CN1727435A - Cement dipping liquid in use for anchor pole made from glass fiber reinforced plastic - Google Patents
Cement dipping liquid in use for anchor pole made from glass fiber reinforced plastic Download PDFInfo
- Publication number
- CN1727435A CN1727435A CN 200510044161 CN200510044161A CN1727435A CN 1727435 A CN1727435 A CN 1727435A CN 200510044161 CN200510044161 CN 200510044161 CN 200510044161 A CN200510044161 A CN 200510044161A CN 1727435 A CN1727435 A CN 1727435A
- Authority
- CN
- China
- Prior art keywords
- parts
- anchor pole
- glass fiber
- reinforced plastic
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A dipping resin liquid for the anchor rod made of glass fibre reinforced plastics is proportionally prepared from resin 928, aluminium hydroxide, talc powder, zinc stearate, dye paste, demoulding agent, methanone ethanone peroxide, peroxybenzoic acid resin and adhesive 116 through low-speed stirring of the first four, adding dye paste and demoulding agent, medium-speed stirring, sequentially adding others, and stirring.
Description
Technical field
The application relates to supporting glass fibre reinforced plastics rockbolts, especially cement dipping liquid in use for anchor pole made from glass fiber reinforced plastic under the coal mine.
Background technology
The glass fibre reinforced plastics rockbolts that supporting is used under the present coal mine, generally all will be through operation such as glass fiber dipped, patrix, the demoulding is made, wherein glass fiber dipped is critical process, and how the quality quality of dipping solution, tensile strength directly have influence on the anchor pole quality that is processed into.Chinese patent publication number (200410044979.9) discloses a kind of anchor pole and its complete processing and the used device of this technology, and the cement dipping liquid in use for anchor pole made in this patent is made up of 100 part of 972 resin, 3-5 part solidifying agent, promotor 2-5 part, fire retardant 3-5 part, stopping composition 5-10 part, mold oil.Chinese patent publication number (97121002.0) also discloses a kind of glass fibre reinforced plastics rockbolts and manufacture method thereof, and wherein said dipping solution is made up of 100 parts unsaturated 191 or 196 resins, 3-8 part solidifying agent, 2-7 part promotor.All only proposed the prescription of dipping solution in above-mentioned disclosed two patents, if all prepare dipping solution according to the common method for preparing dipping solution, those two kinds of dipping solution quality that prepare are uncontrollable at all.In fact, prescription is different, and the preparation method also should be different thereupon with processing parameter control.Owing to the progress and the industrial improvement of science and technology, the resin of glass reinforced plastic production usefulness also constantly has new variety to occur in addition, and according to the difference of new variety, the prescription of dipping solution is also different.Be the specification of quality that satisfies glass fibre reinforced plastics rockbolts and the requirement of production technique, the reply prescription further improves.Therefore, necessity that a kind of prescription is provided and technology is corresponding, the reliable quality cement dipping liquid in use for anchor pole made from glass fiber reinforced plastic.
Summary of the invention
The purpose of this invention is to provide a kind of reliable in quality, be suitable for the cement dipping liquid in use for anchor pole made from glass fiber reinforced plastic of suitability for industrialized production.
For achieving the above object, cement dipping liquid in use for anchor pole made of the present invention, be made up of following substances in parts by weight: 200 part of 928 resin, 14 parts of aluminium hydroxides, 10 parts of talcum powder, 1 part of Zinic stearas, 2 parts of color pastes, 1.2 parts of releasing agents, 2 parts of methylethyl ketone peroxides, 2 parts of peroxidation phenylformic acid resins, 8 part of 116 glue are formed, and are prepared by following method:
928 resins, aluminium hydroxide, talcum powder, Zinic stearas stirring at low speed in container with above-mentioned parts by weight, when treating that material is dissolved in resin substantially, adding color paste, releasing agent middling speed stir, the methylethyl ketone peroxide, the peroxidation phenylformic acid resin that add above-mentioned umber then, 116 glue of the above-mentioned umber of back adding that stirs stir and get final product.
Its advantage is, with the dipping solution of above-mentioned component and method preparation, is suitable for mechanical mold pressing, the thermofixation production technique of glass fibre reinforced plastics rockbolts, and the anchor pole steady quality of producing reaches the requirement of downhole coal mine exploitation supporting.
Embodiment
The invention will be further described below in conjunction with an embodiment.
1, takes by weighing 20kg928 resin, 1.4kg aluminium hydroxide, 1kg talcum powder, 0.1kg Zinic stearas, 0.2kg color paste, 0.12kg releasing agent, 0.2kg methylethyl ketone peroxide, 0.2kg peroxidation phenylformic acid resin, 0.8kg116 glue.
928 resins that 2, will take by weighing, aluminium hydroxide, talcum powder, Zinic stearas be 5 parts of clocks of mechanical stirring at low speed in container, add color paste, 75 parts of clocks of releasing agent middling speed stirring again, add methylethyl ketone peroxide, 30 parts of clocks of peroxidation phenylformic acid resin continuation stirring then, add 10 parts of clocks of 116 glue stirring at last and can make dipping solution.
In addition, the dipping solution that is used for the teeming of bar afterbody should add short ORGANDY (every 1kg dipping solution adds the short yarn of 0.4kg) at the glue of above-mentioned preparation, manually fills a part stirring, till fluffing.The dipping solution that adds short yarn is the screw thread that goes out the anchor pole afterbody for mold pressing.
Claims (2)
1, a kind of cement dipping liquid in use for anchor pole made from glass fiber reinforced plastic, it is characterized in that, it is made up of following substances in parts by weight: 200 part of 928 resin, 14 parts of aluminium hydroxides, 10 parts of talcum powder, 1 part of Zinic stearas, 2 parts of color pastes, 1.2 parts of releasing agents, 2 parts of methylethyl ketone peroxides, 2 parts of peroxidation phenylformic acid resins, 8 part of 116 glue are formed, and are prepared by following method:
928 resins, aluminium hydroxide, talcum powder, Zinic stearas stirring at low speed in container with above-mentioned parts by weight, when treating that material is dissolved in resin substantially, adding color paste, releasing agent middling speed stir, add methylethyl ketone peroxide, the peroxidation phenylformic acid resin of above-mentioned umber then, 116 glue that add above-mentioned umber after stirring again stir and get final product.
2, cement dipping liquid in use for anchor pole made from glass fiber reinforced plastic as claimed in claim 1 is characterized in that, the short ORGANDY that adds 0.4kg in every 1kg dipping solution is used for teeming anchor pole afterbody.