CN1749343A - Composite flame retardant insulation water-proof seal adhesive tape and preparation method thereof - Google Patents
Composite flame retardant insulation water-proof seal adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN1749343A CN1749343A CN 200510017070 CN200510017070A CN1749343A CN 1749343 A CN1749343 A CN 1749343A CN 200510017070 CN200510017070 CN 200510017070 CN 200510017070 A CN200510017070 A CN 200510017070A CN 1749343 A CN1749343 A CN 1749343A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive tape
- proportioning
- proof seal
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the insulation tape technical field, relate to composite flame retardant insulation water-proof seal adhesive tape and preparation method thereof.This adhesive tape has outer A and inner layer B is composited through calendering.Outer A is by elastic flame insulation paste EPDM4045, CPE and stablizer, and strengthening agent, fire retardant, anti-aging agent, oxidation inhibitor, promotor constitutes.Inner layer B is to have the strong polyisobutene of good autohension insulativity water-repellancy, isoprene-isobutylene rubber, and sticky agent terpine resin and carbon black, fine particle calcium carbonate and stearic acid constitute.Outer component materials is mixing repeatedly through mill, place again on the tri-roll press machine, make band.With under the internal layer component materials normal temperature on the machine of beginning to pratise mixing and be cut into rectangularly, in forcing machine, extrude then and make sheet material through special mouthful mould; At last inside and outside two-layer the calendering on tractor is composited.This adhesive tape can be used for avoiding the flame retardant insulation water-proof seal of the various electric power facility joints under the particular surroundings of naked light.
Description
Technical field
The invention belongs to insulated enclosure adhesive tape and preparing technical field thereof, be specifically related to a kind of composite flame retardant insulation water-proof seal adhesive tape and preparation method thereof.
Background technology
The band that the insulation processing of at present all kinds of electric wire joints being carried out adopts heat-shrinkage material to make more.Based on the characteristic of heat-shrinkage material, when the band that the use heat shrink-down material is made, the essential naked light that uses heats.Yet, do not allow to adopt working with naked fire at some special occasions: as under the coal mine, the absolute scene of a fire institute that prohibits such as oil field, chemical industry department; The material used in these occasions not only requires insulation but also must seal by fire-resistant waterproof.By the insulated enclosure adhesive tape that heat-shrinkage material is made, it does not possess the function that satisfies above-mentioned service requirements simultaneously.
Summary of the invention
In order to solve the technology technical problem that not only requires to insulate but also must the fire-resistant waterproof sealing, the invention provides a kind of composite flame retardant insulation water-proof seal adhesive tape and preparation method thereof.
The invention provides a kind of is that fire retardant insulating resilient material A and internal layer are fire-retardant water-tight self adhesive material B by skin, through rolling the compound composite flame retardant insulation water-proof seal adhesive tape of making.Component and the proportioning (parts by weight) of outer fire retardant insulating resilient material A are: 30～50 parts of terpolymer EP rubber EPDM4045,40～60 parts of chlorinatedpolyethylenees (CPE), 10～20 parts in flyash, 8～15 parts in sticking machine oil, 10～15 parts of decabromodiphenyl oxides, 10～15 parts of pentabromotoluenes, 6～10 parts of weisspiessglanzs, 3～8 parts of carbon blacks, 3～8 parts in paraffin, 1～3 part of stearic acid, 0.5～2 part of anti-aging agent RD, 0.5～1.5 part of antioxidant 1010,1～3 part of TM monex TD.Component and the proportioning (parts by weight) of the fire-retardant water-tight self adhesive material of internal layer B are: 20～30 parts of polyisobutene, 18～22 parts of terpine resins, 32～38 parts of isoprene-isobutylene rubbers, 3～5 parts of carbon blacks, 10～20 parts of fine particle calcium carbonates, 0.8～2 part of stearic acid.
The preparation method of composite flame retardant insulation water-proof seal adhesive tape is:
After the constitutive material of outer fire retardant insulating resilient material A taken by weighing by proportioning, place in the mill,, mixingly repeatedly take off up to molten fully good mixing in 140～160 ℃; Place on 130 ℃ of tri-roll press machines, adjusting the roller spacing is 0.1～0.3cm again, rolls and be cut into the band of the wide 5cm of being or other specifications with the 1m/min speed drawing.
After the constitutive material of the fire-retardant water-tight self adhesive material of internal layer B taken by weighing by proportioning, under the normal temperature on the machine of beginning to pratise mixing and be cut into rectangularly, at room temperature place forcing machine to extrude then; Notice that forcing machine adopts special mouthful of mould, export the thick 0.1～0.3cm of being of sheet material to reach, wide is the band of 5cm or other specifications.Certainly, the width of cladding material A and inner layer material B and length should be consistent with each other.
At last above-mentioned cladding material A and inner layer material B are rolled compoundly on tractor, make composite flame retardant insulation water-proof seal adhesive tape.Then, can cut and grow into 300cm or other specification length, invest on the internal layer with interleaving paper again, roll up with winder.
Composite flame retardant insulation water-proof seal adhesive tape of the present invention twines cable or other electric power facility that needs processing with 1/2 or 1/3 width overlap joint when using, can stretch 30%～50% during winding.Composite flame retardant insulation water-proof seal adhesive tape of the present invention has good " conformal performance ", is easy to stretch to twine, and need not do anyly to tie up processing and can form the extruding contraction effect.Especially very convenient for the coating of the irregular joint of geometrical shape.Waterproof and dampproof, insulated enclosure.Flame retardant properties is good, can be used for no open flames and requires fire-retardant particular surroundings, and oxygen index can reach 28.Its outer substrate intensity is good, has remedied the defective of internal layer seal gum intensity difference.This composite flame retardant insulation water-proof seal adhesive tape compare with the heat-shrinkage material adhesive tape have simple to operate, without naked light, advantages such as " conformal performance " is strong have solved the flame retardant insulation water-proof seal technical problem of the following various electric power facility joints of 10KV, are with a wide range of applications.
Description of drawings
Fig. 1 is the structural representation of composite flame retardant insulation water-proof seal adhesive tape.Cladding material A and inner layer material B.This figure also is the accompanying drawing of specification digest.
Embodiment
Embodiment 1:
The constitutive material of outer fire retardant insulating resilient material A takes by weighing by following proportioning (parts by weight): EPDM4045 is 30 parts, 40 parts of CPE, 10 parts in flyash, 8 parts in sticking machine oil, 10 parts of decabromodiphenyl oxides, 10 parts of pentabromotoluenes, 6 parts of weisspiessglanzs, 3 parts of carbon blacks, 3 parts in paraffin, 1 part of stearic acid, 0.5 part of anti-aging agent RD, 0.5 part of antioxidant 1010,1 part of TM monex TD; Above-mentioned materials is placed in the mill, mixingly repeatedly take off up to molten fully good mixing in 140 ℃; Place on 130 ℃ of tri-roll press machines, rolling spacing is 0.1cm again; With the 1m/min speed drawing and be cut into the outer band of the wide 5cm of being.
The constitutive material of the fire-retardant water-tight self adhesive material of internal layer B is taken by weighing by following proportioning (parts by weight): 20 parts of polyisobutene, 18 parts of terpine resins, 32 parts of isoprene-isobutylene rubbers, 3 parts of carbon blacks, 10 parts of fine particle calcium carbonates, 0.8 part of stearic acid with above-mentioned materials mixing and be cut into rectangularly on the machine of beginning to pratise under the normal temperature, is extruded in forcing machine then; Be molded as the thick 0.1cm that is through the special mouth of forcing machine, wide is 5cm internal layer sheet material.
On tractor, roll above-mentioned cladding material A and inner layer material B compound at last and cut and grow into 300cm, invest on the internal layer with interleaving paper again, roll up, make composite flame retardant insulation water-proof seal adhesive tape with winder.
Embodiment 2:
The constitutive material of outer fire retardant insulating resilient material A takes by weighing by following proportioning (parts by weight): 50 parts of EPDM4045,60 parts of CPE, 20 parts in flyash, 15 parts in sticking machine oil, 15 parts of decabromodiphenyl oxides, 15 parts of pentabromotoluenes, 10 parts of weisspiessglanzs, 8 parts of carbon blacks, 8 parts in paraffin, 3 parts of stearic acid, 2 parts of anti-aging agent RDs, 1.5 parts of antioxidant 1010s, 3 parts of TM monex TD; Above-mentioned materials is placed in the mill, mixingly repeatedly take off up to molten fully good mixing in 160 ℃; Place on 130 ℃ of tri-roll press machines, rolling spacing is 0.3cm again; With the 1m/min speed drawing and be cut into the outer band of the wide 5cm of being.
The constitutive material of the fire-retardant water-tight self adhesive material of internal layer B is taken by weighing by following proportioning (parts by weight): 30 parts of polyisobutene, 22 parts of terpine resins, 38 parts of isoprene-isobutylene rubbers, 5 parts of carbon blacks, 20 parts of fine particle calcium carbonates, 2 parts of stearic acid, with under the above-mentioned materials normal temperature on the machine of beginning to pratise mixing and be cut into rectangularly, in forcing machine, extrude then; Be molded as the thick 0.3cm that is through the special mouth of forcing machine, wide is 5cm internal layer sheet material.
At last above-mentioned cladding material A and inner layer material B are rolled compoundly on tractor, and cut and grow into 300cm, invest on the internal layer with interleaving paper again, roll up, make composite flame retardant insulation water-proof seal adhesive tape with winder.
Embodiment 3
The constitutive material of outer fire retardant insulating resilient material A takes by weighing by following proportioning (parts by weight): EPDM4045 is 40 parts, 50 parts of CPE, 15 parts in flyash, 12 parts in sticking machine oil, 13 parts of decabromodiphenyl oxides, 8 parts of 13 parts of weisspiessglanzs of pentabromotoluene, 6 parts of carbon blacks, 6 parts in paraffin, 1.5 parts of stearic acid, 1 part of anti-aging agent RD, 1 part of antioxidant 1010,1 part of TM monex TD; Above-mentioned materials is placed in the mill, mixingly repeatedly take off up to molten fully good mixing in 150 ℃; Place on 130 ℃ of tri-roll press machines, rolling spacing is 0.2cm again; Be cut into the outer band of the wide 5cm of being with 1m/min speed drawing and attention.
The constitutive material of the fire-retardant water-tight self adhesive material of internal layer B is taken by weighing by following proportioning (parts by weight): 25 parts of polyisobutene, 20 parts of terpine resins, 35 parts of isoprene-isobutylene rubbers, 4 parts of carbon blacks, 15 parts of fine particle calcium carbonates, 1.2 parts of stearic acid with above-mentioned materials mixing and be cut into rectangularly on the machine of beginning to pratise under the normal temperature, are extruded in forcing machine then; Be molded as the thick 0.2cm that is through the special mouth of forcing machine, wide is 5cm internal layer sheet material.
On tractor, roll above-mentioned cladding material A and inner layer material B compound at last and cut and grow into 300cm, invest on the internal layer with interleaving paper again, roll up, make composite flame retardant insulation water-proof seal adhesive tape with winder.
Claims (9)
1. a composite flame retardant insulation water-proof seal adhesive tape is characterized in that it is compounded through calendering by outer fire retardant insulating resilient material A and the fire-retardant water-tight self adhesive material of internal layer B;
The component of described outer fire retardant insulating resilient material A and proportioning (parts by weight) are: 30～50 parts of terpolymer EP rubber EPDM4045,40～60 parts of chlorinatedpolyethylenees (CPE), 10～20 parts in flyash, 8～15 parts in sticking machine oil, 10～15 parts of decabromodiphenyl oxides, 10～15 parts of pentabromotoluenes, 6～10 parts of weisspiessglanzs, 3～8 parts of carbon blacks, 3～8 parts in paraffin, 1～3 part of stearic acid, 0.5～2 part of anti-aging agent RD, 0.5～1.5 part of antioxidant 1010,1～3 part of TM monex TD;
Component and the proportioning (parts by weight) of the fire-retardant water-tight self adhesive material of internal layer B are: 20～30 parts of polyisobutene, 18～22 parts of terpine resins, 32～38 parts of isoprene-isobutylene rubbers, 3～5 parts of carbon blacks, 10～20 parts of fine particle calcium carbonates, 0.8～2 part of stearic acid.
2. a kind of composite flame retardant insulation water-proof seal adhesive tape as claimed in claim 1, it is characterized in that the component of outer fire retardant insulating resilient material A and proportioning (parts by weight) are: EPDM4045 is 30 parts, 40 parts of CPE, 10 parts in flyash, 8 parts in sticking machine oil, 10 parts of decabromodiphenyl oxides, 10 parts of pentabromotoluenes, 6 parts of weisspiessglanzs, 3 parts of carbon blacks, 3 parts in paraffin, 1 part of stearic acid, 0.5 part of anti-aging agent RD, 0.5 part of antioxidant 1010, TM monex TD1 part; Component and the proportioning (parts by weight) of the fire-retardant water-tight self adhesive material of internal layer B are: 20 parts of polyisobutene, 18 parts of terpine resins, 32 parts of isoprene-isobutylene rubbers, 3 parts of carbon blacks, 10 parts of fine particle calcium carbonates, 0.8 part of stearic acid.
3. a kind of composite flame retardant insulation water-proof seal adhesive tape as claimed in claim 1 is characterized in that the component of outer fire retardant insulating resilient material A and proportioning (parts by weight) are: 50 parts of EPDM4045,60 parts of CPE, 20 parts in flyash, 15 parts in sticking machine oil, 15 parts of decabromodiphenyl oxides, 15 parts of pentabromotoluenes, 10 parts of weisspiessglanzs, 8 parts of carbon blacks, 8 parts in paraffin, 3 parts of stearic acid, 2 parts of anti-aging agent RDs, 1.5 parts of antioxidant 1010s, 3 parts of TM monex TD; Component and the proportioning (parts by weight) of the fire-retardant water-tight self adhesive material of internal layer B are: 30 parts of polyisobutene, 22 parts of terpine resins, 38 parts of isoprene-isobutylene rubbers, 5 parts of carbon blacks, 20 parts of fine particle calcium carbonates, 2 parts of stearic acid.
4. a kind of composite flame retardant insulation water-proof seal adhesive tape as claimed in claim 1, it is characterized in that the component of outer fire retardant insulating resilient material A and proportioning (parts by weight) are: EPDM4045 is 40 parts, 50 parts of CPE, 15 parts in flyash, 12 parts in sticking machine oil, 13 parts of decabromodiphenyl oxides, 8 parts of 13 parts of weisspiessglanzs of pentabromotoluene, 6 parts of carbon blacks, 6 parts in paraffin, 1.5 parts of stearic acid, 1 part of anti-aging agent RD, 1 part of antioxidant 1010,1 part of TM monex TD; Component and the proportioning (parts by weight) of the fire-retardant water-tight self adhesive material of internal layer B are: 25 parts of polyisobutene, 20 parts of terpine resins, 35 parts of isoprene-isobutylene rubbers, 4 parts of carbon blacks, 15 parts of fine particle calcium carbonates, 1.5 parts of stearic acid.
5. as the preparation method of the described a kind of composite flame retardant insulation water-proof seal adhesive tape of 1 to 4 any one claim, after it is characterized in that constitutive material with outer fire retardant insulating resilient material A takes by weighing by proportioning, place in the mill, in 140～160 ℃, mixingly repeatedly take off up to molten fully good mixing; Place on the tri-roll press machine in 130 ℃, adjusting the roller spacing is 0.1～0.3cm, rolls into band with the 1m/min speed drawing again; After the constitutive material of the fire-retardant water-tight self adhesive material of internal layer B taken by weighing by proportioning, under the normal temperature on the machine of beginning to pratise mixing and be cut into rectangularly, at room temperature place forcing machine to extrude then; Special mouthful of mould of attention forcing machine should make and export the thick 0.1～0.3cm of being of sheet material, width is consistent with the width of outer fire retardant insulating resilient material A, at last above-mentioned cladding material A and inner layer material B are rolled compoundly on tractor, make composite flame retardant insulation water-proof seal adhesive tape.
6. the preparation method of a kind of composite flame retardant insulation water-proof seal adhesive tape as claimed in claim 5, after it is characterized in that constitutive material with outer fire retardant insulating resilient material A takes by weighing by proportioning, above-mentioned materials is placed in the mill, mixingly repeatedly take off up to molten fully good mixing in 140 ℃; Place on 130 ℃ of tri-roll press machines, the roller spacing is 0.1cm; Roll into band with the 1m/min speed drawing; After the constitutive material of the fire-retardant waterproof sealing material B of internal layer taken by weighing by proportioning,, in forcing machine, extrude then above-mentioned materials mixing and be cut into rectangularly on the machine of beginning to pratise under the normal temperature; Be molded as the thick 0.1cm that is through the special mouth of forcing machine, width is consistent with the width of outer fire retardant insulating resilient material A, at last above-mentioned cladding material A and inner layer material B is rolled compoundly on tractor, makes composite flame retardant insulation water-proof seal adhesive tape.
7. the preparation method of a kind of composite flame retardant insulation water-proof seal adhesive tape as claimed in claim 5, after it is characterized in that constitutive material with outer fire retardant insulating elasticity self adhesive material A takes by weighing by proportioning, above-mentioned materials is placed in the mill, mixingly repeatedly take off up to molten fully good mixing in 160 ℃; Place on 130 ℃ of tri-roll press machines, the roller spacing is 0.3cm again; Roll into band with the 1m/min speed drawing; After the constitutive material of the fire-retardant water-tight self adhesive material of internal layer B taken by weighing by proportioning, with under the above-mentioned materials normal temperature on the machine of beginning to pratise mixing and be cut into rectangularly, in forcing machine, extrude then; Be molded as the thick 0.3cm that is through the special mouth of forcing machine, width is consistent with the width of outer fire retardant insulating resilient material A, at last above-mentioned cladding material A and inner layer material B is rolled compoundly on tractor, makes composite flame retardant insulation water-proof seal adhesive tape.
8. the preparation method of a kind of composite flame retardant insulation water-proof seal adhesive tape as claimed in claim 5, after it is characterized in that constitutive material with outer fire retardant insulating resilient material A takes by weighing by proportioning, above-mentioned materials is placed in the mill, mixingly repeatedly take off up to molten fully good mixing in 150 ℃; Place on 130 ℃ of tri-roll press machines, the roller spacing is 0.2cm; Be cut into the outer band of the wide 5cm of being with 1m/min speed drawing and attention; After the constitutive material of the fire-retardant water-tight self adhesive material of internal layer B taken by weighing by proportioning,, in forcing machine, extrude then above-mentioned materials mixing and be cut into rectangularly on the machine of beginning to pratise under the normal temperature; Be molded as the thick 0.2cm that is through the special mouth of forcing machine, width is consistent with the width of outer fire retardant insulating resilient material A, at last above-mentioned cladding material adhesive tape A and inner layer material B is rolled compoundly on tractor, makes composite flame retardant insulation water-proof seal adhesive tape.
9. the preparation method of a kind of composite flame retardant insulation water-proof seal adhesive tape as claimed in claim 5, it is characterized in that: the described composite flame retardant insulation water-proof seal adhesive tape of making, invest with interleaving paper on the surface of inner layer B, and then be cut into wide for 5cm, long for 300cm, roll up with winder again.