CN1724964A - Energy-saving ceramic fire resistant bearing board - Google Patents
Energy-saving ceramic fire resistant bearing board Download PDFInfo
- Publication number
- CN1724964A CN1724964A CN 200510035664 CN200510035664A CN1724964A CN 1724964 A CN1724964 A CN 1724964A CN 200510035664 CN200510035664 CN 200510035664 CN 200510035664 A CN200510035664 A CN 200510035664A CN 1724964 A CN1724964 A CN 1724964A
- Authority
- CN
- China
- Prior art keywords
- bearing board
- space
- energy
- fire resistant
- load bearing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention is an energy-saving ceramic flame-resistant bearing firing plate, for solving the technical problem of making the glazed outside wall bricks fired by the same kiln have no obvious color difference but small deformation, thus improving the quality of finished products, and besides, for strengthening the intensity of bearing firing plate, reducing its breakage rate. For this, the invention fills ribs and blanks at the bottom of the bearing firing plate, where a through hole is equipped within each blank. The blanks and holes can be regularly shaped or irregularly shaped. The invention is mainly used in ceramic kiln to bear and transport the fired ceramic blanks in the course of firing and especially applied to the glazed outside wall blanks.
Description
Technical field
The present invention relates to ceramic kiln combustion chamber support unit technical field, particularly a kind of energy-conservation refractory load bearing board that is used for the support ceramic body.
Background technology
Support is burnt ceramic body in the existing ceramic kiln combustion chamber, as glazed tile base substrates such as ceramic exterior wall brick, mosaics, is to adopt the end, the smooth load bearing board of face, and its specification is generally 460 * 460 * 10.5mm, and these load bearing boards are all made with refractory material.Owing to adopt the end, face to be the load bearing board on plane, be subjected to heat conduction velocity slow, it is inhomogeneous to be heated, and burns till the energy consumption height, and firing time is long, and reduces output.Inhomogeneous owing to be heated, the bottom that is placed on the glaze adobe around the load bearing board is conducted heat fast, and to conduct heat in the bottom that is placed on the glaze adobe load bearing board in the middle part of slower, cause to be placed on load bearing board glazed tile burning all around, and the glazed tile that is placed in the middle part of the load bearing board is underdone.Its consequence is that each the glazed tile aberration on the same load bearing board is obvious, is out of shape also greatlyyer, and product percent of pass that the whole piece kiln burns till descends.In addition, the intensity of above-mentioned load bearing board is relatively poor, and is damaged easily.
Summary of the invention
The technical problem to be solved in the present invention is: improve the load bearing board heat conduction velocity, make to hold and burn product and be heated evenly, effectively cut down the consumption of energy and speed is burnt till in quickening, improve output; The product that same klining is become do not have obvious aberration and be out of shape little, thereby improved product quality; To improve the intensity of load bearing board in addition, reduce its breakage rate.
Technical solution proposed by the invention is such: a kind of energy-saving ceramic fire resistant bearing board, the face of this load bearing board are smooth plane, and the base plane of described load bearing board is covered with muscle and space, are provided with through hole in the described space.The height h scope of described muscle is 2-4mm, and load bearing board thickness b scope is 8-13mm, and the ratio of the height h of muscle and load bearing board thickness b is in the 0.15-0.5 scope.Described muscle can be to hang down mutually in length and breadth to be arranged, and forms one group of continuous square or rectangle space, is provided with round tube hole in the described space.Described muscle also can be arranged askew in length and breadth, forms one group of continuous rhombus space, is provided with round tube hole in the described space.Described muscle also can be irregular alignment, forms one group of continuous erose space, is provided with round tube hole in the described space.Also the space that can have one group of rule to arrange in the base plane punching press of load bearing board is provided with round tube hole in the described space.Also one group of irregular space of arranging can be arranged in the base plane punching press of load bearing board, be provided with round tube hole in the described space.
Compared with prior art, the present invention has following remarkable result:
(1) the plate baseplane of this ceramic fire resistant burning board is covered with muscle, space and through hole, forms by mold pressing, sintering, and the structure of load bearing board is changed, and intensity is better.Because load bearing board bottom is covered with space and through hole, heat makes to hold by these round tube holes and burns product and directly be heated from the bottom of load bearing board, thoroughly changed and held the hot mode that is subjected to that burns product, and then make hold burn product at the bottom of, the face basically identical that is heated.Fundamentally changed and held the heating status of burning product, improved its uniformity that is subjected to hot property and is subjected to thermal velocity and is heated, burnt burning till quality and burning till speed of product thereby improved to hold.Under identical firing condition, adopt this load bearing board to hold to burn product (as the glaze exterior wall tile etc.), its firing temperature can reduce more than 15 ℃, has shortened firing period, thereby energy consumption is reduced, energy-conservation reaching more than 10%.
(2) adopt this ceramic fire resistant bearing board after, since hold burn product can the end, face directly is heated, heat transfer rate is fast, thereon each piece of supporting is burnt, and product (as the adobe of glaze exterior wall) is heated evenly, its bottom surface, in enclose and the middle part three between have a narrow range of temperature, the basic no color differnece of the product that burns till, the distortion little, improved product quality.
The present invention is mainly used in the inherent sintering procedure of ceramic kiln and is burnt ceramic body as carrying, conveying, is specially adapted to the adobe of glaze exterior wall.
Description of drawings
Fig. 1 is a kind of energy-saving ceramic fire resistant bearing board of the present invention bottom surface front view.
Fig. 2 is the A-A cutaway view of Fig. 1.
Fig. 3 is the E place partial enlarged drawing of Fig. 2.
Fig. 4 is the another kind of energy-saving ceramic fire resistant bearing board of a present invention bottom surface front view.
Fig. 5 is the B-B cutaway view of Fig. 4.
Fig. 6 is the F place partial enlarged drawing of Fig. 5.
Fig. 7 is the third energy-saving ceramic fire resistant bearing board bottom surface front view of the present invention.
Fig. 8 is the C-C cutaway view of Fig. 7.
Fig. 9 is the G place partial enlarged drawing of Fig. 8.
The specific embodiment
By following embodiment the present invention is further elaborated.
Embodiment 1
Referring to Fig. 1, Fig. 2, shown in Figure 3, a kind of face of energy-saving ceramic fire resistant bearing board 1 is smooth plane, and its base plane is covered with the muscle 2 that hangs down and arrange mutually in length and breadth, and forms one group of continuous square space 3, is equipped with a round tube hole 4 in each space 3.This routine load bearing board specification is: 460 * 460 * 10mm (long * wide * thick), the specification in each space 3 is 40 * 40mm, load bearing board thickness b=10mm, every muscle 2 high h=2.5mm, the ratio of muscle 2 high h and load bearing board 1 thickness b
The diameter D=10mm of circular hole 4.
Square, the rectangle, rhombus, triangle, polygon, circle, quincunx etc. of regular arrangement can be made in space 3, ceramic fire resistant bearing board bottom, also can make the different shape of irregular alignment, described through hole 4 can be selected circular hole, square hole, polygonal hole or irregularly shaped hole, the capital produces appreciable results, but is the best to adopt circular hole.
Referring to Fig. 4, Fig. 5, shown in Figure 6, the face of the ceramic fire resistant bearing board 5 of present embodiment is smooth plane, and its base plane is covered with the muscle 6 of arranged askew in length and breadth, is equipped with a round tube hole 8 in each space 7.This routine load bearing board specification is: 460 * 460 * 13mm (long * wide * thick), muscle 6 high h=2mm, the ratio of muscle 6 high h and load bearing board 5 thickness b
The diameter D=12mm of round tube hole 8.
Referring to Fig. 7, Fig. 8, shown in Figure 9, the face of the ceramic fire resistant bearing board 9 of present embodiment is smooth plane, and its base plane punching press has by regularly arranged pentagon space 11, is equipped with a round tube hole 12 in each space 11, is muscle 10 between each space.This routine load bearing board specification is: 460 * 460 * 8mm (long * wide * thick), muscle 10 high h=4mm, the ratio of muscle 10 high h and load bearing board 9 thickness b
The diameter D=8mm of round tube hole 12.
Claims (7)
1, a kind of energy-saving ceramic fire resistant bearing board, the face of this load bearing board is smooth plane, it is characterized in that: the base plane of described load bearing board is covered with muscle and space, is provided with through hole in the described space.
2, energy-saving ceramic fire resistant bearing board according to claim 1 is characterized in that: the height of described muscle (h) scope is 2-4mm, and load bearing board thickness (b) scope is 8-13mm, and the ratio of height of muscle (h) and load bearing board thickness (b) is in the 0.15-0.5 scope.
3, energy-saving ceramic fire resistant bearing board according to claim 1 is characterized in that: described muscle is to hang down mutually in length and breadth to be arranged, and forms one group of continuous square or rectangle space, is provided with round tube hole in the described space.
4, energy-saving ceramic fire resistant bearing board according to claim 1 is characterized in that: described muscle is arranged askew in length and breadth, forms one group of continuous rhombus space, is provided with round tube hole in the described space.
5, energy-saving ceramic fire resistant bearing board according to claim 1 is characterized in that: described muscle is irregular alignment, forms one group of continuous erose space, is provided with round tube hole in the described space.
6, energy-saving ceramic fire resistant bearing board according to claim 1 is characterized in that: the space that the base plane punching press of described load bearing board has one group of rule to arrange is provided with round tube hole in the described space.
7, energy-saving ceramic fire resistant bearing board according to claim 1 is characterized in that: the base plane punching press of described load bearing board has one group of irregular space of arranging, is provided with round tube hole in the described space.