CN1793017A - Mullite whisker-mullite composite coating and preparation process thereof - Google Patents
Mullite whisker-mullite composite coating and preparation process thereof Download PDFInfo
- Publication number
- CN1793017A CN1793017A CN 200510019865 CN200510019865A CN1793017A CN 1793017 A CN1793017 A CN 1793017A CN 200510019865 CN200510019865 CN 200510019865 CN 200510019865 A CN200510019865 A CN 200510019865A CN 1793017 A CN1793017 A CN 1793017A
- Authority
- CN
- China
- Prior art keywords
- mullite
- coating
- raw material
- slip
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to mullite crystal whisker mullite compounding coating layer that the manufacture method includes the following steps: coating the mixture slime of silica sol, aluminum sol and mullite slime in vacuum of the basal material, or coating orderly, under the catalyzing effect of metal fluoride mineralizer, sintering by high temperature. The invention is simple structure, low cost of raw material, acid proof, alkali proof, etc. it could improve the intension of the material and prolong the use life.
Description
Technical field
The present invention relates to field of non-metallic materials, particularly a kind of mullite crystal whisker-mullite compound coating and preparation method thereof.
Background technology
In recent years, along with high-temperature structural ceramics particularly non-oxidized substance structural ceramics (, silicon carbide grand, silicon nitride ceramics etc.) as matching in the widespread use in each field, both at home and abroad progressively deeply to the research of this type of ceramic oxidation resistant coating.The high-temperature oxidation resistant coating that is used for non-oxide ceramics at present is mainly systems such as molybdenum disilicide, aluminum oxide, silicon oxide, spinel, mullite.Mullite has excellent mechanical property, and its coefficient of thermal expansion coefficient of thermal expansion with non-oxide ceramics such as silicon carbide in quite wide scope is close, and the preparation technology of mullite coating is simple, cheap.The good stability that the mullite coating is showed under oxidizing atmosphere and acidity, alkaline condition makes it have a good application prospect in the high-temperature oxidation resistant coating field.Apply the silica-based non-oxide ceramics of mullite coating; in use in fact can form new silicon-dioxide because of the matrix oxidation; and become silicon-dioxide and mullite compound coating; because there is the phase transformation volume effect in silicon-dioxide in the time of 723 ℃; there is small difference after all in the coefficient of thermal expansion of mullite coating and matrix in addition; therefore under frequent thermal cycle impact, cause coating cracking easily, the provide protection of mullite coating is reduced.Whisker can effectively be born transformation stress as a kind of material of almost flawless high-strength, high elastic coefficient, hinders the expansion of crackle, increases the toughness of coating, thereby improves the thermal-shock resistance of coating.The synthetic method of mullite crystal whisker was constantly expanded in the last few years, but the preparation condition of mullite crystal whisker is still comparatively harsh, and the difficulties in dispersion of whisker, the low mucilage material preparation difficulty of high whisker content, if directly in coating preparation, add whisker, will the production cost of coating be increased sharply.
At present, the method for preparing the mullite coating mainly contains: sluny impregnation cladding process, sol-gel method, spraying slurry process, squeegee process, plasma spraying method, vapour deposition process etc.It mainly is to adopt the sluny impregnation method that ceramic surface is applied the mullite coating, but because of the coating particles particle diameter is bigger, undesirable for the infiltration of micropore in the matrix, coat-thickness is inhomogeneous, easily cause coating cracking, the sintering temperature of mullite is very high in addition, is difficult to obtain fine and close coating.Sol-gel can prepare uniform coating, and the thermal treatment temp of coating is low, but the colloidal sol solid content is very low, needs ten to apply the coating that just can obtain micron order thickness for several times, and colloidal sol is dry and easy to crack during sintering, causes coating damaged; Plasma spraying and squeegee process can only form coating at matrix surface.Though vapour deposition process can obtain coating than the depths at matrix, vapour deposition requires very high to equipment, processing parameter, Working environment, and industrial applications is restricted.
Summary of the invention
Technical problem to be solved by this invention is: a kind of problem that exists at above coating technology is provided, employing has the mullite chemistry and measures the sol-gel of ratio and the compound slip of pre-mullite synthesizing micro mist, improves the sintering temperature of the solid content and the reduction coated material of slip.By introducing suitable mineralizer, original position mullite synthesizing whisker in the coating sintering process obtains to have the fine and close mullite crystal whisker-mullite composite ceramic coating of toughening effect at a lower temperature.
The technical solution adopted for the present invention to solve the technical problems is as follows:
Mullite crystal whisker provided by the invention-mullite compound coating, it is obtained by in-situ synthetic method, that is: be that raw material forms compound slip with aluminium colloidal sol, silicon sol and mullite slip, under vacuum, body material is applied, dry back sintering, under the katalysis of metal fluoride mineralizer, original position mullite synthesizing whisker-mullite compound coating.
The preparation method of original position mullite synthesizing whisker provided by the invention-mullite compound coating, its step is as follows:
(1) preparation mullite slip: aluminum raw material, quartzose raw material are prepared burden than the requirement that meets mullite chemistry metering ratio according to aluminum oxide and silicon-dioxide quality, and mix with the water of raw material total mass 30~50%, ball milling 10~24 hours, the metal fluoride mineralizer that adds raw material total mass 4-10% again, ball milling 1~2 hour, be shaped to block base substrate, base substrate is in 1 hour mullite synthesizing of 1400~1550 ℃ of insulations, then through pulverize and ball milling to obtain median size be 0.5~1.5 μ m mullite slip; Perhaps, directly use industrial electrofused mullite to be raw material, add the metal fluoride mineralizer of raw material total mass 4-10%, obtain through pulverizing and ball milling then.
(2) applying coating: coated body material is applied the compound slip that stoichiometric ratio meets silicon sol, aluminium colloidal sol and the mullite slip of mullite composition in vacuum, or successively silicon-coating colloidal sol, aluminium colloidal sol, mullite slip successively in a vacuum, or vacuum silicon-coating colloidal sol, aluminium colloidal sol and metal fluoride supersaturated solution successively; Or be raw material with tetraethoxy and the aluminium salt that meets mullite chemistry metering ratio, adopt hydrolysis-coprecipitation method deposition oxide, apply the mullite slip again; Material after the coating is 60~90 ℃ of dryings.
(3) with dried coating material 1100~1500 ℃ of sintering 1~3 hour, obtain original position mullite synthesizing whisker-mullite compound coating.
The present invention compared with prior art has following unusual effect:
One. employing has the sol-gel of mullite chemistry metering ratio and the method for the pre-compound slip of mullite synthesizing micro mist prepares the high slip of solids content, and it is moderate to help obtaining thickness, does not have the coating of dry and cracked line; The coating that has overcome simple colloidal sol coating is thin, dry problem easy to crack.
Shown by Fig. 2, Fig. 3: mullite crystal whisker of the present invention-mullite compound coating thickness distribution is even, original position grows a great deal of mullite crystal whisker with certain length-to-diameter ratio in the mullite coating, whisker concentration is higher, after 40 heat resistanceheat resistant circulation impacts (room temperature~1200 ℃) experiment, coating does not have cracking phenomena.
Shown by Fig. 4, Fig. 5: traditional single mullite coat-thickness is very inhomogeneous, after 40 heat resistanceheat resistant circulation impacts (room temperature~1200 ℃) experiment, tangible crackle occurs along the trench of coating.
They are two years old. and reduce the sintering temperature of mullite crystal whisker-mullite compound coating with highly active aluminium matter or siliceous raw material, helped coating agglomerating densification (see figure 2).
They are three years old. and under the mineralizer effect, synthesized mullite crystal whisker-mullite compound coating, made coating have the excellent high-temperature oxidation-resistance, thermal-shock resistance and acid-alkali-corrosive-resisting performance (see figure 6) with highly active raw material original position; Improved traditional single mullite coating deficiency (seeing Fig. 4 and Fig. 5) in these areas.
Fig. 6 has shown mullite crystal whisker of the present invention-mullite compound coating and traditional single mullite coating oxidation weightening finish correlation curve.To be the material that will apply mullite crystal whisker-mullite compound coating draw after 40 heat resistanceheat resistant circulation impacts (room temperature~1200 ℃) experiment this curve.
The experiment of above-mentioned heat resistanceheat resistant circulation impact, its method is: placing constant temperature 1200 ℃ electric furnace insulation 15 minutes in sample, with crucible sample is taken out and be cooled to room temperature in air, and then place 1200 ℃ electric furnace to be incubated, so is a circulation.Repeat above operation 40 times.As shown in Figure 6, the increasing weight of oxidation of compound coating of the present invention only is half of traditional single coating.
They are four years old. and technology is simple, and raw material sources are extensive, technology is simple, and production cost is low.
They are five years old. are widely used: can be widely used in light industry, chemical industry and field of aerospace, be particularly suitable as high temperature non-oxidized substance structural ceramics, satellite posture adjustment rocket throat liner material, C-C composite etc. and need stand anti-oxidant, the anti-thermal shock coating of thermal shocking material and enhancing, the toughness reinforcing phase of porous materials such as filtering material, heat-insulation and heat-preservation material and support of the catalyst repeatedly, the performance of material be can improve, the use range of material and the work-ing life of prolongation material widened.
Description of drawings
Fig. 1: the X-ray diffraction of mullite (XRD) spectrogram in the mullite slip.
Fig. 2: 2000 times scanning electron microscope (SEM) figure of the mullite crystal whisker-mullite compound coating of the present invention's preparation after 40 thermal cycle impact experiments.
Fig. 3: 10000 times scanning electron microscope (SEM) figure of the mullite crystal whisker-mullite compound coating of the present invention's preparation after 40 heat resistanceheat resistant circulation impact experiments.
Fig. 4: the 5000 times SEM figures of traditional single mullite coating after 40 heat resistanceheat resistant circulation impact experiments.
Fig. 5: the 10000 times side SEM figures of traditional single mullite coating after 40 heat resistanceheat resistant circulation impact experiments.
Fig. 6: mullite crystal whisker of the present invention-mullite compound coating and traditional single mullite coating oxidation weightening finish correlation curve.
Among above-mentioned Fig. 2, Fig. 3, Fig. 4 and Fig. 5, the thermal cycle impact experimental temperature is room temperature~1200 ℃.
Embodiment
The present invention relates to a kind of mullite crystal whisker-mullite compound coating and preparation method thereof.
The invention will be further described below in conjunction with embodiment and accompanying drawing.
One. mullite crystal whisker-mullite compound coating
Mullite crystal whisker-mullite compound coating is obtained by in-situ synthetic method, that is: be that raw material forms compound slip with aluminium colloidal sol, silicon sol and mullite slip, under vacuum, body material is applied, dry back sintering, under the katalysis of metal fluoride mineralizer, original position mullite synthesizing whisker-mullite compound coating, the thickness of this coating are 1~5 μ m.
The collection of illustrative plates that shows from Fig. 1 is as can be known: mullite crystal whisker-mullite compound coating, be main crystallization phases mutually with mullite, and contain a spot of aluminum oxide and quartz.
Two. the method for original position mullite synthesizing whisker-mullite compound coating
Present method is: by successively silicon-coating colloidal sol, aluminium colloidal sol, mullite slip in the body material vacuum, or the mixed slurry of employing vacuum coat silicon sol, aluminium colloidal sol and mullite slip, or be that raw material adopts hydrolysis-coprecipitation method deposition oxide to apply the mullite slip again with tetraethoxy and the aluminium salt that meets mullite chemistry metering ratio, under the catalysis of metal fluoride mineralizer, through high temperature sintering original position mullite synthesizing whisker-mullite compound coating.
(1) present method adopts preparation, applying coating and three steps of coating sintering of mullite slip, and is specific as follows:
1. prepare the mullite slip: aluminum raw material, quartzose raw material are prepared burden than the requirement that meets mullite chemistry metering ratio according to aluminum oxide and silicon-dioxide quality, and mix with the water of raw material total mass 30~50%, ball milling 10~24 hours, the metal fluoride mineralizer that adds raw material total mass 4-10% again, ball milling 1~2 hour, be shaped to block base substrate, base substrate is in 1 hour mullite synthesizing of 1400~1550 ℃ of insulations, then through pulverize and ball milling to obtain median size be 1~2 μ m mullite slip; Perhaps, directly use industrial electrofused mullite raw material, add the metal fluoride mineralizer of raw material total mass 4-10%, obtain through pulverizing and ball milling then.
Above-mentioned aluminum raw material aluminum raw material can be selected aluminum oxide, aluminium hydroxide, aluminium colloidal sol, exsiccated ammonium alum, aluminium salt, clay, kaolin for use, perhaps a kind of by in the aluminum-containing raw material, or its mixture obtains.The quartzose raw material can be selected white carbon black, silicon sol etc. for use.The mineralizer agent is a metal fluoride, as: AlF
3, CaF
2, BaF
2Deng.
2. applying coating: coated body material is applied the compound slip that stoichiometric ratio meets silicon sol, aluminium colloidal sol and mullite slip that mullite forms in vacuum, or successively silicon-coating colloidal sol, aluminium colloidal sol, mullite slip successively in a vacuum, or vacuum silicon-coating colloidal sol, aluminium colloidal sol and metal fluoride supersaturated solution successively; Or be raw material with tetraethoxy and the aluminium salt that meets mullite chemistry metering ratio, adopt hydrolysis-coprecipitation method deposition oxide, apply the mullite slip again; Material after the coating is 60~90 ℃ of dryings.
3. coating sintering: dried coating material 1100~1500 ℃ of sintering 1~3 hour, is obtained original position mullite synthesizing whisker-mullite compound coating.The XRD spectra of mullite synthesizing is seen Fig. 1.
Based on forming new silicon-dioxide after the silica-based non-oxide ceramics oxidation, the prescription of coating of the present invention can be designed as the mullite of rich aluminium and forms.
(2) specific embodiment
Embodiment 1:
(1) preparation of mullite slip: with ultra-fine industrial α-Al
2O
3Micro mist (AL
2O
3〉=99.6%, d
50≤ 1.0 μ m) and industrial quartz micropowder (SiO
2〉=99.1%, d
50≤ 1.0 μ m) add 5% alumina sol (pH:6.7~7.3, Al for raw material
2O
310 ± 0.5%) and silicon dioxide gel (pH:6.5~8.0, SiO concentration:
2Concentration: 30 ± 1%) make the aluminum oxide and the proportioning of silicon-dioxide meet the metering of mullite chemistry than (Al
2O
3: SiO
2Mass ratio is 3: 1), add 6%BaF
2(chemical pure) regulates pH value to 7.0~8.0, and according to material: ball: water is 1: 1: 0.5 ratio ball milling 10~24 hours, and injection forming is a base substrate, and base substrate is incubated 1~3 hour mullite synthesizing at 1400~1550 ℃.The synthetic mullite is crushed to below the 2mm, and by material: ball: water is to place planetary ball mill ball milling 2h at 1: 1.5: 0.4, makes particle diameter d
50The slip of≤1.5 μ m.
(2) applying coating: (vacuum tightness is 1~2 * 10 in vacuum with re-crystallized silicon carbide
4Pa) apply SiO
2Colloidal sol (pH:6.5~8.0, SiO
2Content: 30 ± 1%, with material 70~80 ℃ of dryings; (vacuum tightness is 1~2 * 10 to vacuum
4Pa) apply Al
2O
3Colloidal sol, 70~80 ℃ slowly dry.The mixed slurry (the relative mass content of mullite is 35 ± 3%) of vacuum coat mullite and silicon, aluminium colloidal sol (the pH value is 7.0~8.0), 70~80 ℃ of dryings.Two step processes of above-mentioned coating 3 times are repeatedly guaranteed the thickness of coating.Sintering 1~2h densification in 1200~1400 ℃ of air.
(3) apply the packing layer: the high quartzy borosilicate glass that will prepare in advance is by material: water: the ball ratio be 1: 1: 0.4 at planetary ball mill ball milling 1~2h (pan feeding particle diameter≤4mm) wear into the glass slip is got glass slip (d
50≤ 1.0 μ m), (vacuum tightness is 1~2 * 10 in vacuum coat
4Pa) sample of preparation is in 70~80 ℃ of dryings in.
(4) coating sintering: the stupalith of the good coating of packing is incubated a hour in 1300~1500 ℃ of following atmospheric airs, makes glass coating melt packing coating, coating densification, original position mullite synthesizing whisker-mullite compound coating.
Embodiment 2:
(1) preparation of mullite slip: with kaolin is main raw material (SiO
2: 52 ± 0.5%, Al
2O
3: 45 ± 0.5%, d
50≤ 2.0 μ m), add Al according to clay component
2O
3And SiO
2(granularity, purity is with embodiment 1), the ratio of regulating both makes it meet mullite proportioning (Al
2O
3: SiO
2Mass ratio is 3: 1), add 8%BaF
2Make mineralizer.Ball milling, moulding, sintering also prepare the mullite slurry process with embodiment 1.
(2) applying coating: with re-crystallized silicon carbide vacuum coat SiO
2Colloidal sol (pH:6.5~8.0, SiO
210 ± 1%) and Al content:
2O
3Colloidal sol (with embodiment 1) repeats 3 times.Vacuum coat mullite slip, 70~80 ℃ of dryings.The visual particular case repeatable operation of two step processes that applies 3 times is guaranteed the thickness of coating.Material after the coating is sintering (with embodiment 1) in 1100~1400 ℃ of air.
In this example, its coating packing layer and coating densification steps are all with embodiment 1.
Embodiment 3:
(1) preparation of mullite slip: with the BaF of industrial electrofused mullite and its quality 5%
2, 5% AlF
3At the planetary ball mill ball milling, be prepared into mullite slip (mullite particle d
50=1.5 μ m).
(2) applying coating: be 11% silicon nitride combined silicon carbide material vacuum coat SiO with void content
2Colloidal sol, dry (with embodiment 2).Vacuum coat Al
2O
3Colloidal sol, dry (with embodiment 1).Vacuum coat mullite slip, dry (with embodiment 2) guarantees the compactness of coating.Sintering in 1100~1400 ℃ of air (with embodiment 1).
In this example, the step of the coating of its packing layer and the densification of coating is all with embodiment 1.
Embodiment 4:
With re-crystallized silicon carbide at 1200~1300 ℃ of oxidation pre-treatment 24 hours, vacuum coat Al
2O
3Colloidal sol (with embodiment 1), 70~80 ℃ slowly dry down.Vacuum coat 8%AlF
3Supersaturated solution applies AlF
3Want before the supersaturated solution earlier solution to be stirred evenly fast.60~80 ℃ of dryings, repetitive operation 5 times.Then, sintering makes its densification in 1000~1400 ℃ of air, and original position generates mullite crystal whisker-mullite compound coating.
Embodiment 5: replace pre-oxidation treatment among the embodiment 4 with vacuum coat silicon sol (with embodiment 2), original position generates mullite crystal whisker-mullite compound coating (with embodiment 4)
Embodiment 6:
(1) preparation of mullite slip is with embodiment 1.
(2) applying coating: the ethanolic soln of the tetraethoxy of preparation 1.2mol/L, being adjusted to the pH value with rare nitric acid is 2~3, stirring at room left standstill after 2~3 hours 24 hours, mixed with the aluminum nitrate aqueous solution of 0.7mol/L then, did dispersion agent with acetic acid.Slowly adding ammoniacal liquor to pH value is 3~7.5, and solution is precipitated, and post precipitation occurs, adds ammoniacal liquor to pH value fast and reaches 9~9.5, the preparation coprecipitation mixture.(vacuum tightness is 1~2 * 10 in vacuum coat
4Pa) coprecipitation mixture, (vacuum tightness is 1~2 * 10 to the oven dry final vacuum
4Pa) apply 5% supersaturation BaF
2Solution, 70~80 ℃ of dryings, repetitive operation 3 times.Mullite that vacuum coat mixes and aluminium colloidal sol, silicon dioxide gel mixed slurry, sintering in 1200~1400 ℃ of air (with embodiment 1).
In this example, the step of the coating of its packing layer and the densification of coating is all with embodiment 1.
Embodiment 7:
Replace silicon carbide in conjunction with silicon nitride the silicon carbide porous filtering material, then, according to embodiment 3 preparation mullite crystal whisker-mullite compound coatings.
Claims (7)
1. compound coating, it is characterized in that mullite whisker-mullite composite coating, it is obtained by in-situ synthetic method, that is: be that raw material forms compound slip with aluminium colloidal sol, silicon sol and mullite slip, under vacuum, body material is applied, dry back sintering, under the katalysis of metal fluoride mineralizer, original position mullite synthesizing whisker-mullite composite coating.
2. compound coating according to claim 1 is characterized in that: the thickness of mullite whisker-mullite composite coating is 1~5 μ m.
3. the preparation method of a compound coating comprises preparation mullite slip, applying coating and coating sintering, it is characterized in that a kind of preparation method of original position mullite synthesizing whisker-mullite composite coating, and its step is as follows:
(1) preparation mullite slip: aluminum raw material, quartzose raw material are prepared burden than the requirement that meets mullite chemistry metering ratio according to aluminum oxide and silicon-dioxide quality, and mix with the water of raw material total mass 30~50%, ball milling 10~24 hours, the metal fluoride mineralizer that adds raw material total mass 4-10% again, ball milling 1~2 hour, be shaped to block base substrate, base substrate is in 1 hour mullite synthesizing of 1400~1550 ℃ of insulations, then through pulverize and ball milling to obtain median size be 0.5~1.5 μ m mullite slip; Perhaps, directly use industrial electrofused mullite to be raw material, add the metal fluoride mineralizer of raw material total mass 4-10%, obtain through pulverizing and ball milling then,
(2) applying coating: coated body material is applied the compound slip that stoichiometric ratio meets silicon sol, aluminium colloidal sol and the mullite slip of mullite composition in vacuum, or successively silicon-coating colloidal sol, aluminium colloidal sol, mullite slip successively in a vacuum, or vacuum silicon-coating colloidal sol, aluminium colloidal sol and metal fluoride supersaturated solution successively; Or be raw material with tetraethoxy and the aluminium salt that meets mullite chemistry metering ratio, adopt hydrolysis-coprecipitation method deposition oxide, apply the mullite slip again; Material after the coating is 60~90 ℃ of dryings,
(3) with dried coating material 1100~1500 ℃ of sintering 1~3 hour, obtain original position mullite synthesizing whisker-mullite composite coating.
4. the preparation method of compound coating according to claim 3 is characterized in that: original position mullite synthesizing whisker in coating.
5. the preparation method of compound coating according to claim 3, it is characterized in that: aluminum raw material is aluminum oxide, aluminium hydroxide, aluminium colloidal sol, exsiccated ammonium alum, aluminium salt, clay, kaolin, perhaps a kind of by in the aluminum-containing raw material, or its mixture obtains.
6. the preparation method of compound coating according to claim 3 is characterized in that: metal fluoride mineralizer employing AlF
3, CaF
2, BaF
2, perhaps their mixture.
7. the preparation method of compound coating according to claim 3 is characterized in that: the quartzose raw material is white carbon black or silicon sol, silica powder.