CN1843722A - Diametral plane section-aligning bamboo panel for composite board and method for manufacturing the composite board - Google Patents
Diametral plane section-aligning bamboo panel for composite board and method for manufacturing the composite board Download PDFInfo
- Publication number
- CN1843722A CN1843722A CN 200610067198 CN200610067198A CN1843722A CN 1843722 A CN1843722 A CN 1843722A CN 200610067198 CN200610067198 CN 200610067198 CN 200610067198 A CN200610067198 A CN 200610067198A CN 1843722 A CN1843722 A CN 1843722A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- face
- joint
- panel
- footpath
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method for producing quarter-sawn bamboo surface plate and relative composite floor. Wherein, said invention is formed by compressed connecting quarter-sawn bamboo surface plate, middle plate and bottom plate, which are connecting by glue; said quarter-sawn bamboo surface plate is formed by several blanks of surface plates, which are belongs to one blank; said blank is formed by the bamboo bars of one raw bamboo; the central line of each bamboo section are in one line; the preparing method comprises; cutting raw bamboo into several bars to be roughly milled; bonding; carbonizing; braising; dewatering; plate selecting; fine milling; assembly blank; thermally compressing; solidifying; slicing thin plate; and assembling blank; then according to the demand of different size, selecting different bamboo bars to be glues and assembling the bottom and middle plates in the same width and length; then assembling, thermally compressing, solidifying, and coloring, to attain final product. The invention can solve the defects of easy glue-loose and distortion, with lower bamboo consumption.
Description
Technical field
The present invention relates to building and ornament materials, particularly a kind of preparation method that is used for the footpath of composite floor board in the face of joint bamboo panel and composite floor board thereof.
Background technology
Traditional bamboo floor panel is divided into string face integrated (horizontal assembly, the flat assembly or concora crush) and diametric plane integrated (the perpendicular assembly or the side assembly) two classes, because the bamboo floor producing technology development time is not long, technology is not mature enough, the production process quality control is difficult, above-mentioned two kinds of integration modes all are combined into the joint bamboo-skin panel that looses, and do not have the visual impression of nature bamboo.
String is faced the visual impression of the trial of joint bamboo floor to a kind of bamboo natural stype of people, is subjected to general welcome.But because the utilization of this string face is the individual layer bamboo string face of thick bamboo tube when launching, be subjected to the limitation of bamboo thick bamboo tube girth diameter size, during greater than 70MM, utilization rate of bamboo is low in wide format.
Patent CN94224676.4 " side pressure bamboo offset plate and bamboo floor thereof " discloses a kind of diametric plane integrated floor, it is thick bamboo tube to be rived into 1-2.5 centimetre wide bamboo bar according to the ground plate thickness, scrape off the bamboo bar as the tabasheer of thick bamboo tube inboard and the surf green in the outside, thick according to different bamboo material, processing keeps bamboo bar thickness between 0.6-1.2 centimetre, then according to the width on floor, with the bamboo bar single face uniform gluing crimping of tens 0.6-1.2 cm thicks, the integrated bamboo of the diametric plane floor of producing the 1-2.5 cm thick.But because the bamboo bar of this kind bamboo floor is not from same former thick bamboo tube, and the ring journey looses shape to joint, and ring is different with non-ring place density, so exists the bamboo floor in different temperatures and humidity, comes unglued easily between the bamboo bar and is out of shape; And the floor of this kind structure is full bamboo floor, and bamboo wood consumption is big; Shape is to joint because the ring journey is loose, and visual effect is not so good as joint bamboo floor.
Summary of the invention
Purpose of the present invention, be utilize bonding with joint bamboo blank string face, dissect processing, diametric plane is integrated to the joint technology, realize a kind of preparation method that is used for the footpath of composite floor board in the face of joint bamboo panel and composite floor board thereof, finishing does not have the present situation of footpath in the face of the plate that saves land, and improves utilization rate of bamboo; For people provide a kind of not yielding, visual effect attractive in appearance to joint bamboo floor.
Technical scheme of the present invention is achieved in that
A kind of footpath that is used for composite floor board is in the face of the joint bamboo panel, and this directly has decorative cover and adhesive surface in the face of the joint bamboo panel, it is characterized in that described decorative cover is constituted by the diametric plane of multi-disc panel blanket;
Described multi-disc panel blanket belongs to a bamboo blank plate together; Described bamboo blank plate, constitute by the bamboo bar that belongs to a former bamboo together; Each ring center line of described panel blanket diametric plane is positioned on the same straight line of each ring.
Described footpath is 0.6 millimeter to 6 millimeters in the face of joint bamboo panel thickness.
The specification of described multi-disc panel blanket is identical.
A kind of footpath is characterized in that in the face of joint bamboo composite floor in the face of the joint bamboo panel, form by middle plate and the crimping of base plate gluing by the footpath for this bamboo composite floor;
Described footpath is constituted by multi-disc panel blanket in the face of the joint bamboo panel; Described multi-disc panel blanket belongs to a bamboo blank plate together; Described bamboo blank plate is constituted by the bamboo bar that belongs to a former bamboo together; Each ring center line of described panel blanket diametric plane is positioned on the same straight line of each ring.
Plate can be a lamina in described, also can be multi-layer sheet;
Plate and base plate can be bamboo clappers in described, also can be planks.
The preparation method of joint bamboo composite floor is faced in a kind of footpath, it is characterized in that,
I. the footpath is in the face of saving the preparation method of bamboo panel:
A. the raw material thick bamboo tube is cutd open into a plurality of bamboo bars;
B. rough mill: remove bamboo bar burr all around;
C. prick with joint: select bamboo bar colligation that same thick bamboo tube cuts together;
D. carburising step: the bamboo bar is placed closed container, pressure 0.15 to 0.3MPa, 110 to 125 ℃ of temperature, 0.5 to 2.5 hour time;
E. boiling step: with the boiling in boiling water of bamboo bar, digestion time was greater than 2 hours;
F. processed: with the oven dry of bamboo bar, control bamboo bar moisture content is below 12%;
G. chip select, finish-milling: the bamboo bar rejecting section nodal plate that drying is good, damaged sheet, moth sheet, the sheet that goes mouldy, heartburn, aberration sheet, finish-milling goes green grass or young crops, goes Huang fully then, and the string face is smooth;
H. assembly: the bamboo bar of same thick bamboo tube is alignd bamboo bar string face gluing with ring;
I. hot pressing, curing schedule: with assembly hot pressing, be solidified into joint bamboo clappers base, pressure 5 to 15MPa, 105～130 ℃ of temperature, 10 to 15 minutes hardening times;
J. cut open thin plate, will be sawn into multi-disc with joint bamboo clappers base is the thin plate of face with the bamboo diametric plane;
K. thin plate finish-milling is with the panel blanket of thin plate four sides finish-milling to the floor panel size;
L. assembly: according to the size needs one group of panel blanket string face is gluedd joint, form the footpath in the face of the joint bamboo panel.
II. the preparation method of composite floor board:
A. make the footpath in the face of the joint bamboo panel according to above-mentioned I step;
B. make base plate and middle plate; According to the bamboo bar that will ask for different-thickness or the batten gluing of different size, splice with the footpath and face joint bamboo panel width base plate and the middle plate identical with length;
C. assembly: will the footpath in the face of joint bamboo panel, middle plate, the butt joint of base plate gluing;
D. hot pressing, curing schedule: with the hot pressing of assembly plate, curing, pressure 5 to 15MPa, 105～130 ℃ of temperature, 10 to 15 minutes hardening times;
E. tongue and groove: processing floor splicing tongue and groove;
F. application: client's required color coating is coated on the floor, the ground board finished product.
The present invention to the contribution of prior art is, because the bamboo bar of this kind bamboo floor comes from same joint thick bamboo tube, and therefore ring has overcome the bamboo floor in different temperatures and humidity, the deficiency of coming unglued easily and being out of shape between the bamboo bar to joint; Adopt the floor of composite construction, bamboo wood consumption is few; And diametric plane is integrated little to the joint bamboo floor integral body aberration of mating formation, and with respect to the diametric plane joint that looses, joint bamboo floor neatly, is more pressed close to the natural stype of bamboo; The integrated history that can only produce the joint bamboo floor that looses of the diametric plane that is through with simultaneously.
Below in conjunction with drawings and Examples the present invention is made a detailed description.
Description of drawings
Fig. 1 directly faces joint bamboo panel structural representation for the present invention;
Fig. 2 is the existing integrated diffusing joint bamboo floor structural representation of diametric plane;
Fig. 3 directly faces joint bamboo composite floor structural representation for the present invention;
Fig. 4 is bamboo bar schematic diagram for thick bamboo tube of the present invention dissects;
Fig. 5 is the schematic diagram with joint bamboo clappers base for the bamboo bar of the same thick bamboo tube of the present invention is bonding;
Fig. 6 is several pieces footpath faceplate panels blanket schematic diagrames for the present invention dissects with joint bamboo clappers base;
Fig. 7 directly faces the manufacture craft flow chart of joint bamboo panel for the present invention;
Fig. 8 directly faces the manufacture craft flow chart of joint bamboo composite floor for the present invention.
The specific embodiment
Existing diametric plane looses joint bamboo floor referring to Fig. 2, and wherein, the diffusing joint of diametric plane bamboo floor is by bonding the forming of bamboo bar 1 radial facing; Done tongue and groove 5 (floor splicing mouth) in the outside on floor, ring 4 diffusing shapes are distributed in the surface of panel, because the bamboo bar of this kind bamboo floor is not from same joint thick bamboo tube, and the diffusing shape of ring 4 journeys distributes, the ring place is different with non-ring place density, therefore exist the bamboo floor in different temperatures and humidity, come unglued easily between the bamboo bar and be out of shape; And the floor of this kind structure is full bamboo, and bamboo wood consumption is big; Shape distributes because ring 4 journeys are loose, and gives a kind of in disorder no chapter of people, the visual impression of no bamboo wood characteristic.
The present invention is directly in the face of saving the bamboo composite floor referring to Fig. 3, it is to face joint bamboo floor by the footpath in the face of joint bamboo panel 6, middle plate 2 and base plate 3 glued joint the compound footpath that forms, wherein, middle plate 2 and base plate 3, according to resource situation, can adopt full bamboo or full wood or bamboo wood mixed plate, promptly middle plate 2 is a wood, and base plate 3 is a bamboo; If the floor is thinner, can remove middle plate, if instead plate can be two or three in thicker; Owing to adopt composite construction, bamboo wood consumes little; And the footpath is little in the face of the joint bamboo floor integral body aberration of mating formation, and with respect to the diametric plane joint that looses, joint bamboo floor neatly, is more pressed close to the natural stype of bamboo; Give a kind of aesthetic feeling in bamboo grove of people.
The footpath is in the face of the structure of joint bamboo panel 6 and form referring to Fig. 1, Fig. 4, Fig. 5, Fig. 6, in Fig. 4 to Fig. 6, the periphery and the inner headed face of thick bamboo tube 7 is referred to as string face 8, will be referred to as diametric plane 9 perpendicular to the face of string face 8; Thick bamboo tube 7 is cut, dissects into several bamboo bars 10 according to floor length sanction to be processed; Bamboo bar 10 processing is flattened, and at string face 8 gluings of bamboo bar 10, same ring 4 alignment of bamboo bar 10 bond together the string face 8 of several bamboo bars 10 mutually, form with joint bamboo clappers base 11; To be face, cut into several pieces panel blankets 12 by direction shown in the arrow A among Fig. 5, with diametric plane 9 with joint bamboo clappers base 11 referring to Fig. 6; The thickness of panel blanket 12 can be from 0.6 millimeter to 6 millimeters in the face of the thickness needs of joint bamboo panel according to the footpath; Fig. 1 has illustrated to face the joint bamboo panel by the footpath that several piece panel blanket 12 is spliced.
Embodiment 1:
Referring to Fig. 1, Fig. 3 to Fig. 6, according to the specification requirement of the footpath that produces wide 130mm, long 968mm, thickness 20mm in the face of the compound bamboo floor of joint bamboo, blanket before the required tongue and groove:
The footpath is in the face of joint bamboo panel, wide 138 millimeters, long 975mm, thickness 3.5mm;
Plate in bamboo or the wood, wide 138mm, long 975mm, thick 12mm;
Bamboo or timber apron, wide 138mm, long 975mm, thick 4.5mm.
The footpath is as follows in the face of the textural association of joint bamboo panel:
Get common bamboo raw material thick bamboo tube 7: internal diameter 65mm, the long 975mm of thick bamboo tube, thick bamboo tube wall thickness 7mm; With bamboo tube 7 rive ten process processing after, forming ten string faces 8 wide is the bamboo bar 10 of 15mm, diametric plane 9 wide 5mm; With string face 8 gluings of bamboo bar 10, with ring 4 alignment, ten bamboo bars 10 are glued together, the integrated width that forms diametric plane 9 is that 50mm, string face 8 width are the same joint bamboo clappers base 11 of 15mm; After fine finishining, will be that face is according to being split into three thick panel blankets 12 of 5mm with diametric plane 9 then with joint bamboo clappers base 11; Polished surface slab plate 12 is that the integrated width of 3.5mm, diametric plane 9 is the panel blanket 12 of 46mm to string face 8 thickness once more; Three unilateral slab plates 12 risk wide, the long 975mm of 138mm, thickness be the footpath of 3.5mm in the face of joint bamboo floor with the footpath in the face of joint bamboo panel 6;
The textural association of plate 2 is as follows in bamboo or the wood:
Getting thickness is that 12mm, long 975mm, width are that plate 2 in wide bamboo of 138mm or the wood is processed in bamboo bar or the splicing of batten side gluing that 10mm to 30mm does not wait;
The textural association of bamboo or timber apron 3 is as follows:
Getting thickness is that 4.5mm, long 975mm, width are that wide bamboo of 138mm or timber apron 3 are processed in bamboo bar or the splicing of batten side gluing that 10mm to 30mm does not wait;
The compound bamboo floor of joint bamboo blanket is faced in the face of plate 2, bamboo or timber apron 3 gluing crimping Cheng Jing in joint bamboo panel 6, bamboo or the wood in the footpath of making.
The preparation method of the compound bamboo floor of joint bamboo is faced referring to embodiment 4 to 6 in concrete footpath.
Embodiment 2:
Referring to Fig. 1, Fig. 3 to Fig. 6, reference example 1 parameter will be if will be that face is according to being split into six unilateral slab plates 12 with diametric plane 9 with joint bamboo clappers base 11; Then can be 1.7mm after the processing of the thickness of panel blanket 12, therefore can process the panel blanket 12 of different-thickness according to the needs of plate thickness; Face the joint bamboo panel if panel blanket 12 is used for decorating with the footpath, its thickness can be thinned to 0.6mm, can arrive 6mm if panel blanket 12 is used for the footpath of specific use in the face of its thickness of joint bamboo panel, even thicker.Therefore the footpath after integrated can be from 0.6 millimeter to 6 millimeters in the face of the thickness of joint bamboo panel 6.
Equally, if change the number of bamboo tube 7 being rived into bamboo lath 10, also will change with joint bamboo clappers base 11 is the integrated width of face with diametric plane 9, and the concrete preparation method in floor is referring to embodiment 4 to 6.
Embodiment 3:
Referring to Fig. 1, Fig. 3 to Fig. 6, bamboo blank 11 all right string faces 8 are realized joint is spliced into the wide cut string in the face of the nodal section plate for face cuts, and the concrete preparation method of bamboo floor is referring to embodiment 4 to 6.
Embodiment 4:
Joint bamboo panel manufacture craft flow chart is faced referring to Fig. 7 in the footpath, wherein, and with reference to the floor dimensional parameters of embodiment 1;
The 7-1 bamboo cuts material: raw material bamboo tube is blocked according to institute's panel machining length;
7-2 splits bamboo: thick bamboo tube 7 usefulness that cut are split the bamboo machine dissect into ten bamboo bars 10;
7-4 pricks with joint: ten bamboo bars 10 that same thick bamboo tube 7 dissects are selected colligation;
The 7-5 carbonization: bamboo bar 10 is placed in the closed container, and the bamboo panel look is the bamboo primary colors: container inner pressure 0.15MPa, temperature 110 degree, time are after reaching pressure and temperature 0.5 hour; The bamboo panel look is for dark: container inner pressure 0.3MPa, temperature 125 degree, time are after reaching pressure and temperature 2.5 hours;
The 7-6 boiling: the bamboo bar boiled in boiling water 2.5 hours, and purpose is the high temperature degreasing;
The 7-7 drying: bamboo lath 10 is dried, and the control moisture content is below 12%;
7-8 chip select, finish-milling: the bamboo bar 10 rejecting section nodal plates that drying is good, damaged sheet, moth sheet, the sheet that goes mouldy, heartburn, aberration sheet, finish-milling goes green grass or young crops, goes Huang fully then, and the string face is smooth;
7-9 gluing: bamboo bar 10 string faces 8 gluings that finish-milling is good (adopting Finland to produce " Tai Er " adhesive);
7-10 assembly, hot pressing, curing: with the same ring 4 alignment hot pressing of string face 8 glue-coated bamboo bars 10, solidify the well-thought-out plan blank 11 that bonds together, pressure 5MPa, temperature 105 degree, 12 minutes hardening times;
7-11 four side moulder: with bonding bamboo blank 11 S4Ss;
7-12 cuts open thin plate: will dig good bamboo blank 11 usefulness sawing machine or splitting machines, being sawn into three is the panel blanket 12 of face with bamboo diametric plane 9;
The 7-13 finish-milling: panel blanket 12 four sides finish-millings are faced the size that saves bamboo panel to the footpath of same size, and diametric plane 9 integrated width are that 46mm, string face 8 thickness are 3.5mm, length 975mm;
The 7-14 assembly: nodal section slab plate 12 is faced once more to joint in the footpath that will process, and the adhesive surface of string face 8 and diametric plane 9 is gluing respectively, and string face 8 is pasted mutually, and diametric plane 9 sticks on middle plate 2 surfaces that process, and changes composite floor board manufacture craft assembly step over to.
Embodiment 5, and compound footpath is in the face of saving bamboo floor manufacture craft flow process referring to Fig. 8;
8-1 panel machining: face joint bamboo panel processes by the footpath, referring to embodiment 4;
Plate in the 8-2 processing: getting thickness is that 12mm, long 975mm, width are the batten that 10mm to 30mm does not wait, and plate in the wide wood of 138mm is processed in gluing splicing in side;
8-3 processes base plate: getting thickness is that 4.5mm, long 975mm, width are that the wide bamboo base plate of 138mm is processed in the bamboo bar side gluing splicing that 10mm to 30mm does not wait;
8-4 assembly: panel, middle plate, base plate gluing are pasted together;
8-5 hot pressing: three-layer composite board is compressed together, pressure 15MPa, temperature 130 degree, 15 minutes hardening times;
The 8-6 tongue and groove: the fine finishining floor is to the specification requirement size, and ground plate thickness 20mm, width are 130mm, length 968mm, the tongue and groove 5 on processing floor;
8-7 application: the required coating of client is coated on the floor;
8-8 packing: finish the integrated making of diametric plane to joint bamboo floor.
Embodiment 6, and referring to embodiment 5, wherein, plate in the 8-2 processing: getting thickness is that 12mm, long 975mm, width are that plate in the wide bamboo of 138mm is processed in the bamboo bar side gluing splicing that 10mm to 30mm does not wait; Other technology needn't become.
Claims (10)
1. a footpath that is used for composite floor board is in the face of the joint bamboo panel, and this directly has decorative cover and adhesive surface in the face of joint bamboo panel (6), it is characterized in that described decorative cover is constituted by the diametric plane (9) of multi-disc panel blanket (12);
Described multi-disc panel blanket (12) belongs to a bamboo blank plate (11) together;
Described bamboo blank plate (11) is constituted by the bamboo bar (10) that belongs to a former bamboo together;
Each ring (4) center line of described panel blanket (12) diametric plane (9) is positioned on the same straight line of each ring (4).
2. the footpath that is used for composite floor board according to claim 1 is characterized in that in the face of the joint bamboo panel described footpath is 0.6 millimeter to 6 millimeters in the face of joint bamboo panel (6) thickness.
3. the footpath that is used for composite floor board according to claim 1 is characterized in that in the face of the joint bamboo panel specification of described multi-disc panel blanket (12) is identical.
4. a compound footpath is characterized in that in the face of joint bamboo floor, and in the face of joint bamboo panel (6), form by middle plate (2) and base plate (3) gluing crimping by the footpath for this bamboo floor;
Described footpath is constituted by multi-disc panel blanket (12) in the face of joint bamboo panel (6);
Described multi-disc panel blanket (12) belongs to a bamboo blank plate (11) together;
Described bamboo blank plate (11) is constituted by the bamboo bar (10) that belongs to a former bamboo together;
Each ring (4) center line of the diametric plane (9) of described panel blanket (12) is positioned on the same straight line of each ring (4).
5. a kind of compound bamboo floor according to claim 4 is characterized in that, described middle plate (2) and base plate (3) can be bamboo clappers, also can be planks.
6. a footpath is characterized in that in the face of saving the preparation method of bamboo composite floor,
I. the footpath is in the face of saving the preparation method of bamboo panel (6):
A. raw material thick bamboo tube (7) is cutd open into a plurality of bamboo bars (10);
B. rough mill: remove bamboo bar (10) burr all around;
C. prick with joint: select bamboo bar (10) colligation that same thick bamboo tube (7) cuts together;
D. carburising step: the bamboo bar is placed closed container, pressure 0.15 to 0.3MPa, 110 to 125 ℃ of temperature, 0.5 to 2.5 hour time;
E. boiling step: with the boiling in boiling water of bamboo bar, digestion time was greater than 2 hours;
F. processed: with bamboo bar (10) oven dry, control bamboo bar moisture content is below 12%;
G. chip select, finish-milling: bamboo bar (10) the rejecting section nodal plate that drying is good, damaged sheet, moth sheet, the sheet that goes mouldy, heartburn, aberration sheet, finish-milling goes green grass or young crops, goes Huang fully then, and the string face is smooth;
H. assembly: with the same ring of bamboo bar (10) (4) alignment of same thick bamboo tube (7), bamboo bar (10) string face (8) gluing;
I. hot pressing, curing schedule: with assembly hot pressing, be solidified into the joint bamboo clappers base (11), pressure 5 to 15MPa, 105～130 ℃ of temperature, 10 to 15 minutes hardening times;
J. cut open thin plate: will be sawn into multi-disc with joint bamboo clappers base (11) is the thin plate of face with bamboo diametric plane (9);
K. thin plate finish-milling: with the panel blanket (12) of thin plate four sides finish-milling to the floor panel size;
L. assembly: according to the size needs one group of panel blanket (12) string face is gluedd joint, form the footpath in the face of joint bamboo panel (6);
The preparation method of II. compound bamboo floor:
A. make the footpath in the face of joint bamboo panel (6) according to above-mentioned I step;
B. make base plate (3) and middle plate (2):, splice with the footpath and face joint bamboo panel (6) width base plate (3) and the middle plate (2) identical with length according to the bamboo bar that will ask for different-thickness or the batten gluing of different size;
C. assembly: will the footpath in the face of joint bamboo panel (6), middle plate (2), the butt joint of base plate (3) gluing;
D. hot pressing, curing schedule: with the hot pressing of assembly plate, curing, pressure 5 to 15MPa, 105～130 ℃ of temperature, 10 to 15 minutes hardening times;
E. tongue and groove: processing floor splicing tongue and groove (5);
F. application: client's required color coating is coated on the floor, the ground board finished product.
7. footpath according to claim 6 is characterized in that described carburising step: the bamboo bar is placed closed container, pressure 0.15MPa, 110 ℃ of temperature, 0.5 hour time in the face of the preparation method of joint bamboo composite floor.
8. footpath according to claim 6 is characterized in that described carburising step: the bamboo bar is placed closed container, pressure 0.3MPa, 125 ℃ of temperature, 2.5 hours time in the face of the preparation method of joint bamboo composite floor.
9. footpath according to claim 6 is characterized in that in the face of the preparation method of joint bamboo composite floor, 105 ℃ of pressure 5MPa, temperature, 12 minutes hardening times that hot pressing in the described I step, curing are adopted.
10. footpath according to claim 6 is characterized in that in the face of the preparation method of joint bamboo composite floor, 130 ℃ of pressure 15MPa, temperature, 15 minutes hardening times that hot pressing in the described II step, curing are adopted.