CN1730421A - Low alkali high-strength cement - Google Patents
Low alkali high-strength cement Download PDFInfo
- Publication number
- CN1730421A CN1730421A CN 200510017769 CN200510017769A CN1730421A CN 1730421 A CN1730421 A CN 1730421A CN 200510017769 CN200510017769 CN 200510017769 CN 200510017769 A CN200510017769 A CN 200510017769A CN 1730421 A CN1730421 A CN 1730421A
- Authority
- CN
- China
- Prior art keywords
- parts
- low alkali
- cement
- strength cement
- caso
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a low-alkali high-strength cement comprising the following clinker components (by weight parts), C4A3S 20-30 parts, C2S 20-30 parts, C3S 15-30 parts, CaSO4 5-15 parts, C4AF 5-10 parts, C3A 2-5 parts, the cement may also contain CaCO3 5-10 parts or/and SiO2 t-10 parts as additives.
Description
Technical field
The present invention relates to a kind of cement, particularly relate to a kind of low alkali cement.
Background technology
Its major ingredient of existing low alkali cement is anhydrous calcium sulphoaluminate, Dicalcium Phosphate (Feed Grade) and a small amount of gypsum, and its pH value of 1～7 day is 10.5～11.5, and pH value is higher.When being used for cement products such as GRC member when it, the compositions such as fiber in these goods can be comparatively fast ineffective under the corrosion of alkali lye.In addition, performances such as the setting time of existing Portland cement and low alkali cement and intensity can not finely satisfy the needs of rapid construction.
Summary of the invention
The purpose of this invention is to provide a kind of low alkali high-strength cement, this cement has low alkali, high-strength, fast hard, fast characteristic such as do, and 1～7 day pH value of this cement is 8～9.5.
For achieving the above object, the present invention adopts following technical scheme: a kind of low alkali high-strength cement, contain following mineral clinker component: C by weight
4A
320 parts～30 parts of S, C
220 parts～30 parts of S, C
315 parts～30 parts of S, CaSO
45 parts～15 parts, C
45 parts～10 parts of AF, C
32 parts～5 parts of A.
The method for preparing above-mentioned low alkali high-strength cement is: will cooperate calcining with correction material, gypsum process with the corresponding aluminum raw material without calcination of above-mentioned mineral clinker, calcareous raw material, clayey raw material, and mix the levigate mixing of proper amount of gypsum again, and can make.
Also can contain CaCO in the low alkali high-strength cement of the present invention
35～10 parts or/and SiO
2Make additive for 5 parts～10 parts.
The salient features of low alkali high-strength cement of the present invention is as follows: time of coagulation: about about 10 minutes of initial set, about 1 and a half hours of final set, ultimate compression strength (Mpa): 32.5/ day, 45.3/3 day, 56.5/7 day, folding strength (Mpa): 6.8/ day, 7.5/3 day, 9/7 day.
Embodiment
Embodiment 1: the mineral clinker by following weight part is prepared burden
C
4A
320 parts of S, C
230 parts of S, C
325 parts of S, CaSO
410 parts, C
410 parts of AF, C
35 parts of A.
Its preparation method is: the aluminum raw material without calcination that will be corresponding with above-mentioned mineral clinker, calcareous raw material, clayey raw material cooperate calcining with correction material, gypsum process, will can make through mineral clinker and levigate the mixing of gypsum of calcining gained.
Embodiment 2: the mineral clinker by following weight part is prepared burden
C
4A
330 parts of S, C
220 parts of S, C
315 parts of S, CaSO
415 parts, C
45 parts of AF, C
32 parts of A.
Embodiment 3: the mineral clinker by following weight part is prepared burden
C
4A
322 parts of S, C
222 parts of S, C
330 parts of S, CaSO
45 parts, C
48 parts of AF, C
34 parts of A.
Embodiment 2～3 is identical with the preparation method of embodiment 1.
Embodiment 4: mineral clinker and addition material by following weight part are prepared burden
C
4A
320 parts of S, C
230 parts of S, C
325 parts of S, CaSO
410 parts, C
410 parts of AF, C
35 parts of A, CaCO
35 parts.
Embodiment 5: mineral clinker and addition material by following weight part are prepared burden
C
4A
330 parts of S, C
220 parts of S, C
315 parts of S, CaSO
415 parts, C
45 parts of AF, C
32 parts of A, CaCO
37 parts.
Embodiment 6: mineral clinker and addition material by following weight part are prepared burden
C
4A
322 parts of S, C
222 parts of S, C
330 parts of S, CaSO
45 parts, C
48 parts of AF, C
34 parts of A, CaCO
310 parts.
Embodiment 7: mineral clinker and addition material by following weight part are prepared burden
C
4A
320 parts of S, C
230 parts of S, C
325 parts of S, CaSO
410 parts, C
410 parts of AF, C
35 parts of A, SiO
25 parts.
Embodiment 8: mineral clinker and addition material by following weight part are prepared burden
C
4A
330 parts of S, C
220 parts of S, C
315 parts of S, CaSO
415 parts, C
45 parts of AF, C
32 parts of A, SiO
27 parts.
Embodiment 9: mineral clinker and addition material by following weight part are prepared burden
C
4A
322 parts of S, C
222 parts of S, C
330 parts of S, CaSO
45 parts, C
48 parts of AF, C
34 parts of A, SiO
210 parts.
Embodiment 10: mineral clinker and addition material by following weight part are prepared burden
C
4A
320 parts of S, C
230 parts of S, C
325 parts of S, CaSO
410 parts, C
410 parts of AF, C
35 parts of A, CaCO
35 parts, SiO
25 parts.
Embodiment 11: mineral clinker and addition material by following weight part are prepared burden
C
4A
330 parts of S, C
220 parts of S, C
315 parts of S, CaSO
415 parts, C
45 parts of AF, C
32 parts of A, CaCO
36 parts, SiO
210 parts.
Embodiment 12: mineral clinker and addition material by following weight part are prepared burden
C
4A
322 parts of S, C
222 parts of S, C
330 parts of S, CaSO
45 parts, C
48 parts of AF, C
34 parts of A, CaCO
310 parts, SiO
27 parts.
The preparation method of embodiment 4～12 is: will cooperate calcining with correction material, gypsum process with the corresponding aluminum raw material without calcination of above-mentioned mineral clinker, calcareous raw material, clayey raw material, will through the mineral clinker of calcining gained and gypsum be levigate mixes, mix the CaCO of specified amount again
3Or/and SiO
2Can make.
Claims (3)
1, a kind of low alkali high-strength cement is characterized in that, contains by weight following mineral clinker component: C
4A
320 parts～30 parts of S, C
220 parts～30 parts of S, C
315 parts～30 parts of S, CaSO
45 parts～15 parts, C
4AF5 part～10 part, C
32 parts～5 parts of A.
2, low alkali high-strength cement as claimed in claim 1 is characterized in that, also contains CaCO
35～10 parts.
3, low alkali high-strength cement as claimed in claim 1 or 2 is characterized in that, also contains SiO
25 parts～10 parts.