CN1804204A - Silica gel waterproof cloth and its production process, production apparatus and application - Google Patents
Silica gel waterproof cloth and its production process, production apparatus and application Download PDFInfo
- Publication number
- CN1804204A CN1804204A CN 200610033072 CN200610033072A CN1804204A CN 1804204 A CN1804204 A CN 1804204A CN 200610033072 CN200610033072 CN 200610033072 CN 200610033072 A CN200610033072 A CN 200610033072A CN 1804204 A CN1804204 A CN 1804204A
- Authority
- CN
- China
- Prior art keywords
- silicon rubber
- silica gel
- gel waterproof
- cloth
- waterproof cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The disclosed silica-gel waterproof fabric for water sports has double structures and prepared by bonding the silicon rubber and elastic fabric. This product has strong elasticity and resistance to age, crack and deciduousness, well gas permeability and water discharge, and applies FDA-grade sizing material too eliminate harm to human.
Description
Technical field
The invention belongs to field of waterproof materials, specifically relate to a kind of silica gel waterproof cloth and production technology thereof, production equipment and application.
Background technology
The elastic water-proof cloth of Shi Yonging adopts mylar PU cloth morely in the market, the surface coverage that is elastic woven material has one deck PU plastic coating, this cloth is used to make the aquatic sports clothing in a large number, as bathing cap, swimsuit etc., the product that adopts this cloth to make, though can reach the effect of waterproof and sealing, but have open defect, the one, mylar PU coating easily wears out and produces the phenomenon of separating and coming off with bed of cloth, makes the minimizing in service life of product and makes product lose water proofing property; The 2nd, the user there is tangible sense of discomfort; The 3rd, drainage and extensibility are good not as good as silicone rubber products, and simple silastic product direct body contact surface when dressing can produce sense of discomfort because of the gas permeability difference makes the user, very easily tear again when running into sharp thing simultaneously.
Chinese patent CN200410051869.5 discloses a kind of elastic water-proof cloth and production equipment and technology, and the elastic water-proof cloth that makes by this patented method can improve its performance to a certain extent, improves its service life; But it is loaded down with trivial details that this patent also exists complicated process of preparation, and may understand residual harmful noxious materials such as peroxide in product, thereby to shortcomings such as human body damage.
Summary of the invention
The objective of the invention is to overcome the defective that prior art exists, provide a kind of high-performance, long-life, avirulent silica gel waterproof cloth.
Another object of the present invention is to provide the production technology of this silica gel waterproof cloth.
A further object of the invention is to provide the production equipment of this silica gel waterproof cloth.
A further object of the invention is silica gel waterproof cloth is used for the aquatic sports field.
For achieving the above object, the present invention has taked following technical scheme:
Silica gel waterproof cloth is double-decker, and lower floor is the elastical cloth bed of material, and the upper strata is a silastic-layer.
Wherein, used silicon rubber is regular grade silicon rubber or FDA level silicon rubber.
The production technology of above-mentioned silica gel waterproof cloth comprises following technical step:
1, silicon rubber is rolled on the elasticity cloth cover with the method for calendering;
Wherein, used silicon rubber is regular grade silicon rubber or FDA level silicon rubber;
2, the method with baking continuously makes silicon rubber vulcanization;
The temperature of baking sulfuration is 100～175 ℃, and the time is 2～10 minutes;
3, talcum powder is coated in equably the surface of silicon rubber, falls unnecessary talcum powder with flushing with clean water then;
4, with the method for baking continuously adhesive plaster is dried and batched and pack.
Bake out temperature is 70～150 ℃, and the time is 5～15 minutes.
The production equipment of silica gel waterproof cloth, successively by calender 1, elastic woven material 2, the silicon rubber that modulates (Containing Sulfur agent) 3, guiding roller group 4, silicon rubber vulcanization chamber conveyer belt 5, silicon rubber vulcanization chamber 6, powder coating conveyer belt 7, powder coating screen cloth band 8 cleans water tank 9, fountain brush cleaning device 10, drying chamber conveyer belt 11, drying chamber 12, batching packing device 13 constitutes.
Silica gel waterproof cloth of the present invention can apply to the aquatic sports field.
Compared with prior art, the present invention has following beneficial effect:
The present invention adopts silicon rubber to combine with elastic woven material and makes the elastic water-proof cloth that aquatic sports is used, the silicon rubber that constitutes cloth has better elastic, be difficult for agingly, and by silicon rubber and elastic woven material are combined closely, make the elasticity of the present invention cloth good springiness of using waterborne, cracking resistance, anti-exfoliation ability is strong, gas permeability, and drainage and retractility are good, satisfied the needs of aquatic sports clothes, also can reach harmless purpose simultaneously by using FDA level sizing material.
Description of drawings
Fig. 1 is the structural representation of silica gel waterproof cloth of the present invention;
Fig. 2 is the technological process of production figure of silica gel waterproof cloth of the present invention;
Fig. 3 is the production equipment structural representation of silica gel waterproof cloth of the present invention.
The specific embodiment
Come the present invention is further described below in conjunction with Figure of description, but the present invention's scope required for protection is not limited to the scope that embodiment is described to.
Accompanying drawing 1 is the structural representation of silica gel waterproof cloth of the present invention;
Wherein, 1 is silastic-layer, and 2 is the elastical cloth bed of material.
Accompanying drawing 2 is the technological process of production figure of silica gel waterproof cloth of the present invention;
The preparation flow of the silica gel waterproof cloth of embodiment 1～5 all carries out according to the technological process of production figure of accompanying drawing 2.
Accompanying drawing 3 is the production equipment structural representation of silica gel waterproof cloth of the present invention;
Wherein, 1 is calender, and 2 is elastic woven material, 3 is the silicon rubber (Containing Sulfur agent) that modulates, and 4 are guiding roller group, and 5 is silicon rubber vulcanization chamber conveyer belt, 6 is the silicon rubber vulcanization chamber, 7 is the powder coating conveyer belt, and 8 is powder coating screen cloth band, and 9 for cleaning water tank, 10 is the fountain brush cleaning device, 11 is the drying chamber conveyer belt, and 12 is drying chamber, and 13 is the batching packing device.
Embodiment 1
The production technology of silica gel waterproof cloth comprises following technical step:
1, silicon rubber is rolled on the elasticity cloth cover with the method for calendering;
Wherein, used silicon rubber is simple silicon rubber;
2, the method with baking continuously makes silicon rubber vulcanization;
The temperature of baking sulfuration is 100 ℃, and the time is 10 minutes;
3, talcum powder is coated in equably the surface of silicon rubber, falls unnecessary talcum powder with flushing with clean water then;
4, with the method for baking continuously adhesive plaster is dried and batched and pack.
Bake out temperature is 70 ℃, and the time is 15 minutes.
Embodiment 2
The production technology of silica gel waterproof cloth comprises following technical step:
1, silicon rubber is rolled on the elasticity cloth cover with the method for calendering;
Wherein, used silicon rubber is the silicon rubber that scribbles FAD level sizing material;
2, the method with baking continuously makes silicon rubber vulcanization;
The temperature of baking sulfuration is 175 ℃, and the time is 2 minutes;
3, talcum powder is coated in equably the surface of silicon rubber, falls unnecessary talcum powder with flushing with clean water then;
4, with the method for baking continuously adhesive plaster is dried and batched and pack.
Bake out temperature is 150 ℃, and the time is 5 minutes.
Embodiment 3
The production technology of silica gel waterproof cloth comprises following technical step:
1, silicon rubber is rolled on the elasticity cloth cover with the method for calendering;
Wherein, used silicon rubber is the silicon rubber that scribbles FAD level sizing material;
2, the method with baking continuously makes silicon rubber vulcanization;
The temperature of baking sulfuration is 140 ℃, and the time is 6 minutes;
3, talcum powder is coated in equably the surface of silicon rubber, falls unnecessary talcum powder with flushing with clean water then;
4, with the method for baking continuously adhesive plaster is dried and batched and pack.
Bake out temperature is 110 ℃, and the time is 10 minutes.
Embodiment 4
The production technology of silica gel waterproof cloth comprises following technical step:
1, silicon rubber is rolled on the elasticity cloth cover with the method for calendering;
Wherein, used silicon rubber is the silicon rubber that scribbles FAD level sizing material;
2, the method with baking continuously makes silicon rubber vulcanization;
The temperature of baking sulfuration is 120 ℃, and the time is 8 minutes;
3, talcum powder is coated in equably the surface of silicon rubber, falls unnecessary talcum powder with flushing with clean water then;
4, with the method for baking continuously adhesive plaster is dried and batched and pack.
Bake out temperature is 85 ℃, and the time is 13 minutes.
Embodiment 5
The production technology of silica gel waterproof cloth comprises following technical step:
1, silicon rubber is rolled on the elasticity cloth cover with the method for calendering;
Wherein, used silicon rubber is the silicon rubber that scribbles FAD level sizing material;
2, the method with baking continuously makes silicon rubber vulcanization;
The temperature of baking sulfuration is 160 ℃, and the time is 4 minutes;
3, talcum powder is coated in equably the surface of silicon rubber, falls unnecessary talcum powder with flushing with clean water then;
4, with the method for baking continuously adhesive plaster is dried and batched and pack.
Bake out temperature is 130 ℃, and the time is 7 minutes.
Claims (7)
1, silica gel waterproof cloth is characterized in that having double-decker, is made of the silastic-layer (1) and the elastical cloth bed of material (2) successively.
2, silica gel waterproof cloth according to claim 1 is characterized in that described silastic-layer is regular grade silicon rubber or FDA level silicon rubber.
3, the production technology of claim 1 or 2 described silica gel waterproof cloths is characterized in that comprising the steps:
(1) silicon rubber is rolled on the elasticity cloth cover with the method for calendering;
(2) method with baking continuously makes silicon rubber vulcanization;
(3) talcum powder is coated in equably the surface of silicon rubber, falls unnecessary talcum powder with flushing with clean water then;
(4) with the method for baking continuously adhesive plaster is dried and batched and pack.
4, the production technology of silica gel waterproof cloth according to claim 3 is characterized in that the temperature of the baking sulfuration of step (2) is 100～175 ℃, and the time is 2～10 minutes.
5, the production technology of silica gel waterproof cloth according to claim 3, the bake out temperature that it is characterized in that step (4) is 70～150 ℃, the time is 5～15 minutes.
6, the production equipment of claim 1 or 2 described silica gel waterproof cloths is characterized in that successively by calender (1) elastic woven material (2), the silicon rubber that modulates (3), guiding roller group (4), silicon rubber vulcanization chamber conveyer belt (5), silicon rubber vulcanization chamber (6), powder coating conveyer belt (7), powder coating screen cloth band (8) cleans water tank (9), fountain brush cleaning device (10), drying chamber conveyer belt (11), drying chamber (12), batching packing device (13) constitutes.
7, claim 1 or the 2 described silica gel waterproof cloths utilization in the motion field on the water.