CN1814676A - High-strength water-resistant putty powder - Google Patents
High-strength water-resistant putty powder Download PDFInfo
- Publication number
- CN1814676A CN1814676A CN 200610042486 CN200610042486A CN1814676A CN 1814676 A CN1814676 A CN 1814676A CN 200610042486 CN200610042486 CN 200610042486 CN 200610042486 A CN200610042486 A CN 200610042486A CN 1814676 A CN1814676 A CN 1814676A
- Authority
- CN
- China
- Prior art keywords
- powder
- putty powder
- strength water
- ultramarine
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention discloses a high intensity water-proof putty material suitable for metope decoration in the following proportion: double-fly powder: 30-70, ash calcium powder: 30-70, methyl-fibrin: 0.025-1.5 and French blue: 0.02-0.15, in which, white cement, cassava starch and natural free of radioactivity color stone powder are added to produce color putty.
Description
Technical field
The invention belongs to a kind of putty powder material for building, a kind of specifically high-strength water-proof putty powder that is applicable to that the indoor and outdoor metope is used.
Background technology
Along with the development of technology, the plastering material of the decorative wall that uses in the modern architecture is more and more.Existingly whitewash the putty powder that the indoor and outdoor metope is used, have following defective in the application; 1, general wall plastering operation is first brushing putty powder, and the brushing emulsion paint because twice construction brought the expense material, is taken a lot of work again, and is time-consuming, the cost height.2, the existing disposable putty powder surface color and polish dullness of whitewashing, not bright-coloured, whiteness is not high.3, putty powder whitewashes the back intensity difference, and is not wear-resisting, not water-fast, not corrosion-resistant, easily goes mouldy.4, the sun be exposed to the sun and cold snap easy to crack, elephant skin.Because the existence of these defectives has brought inconvenience for construction and life staying idle at home.
Summary of the invention
The objective of the invention is to be to provide a kind of wall fitting to whitewash one-off construction, bright in luster, the whiteness height, strong adhesion does not ftracture, the intensity height, water-fast, wear-resisting, scrubbing resistance, corrosion-resistant, be difficult for going mouldy, produce easily, cost is low, easy construction, the high-strength water-proof putty powder with multicolour.
Putty powder of the present invention is made by following component: (consumption is a weight part)
Dry powder 30-70
Ash calcium powder 30-70
Methylcellulose gum 0.25-1.5
Or Vltra tears
Ultramarine 0.02-0.15
The invention provides a kind of high water-proof putty powder of intensity for the exterior wall use, the weight proportion of each component is
Dry powder 30-70
Ash calcium powder 25-40
White cement 15-30
Methylcellulose gum 0.3-1.5
Or Vltra tears
Ultramarine 0.02-0.05
Tapioca (flour) 0.1-1
The invention provides a kind of beautiful smooth and bright like a mirror high-strength water-proof putty powder of color for the interior wall use, the weight proportion of its each raw material is
Dry powder 30-70
Ash calcium powder 30-70
Methylcellulose gum 0.25-1.0
Or Vltra tears
Ultramarine 0.02-0.15
Tapioca (flour) 0.1
The quality of each component of putty powder of the present invention is:
The dry powder fineness is the 300-500 order, and whiteness is the 90-98 degree, and the whiteness height can strengthen metope hardness.
Ash calcium powder fineness is 325 orders, and whiteness is that whiteness is pure more than 90, and sulphur, phosphorus content are low, the fineness height, and Calcium of intensifiens content height, viscosity is good.Be used for coating and can reduce the fine particle calcium carbonate consumption, increase the water tolerance of coating, scrub resistance strengthens metope hardness, easy construction.
White cement is 425 labels.
The methylcellulose gum fineness is 325 orders, and viscosity is 6-14 ten thousand, the viscosity height, and viscosity is strong.
The ultramarine fineness is 325 orders, pH value 6.5-7.5, and free sulphur content is less than 1.5%, and volatile content is less than 1.0%.Have whitening effect, can eliminate and lower yellow color spot in the coating, and alkaline-resisting, high temperature resistant, in atmosphere, under Exposure to Sunlight, the wind and rain condition, stable performance.
The fineness of tapioca (flour) is 200 orders, and starch content is greater than 85%, and moisture is less than 13%, PH 5-7, and whiteness 90, glossy, free from extraneous odour can play the effect that increases sticking power.
The natural "dead" color ore powder that the present invention adds, for example emerald green stone flour, purplish red stone flour, the Peal blackberry stone flour, sapphire blue stone flour, Chrysan Yellow stone flour etc., by natural "dead" colored stone, fragmentation is milled into powder, sieves to form, and fineness is the 325-800 order.Requirement that can be different according to the color depth, the natural "dead" color ore powder of interpolation different quantities is produced colored high-strength water-proof putty powder.
The production method of putty powder of the present invention is, according to prescription provided by the invention, above-mentioned each component accurately taken by weighing, and fully mixes to get final product.
Putty powder of the present invention is easy to use, and product of the present invention is added clear water, stirs into a paste, and after 20 minutes, with the putty powder cream that stirs, criticizes and scrapes on metope thickness 0.1-0.3 millimeter.Metope is criticized and is scraped once after doing.Treat that metope is done soon and receive light when tack-free, do back wall color light, smooth and bright like a mirror; The intensity height, water-fast anti-wiping, not shedding.Need not re-use the emulsion paint brushing.
The present invention has the following advantages: 1, cost is low, and the putty powder for exterior wall cost of producing by the present invention only is 350 yuan per ton, and the inner wall putty powder cost only is 280 yuan.2, because the present invention has added the whitening agent ultramarine, make putty powder of the present invention have the color light, whiteness height, the effect that metope is smooth and bright like a mirror.3, because the effect of each component of the present invention makes product of the present invention have the intensity height, strong adhesion, water-fast, wear-resisting, scrubbing resistance, corrosion-resistant,, the advantage that is difficult for going mouldy.4, the raw material of the present invention's use is easily purchased, and produces easily.5, product of the present invention has multiple different advantages such as color.
Embodiment
Below in conjunction with specific embodiment, the present invention will be further described.
Embodiment one: a kind of putty powder prescription that uses for exterior wall is
500 kilograms of dry powders
300 kilograms of ash calcium powders
200 kilograms of white cements
7 kilograms of methylcellulose gum
0.3 kilogram in ultramarine
5 kilograms of tapioca (flour)s
Embodiment two: a kind of putty powder prescription that uses for interior wall is
550 kilograms of dry powders
450 kilograms of ash calcium powders
5 kilograms of methylcellulose gum
1.0 kilograms in ultramarine
5 kilograms of tapioca (flour)s
Embodiment three: a kind of color lacquer putty powder prescription that uses for exterior wall is
300 kilograms of dry powders
300 kilograms of ash calcium powders
200 kilograms of white cements
7 kilograms of Vltra tearss
0.3 kilogram in ultramarine
200 kilograms of purplish red stone flours
Embodiment four: a kind of color lacquer putty powder prescription that uses for interior wall is
250 kilograms of dry powders
450 kilograms of ash calcium powders
5 kilograms of Vltra tearss
1 kilogram in ultramarine
300 kilograms of emerald green stone flours
The dry powder fineness of using in the foregoing description is the 300-500 order, and whiteness is the 90-98 degree.Buy by market.
Ash calcium powder fineness is 325 orders, and whiteness is more than 90.Connection material of construction company limited produces by Shanghai, Jiande City, Zhejiang Province.It is pure to have whiteness, and sulphur, phosphorus content are low, the fineness height, and Calcium of intensifiens content height, characteristics such as viscosity is good, quality meets Zhejiang B/JC69-88 standard.Be used for coating and can reduce the fine particle calcium carbonate consumption, increase the water tolerance of coating, scrub resistance strengthens its workability and metope hardness.
White cement is 425 labels.Produce by Shanghai Cement Plant.
The methylcellulose gum fineness is 325 orders, and viscosity is 6-14 ten thousand.Company limited produces by the auspicious safe chemical industry in Shandong.
The ultramarine fineness is 325 orders, and pH value 6.5-7.5 is produced by East China, Longkou City, Shandong Province gas company limited.Ultramarine has whitening effect, can eliminate and lower yellow color spot in the coating, and alkaline-resisting, high temperature resistant, in atmosphere, and under Exposure to Sunlight, the wind and rain condition, stable performance.Its quality accord with Q/LHF003-2003 standard, free sulphur content is less than 1.5%, and volatile content is less than 1.0%.
The fineness of tapioca (flour) is 200 orders.Starch content is greater than 85%, and moisture is less than 13%, PH 5-7, and whiteness 90, glossy, free from extraneous odour can play the effect that increases sticking power.Import and export corporation provides by the Fujian Rongjiang.
Using purplish red stone flour, emerald green stone flour fineness is 400 orders, and by natural "dead" purplish red stone, natural "dead" emerald green stone fragmentation is milled into powder, sieves and makes.
According to the prescription that the foregoing description provides, each component accurately by the prescription weighing, fully mixes, and promptly can be made into high-strength water-proof putty powder.
Above-mentioned putty powder is added clear water, stir into a paste.After 20 minutes,, criticize and scrape on metope thickness 0.1-0.3 millimeter the putty powder cream that stirs.After treating that metope is done, criticize again and scrape once, receive light when metope is tack-free, do back wall color light, smooth and bright like a mirror, bright as quartzy.Have once construction, need not re-use emulsion paint, the labor and material saving cost is low; The whiteness height, metope is smooth and bright like a mirror; The intensity height, strong adhesion, water-fast, wear-resisting, scrubbing resistance, corrosion-resistant, be difficult for going mouldy; Produce easily, cost is low; Have advantages such as multicolour.
Claims (4)
1, a kind of high-strength water-proof putty powder is characterized in that being made up of the following weight parts proportion raw material
Dry powder 30-70
Ash calcium powder 30-70
Methylcellulose gum 0.25-1.5
Or Vltra tears
Ultramarine 0.02-0.15
2, high-strength water-proof putty powder according to claim 1, wherein the weight proportion of each raw material is
Dry powder 30-70
Ash calcium powder 25-40
White cement 15-30
Methylcellulose gum 0.3-1.5
Or Vltra tears
Ultramarine 0.02-0.05
Tapioca (flour) 0.1-1
3, high-strength water-proof putty powder according to claim 1, wherein the weight proportion of each raw material is
Dry powder 30-70
Ash calcium powder 30-70
Methylcellulose gum 0.25-1.0
Or Vltra tears
Ultramarine 0.02-0.15
Tapioca (flour) 0.1-1
4, according to the described high-strength water-proof putty powder of claim 1,2 or 3, it is characterized in that: add natural "dead" color ore powder, produce colored high-strength water-proof putty powder.