CN1776153A - Decorating plate using medical stone leftover and light material and its manufacturing method - Google Patents
Decorating plate using medical stone leftover and light material and its manufacturing method Download PDFInfo
- Publication number
- CN1776153A CN1776153A CNA2005100479267A CN200510047926A CN1776153A CN 1776153 A CN1776153 A CN 1776153A CN A2005100479267 A CNA2005100479267 A CN A2005100479267A CN 200510047926 A CN200510047926 A CN 200510047926A CN 1776153 A CN1776153 A CN 1776153A
- Authority
- CN
- China
- Prior art keywords
- medical stone
- shelving
- broken
- soft material
- biscuit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A decoration plate made from leftover material of medical stone (Maifanshi) and other soft material and making method thereof, the weight ratio of medical stone and soft material is 100 : 10-15. The process contains selecting material, initial integrating, blending, fine integrating, pulverizing, watering, first stuffing, wheel grinding, sieving, second stuffing, drying, press molding, firing, biscuit, checking, polishing and packaging. Said invention has advantages of environment protection, absorbing harmful substance of heavy metal ion in water and hydrogen sulfide in air, stripping out beneficial element to human body such as silicon, iron, copper and zinc etc with stable and reliable making process.
Description
Technical field
The prescription design and the manufacturing technology field of the interior decoration panel that the present invention relates to form by a firing, the prescription that particularly relates to the interior decoration panel of firing with medical stone leftover pieces and soft material designs and the manufacturing technology field.
Background technology
Indoor decorative plate, also claim panel.Present widely used Indoor decorative plate mainly contains ceramic tile, glazed tile, marble tile etc.Wherein glazed tile is because external causes such as friction easily cause glaze to come off; Have indivedual marble radioactivity to exceed standard in the marble tile, long-term contact is detrimental to health.Because medical stone has adsorptivity and stripping property, and is ideal with its make-up room inner trim panels.So-called adsorptivity is exactly that it can absorbing heavy metal ions in water, airborne hydrogen sulfide (H
2S) etc., can reach 78-99% to colibacillary adsorptivity.So-called stripping property is exactly its its elemental silicon to the human body beneficial that contains of energy stripping, iron, copper, zinc etc.But the medical stone mineral resources is original just few especially, and the lumber recovery with medical stone system decoration panel is extremely low in addition.Specification ore and saw lumber leftover pieces completely do not discard in a large number, and are excessive to rare ore resource waste.
Summary of the invention
The objective of the invention is, dress meal plaque and the manufacture method thereof made with medical stone leftover pieces and soft material are provided.
The present invention is achieved through the following technical solutions:
Composition of raw materials is: the weight part ratio of medical stone leftover pieces and soft material is 100: 10～15, and soft material is kaolin or feldspar.
Its technology is described below: can not make the medical stone ore of specification decorative panel and making sheet corner ore through range estimation selection, thick broken, batching, in small, broken bits, grinding, Jia Shui, shelving, wheel are rolled over, are sieved for the first time, activitiess such as secondary shelving, drying, die mould, biscuit check, polishing, finished product packing make the medical stone decoration panel.
In the medical stone Main Ingredients and Appearance be silica, alundum (Al, calcium oxide, magnesia, iron oxide, etc. kind surplus 10; 18 kinds of rare-earth element cerium, 15 kinds of lanthanums and trace element strontium, barium etc.
Kaolin claims china clay again, mainly the mineral of being made up of the trickle crystal of kaolinite.Pure is white.Generally have impurity, gray or faint yellow.Major part is close shape of matter or loose soil block shape.Matter is soft, easily is scattered in water or other liquid.Soapy feeling is arranged and the soil flavor is arranged.
Feldspar is the general name of feldspar family mineral.It is the aluminosilicate of potassium, sodium, calcium and rare barium.White, grey or flesh pink can be used as the raw material of making pottery.
The concrete composition of raw materials and the technology of scheme are described below:
Qualified ore is selected in the range estimation selection.
Just broken, it is the stone of 150mm * 250mm that ore is broken.
Batching: add kaolin, the weight part ratio of the two is 100: 10～15.
In small, broken bits, material is in small, broken bits to≤1mm particle.
Grinding is with improved grinding to 90～120 order fine powders.
Add water, in material, add an amount of water.
Shelving makes material moisture evenly for the first time.
Rolling is with material grind up shape.
Sieve, discard greater than 90 purpose oversizes.
The secondary shelving makes material moisture evenly.
Drying, it is qualified doing material extremely moisture.
Die mould is used forcing press compression moulding.
Burning till, is 1100～1200 ℃ with tunnel cave preheating firing temperature, from the Cooling Section of Tunnel Kiln kiln discharge.
Check, the biscuit check.
Polishing with the sanding machine polishing, checks that packing is finished product.
Advantage of the present invention is, product-forming is attractive in appearance, and environmentally-friendly sanitary, medical stone have the adsorptivity of hazardous substancess such as absorbing heavy metal ions in water and airborne hydrogen sulfide, itself can stripping to human body beneficial's elemental silicon, iron, copper, zinc etc.Its manufacturing technology is reliable, process stabilizing.
Description of drawings
The present invention does not have figure.
The specific embodiment
Raw materials used be can't making sheet medical stone and making sheet leftover pieces and soft material kaolin or feldspar, weight part ratio therebetween is 100: 10～15.Manufacture method is through the range estimation selection, to select qualified ore earlier.With ore with crushing engine just broken to lumpiness be 150mm * 250mm fritter, and be equipped with the kaolin of wanting weight by prescription.Through in small, broken bits, promptly with stone is carefully broken to granularity be≤particle of 1mm with hammer mill.Again through grinding, promptly with ball mill general≤1mm improved grinding to 90～120 order fine powders.Add water, amount of water is as system sun-dried mud brick water supply volume during loam brick.Shelving for the first time, shelving in the shelving storehouse, it is evenly wet that whole material is done, again through rolling, with material grind up shape.Sieve, discard greater than 90 purpose oversizes, again through the secondary shelving.Carry out drying then, deliver in the tunnel dryer vexed good material dry.Dried material friction press die mould.Burn till, slab delivered in the tunnel cave through the preheating zone, clinkering zone and salband, kiln discharge be biscuit.Through polishing,, check that packing is finished product again with the sanding machine polishing.
Embodiment 1:
Selection making sheet medical stone leftover pieces 1000kg, broken with jaw crusher to 150mm * 250mm fritter, and adding 150kg kaolin, be crushed to≤the 1mm particle with hammer mill, with the QT-1.5 ball mill improved grinding is become 90-120 order fine powder again, again material is delivered to shelving in the shelving storehouse, vexed good material rolls with the edge runner of W1500 * 450, sieve, discard granularity greater than 90 order oversizes, undersize material carries out the secondary shelving, expects that vexed sending into after good carry out drying in the 65M tunnel drying kiln, the JT35-60 friction press compression moulding of dry qualified back, shaping slab is delivered to and is carried out preheating in the 115M tunnel cave, burn till, cooling, kiln discharge becomes biscuit.Biscuit is packed on inspection and is finished product with the polishing of BM3170 sanding machine.Product conforms to medical stone decorative panel standard.
Embodiment 2:
Selection can not be made the medical stone 1000kg of dimension board, with its broken piece to 150mm * 250mm, and adds feldspar 135kg with jaw crusher, below is undertaken by activities and the technical condition of embodiment 1.Wherein have be: burning till temperature is 1150 ℃.Product conforms to the standard of medical stone decorative panel.
Claims (3)
1, the decorative panel made from medical stone leftover pieces and soft material, it is characterized in that its constitutive material is medical stone leftover pieces and soft material, the kaolinic weight part ratio of medical stone leftover pieces and soft material is 100: 10～15, above-mentioned raw materials through selection, just broken, batching, thin broken, grinding, Jia Shui, shelving, a rolling, sieve, secondary shelving, drying, die mould, burn till, biscuit check, polishing, packaging process make.
2, decorative panel according to claim 1, its characteristics are that the weight part ratio of medical stone leftover pieces and soft material feldspar is 100: 10～15.
3, the manufacture method of medical stone and soft material decorative panel, it is characterized in that by range estimation selection, just broken, batching, in small, broken bits, grinding, Jia Shui, shelving, a rolling, sieve, secondary shelving, drying, die mould, burn till, biscuit check, polishing, packaging process form
The range estimation selection, the medical stone leftover pieces that sort out is qualified,
Just broken, leftover pieces are just broken into the stone of 150～250mm,
Batching, the weight part ratio of medical stone and soft material 100: 10～15 proportionings add soft material,
In small, broken bits, with the mixed material particle to≤1mm in small, broken bits,
Grinding is ground to 90～120 purpose fine powders with the material particles of≤1mm,
Add water, in fine powder, add suitable quantity of water,
A shelving in the shelving storehouse, makes material moisture evenly,
Rolling, with vexed good material rolling grind up shape,
Sieve, sift out the bulky grain of powder, discard greater than 90 purpose oversizes with sieve,
The secondary shelving is delivered to undersize material and is carried out the secondary shelving in the shelving storehouse,
Drying, vexed good material is dry to the tunnel drying kiln,
Die mould, the material forcing press compression moulding that drying is qualified,
Burn till, the slab of die mould delivered in the tunnel cave in 1100～1200 ℃, burnt till,
The biscuit check is tested to the kiln discharge biscuit,
Polishing is polished with sanding machine the biscuit that is up to the standards,
Packing is packed qualified products.