reached can treat disease not cause serious tissue adhesion again and infect complication, is problem demanding prompt solution medically now.There are nearly various types of operation cases of ten million in the whole nation every year, and nearly all operation all relates to anti and local anti-inflammatory problem between the tissue.It not only can cause severe complication, as: can cause adhesive ileus after abdominal part, the operation on pelvis, can cause postoperative epilepsy after the operation of opening cranium, the thyroid postoperative can cause Secondary cases recurrent nerve injury etc., and is one of main reason that complication obviously increases when performing the operation once more.At present in the surgical operation, prevent that the wound surface adhesion from being the problem of not fine solution always, the present silicone oil of using clinically, hyaluronic acid, chitin glue etc., this class material all is fluid or semi-fluid condition, exist purity not high enough, use inconvenience, some operation antiblocking weak effect, even do not have the anti effect, approximately the case of 60%-70% still will produce adhesion.Recently, prevent that with absorbable physical isolation body the surgical wound surface adhesion from having good result.As: the INTERCEED fiber isolating membrane of U.S. ETHICON company exploitation, this film is to be made by the oxidation regeneration fiber, can absorb fully in 28 days in vivo.Along with the development of polymer science, macromolecular material in the application of biomedical sector more and more widely, Biodegradable Polymers particularly.In the biodegradation type macromolecular material, what research was maximum, range of application is the widest is aliphatic polyester.Existing synthesized degradable macromolecule Antiadhesive film mainly is the co-polymer membrane of polylactic acid membrane and lactic acid and glycolic.These macromolecule Antiadhesive films have certain effect to some operation antiblocking.
2003.08.20 disclosed application number is 02113330.1 Chinese patent application, " a kind of synthetic and application of post-operative adhesion-preventing material " discloses polylactic acid-polyglycolic acid copolymer processing film forming, through sterilization, after the sterilization, is used for post-operation adhesion preventing.2004.01.14 disclosed application number is 02133444.7 Chinese patent application " a kind of new material of surgical postoperative anti " disclose a kind of by biodegradable polytrimethylene carbonyl acid ester bill of materials alone become film or with other adip cluster polyester material copolymerization or blend after adopt the film forming post-operation adhesion preventing materials of conventional method such as blowing, calendering, curtain coating.Polymer began degraded after one month, finally degraded fully, thus reach the purpose of anti.2004.02.11 day disclosed application number be that 03133843.7 Chinese patent application " the band medicine of the back anti that is used to perform the operation adds the hyaluronic acid derivatives of iron ion " discloses mixed hyaluronic acid and iron chloride under the acid condition, make iron ion and hyaluronic acid full cross-linked, by forming the crosslinked derivatives of hyaluronic acids of ferrum the hyaluronan molecule amount is increased, prolong its degradation cycle.All there are some problems in above-described post-operation adhesion preventing film: preventing adhesiving effect is not satisfactory, the difficult healing of wound surface and bring some post-operative complication such as tissue infection.Reason is that these post-operation adhesion preventing films all are the positions of only adopting mechanical isolation postoperative spatially easily to stick together.
Disclose a kind of hyaluronate sodium anti thin film 2004.10.20 disclosed application number is 03116474.9 Chinese patent application " hyaluronate sodium anti thin film and preparation method thereof ", it consists of transparent hyaluronate sodium 0.1-2.0%W/V, pain is gone out and decided 0.03-1.0%W/V, carrageenan 0.1-1.5%W/V, sodium carboxymethyl cellulose 1.0-1.5%W/V.This hyaluronate sodium thin film has good antiinflammatory, pain relieving, anti function.2002.06.05 disclosed application number is an application number is that 01132250.0 Chinese patent application " self degraded epidural adhesion preventing and composite medicine slow-release biological film thereof in the body " discloses self degraded epidural adhesion preventing and composite medicine slow-release biological film thereof in a kind of body, biomembrane is made with chitin and polylactic acid, compound relevant medicine, as neurotrophy medicine, chemotherapeutic and antibiotic medicine, can play the effect of medicine local sustained release.These two pieces of patents have been considered combination drug on Antiadhesive film, and still only compound antiinflammatory, pain relieving, neurotrophy medicine, chemotherapeutic consider to reduce functions such as tissue fluid infiltration, inhibition fibrin deposition, promotion organization healing simultaneously.And carrying different medicines can only discharge simultaneously, can not reach various medicines and discharge in the time of needs.
A kind of convenience of long-term clinically expectation, safety, effectively and have the new material and a new method appearance of the anti of multiple function, be that postoperative is isolated anti and reduced the bodily tissue organ infection, reduces the tissue fluid infiltration, suppresses fibrin deposition, promotes multi-functional bonded postoperative isolating membrane such as organization healing, i.e. post-surgery functional barrier film.
Summary of the invention
Technical scheme of the present invention provides the post-surgery functional barrier film of a kind of postoperative preventing tissue infection and anti, and the preparation method of this film.
The object of the present invention is achieved like this:
Post-surgery functional barrier film provided by the invention, post-surgery functional barrier film is made up of for the host material carrying medicaments Biodegradable material, and the total amount of the wherein said medicine that carries is the 0.01-20% of isolating membrane gross weight; Described isolating membrane host material is that the material of the different degradation rates of 1 week-6 month is formed by degradation half life; In described pharmaceutical pack fibre-bearing protein inhibitor class medicine, ockers class medicine, anticoagulant class medicine, antibiotics or the Chinese patent medicine that carries one or more.
Wherein, one or more polymer that are polymerized, chitosan, collagen or hyaluronate sodium or their blend in described isolating membrane host material DL-lactic acid, L-lactic acid, glycolic, dioxane ketone, 6-caprolactone, the ethylene glycol monomer.
Further, described isolating membrane host material is made up of the material in 1 week-2 week of degradation half life, 2 week-1 month and 1 month-6 months, the host material in 1 week-2 week of degradation half life is: hyaluronate sodium or molecular weight are polymer or the chitosan of 1-10 ten thousand, the host material of degradation half life 2 week-1 month is that molecular weight is polymer or the chitosan of 10-30 ten thousand, and the host material of 1 month degradation half life phase-6 month is that collagen or molecular weight are polymer or the chitosan of 30-150 ten thousand.Wherein, the material weight percentage ratio in 1 week-2 week of degradation half life in the described isolating membrane host material, 2 week-1 month and 1 month-6 months is 0-50%, 1-80%, 0-50%.
In the technique scheme, the described medicine that carries comprises one or more in anti-inflammatory type medicine, fibrin inhibitor class medicine, ockers class medicine, anticoagulant class medicine, antibiotics or the Chinese patent medicine; The described medicine that carries is counted 0.01-5% with the post-surgery functional barrier film total weight percent.
Further, described antibiotics is: one or more in streptomycin, gentamycin, kanamycin, tetracycline or the erythromycin; Described hormone medicine is: one or more in dexamethasone, hydrocortisone, cortisone, prednisolone or the prednisone; Described fibrin inhibitor class medicine is: one or more in hyaluronidase, streptokinase, urokinase, trypsin or the plasminogen; Described ockers class medicine is: one or more in diltiazem hydrochloride, nifedipine, hydrochloric acid verapamil, bepridil or the sparteine; Described anticoagulant class medicine is: one or more in dicoumarol, hirudin, heparin, dextran or the polysaccharide dextrin; Described Chinese patent medicine class medicine is: one or more in YUNNAN BAIYAO, Radix Salviae Miltiorrhizae, the Radix Astragali, Radix Et Rhizoma Rhei or the soap pin; Described anti-inflammatory type medicine is: ibuprofen, hydroxyl phenylbutazone, indomethacin, in acetamido phenol or the piroxicam one or more.
Isolating membrane provided by the invention can be made up of one deck or two-layer above thin film, medicine be carried in the single thin film or thin film and thin film between.
One of preparation method of post-surgery functional barrier film provided by the invention is that one or more materials and one or more medicine blend are adopted conventional method, blowing, calendering or casting film-forming.Two of the preparation method of post-surgery functional barrier film provided by the invention is that one or more materials adopt conventional method carrying medicaments such as grafting, absorption and parcel in the polymer after conventional method film forming such as blowing, calendering, curtain coating.Also can two kinds of methods be used in combination, carry certain medicine during the system film, carry other medicine after the film forming again.It is the 0.001-5 millimeter that film is processed into thickness, is cut into the sheet material of different sizes, behind sterilization, gets corresponding film according to the size of need anti position area in the surgery art and is used for anti.
Post-surgery functional barrier film provided by the invention has better elastic and pliability, can overcome the shortcoming of the Antiadhesive film of reporting in the past, except the easy adhesion organization of mechanical isolation postoperative, carrying medicaments can effectively reduce the bodily tissue organ infection in the release of operative site, reduce the tissue fluid infiltration, suppress fibrin deposition, promote organization healing and prevent tissue adhesion etc., and owing to be used in combination the base material of different degradation rates, according to clinical application require can so that various medicine time of needs along with different base material degradeds discharges, reach anti and have the effect of other multiple functions.The release characteristic of medicine can be by material degraded speed, medicine in film diffusion velocity and the means such as the thin film number of plies of isolating membrane regulated.Prove through biotic experiment, zoopery and safety testing, made functional film is not found toxicity, stimulation and pyrogen reaction, and biocompatibility is good, can obviously reduce the postoperative tissue infection, promote organization healing, can effectively prevent behind the vertebrae plate resection tissue adhesion of fibrosis and adhesion around the dura mater, operation on tendon, enteric cavity operation, operation on heart, operation on biliary tract, cranial cavity operation etc.
Description of drawings
The variation of weight and polymer molecular weight after the postoperative isolating membrane of Fig. 1 embodiment two is imbedded in the animal body.
The variation of weight and polymer molecular weight after the postoperative isolating membrane of Fig. 2 embodiment three is imbedded in the animal body.
The postoperative isolating membrane of Fig. 3 embodiment two is imbedded at back drug release behavior in the animal body.
The postoperative isolating membrane of Fig. 4 embodiment three is imbedded at back drug release behavior in the animal body.
The invention will be further described below in conjunction with specific embodiments and the drawings, but should not be construed as is limitation of the invention further, according to foregoing of the present invention, ordinary skill knowledge and customary means according to this area, do not breaking away under the above-mentioned basic fundamental thought of the present invention prerequisite, the technical scheme that modification, replacement or change realized of making other various ways all belongs to scope of the present invention.
Specific embodiment
Embodiment one:
Get the poly-D of 10 gram-molecular weights 400,000, L-lactic acid and 0.2 gram cortisone add in 100 milliliters of ethyl acetate, fully behind the dissolving mixing, pour film forming in the dull and stereotyped container into, ethyl acetate fully being volatilized make thickness is 0.04 millimeter thin film, be cut into the sheet material of 4 * 6 (millimeters), 10 * 20 (millimeters) and 50 * 80 (millimeters), keep in Dark Place standby through sterilization, the sealing of sterilization treatment final vacuum.
Embodiment two:
Get the D of 10 gram-molecular weights 150,000, L-lactic acid, glycolic and caprolactone copolymer add in 100 milliliters of acetone, fully the dissolving back adds 0.15 gram gentamycin, 0.15 gram dexamethasone, fully behind the mixing, pour film forming in the dull and stereotyped container into, acetone fully being volatilized make thickness is 0.08 millimeter thin film, be cut into the sheet material of 4 * 6 (millimeters), 10 * 20 (millimeters) and 50 * 80 (millimeters), keep in Dark Place standby through sterilization, the sealing of sterilization treatment final vacuum.
Embodiment three:
Get the poly-D of 5 gram-molecular weights 350,000, L-lactic acid adds 50 milliliters of ethyl acetate, and fully the dissolving back adds 0.15 gram hydrocortisone, fully behind the mixing, pours film forming in the dull and stereotyped container into, and ethyl acetate fully being volatilized make thickness is 0.03 millimeter topmost thin film.Get the D of 3 gram-molecular weights 150,000, L-lactic acid and ethanol copolymer add 50 milliliters of ethyl acetate, and fully the dissolving back adds 0.15 gram nifedipine, fully behind the mixing, pour film forming in the dull and stereotyped container into, ethyl acetate fully being volatilized make thickness is 0.02 millimeter middle layer film.Get 2 gram-molecular weights, 50,000 poly-D, L-lactic acid and ethylene glycol copolymer add in 20 milliliters of acetone, and fully the dissolving back adds that mycin of 0.15 gram calorie, fully behind the mixing, pour film forming in the dull and stereotyped container into, acetone fully being volatilized make thickness is 0.01 millimeter bottom film.It is 0.06 millimeter film that upper strata, middle level and the underlying membrane of preparation rolled into thickness together, is cut into the sheet material of 4 * 6 (millimeters), 10 * 20 (millimeters) and 50 * 80 (millimeters), through sterilize, the sterilization treatment final vacuum seal keep in Dark Place standby.
Embodiment four:
Preparation method is with embodiment 3, only different is carrying medicaments not.
Embodiment five:
Get the D of 8 gram-molecular weights 250,000, L-lactic acid and dioxane ketone copolymers, the chitosan of 1 gram collagen and 1 gram-molecular weight 50,000 adds in 100 milliliters of acetone, fully the dissolving back adds 0.15 gram indomethacin, 0.15 gram heparin, 0.7 gram Radix Salviae Miltiorrhizae powder, fully behind the mixing, pour film forming in the dull and stereotyped container into, acetone fully being volatilized make thickness is 0.1 millimeter thin film, be cut into the sheet material of 4 * 6 (millimeters), 10 * 20 (millimeters) and 50 * 80 (millimeters), keep in Dark Place standby through sterilization, the sealing of sterilization treatment final vacuum.
Embodiment six:
Getting the L-lactic acid of 8 gram-molecular weights 150,000 and the chitosan of caprolactone copolymer and 1 gram-molecular weight 50,000 adds in 100 milliliters of acetone, fully adds 0.15 gram indomethacin after the dissolving, 0.15 gram bepridil, fully behind the mixing, pour film forming in the dull and stereotyped container into, acetone fully being volatilized make thickness is 0.2 millimeter thin film.In the urokinase of thin film immersion 2%, take out after 2 hours, after the lyophilization, be cut into the sheet material of 4 * 6 (millimeters), 10 * 20 (millimeters) and 50 * 80 (millimeters), keep in Dark Place standby through sterilization, the sealing of sterilization treatment final vacuum.
Embodiment seven:
Getting the L-lactic acid of 8 gram-molecular weights 200,000 and the chitosan of dioxane ketone copolymers and 1 gram-molecular weight 50,000 adds in 100 milliliters of acetone, fully adds 0.15 gram prednisolone after the dissolving, fully behind the mixing, pour film forming in the dull and stereotyped container into, acetone fully being volatilized make thickness is 0.2 millimeter thin film.Add streptokinase and Radix Astragali mixed dust formulation between two thin film, roll film forming, be cut into the sheet material of 4 * 6 (millimeters), 10 * 20 (millimeters) and 50 * 80 (millimeters), keep in Dark Place standby through sterilization, the sealing of sterilization treatment final vacuum.
Prove that through biotic experiment, zoopery and safety testing made functional film is not found toxicity, stimulation and pyrogen reaction.
Below in conjunction with concrete test beneficial effect of the present invention is described in further detail.
Experimental example 1: the vivo degradation of postoperative isolating membrane and drug release test test
Select 8 of healthy adult rabbit, male and female are not limit, body weight 2.0-2.5 kilogram, the pentobarbital sodium with 1.5% (2ml/Kg) rabbit ear vein injecting anesthetic.Select six places at the back, aseptic following postoperative isolating membrane at every place subdermal implantation 10 * 20 (millimeter).The isolating membrane of preparation among 4 rabbit subdermal implantation embodiment two wherein, the isolating membrane of preparation among other 4 heeling-in embodiment three.Open operative site after surgery 1,2,3,4,5,6 weeks and take out film, the drip washing of pH7.4 phosphate buffer, drying is weighed.With the molecular weight of gel permeation chromatography polymer, measure left drug content in the film with the pharmacopeia prescriptive procedure.Fig. 1 and Fig. 2 are respectively the isolating membrane weight of embodiment two and embodiment three and the change curve of polymer molecular weight, and Fig. 3 is the release profiles of two kinds of medicines in the isolating membrane of embodiment two, and Fig. 4 is the release profiles of three kinds of medicines in the isolating membrane of embodiment three.Postoperative isolating membrane polymer molecular weight reduces comparatively fast in time, and weight is slower in the minimizing in early stage, to the 6th week, and the equal complete obiteration of postoperative isolating membrane.The medicine that the postoperative isolating membrane carries presents the gradient release characteristic, as shown in Figure 4 in the isolating membrane of embodiment three, kanamycin continues to have discharged 90% in 0-2 week, and the nitro Horizon continues to have discharged 80% in 1-4 week, and hydrocortisone continues to have discharged 70% in 2-5 week.Evidence is by host material, the diffusion velocity of medicine in film and the version of plural layers of different degradation rates, the release characteristic of scalable postoperative isolating membrane Chinese medicine, to satisfy the requirement of clinical application, make the postoperative isolating membrane in the easy adhesion organization of mechanical isolation, have the bodily tissue of reducing organ infection, reduce multiple functions such as tissue fluid is permeated, inhibition fibrin deposition, promotion organization healing, and these functions are with more effective inhibition tissue adhesion's generation.
Experimental example 2: tissue adhesion test behind the operation on peritoneum of postoperative isolating membrane
Select 6 of healthy adult rabbit, male and female are not limit, body weight 2.0-2.5 kilogram, the pentobarbital sodium with 1.5% (2ml/Kg) rabbit ear vein injecting anesthetic.The center line laparotomy ventrotomy selects three places as experimental point, and the parietal peritoneum of 20 * 40 * 1 millimeter of excision is dissected at every place, and the serosa surface of contiguous large intestine is swiped with dissecting knife, until the bleeding that the speckle redness occurs.Two place's experimental points are used not pastille antiadhesion barrier (isolating membrane that does not add medication preparation among the embodiment four) of pastille postoperative antiadhesion barrier (isolating membrane of embodiment three preparations), polymer respectively therein, and another place does blank contrast and uses.Part is used to estimate preventing adhesiving effect between excision parietal peritoneum and contiguous large intestine serous coat.Postoperative 5 all rabbits kill with excessive pentobarbital, and the adhesion evaluation criterion is: 0 grade: no adhesion; 1 grade: separable film like adhesion is lower than 10% of test area; 2 grades: inseparable slight adhesion is lower than 30% of test area; 3 grades: inseparable moderate adhesion is the 30-60% of test area; 4 grades: serious adhesion is more than 60% of test area, complete filling defective, the hard and fine and close adhesion of quality.Table 1 is tissue adhesion's classification results, shows that pastille postoperative antiadhesion barrier group obviously is better than not pastille antiadhesion barrier group and blank group.All there is significant difference (p＜0.05) in statistical disposition pastille postoperative antiadhesion barrier group with matched group with pastille antiadhesion barrier group not, pastille antiadhesion barrier group and do not have significant difference (p＜0.05) between pastille antiadhesion barrier group.
The preventing adhesiving effect of the isolating membrane of table 1 embodiment three preparations
| Rabbit number | 1 | 2 | 3 | 4 | 5 | 6 | Meansigma methods | |
| Adhesion area (%) | | 0 | 5 | 5 | 0 | 5 | 5 | - |
| Pastille film group not | 20 | 10 | 40 | 25 | 35 | 15 | - | |
| Matched | 80 | 80 | 75 | 90 | 100 | 100 | - | |
| The adhesion grade | | 0 | 1 | 0 | 0 | 1 | 1 | 0.5 |
| Pastille film group not | 2 | 1 | 3 | 2 | 3 | 2 | 2.2 | |
| Matched | 4 | 4 | 4 | 4 | 4 | 4 | 4.0 | |
In a word, post-surgery functional barrier film provided by the invention is except the easy adhesion organization of mechanical isolation postoperative, carrying medicaments can effectively reduce the bodily tissue organ infection in the release of operative site, reduces the tissue fluid infiltration, suppress fibrin deposition, promotes organization healing and prevent tissue adhesion etc., and the degraded speed by material, the medicine diffusion velocity and the means such as the thin film number of plies of isolating membrane in film are regulated and can effectively be prevented tissue adhesion.
Claims (9)
1. post-surgery functional barrier film, it is characterized in that: described post-surgery functional barrier film is made up of for the host material carrying medicaments Biodegradable material, and wherein, the described medicine that carries accounts for the 0.01-20% of post-surgery functional barrier film gross weight; Described isolating membrane host material is that the barrier material of one or more degradation rates of 1 week-6 month is formed by degradation half life; In described pharmaceutical pack fibre-bearing protein inhibitor class medicine, ockers class medicine, anticoagulant class medicine, antibiotics or the Chinese patent medicine that carries one or more.
2. post-surgery functional barrier film according to claim 1 is characterized in that: one or more polymer that are polymerized, chitosan, collagen or hyaluronate sodium or their blend in described isolating membrane host material DL one lactic acid, L one lactic acid, glycolic, dioxane ketone, ε one caprolactone, the ethylene glycol monomer.
3. post-surgery functional barrier film according to claim 2, it is characterized in that: described isolating membrane host material is made up of the material in 1 week-2 week of degradation half life, 2 week-1 month and 1 month-6 months, wherein the host material in 1 week-2 week of degradation half life is: hyaluronate sodium or molecular weight are polymer or the chitosan of 1-10 ten thousand, the host material of degradation half life 2 week-1 month is that molecular weight is polymer or the chitosan of 10-30 ten thousand, and 1 month-6 months host material of degradation half life is that collagen or molecular weight are polymer or the chitosan of 30-150 ten thousand.
4. post-surgery functional barrier film according to claim 3 is characterized in that: the material weight percentage ratio in 1 week-2 week of degradation half life in the described isolating membrane host material, 2 week-1 month and 1 month-6 months is 0-50%, 1-80%, 0-50%.
5. post-surgery functional barrier film according to claim 4 is characterized in that: the described medicine that carries comprises one or more in anti-inflammatory type medicine, fibrin inhibitor class medicine, ockers class medicine, anticoagulant class medicine, antibiotics or the Chinese patent medicine; The described medicine that carries accounts for the 0.01-5% of post-surgery functional barrier film gross weight.
6. post-surgery functional barrier film according to claim 5 is characterized in that: described antibiotics is: one or more in streptomycin, gentamycin, kanamycin, tetracycline or the erythromycin; Described hormone medicine is: one or more in dexamethasone, hydrocortisone, cortisone, prednisolone or the prednisone; Described fibrin inhibitor class medicine is: one or more in hyaluronidase, streptokinase, urokinase, trypsin or the plasminogen; Described ockers class medicine is: one or more in diltiazem hydrochloride, nifedipine, hydrochloric acid verapamil, bepridil or the sparteine; Described anticoagulant class medicine is: one or more in dicoumarol, hirudin, heparin, dextran or the polysaccharide dextrin; Described Chinese patent medicine class medicine is: one or more in YUNNAN BAIYAO, Radix Salviae Miltiorrhizae, the Radix Astragali, Radix Et Rhizoma Rhei or the soap pin; Described anti-inflammatory type medicine is: ibuprofen, hydroxyl phenylbutazone, indomethacin, in acetamido phenol or the piroxicam one or more.
7. according to each described post-surgery functional barrier film of claim 1-6, it is characterized in that: isolating membrane is made up of one deck or two-layer above thin film, medicine be carried in the single thin film or thin film and thin film between.
8. prepare the method for the described post-surgery functional barrier film of claim 7, it is characterized in that: host material and one or more medicine blend, adopt blowing, calendering or casting film-forming.
9. prepare the described post-surgery functional barrier film method of claim 7, it is characterized in that: one or more materials adopt grafting, absorption and parcel form to carry one or more medicines after method film forming such as blowing, calendering, curtain coating in the polymer.