CN1824438A - Preparation method of nano-cobalt powder - Google Patents
Preparation method of nano-cobalt powder Download PDFInfo
- Publication number
- CN1824438A CN1824438A CN 200610067164 CN200610067164A CN1824438A CN 1824438 A CN1824438 A CN 1824438A CN 200610067164 CN200610067164 CN 200610067164 CN 200610067164 A CN200610067164 A CN 200610067164A CN 1824438 A CN1824438 A CN 1824438A
- Authority
- CN
- China
- Prior art keywords
- minutes
- millitorrs
- cobalt
- temperature
- operating pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a method for preparing nano cobalt powder. Said method includes the following steps: dissolving cobalt oxalate [CoC2O4.2H2O] crystal powder in ammonia water to obtain clear cobalt ammonia complex solution; using universal nitrogen gas spray gun to make the above-mentioned clear solution be dispersed in liquid nitrogen and prefrozen; placing the above-mentioned obtained frozen material into a freeze-drying machine and vacuum-drying to obtain precursor body; making the dried precursor body undergo the process of hydrogen gas reduction, hydrogen gas flow rate is 0.1cu.m/hr-0.3cu.m/hr, reducing at 200deg.C-400deg.C, heat-insulating for 2-8hr so as to obtain the invented nano cobalt powder.
Description
Technical field
A kind of preparation method of nano-cobalt powder belongs to powder metallurgical technology.
Background technology
Cobalt, hard, malleable pewter metal is rich in gloss.Abundance is 0.0025% in the earth's crust.China is world's second largest cobalt producing country, it also is the second largest country of consumption of refining cobalt, 1998 to 2004 according to statistics, the annual average rate of increase of China's refining cobalt consumption figure is 20.7%, refining cobalt consumption figure reached 9500 tons in 2004, and wherein battery industry is first consumer field, accounts for 57%, the colour glaze industry accounts for 14%, and magnetic material accounts for 8%.Japan is the big cobalt of the first in the world country of consumption, and 60% is used in field of batteries, the third-largest cobalt country of consumption U.S., and 55% is used to make super carbide alloy.
Super-fine cobalt powder shows the performance of many excellences owing to its special physics, chemical property in the application in fields such as carbide alloy, battery, catalyst, magnetic material, absorbing material, pottery.For example, make the permanent magnetism recording materials, can make the packing density of tape and soft or hard dish improve tens of times, and can improve their fidelity performance significantly with super-fine cobalt powder.Simultaneously because super-fine cobalt powder to electromagnetic special absorption, can be used as military high-performance millimeter wave stealth material, visible light, infrared ray stealth material and structural formula stealth material, mobile phone radiation shielding material.The super-fine cobalt powder that uses aspect carbide alloy makes it have higher wearability and crack resistance because cross-breaking strength, hardness and the density of alloy all are improved.If can be at cobalt powder particularly in the preparation of super-fine cobalt powder with use and get along with, to making full use of resource, increasing economic efficiency, shorten and developed country between gap all significant.
The result of literature survey shows that Freeze Drying Technique prepares the research of nano-cobalt powder, does not also have relevant report so far both at home and abroad.
Summary of the invention
Adopt the present invention to prepare nano-cobalt powder, its technology is very simple, and is low for equipment requirements, and raw material cheaply is easy to get.Reduction temperature of the present invention hangs down about 300 ℃ than the reduction temperature of common industry law, greatly reduces energy consumption.Cobalt powder good dispersion, narrow particle size distribution, the pattern prepared are even, and do not need to add surfactant, have avoided the introducing of impurity element.
The preparation method of a kind of nano-cobalt powder provided by the present invention is characterized in that: it may further comprise the steps:
1) with cobalt oxalate [CoC
2O42H
2O] crystal powder is dissolved in the ammoniacal liquor cobalt ammonia complex solution that must clarify;
2) use general nitrogen spray gun, above-mentioned settled solution is dispersed in pre-freeze in the liquid nitrogen;
3) scars after the pre-freeze in the above-mentioned liquid nitrogen are placed freeze dryer carry out vacuum drying and obtain presoma;
4) above-mentioned dried presoma is carried out hydrogen reducing, hydrogen flowing quantity is 0.1 cubic metre/hour~0.3 cubic metre/hour, and 200 ℃~400 ℃ reduction are incubated 2 hours~8 hours and obtain nano-cobalt powder.
Step 2) described nitrogen spray gun, its pressure is 1.5 atmospheric pressure~3.5 atmospheric pressure.
The described vacuum drying of step 3), wherein the performing a programme of freeze dryer is: the operating pressure in 0 minute~2000 minutes is that 450 millitorrs, temperature are-20 ℃; Operating pressure in 2000 minutes~3700 minutes is that 300 millitorrs, temperature are-11 ℃; Operating pressure in 3700 minutes~5000 minutes is that 150 millitorrs, temperature are-6 ℃; Operating pressure in 5000 minutes~5800 minutes is that 80 millitorrs, temperature are 0 ℃; Operating pressure in 5800 minutes~6000 minutes is that 5 millitorrs, temperature are 15 ℃.
The present invention adopts liquid nitrogen pre-freeze-freeze-drying, can prevent the poly-partially and crystallization of solution component, obtains amorphous powder simultaneously.By the low temperature hydrogen reduction, obtain the cobalt powder of nano level crystallite dimension again.
Can know that from the X diffracting spectrum of Fig. 1 the thing phase composition of final products only has cobalt.
From the image of the field emission scanning electron microscope of Fig. 2 as can be seen, the powder size distribution that adopts the method for liquid nitrogen pre-freeze-freeze drying-hydrogen reducing to obtain is even, and particle is about the powder of 40-50nm.
Hence one can see that, and with the obvious refinement of powder crystal grain of desivac preparation, size reaches nanoscale, thereby can improve surface-active, surperficial purity, specific area, has great skin effect and bulk effect.
Description of drawings
Fig. 1: the nano-powder X diffracting spectrum of preparation method's example 1 of the present invention;
Fig. 2: the nano-powder FESEM picture of preparation method's example 1 of the present invention;
The specific embodiment
Example 1: get cobalt oxalate [CoC
2O
42H
2O] pink crystal powder 50 grams are dissolved in 250 milliliters of ammoniacal liquor and get the brown settled solution.Use the nitrogen spray gun, spray gun pressure is 3.5 atmospheric pressure, and the mixed solution of clarifying is dispersed in the liquid nitrogen.Scars with liquid nitrogen frozen place the FTD Dura-stop MP of FTS company type freeze dryer to carry out vacuum drying again, and the performing a programme of freeze dryer is: the operating pressure in 0 minute~2000 minutes is that 450 millitorrs, temperature are-20 ℃; Operating pressure in 2000 minutes~3700 minutes is that 300 millitorrs, temperature are-11 ℃; Operating pressure in 3700 minutes~5000 minutes is that 150 millitorrs, temperature are-6 ℃; Operating pressure in 5000 minutes~5800 minutes is that 80 millitorrs, temperature are 0 ℃; Operating pressure in 5800 minutes~6000 minutes is that 5 millitorrs, temperature are 15 ℃.Adopt the presoma of hydrogen reducing freeze-drying, hydrogen flowing quantity is 0.3 cubic metre/hour, and 200 ℃ of reduction temperatures are incubated 7 hours, obtain the nano-cobalt powder that crystallite dimension is 45.5nm.
Example 2: get cobalt oxalate [CoC
2O
42H
2O] pink crystal powder 50 grams are dissolved in 250 milliliters of ammoniacal liquor and get the brown settled solution.Use the nitrogen spray gun, spray gun pressure is 1.5 atmospheric pressure, and the mixed solution of clarifying is dispersed in the liquid nitrogen.Scars with liquid nitrogen frozen place the FTD Dura-stop MP of FTS company type freeze dryer to carry out vacuum drying again, and the performing a programme of freeze dryer is: the operating pressure in 0 minute~2000 minutes is that 450 millitorrs, temperature are-20 ℃; Operating pressure in 2000 minutes~3700 minutes is that 300 millitorrs, temperature are-11 ℃; Operating pressure in 3700 minutes~5000 minutes is that 150 millitorrs, temperature are-6 ℃; Operating pressure in 5000 minutes~5800 minutes is that 80 millitorrs, temperature are 0 ℃; Operating pressure in 5800 minutes~6000 minutes is that 5 millitorrs, temperature are 15 ℃.Adopt the presoma of hydrogen reducing freeze-drying, hydrogen flowing quantity is 0.1 cubic metre/hour, and 400 ℃ of reduction temperatures are incubated 2 hours, obtain the nano-cobalt powder that crystallite dimension is 57.3nm.
Example 3: get cobalt oxalate [CoC
2O
42H
2O] pink crystal powder 50 grams are dissolved in 250 milliliters of ammoniacal liquor and get the brown settled solution.Use the nitrogen spray gun, spray gun pressure is 2.5 atmospheric pressure, and the mixed solution of clarifying is dispersed in the liquid nitrogen.Scars with liquid nitrogen frozen place the FTD Dura-stop MP of FTS company type freeze dryer to carry out vacuum drying again, and the performing a programme of freeze dryer is: the operating pressure in 0 minute~2000 minutes is that 450 millitorrs, temperature are-20 ℃; Operating pressure in 2000 minutes~3700 minutes is that 300 millitorrs, temperature are-11 ℃; Operating pressure in 3700 minutes~5000 minutes is that 150 millitorrs, temperature are-6 ℃; Operating pressure in 5000 minutes~5800 minutes is that 80 millitorrs, temperature are 0 ℃; Operating pressure in 5800 minutes~6000 minutes is that 5 millitorrs, temperature are 15 ℃.Adopt the presoma of hydrogen reducing freeze-drying, hydrogen flowing quantity is 0.2 cubic metre/hour, and 300 ℃ of reduction temperatures are incubated 2 hours, obtain the nano-cobalt powder that crystallite dimension is 40.7nm.
Example 4: get cobalt oxalate [CoC
2O
42H
2O] pink crystal powder 50 grams are dissolved in 250 milliliters of ammoniacal liquor and get the brown settled solution.Use the nitrogen spray gun, spray gun pressure is 2.0 atmospheric pressure, and the mixed solution of clarifying is dispersed in the liquid nitrogen.Scars with liquid nitrogen frozen place the FTD Dura-stop MP of FTS company type freeze dryer to carry out vacuum drying again, and the performing a programme of freeze dryer is: the operating pressure in 0 minute~2000 minutes is that 450 millitorrs, temperature are-20 ℃; Operating pressure in 2000 minutes~3700 minutes is that 300 millitorrs, temperature are-11 ℃; Operating pressure in 3700 minutes~5000 minutes is that 150 millitorrs, temperature are-6 ℃; Operating pressure in 5000 minutes~5800 minutes is that 80 millitorrs, temperature are 0 ℃; Operating pressure in 5800 minutes~6000 minutes is that 5 millitorrs, temperature are 15 ℃.Adopt the presoma of hydrogen reducing freeze-drying, hydrogen flowing quantity is 0.3 cubic metre/hour, and 250 ℃ of reduction temperatures are incubated 5 hours, obtain the nano-cobalt powder that crystallite dimension is 52.7nm.
Claims (3)
1, a kind of preparation method of nano-cobalt powder is characterized in that, it may further comprise the steps:
1) with cobalt oxalate [CoC
2O
42H
2O] crystal powder is dissolved in the ammoniacal liquor cobalt ammonia complex solution that must clarify;
2) use general nitrogen spray gun, above-mentioned settled solution is dispersed in pre-freeze in the liquid nitrogen;
3) scars after the pre-freeze in the above-mentioned liquid nitrogen are placed freeze dryer carry out vacuum drying and obtain presoma;
4) above-mentioned dried presoma is carried out hydrogen reducing, hydrogen flowing quantity is 0.1 cubic metre/hour~0.3 cubic metre/hour, and 200 ℃~400 ℃ reduction are incubated 2 hours~8 hours and obtain nano-cobalt powder.
2, nano-cobalt powder preparation method according to claim 1 is characterized in that: step 2) described pre-freeze, nitrogen spray gun wherein, its pressure is 1.5 atmospheric pressure~3.5 atmospheric pressure.
3, nano-cobalt powder preparation method according to claim 1 is characterized in that: the described vacuum drying of step 3), and wherein the performing a programme of freeze dryer is: the operating pressure in 0 minute~2000 minutes is that 450 millitorrs, temperature are-20 ℃; Operating pressure in 2000 minutes~3700 minutes is that 300 millitorrs, temperature are-11 ℃; Operating pressure in 3700 minutes~5000 minutes is that 150 millitorrs, temperature are-6 ℃; Operating pressure in 5000 minutes~5800 minutes is that 80 millitorrs, temperature are 0 ℃; Operating pressure in 5800 minutes~6000 minutes is that 5 millitorrs, temperature are 15 ℃.