CN1760348A - 一种铝轧制专用乳化油及其制造方法 - Google Patents

一种铝轧制专用乳化油及其制造方法 Download PDF

Info

Publication number
CN1760348A
CN1760348A CN 200510100711 CN200510100711A CN1760348A CN 1760348 A CN1760348 A CN 1760348A CN 200510100711 CN200510100711 CN 200510100711 CN 200510100711 A CN200510100711 A CN 200510100711A CN 1760348 A CN1760348 A CN 1760348A
Authority
CN
China
Prior art keywords
deddicated
oil
sodium nitrite
emulsified oil
rolling aluminum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510100711
Other languages
English (en)
Inventor
余卓新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200510100711 priority Critical patent/CN1760348A/zh
Publication of CN1760348A publication Critical patent/CN1760348A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铝轧制专用乳化油及其制造方法。主要组分及其所占重量百分比为：5号白矿油45－50％，活性物35－40％的石油磺酸钠15－20％，硫化油5－8％，亚硝酸钠2－5占OP－106－9％，司本－80占3－7％，清水12－16％，5号白矿油、活性物35－40％的石油磺酸钠、硫化油、OP－10、司本－80依次加入转速1800－2000转/分的高切剪乳化机中搅拌均匀；同时将亚硝酸钠、清水加入开口桶中搅拌，直至亚硝酸钠完全溶解，然后再将溶有亚硝酸钠的清水加入剪切乳化机中，继续搅拌30分钟左右，即配制为原液，原液按1∶10－15稀释后即得乳化油。本发明乳化油按1∶10－15用水稀释后用于铝的热轧、冷轧和连铸连轧等铝的轧制加工，可大大降低轧槽、轧机的磨损，其冷却、防锈、抗发黑能力优良。

Description

一种铝轧制专用乳化油及其制造方法
技术领域
本发明涉及润滑剂技术领域，更具体的是一种铝轧制专用乳化油及其制造方法。
背景技术
在铝轧制行业中，热轧铝的温度高达280℃-320℃，如此高的轧制温度对铝轧制油提出了较高的冷却、润滑、防锈性能要求。目前使用的铝轧制油存在由于冷却、防锈性较差，导致铝产品表面氧化，严重发黑的现象；同时由于润滑性能不足，导致铝产品表面起槽。因而，冷却、润滑、防锈性能优良的铝轧制油是市场一个需求发展方向。
发明内容
本发明的目的是提供一种冷却、防锈、润滑性能优良的铝轧制用乳化油及其制造方法。
本发明通过下述技术方案予以实现，一种铝轧制专用乳化油，主要组分及其所占重量百分比如下，
  序号   组分名称   重量百分比(100％)
  1   5号白矿油   45-50
  2   活性物35-40％的石油磺酸钠   15-20
  3   硫化油   5-8
  4   亚硝酸钠   2-5
  5   OP-10   6-9
  6   司本-80   3-7
  7   清水   12-16
这种铝轧制专用乳化油的制作方法是：5号白矿油、活性物35-40％的石油磺酸钠、硫化油、OP-10、司本-80依次加入转速1800-2000转/分的高切剪乳化机中搅拌均匀；同时将亚硝酸钠、清水加入开口桶中搅拌，直至亚硝酸钠完全溶解，然后再将溶有亚硝酸钠的清水加入剪切乳化机中，继续搅拌30分钟左右，即配制为铝轧制专用乳化油原液，原液按1∶10-15稀释后即得可直接使用的铝轧制专用乳化油。
本发明乳化油按1∶10-15用水稀释后用于生产铝杆、铝板、铝带的热轧、冷轧和连铸连轧等铝的轧制加工工艺，可大大降低轧槽、轧机的磨损，其冷却、防锈、抗发黑能力优良，产品表面光洁度高、不起槽、防锈周期长、且无毒无刺激味，操作方便。
具体实施例
以下结合一较佳实施例对本发明作进一步描述，
一、实施例配方见下表：
  序号   组分名称   重量(kg)
  1   5号白矿油   1050
  2   活性物35-40％的石油磺酸钠   378
  3   硫化油   126
  4   亚硝酸钠   42
  5   OP-10   124
  6   司本-80   63
  7   清水   336
二、制作方法：
按照上表中的各组分重量配比，将5号白矿油1050kg、活性物35-40％的石油磺酸钠378kg、硫化油126kg、OP-10124kg、司本-8063kg依次加入转速1800-2000转/分的高剪切乳化机中搅拌均匀；同时将亚硝酸钠42kg、清水336kg加入开口桶中搅拌，直至亚硝酸钠完全溶解，然后再将溶有亚硝酸钠的清水加入剪切乳化机中，继续搅拌30分钟，即配制为铝轧制专用乳化油原液，原液按1∶10-15稀释后即得可直接使用的铝轧制专用乳化油。
三、制得的产品性能指标如下：
  序号   项目   试验结果
  1   运动粘度(40℃) mm2/s   40
  2   凝点℃   -6
  3   冻融性(-8℃冻凝)   恢复室温，保持原油基本外观
  4   乳化液消泡性(55℃±2℃min)ml   2
5   5％乳化液腐蚀性(55℃±2℃全浸T3铜片24h) 1级
  6   析皂量   无
以上所述之实施例只为本发明的较佳实施例，并非以此限制本发明的实施范围，故凡依本发明之组分重量百分比、方法及原理所作的等效变化，均应涵盖于本发明的保护范围内。

Claims (2)

1、一种铝轧制专用乳化油，其特征在于：主要组分及其所占重量百分比如下，   序号   组分名称   重量百分比(100％)   1   5号白矿油   45-50   2   活性物35-40％的石油磺酸钠   15-20   3   硫化油   5-8   4   亚硝酸钠   2-5   5   OP-10   6-9   6   司本-80   3-7   7   清水   12-16
2、一种铝轧制专用乳化油的制作方法，其特征在于：首先将45-50％的5号白矿油、活性物35-40％的石油磺酸纳15-20％、硫化油5-8％、OP-102-5％、司本-803-7％依次加入转速1800-2000转/分的高切剪乳化机中搅拌均匀，同时将亚硝酸钠2-5％、清水12-16％加入开口桶中搅拌，直至亚硝酸钠完全溶解，然后再将溶有亚硝酸钠的清水加入剪切乳化机中，继续搅拌30分钟左右，即配制为铝轧制专用乳化油原液，原液按1∶10-15稀释后即得可直接使用的铝轧制专用乳化油。
CN 200510100711 2005-10-31 2005-10-31 一种铝轧制专用乳化油及其制造方法 Pending CN1760348A (zh)