CN1757828A - 一种添加泡沫沥青的沥青冷再生方法 - Google Patents

一种添加泡沫沥青的沥青冷再生方法 Download PDF

Info

Publication number
CN1757828A
CN1757828A CN 200410051746 CN200410051746A CN1757828A CN 1757828 A CN1757828 A CN 1757828A CN 200410051746 CN200410051746 CN 200410051746 CN 200410051746 A CN200410051746 A CN 200410051746A CN 1757828 A CN1757828 A CN 1757828A
Authority
CN
China
Prior art keywords
asphalt
blowing agent
pavement
mixing drum
inorganic binder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200410051746
Other languages
English (en)
Inventor
周君
鲁红春
何唯平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenzhen Oceanpower Industrial Co Ltd
Original Assignee
Shenzhen Oceanpower Industrial Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenzhen Oceanpower Industrial Co Ltd filed Critical Shenzhen Oceanpower Industrial Co Ltd
Priority to CN 200410051746 priority Critical patent/CN1757828A/zh
Publication of CN1757828A publication Critical patent/CN1757828A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种通过添加泡沫沥青实现沥青现场冷再生的方法，具体为沥青路面再生施工时，在前面用一台红外线板加热机或燃料加热机将旧沥青路面加热至大约 160℃左右，在加热机的后面紧跟一台复拌机，把路面翻松，将混合料回收至搅拌筒内，添加0.5％的水泥与混合料一起搅拌，最后再喷洒3％的泡沫沥青并搅拌混匀，将拌好的再生沥青混合料泵送至摊铺槽进行摊铺成型，5分钟后用压路机碾压密实。

Description

一种添加泡沫沥青的沥青冷再生方法
                        技术领域
本发明涉及一种沥青冷再生的方法，尤其是一种添加泡沫沥青的沥青冷再生方法。
                        背景技术
我国公路建设发展迅速，迄今全国高速公路里程已超过3万公里，位居世界第二位。我国东部地区已初步形成高速公路网，另外高等级公路已突破50万公里，其中绝大部分是沥青路面。
据估计我国公路建设每年沥青用量已突破1200万吨，道路建设与养护消耗了大量的沥青。仅2003年一年，全国道路建设耗用沥青就高达750万吨，其中进口沥青180万吨。石油资源是不可再生资源，过度的开采将造成资源的枯竭。过去用于高速公路摊铺的沥青混凝土，全被当作废料处理掉了，不利于环保，也浪费了资源。使用沥青再生专用设备后，老化的路面沥青铲除后，只要进入高温搅拌机进行加热，运用相关技术后就可以再利用，不仅节约了资源，而且大大降低了生产成本。
从节约资源的角度出发，将旧沥青路面通过再生加以重复利用是一项行之有效的措施。目前，世界各国积极开展沥青路面再生利用的研究与应用，沥青路面再生可以分为冷再生和热再生两种，而热再生按再生地点的不同又可以分为集中厂拌再生和就地热再生。(1)集中厂拌再生，集中厂拌再生将回收的旧沥青路面材料破碎，以20％～30％的比例加入拌和机的拌缸中，依靠新集料的热量使旧料加热而松散。加入新沥青继续拌和，使新料与旧料充分拌和均匀，即成再生沥青混合料而可以用于路面铺筑。但是集中厂拌再生只能掺加20～30％旧料，旧料利用率较低而影响经济效益，沥青拌和厂需要有旧料堆放场地并配备专用的破碎机械。集中厂拌再生在我国公路维修中已经应用了多年，其缺点也越来越明显，旧路面材料的利用率低，废弃料的处理及环境污染等方面存在很多问题，维修时间长，对交通的干扰大等，一般只能用于基层或低级路面的翻修，需要专门的工厂来处理沥青混合料，成本较高。(2)就地热再生，这种再生法就是利用沥青热再生联合机组就地完成沥青路面的热再生修复。原有路面材料可100％的利用，不需要搬运废料及废弃物堆放场地，可减少环境污染；能够改变个别的混合料成分，以便给定沥青混合料的最佳配比；可以快速就地再生，并随着工程进度开放道路交通，对交通干扰最小。
                        发明内容
本发明公开了一种添加泡沫沥青的沥青冷再生方法，其再生方法包括如下几个步骤：(1)用一台红外线板加热机或燃料加热机将旧沥青路面加热到140～180℃，后面紧跟一台复拌机，将路面翻松，紧接着把翻松后的混合料回收至搅拌筒内；(2)在搅拌筒中加入0.5～1％(质量百分比)的无机结合料，与回收的旧料一起混合搅拌均匀；(3)往搅拌筒中喷洒2～5％的泡沫沥青，并充分拌和均匀，最后将再生沥青混合料泵送至后部的摊铺槽摊铺成型，5分钟后用压路机碾压密实。
本发明添加的无机结合料，可以是水泥或石灰或粉煤灰，泡沫沥青是由高温热融沥青(130～150℃)和发泡剂或水混合而成，其中高温热融沥青占94～97％(体积百分比)，发泡剂或水占3～6％(体积百分比)。泡沫沥青的制备：在高温热熔沥青中加入冷水(20～25℃)或发泡剂，加入后沥青迅速发泡，体积膨胀10～15倍，同时粘度降低，能够与集料在常温下拌和。泡沫沥青也可以在常温下储存，随时提供应用。发泡剂可以选用偶氮二甲酰胺或发泡剂BN或发泡剂DPT或发泡剂TSH等，
                        具体实施方式
实施例1在容量为5t的沥青罐里用导热油将200kg的重交AH-90沥青加热至135℃，然后加入10Kg的偶氮二甲酰胺发泡剂，开动搅拌叶片，沥青迅速发泡，体积膨胀10～15倍，即制得泡沫沥青。
沥青路面再生施工时，在前面用一台红外线板加热机或燃料加热机将旧沥青路面加热至大约160℃左右，在加热机的后面紧跟一台复拌机，把路面翻松，将混合料回收至搅拌筒内，添加0.5％的水泥与混合料一起混合，最后喷洒3％的泡沫沥青搅拌并混匀，将拌好的再生沥青混合料泵送至摊铺槽进行摊铺，5分钟后用压路机碾压密实。

Claims (4)

1、一种添加泡沫沥青的沥青冷再生方法，其特征在于包括如下几个步骤：(1)用一台红外线板加热机或燃料加热机将旧沥青路面加热到140～180℃，后面紧跟一台复拌机，将路面翻松，紧接着把翻松后的混合料回收至搅拌筒内；(2)在搅拌筒中加入0.5～1％(质量百分比)的无机结合料，与回收的旧料一起混合搅拌均匀；(3)往搅拌筒中喷洒2～5％的泡沫沥青，并充分拌和均匀，最后将再生沥青混合料泵送至后部的摊铺槽摊铺成型，5分钟后用压路机碾压密实。
2、根据权力要求1所述的无机结合料，其特征在于所添加的无机结合料可以是水泥或石灰或粉煤灰。
3、根据权力要求1所述的泡沫沥青，其特征在于泡沫沥青是由高温热融沥青(130～150℃)和发泡剂或水混合而成，其中高温热融沥青占94～97％(体积百分比)，发泡剂或水占3～6％(体积百分比)。
4、根据权力要求3所述的发泡剂，其特征在于可以选用偶氮二甲酰胺发泡剂或BN发泡剂或DPT发泡剂或TSH发泡剂。
CN 200410051746 2004-10-09 2004-10-09 一种添加泡沫沥青的沥青冷再生方法 Pending CN1757828A (zh)