CN1814425A - Method for producing colour wooden handle - Google Patents
Method for producing colour wooden handle Download PDFInfo
- Publication number
- CN1814425A CN1814425A CN 200610034099 CN200610034099A CN1814425A CN 1814425 A CN1814425 A CN 1814425A CN 200610034099 CN200610034099 CN 200610034099 CN 200610034099 A CN200610034099 A CN 200610034099A CN 1814425 A CN1814425 A CN 1814425A
- Authority
- CN
- China
- Prior art keywords
- suspensor
- handle
- dry
- production method
- impregnation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a colorful woodiness handle manufacture method that includes the following steps: machining the wood into germule handle, coloring the germule, drying, dipping into glue and drying, putting the handle into the mold to repressuring, and demolding to form the handle product. The invention uses wood as raw material and adopts coloring, dipping glue technology to keep the woodiness stripes. It has the feature of colorful and beautiful.
Description
Technical field
The present invention relates to a kind of production method of utilizing log to produce colour wooden handle, is to utilize mould log to be processed as hardness height, fineness are good, the production method of the colour wooden handle of heatproof waterproof specifically.
Background technology
At present, the most former timber that adopts of the wood handle of technology five metals tableware is directly made now, the handle of the type maintains the due wooden striped of log, has log characteristic classic attractive in appearance, but the handle of protolignin is wooden comparatively loose, because of variations such as the temperature difference, psychrometric difference shrinking deformation can occur, fade, influence the outward appearance of handle greatly, its original classic aesthetic is had a greatly reduced quality.Certainly also have handle that simulating log makes or plastic handgrip, rubber stem, bakelite handle or the like, the feature of the handle shortcoming log orderliness line shape of the type, though can be high temperature resistant water-fast, but it can give off a peculiar smell under the condition of high temperature, its result of use is undesirable, and the performance attractive in appearance of its performance attractive in appearance and protolignin is too wide in the gap, moreover its color of handle that utilizes log to produce has only single color, tone is relatively more dull, and the log handle circulation that does not temporarily also have dyeing on the market occurs.
Summary of the invention
The objective of the invention is to overcome the shortcoming of above-mentioned present technology, provide a kind of utilize mould with log be processed into that hardness height, fineness are good, heatproof waterproof, shaping performance are good, the production method of indeformable non-fading colour wooden handle.
The present invention can be achieved through the following technical solutions:
A kind of production method of colour wooden handle, it comprises following production stage:
(1) log is processed into the first suspensor of handle shape;
(2) the first suspensor with handle shape dyes;
(3) the first suspensor oven dry that will dye;
(4) the first suspensor impregnation that will dry;
(5) the first suspensor of seep through is dried;
(6) the first suspensor that will dry places the mould shape of pressurizeing;
(7) the first suspensor demoulding after will pressurizeing and go out to form the handle product.
In step 1, the length of first suspensor, width and cutting radian conform to the size of finished product handle, and the ratio of the thickness of the thickness of first suspensor handle and finished product handle can be 1.2: 1 or 1.3: 1, and best ratio is 1.2: 1.
In step 2, be that the mode of boiling in container dyes with the process of the first suspensor dyeing of handle shape, boiling time is 30～120 minutes.
In step 4, it is 8～20 hours with time of first suspensor impregnation of oven dry.In step 6, be 15～35kg/m with the pressure of mould of the first suspensor press molding of oven dry
2, the mold heated time is 30～60 minutes, the temperature of heating is 100～200 ℃.
Above-mentioned production stage concrete operations flow process is:
At first, select wooden reasonable log, log is processed into the first suspensor of handle shape, make length, width and the cutting radian of first suspensor and finally want the size of the handle of finished product to conform to, but guarantee that just suspensor is bigger, prevent to make final products too little because of excessive wear; Place container to boil dyeing first suspensor then, boiling time is 30～120 minutes, treat that color bleeding goes into the surface of suspensor just, this moment, the handle surface color and polish was even, the first suspensor oven dry that to dye then, first suspensor after the oven dry adopts the mode of impregnation to guarantee its color difficult drop-off, guarantees that handle surfaces is attractive in appearance, is 8～20 hours with time of the first suspensor impregnation of oven dry; The first suspensor that to dry then places the mould press molding, and the pressure of mould is 15～35kg/m
2, the mold heated time is 30～60 minutes, the temperature of heating is 100～200 ℃, at last the first suspensor demoulding is gone out, and then obtains adopting the handle of the inventive method gained.
The present invention compared with prior art has following advantage:
1, utilizes the raw material of log, maintain the due wooden striped of log, have log characteristic classic attractive in appearance, have more environment protection significance as handle.
2, adopt the stainable mode of handle, it is various to make the present invention conceive the product color of gained, an outward appearance great variety of modelsization, and the consumer that can satisfy different levels uses.
3, adopt the mode of wooden handle and resin glue water logging glue seep through, make its handle product heatproof water-fast, avoided common log handle wooden loose and cause being out of shape fade mouldy.
4, adopt the mould pressing mode that the hardness of its handle is increased greatly, shaping performance, fineness are good.
Description of drawings
Accompanying drawing 1 is technological process of production figure of the present invention.
The specific embodiment
Come the utility model is further described below in conjunction with accompanying drawing:
As shown in Figure 1, a kind of production method of colour wooden handle, it comprises following production stage:
(1) log is processed into the first suspensor of handle shape;
(2) the first suspensor with handle shape dyes;
(3) the first suspensor oven dry that will dye;
(4) the first suspensor impregnation that will dry;
(5) the first suspensor of seep through is dried;
(6) the first suspensor that will dry places the mould shape of pressurizeing;
(7) the first suspensor demoulding after will pressurizeing and go out to form the handle product.
In step 1, the length of first suspensor, width and cutting radian conform to the size of finished product handle, and the ratio of the thickness of the thickness of first suspensor handle and finished product handle can be 1.2: 1 or 1.3: 1, and best ratio is 1.2: 1.
In step 2, be that the mode of boiling in container dyes with the process of the first suspensor dyeing of handle shape, boiling time is 30～120 minutes.
In step 4, it is 8～20 hours with time of first suspensor impregnation of oven dry.
In step 6, be 15～35kg/m with the pressure of mould of the first suspensor press molding of oven dry
2, the mold heated time is 30～60 minutes, the temperature of heating is 100～200 ℃.
To describe the present invention's design below by the following technical programs in detail:
Embodiment one:
A kind of production method of colour wooden handle, it comprises following production stage:
(1) log is processed into the first suspensor of handle shape;
(2) the first suspensor with handle shape dyes;
(3) the first suspensor oven dry that will dye;
(4) the first suspensor impregnation that will dry;
(5) the first suspensor of seep through is dried;
(6) the first suspensor that will dry places the mould shape of pressurizeing;
(7) the first suspensor demoulding after will pressurizeing and go out to form the handle product.
In step 1, the length of first suspensor, width and cutting radian conform to the size of finished product handle, and the ratio of the thickness of the thickness of first suspensor handle and finished product handle can be 1.2: 1.
In step 2, be that the mode of boiling in container dyes with the process of the first suspensor dyeing of handle shape, boiling time is 90 minutes.
In step 4, be trimerization chloramines glue with the used glue of first suspensor impregnation of drying, the time of impregnation is 12 hours.
In step 6, be 25kg/m with the pressure of mould of the first suspensor press molding of oven dry
2, mould
Tool heat time heating time is 40 minutes, and the temperature of heating is 140 ℃.
Above-mentioned production stage concrete operations flow process is:
At first, select wooden reasonable log, log is processed into the first suspensor of handle shape, make length, width and the cutting radian of first suspensor and finally want the size of the handle of finished product to conform to, the ratio of the thickness of the thickness of handle and finished product handle is 1.2: 1, guarantee that just suspensor is bigger, prevent to make final products too little because of excessive wear; Place container to boil dyeing first suspensor then, boiling time is 90 minutes, treat that color bleeding goes into the surface of suspensor just, this moment, the handle surface color and polish was even, the first suspensor oven dry that to dye then, the first suspensor after the oven dry adopts the mode of impregnation to guarantee its color difficult drop-off, guarantees that handle surfaces is attractive in appearance, the used glue of impregnation is trimerization chloramines glue, and the time of impregnation is 12 hours; The first suspensor that to dry then places the mould press molding, and the pressure of mould is 25kg/m
2, the mold heated time is 40 minutes, the temperature of heating is 140 ℃, at last the first suspensor demoulding is gone out, and then obtains adopting the handle of the inventive method gained.
Embodiment two:
A kind of production method of colour wooden handle, it comprises following production stage:
(1) log is processed into the first suspensor of handle shape;
(2) the first suspensor with handle shape dyes;
(3) the first suspensor oven dry that will dye;
(4) the first suspensor impregnation that will dry;
(5) the first suspensor of seep through is dried;
(6) Hong Gan first suspensor places the mould shape of pressurizeing;
(7) the first suspensor demoulding after will pressurizeing and go out to form the handle product.
In step 1, the length of first suspensor, width and cutting radian conform to the size of finished product handle, and the ratio of the thickness of the thickness of first suspensor handle and finished product handle can be 1.2: 1.
In step 2, be that the mode of boiling in container dyes with the process of the first suspensor dyeing of handle shape, boiling time is 30 minutes.
In step 4, be phenolic aldehyde glue with the used glue of first suspensor impregnation of drying, the time of impregnation is 8 hours.
In step 6, be 15kg/m with the pressure of mould of the first suspensor press molding of oven dry
2, the mold heated time is 30 minutes, the temperature of heating is 100 ℃.
Above-mentioned production stage concrete operations flow process is:
At first, select wooden reasonable log, log is processed into the first suspensor of handle shape, make length, width and the cutting radian of first suspensor and finally want the size of the handle of finished product to conform to, the ratio of the thickness of the thickness of handle and finished product handle is 1.2: 1, guarantee that just suspensor is bigger, prevent to make final products too little because of excessive wear; Place container to boil dyeing first suspensor then, boiling time is 30 minutes, treat that color bleeding goes into the surface of suspensor just, this moment, the handle surface color and polish was even, the first suspensor oven dry that to dye then, the first suspensor after the oven dry adopts the mode of impregnation to guarantee its color difficult drop-off, guarantees that handle surfaces is attractive in appearance, the used glue of impregnation is phenolic aldehyde glue, and the time of impregnation is 8 hours; The first suspensor that to dry then places the mould press molding, and the pressure of mould is 15kg/m
2, the mold heated time is 30 minutes, the temperature of heating is 100 ℃, at last the first suspensor demoulding is gone out, and then obtains adopting the handle of the inventive method gained.
Embodiment three:
A kind of production method of colour wooden handle, it comprises following production stage:
(1) log is processed into the first suspensor of handle shape;
(2) the first suspensor with handle shape dyes;
(3) the first suspensor oven dry that will dye;
(4) the first suspensor impregnation that will dry;
(5) the first suspensor of seep through is dried;
(6) Hong Gan first suspensor places the mould shape of pressurizeing;
(7) the first suspensor demoulding after will pressurizeing and go out to form the handle product.
In step 1, the length of first suspensor, width and cutting radian conform to the size of finished product handle, and the ratio of the thickness of the thickness of first suspensor handle and finished product handle can be 1.3: 1.
In step 2, be that the mode of boiling in container dyes with the process of the first suspensor dyeing of handle shape, boiling time is 120 minutes.
In step 4, the glue that the first suspensor impregnation of oven dry is used is urine aldehyde glue, and the time of impregnation is 20 hours.
In step 6, be 35kg/m with the pressure of mould of the first suspensor press molding of oven dry
2, the mold heated time is 60 minutes, the temperature of heating is 200 ℃.
Above-mentioned production stage concrete operations flow process is:
At first, select wooden reasonable log, log is processed into the first suspensor of handle shape, make length, width and the cutting radian of first suspensor and finally want the size of the handle of finished product to conform to, the ratio of the thickness of the thickness of handle and finished product handle is 1.3: 1, guarantee that just suspensor is bigger, prevent to make final products too little because of excessive wear; Place container to boil dyeing first suspensor then, boiling time is 120 minutes, treat that color bleeding goes into the surface of suspensor just, this moment, the handle surface color and polish was even, the first suspensor oven dry that to dye then, the first suspensor after the oven dry adopts the mode of impregnation to guarantee its color difficult drop-off, guarantees that handle surfaces is attractive in appearance, the used glue of impregnation is urine aldehyde glue, and the time of impregnation is 20 hours; The first suspensor that to dry then places the mould press molding, and the pressure of mould is 35kg/m
2, the mold heated time is 60 minutes, the temperature of heating is 200 ℃, at last the first suspensor demoulding is gone out, and then obtains adopting the handle of the inventive method gained.
Claims (8)
1, a kind of production method of colour wooden handle is characterized in that comprising following production stage:
(1) log is processed into the first suspensor of handle shape;
(2) the first suspensor with handle shape dyes;
(3) the first suspensor oven dry that will dye;
(4) the first suspensor impregnation that will dry;
(5) the first suspensor of seep through is dried;
(6) the first suspensor that will dry places the mould shape of pressurizeing;
(7) the first suspensor demoulding after will pressurizeing and go out to form the handle product.
2, the production method of colour wooden handle according to claim 1 is characterized in that: the process with the first suspensor dyeing of handle shape in step 2 is to adopt the mode of boiling to dye in container, and boiling time is 30～120 minutes.
3, the production method of colour wooden handle according to claim 2 is characterized in that: the process of first suspensor dyeing is that the time of boiling in container is 90 minutes
4, the production method of colour wooden handle according to claim 1 is characterized in that: the used glue of first suspensor impregnation that will dry in step 4 is a kind of in trimerization chloramines glue, phenolic aldehyde glue, the urine aldehyde glue.
5, the production method of colour wooden handle according to claim 1 is characterized in that: the time of the first suspensor impregnation that will dry in step 4 is 8～20 hours.
6, the production method of colour wooden handle according to claim 5 is characterized in that: the time of the first suspensor impregnation that will dry in step 4 is 12 hours.
7, the production method of colour wooden handle according to claim 1 is characterized in that: the pressure of the mould of the first suspensor press molding that will dry in step 6 is 15～35kg/m
2, the mold heated time is 30～60 minutes, the temperature of heating is 100～200 ℃.
8, the production method of colour wooden handle according to claim 7 is characterized in that: the pressure of the mould of the first suspensor press molding that will dry in step 6 is 25kg/m
2, the mold heated time is 40 minutes, the temperature of heating is 140 ℃.