CN1743480A - A kind of preparation method of aluminium-carbon-dichromium block material - Google Patents
A kind of preparation method of aluminium-carbon-dichromium block material Download PDFInfo
- Publication number
- CN1743480A CN1743480A CN 200510030228 CN200510030228A CN1743480A CN 1743480 A CN1743480 A CN 1743480A CN 200510030228 CN200510030228 CN 200510030228 CN 200510030228 A CN200510030228 A CN 200510030228A CN 1743480 A CN1743480 A CN 1743480A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- preparation
- powder
- alc
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of preparation method of aluminium carbon bis-chromium bulk, or rather aluminium carbon bis-chromium (Cr in the bulk
2AlC) weight percentage of phase is characterized in that greater than the preparation method of 90% block materials: (1) adopts chromium powder, and aluminium powder and graphite are raw material, according to Cr
2The stoichiometric ratio batching of AlC, the wherein aluminium of excessive 5-60wt%; (2) by the hot pressure reaction sintering method, in protective atmosphere, with the temperature rise rate of 10-50 ℃/min, hot pressing time is prepared into Cr under 1250-1500 ℃ of temperature and the 20-30MPa pressure
2The AlC block materials.
Description
Technical field
The present invention relates to a kind of aluminium carbon bis-chromium (Cr
2AlC) preparation method of block materials more precisely is to adopt chromium powder, and aluminium powder and graphite are raw material, by the hot pressure reaction sintering method, and preparation Cr
2The weight percentage of AlC phase is greater than 90% block materials.The bulk preparation field that belongs to non-oxygen base pottery.
Background technology
As everyone knows, the intrinsic fragility of stupalith makes its application be subjected to certain limitation, and (＞1000 ℃) lower intensity has limited its use at high temperature under the metallic substance high temperature.The compound phase material of ceramic base or metal matrix is attempted complementation by performance between metal and pottery just and is overcome separately shortcoming, but from preparation technology's angle, this type of composite diphase material nature is than the preparation difficulty height of monophase materials.
Nowotny and co-worker thereof have reported more than 100 kind of carbide and nitride [H.Nowotny in the sixties, " Struktuchemie Einiger Verbindungen der Ubergangsmetalle mit denelementen C; Si, Ge, Sn ", Prog.Solid State Chem., H.Reiss, Ed., 2 (1970) 27], wherein have kind more than 30 to be called H phase or H gg phase, chemical constitution is M
2AX (M is a transiting group metal elements, and A is IIIA or IVA family element, and X is C or N).Also have three kinds of M
3AX
2Phase, i.e. Ti
3SiC
2, Ti
3GeC
2And Ti
3AlC
2These compounds (being designated as MAX) all have the stratiform hexagonal structure, and the former is M
2The plane layer that X layer and A atom are constituted is stacking at interval; The latter is by M
3X
2Layer and A interlayer are every stacking.Yet, because the difficulty of the single-phase sample of preparation, until 1996, M
2The performance of AX (or MAX) compound is not developed always, and the knowledge of relevant MAX material is very limited, and often most of incorrect.Barsoum in 1996 and co-worker have reported that they are in synthetic technology with form single-phase fine and close Ti
3SiC
2Important breakthrough in the material, promoted MAX Development of Materials [M.W.Barsoum and T.El-Raghy greatly, " Synthesis and Characterization of a Remarkable Ceramic:Ti3SiC2 ", J.Am.Ceram.Soc., 79 (1996) 1953].Result of study shows, Ti
3SiC
2Density more much lower than Ni based high-temperature alloy, and Young's modulus and thermal conductivity are about its twice, Vickers' hardness 4-6GPa, 1000 ℃ yield strength still surpasses 400MPa, the anti-thermal shock temperature reaches 1400 ℃.What is more important, Ti
3SiC
2Can process with universal cutter, this processability is very rare in pottery.These excellent properties make this ceramic layered material have broad application prospects.Yet, no matter be pure phase Ti
3SiC
2Still still there is a weakness in its matrix material, promptly limited temperature-room type plasticity and oxidation-resistance, and this has become restriction Ti
3SiC
2Bottleneck in actual applications.
M
2Cr in the AX system
2AlC forms oxidation resistant Al easily in oxidising process
2O
3And Cr
2O
3Therefore protective layer can expect that it has good antioxidant property in wide temperature range; Higher Cr and Al content has increased the content of metallic bond in the material simultaneously, is expected to improve the plasticity of material.Recently, from the beginning Germany and Sweden scientist utilize total energy computing method (Ab initio total energy calculations) to M
2AlC (M=Ti, V, Cr, Nb, Ta) compound has carried out a series of Theoretical Calculation [Z.M.Sun, R.Ahuja, S.Li and J.M.Schneider, " Structure and Bulk Modulus of M2AlC (M=Ti; V, and Cr) ", Appl.Phys.Lett., 83 (2003) 899], comprising having studied M
2AlC (find at Ti for M=Ti, V by modulus of volume expansion Cr)
2AlC, V
2AlC and Cr
2Three of AlC mutually in, Cr
2AlC has the highest modulus of volume expansion (226GPa), respectively than Ti
2AlC and V
2AlC exceeds 36% and 15%.Result calculated shows, Cr
2AlC is not only at M
2AlC (M=Ti, V, Cr, Nb has the highest modulus of volume expansion and Young's modulus in Ta), and these values also are higher than Ti respectively
3SiC
2Modulus of volume expansion (185-206GPa) and Young's modulus (333-339GPa) [Z.M.Sun, S.Li, R.Ahuja and J.M.Schneider, " Calculated Elastic Properties of M2AlC (M=Ti; V, Cr, Nb and Ta) ", SolidStates Communication, 129 (2004) 589].Therefore, Cr
2AlC probably becomes new useful ternary layered carbide material.Regrettably, up to now both at home and abroad about Cr
2The research of AlC body material preparation then rarely has report.
Therefore, the present invention proposes a kind of Cr
2The weight percentage of AlC phase is greater than the preparation method of 90% block materials, to deepen Cr
2The understanding of AlC material and further exploitation.
Summary of the invention
The object of the invention provides a kind of Cr
2The preparation method of AlC block materials is with method Cr provided by the invention
2The weight percentage of AlC phase is greater than 90%.
The objective of the invention is to implement by following manner.Promptly adopt chromium powder, aluminium powder and graphite are raw material, carry out sintering by the control hot pressure reaction.
Specific implementation method:
(1) raw material: comprise chromium powder (30 μ m, 99.95%), aluminium powder (100 μ m, 99.95%) and carbon dust (1.5 μ m, 99%).Powder is weighed according to the mol ratio of design, and ball milling 24 hours, the powder that obtains mixing after the oven dry of gained slurry.
(2) preparation: powder is pressed into disk, places the graphite jig of internal surface coating B N, vacuumize (10 earlier
-2～10
-3Pa), feed flow Ar or N then
2Protection gas, hot pressing temperature is 1250-1500 ℃, and the time is 1-4 hour, and average temperature rise rate is 10-50 ℃/min, and hot pressing pressure is 20-30MPa.After treating that the sample cooling is taken out, with grinding machine and polishing machine processing, make Cr again
2The AlC bulk.
(3) estimate: with the preparation effect of XRD and density measurement check sample.
Advantage of the present invention is:
(1) less demanding to material purity, preparation process condition is relatively more conventional, realizes easily.
(2) Cr in the prepared body material
2The quality percentage composition of AlC phase is greater than 90%.
Description of drawings
Fig. 1 is the XRD figure spectrum that embodiment 1 provided by the invention obtains sample.
Fig. 2 is the XRD figure spectrum that embodiment 2 provided by the invention obtains sample.
Fig. 3 is the XRD figure spectrum that embodiment 3 provided by the invention obtains sample.
Fig. 4 is the XRD figure spectrum that embodiment 4 provided by the invention obtains sample.
Fig. 5 is the XRD figure spectrum that embodiment 5 provided by the invention obtains sample.
Fig. 6 is the XRD figure spectrum that embodiment 6 provided by the invention obtains sample.
Embodiment
Embodiment 1
With chromium powder (30 μ m, 99.95%), aluminium powder (100 μ m, 99.95%) and carbon dust (1.5 μ m, 99%) be raw material.According to Cr: Al: C=2: 1.1: 1 mol ratio is weighed, and ball milling 24 hours, the powder that obtains mixing after the oven dry of gained slurry.Powder is pressed into disk, places the graphite jig of surface applied B N, vacuumize earlier, the Ar protection gas that feed to flow then, at 1400 ℃ with 25MPa pressure hot pressing 2 hours.After treating that the sample cooling is taken out, with grinding machine and polishing machine processing, just obtain Cr again
2The AlC bulk.The XRD of material is as scheming shown in (1) Cr
2The AlC phase content is 94wt%.Volume density is 5.20g/cm
3
With chromium powder (30 μ m, 99.95%), aluminium powder (100 μ m, 99.95%) and carbon dust (1.5 μ m, 99%) be raw material.According to Cr: Al: C=2: 1.2: 1 mol ratio is weighed; and ball milling 24 hours; the powder that obtains mixing after the oven dry of gained slurry; powder is pressed into disk; place the graphite jig of surface applied B N; vacuumize earlier, the Ar protection gas that feed to flow then, at 1450 ℃ with 20MPa pressure hot pressing 1 hour.After treating that the sample cooling is taken out, with grinding machine and polishing machine processing, just obtain Cr again
2The AlC bulk.The XRD of material is as scheming shown in (2) Cr
2The AlC phase content is 99wt%.Volume density is 5.12g/cm
3
Embodiment 3
With chromium powder (30 μ m, 99.95%), aluminium powder (100 μ m, 99.95%) and carbon dust (1.5 μ m, 99%) be raw material.According to Cr: Al: C=2: 1.4: 1 mol ratio is weighed, and ball milling 24 hours, the powder that obtains mixing after the oven dry of gained slurry.Powder is pressed into disk, places the graphite jig of surface applied B N, vacuumize earlier, feed the Ar protection gas that flows then, in the time of 1350 ℃, add 20MPa pressure hot pressing 1 hour.After treating that the sample cooling is taken out, with grinding machine and polishing machine processing, just obtain Cr again
2The AlC bulk.The XRD of material is as scheming shown in (3) Cr
2The AlC phase content is 99wt%.Volume density is 5.09g/cm
3
Embodiment 4
With chromium powder (30 μ m, 99.95%), aluminium powder (100 μ m, 99.95%) and carbon dust (1.5 μ m, 99%) be raw material.According to Cr: Al: C=2: 1.6: 1 mol ratio is weighed, and ball milling 24 hours, the powder that obtains mixing after the oven dry of gained slurry.Powder is pressed into disk, places the graphite jig of surface applied B N, vacuumize earlier, feed the Ar protection gas that flows then, in the time of 1350 ℃, add 20MPa pressure hot pressing 1 hour.After treating that the sample cooling is taken out, with grinding machine and polishing machine processing, just obtain Cr again
2The AlC bulk.The XRD of material is as scheming shown in (4) Cr
2The AlC phase content is 99wt%.Volume density is 5.00g/cm
3
Embodiment 5
With chromium powder (30 μ m, 99.95%), aluminium powder (100 μ m, 99.95%) and carbon dust (1.5 μ m, 99%) be raw material.According to Cr: Al: C=2: 1.1: 1 mol ratio is weighed, and ball milling 24 hours, the powder that obtains mixing after the oven dry of gained slurry.Powder is pressed into disk, places the graphite jig of surface applied B N, vacuumize earlier, feed the N that flows then
2The protection gas, at 1400 ℃ with 20MPa pressure hot pressing 1 hour.After treating that the sample cooling is taken out, with grinding machine and polishing machine processing, just obtain Cr again
2The AlC bulk.The XRD of material is shown in figure (1), and the Cr2AlC phase content is 96wt%.Volume density is 5.19g/cm
3
Embodiment 6
With chromium powder (30 μ m, 99.95%), aluminium powder (100 μ m, 99.95%) and carbon dust (1.5 μ m, 99%) be raw material.According to Cr: Al: C=2: 1.1: 1 mol ratio is weighed, and ball milling 24 hours, the powder that obtains mixing after the oven dry of gained slurry.Powder is pressed into disk, places the graphite jig of surface applied B N, vacuumize earlier, the Ar protection gas that feed to flow then is warmed up to 1400 ℃ with the speed of 10 ℃/min, under this temperature with 20MPa pressure hot pressing 1 hour.After treating that the sample cooling is taken out, with grinding machine and polishing machine processing, just obtain Cr again
2The AlC bulk.The XRD of material is shown in figure (5), and the Cr2AlC phase content is 98.5wt%.Volume density is 5.20g/cm
3
Claims (5)
1. the preparation method of an aluminium-carbon-dichromium block material is characterized in that:
(1) raw material adopts chromium powder, and aluminium powder and graphite are according to Cr
2During the stoichiometric ratio proportioning of AlC, the aluminium powder of excessive 5～60at%;
(2) set by step after (1) weighing, be solvent, use Si with the dehydrated alcohol
3N
4The powder that obtains mixing after the oven dry of ball ball milling gained slurry is pressed into biscuit;
(3) step (2) is obtained that biscuit is placed in the graphite jig of inner wall surface coating BN, vacuumize earlier, feed mobile argon gas or nitrogen protection atmosphere then; carry out hot pressure reaction sintering; hot pressing temperature is 1250-1500 ℃, insulation 1-4hr, and pressure is 20-30Mpa.
2. by the preparation method of the described a kind of aluminium-carbon-dichromium block material of claim 1, it is characterized in that:
(1) described chromium powder, purity are 99.95%, and particle diameter is 30 μ m.
(2) described aluminium powder, purity are 99.95%, and particle diameter is 100 μ m
(3) described graphite, purity are 99%, and particle diameter is 1.5 μ m
3. by the preparation method of the described a kind of aluminium-carbon-dichromium block material of claim 1, temperature rise rate is 10-50 ℃/min when it is characterized in that hot pressed sintering.
4. by the preparation method of the described a kind of aluminium-carbon-dichromium block material of claim 1, the vacuum tightness that vacuumizes earlier when it is characterized in that hot pressed sintering is 10
-2～10
-3Pa.
5. by the preparation method of any described a kind of aluminium-carbon-dichromium block material of claim in the claim 1～4, it is characterized in that Cr in the prepared block materials
2The weight percentage of AlC phase is greater than 90%.