CN201463598U - Firing plate for mullite beehive kilns - Google Patents
Firing plate for mullite beehive kilns Download PDFInfo
- Publication number
- CN201463598U CN201463598U CN2009200906294U CN200920090629U CN201463598U CN 201463598 U CN201463598 U CN 201463598U CN 2009200906294 U CN2009200906294 U CN 2009200906294U CN 200920090629 U CN200920090629 U CN 200920090629U CN 201463598 U CN201463598 U CN 201463598U
- Authority
- CN
- China
- Prior art keywords
- mullite
- supports
- convenient table
- load bearing
- tunnel kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to a firing plate for mullite beehive kilns, which is used to bear ceramic bodies. The firing plate comprises a firing support plate (3), supports (1), heat holes (4), a notched fixing leg (5) and a through-hole fixing leg (2); the four supports (1) are respectively arranged at the four corners of the firing support plate; the notched fixing leg (5) and the through-hole fixing leg (2) are respectively arranged between two supports; and the heat holes (4) are evenly arranged on the firing support plate. The firing plate has high stability and heat permeability, and overcomes the defect that the conventional firing plate is heavy; and the firing plate has the advantages of low energy consumption, sufficient burning, deformation resistance and extremely high loadage, and can reduce the cost of fired products.
Description
Technical field
The utility model relates to ceramic kiln combustion chamber support unit technical field, especially a kind of mullite polychannel tunnel kiln load bearing board that is used for the support ceramic body.
Background technology
Kiln furnitures are the special-shaped refractory materials that are used to support, protect ceramic product in the firing process, and the quality and the energy consumption of ceramic had extremely important influence.At present, most of kiln furnitures such as the push pedal that has mullite to fire to form, load bearing board, liner plate, saggar, cover alms bowl that adopt when the baked for producing ceramic.And mullite is as a kind of senior refractory raw material of anti-erosion high-quality, it have high temperature resistant, heat transfer efficiency is high, mechanical load power is strong, stable chemical performance, cold and hot stability is good, creep-resistant property is good, long service life, cost performance is than characteristics such as height, is that electronic kiln sintering process first-selection is held the firing tool.Traditional load bearing board is tabular, brick shape or be solid material, in use, diathermanous poor-performing, and traditional load bearing board itself is heavier, energy consumption is big, its useful load is because of being subjected to kiln furnitures restriction itself, useful load is also lower.
Summary of the invention
In order to overcome the deficiency in the background technology, the utility model discloses a kind of mullite polychannel tunnel kiln load bearing board, it is low that described mullite polychannel tunnel kiln has energy consumption with load bearing board, sufficient combustion, not yielding, useful load is high, can reduce the advantage of being burnt till product cost.
In order to realize the foregoing invention purpose, the utility model adopts following technical scheme:
A kind of mullite polychannel tunnel kiln load bearing board when the baked for producing ceramic, is used for the support ceramic body; Described mullite polychannel tunnel kiln load bearing board comprises holding and burns supporting plate, support, diathermanous hole, trough of belt Convenient table and open-work Convenient table; Be respectively arranged with four supports at the four corners position that holds burning supporting plate plate body; Trough of belt Convenient table and open-work Convenient table are set respectively between two supports; Diathermanous hole is evenly distributed on the load bearing board plate body.
Described mullite polychannel tunnel kiln load bearing board is same length at the mullite polychannel tunnel kiln with the height that holds four supports that are provided with respectively on the corner location that burns supporting plate.
Described mullite polychannel tunnel kiln load bearing board, being shaped as of four supports being provided with respectively on the corner location that burns supporting plate is cylindrical with holding at the mullite polychannel tunnel kiln, square column type or elliptical cylinder-shape.
Described mullite polychannel tunnel kiln load bearing board, the trough of belt Convenient table that is provided with between two supports therein, its end has rectangular through slot.
Described mullite polychannel tunnel kiln load bearing board, the open-work Convenient table that is provided with between two supports is the hollow setting therein.
Described mullite polychannel tunnel kiln load bearing board, the trough of belt Convenient table and the open-work Convenient table that between two supports, are provided with respectively, its central axis is identical or parallel lines.
Described mullite polychannel tunnel kiln load bearing board is identical size at the mullite polychannel tunnel kiln with holding the diameter that burns the diathermanous hole that evenly is provided with on the supporting plate plate body.
Owing to adopt aforesaid technical scheme, the utlity model has following superiority:
Mullite polychannel tunnel kiln load bearing board described in the utility model owing to burn the supporting plate plate body and be respectively arranged with four supports and trough of belt Convenient table and open-work Convenient table holding, has improved the stability of support ceramic body greatly; Evenly be provided with the identical diathermanous hole of diameter at described mullite polychannel tunnel kiln with holding to burn on the supporting plate plate body simultaneously, diathermanous functional, and having overcome itself heavier this disadvantage of traditional load bearing board. it is low that mullite polychannel tunnel kiln described in the utility model has energy consumption with load bearing board, sufficient combustion, not yielding, useful load is high, can reduce the advantage of being burnt till product cost.
Description of drawings
Fig. 1 is a perspective view of the present utility model.
In the drawings: 1, support; 2, open-work Convenient table; 3, hold the burning supporting plate; 4, diathermanous hole; 5, trough of belt Convenient table.
The specific embodiment
The embodiment that provides is in conjunction with the accompanying drawings further specified structure of the present utility model:
As shown in Figure 1, a kind of mullite polychannel tunnel kiln load bearing board when the baked for producing ceramic, is used for the support ceramic body; Described mullite polychannel tunnel kiln load bearing board comprises holding and burns supporting plate 3, support 1, diathermanous hole 4, trough of belt Convenient table 5 and open-work Convenient table 2; Be respectively arranged with four supports 1 at the four corners position that holds burning supporting plate plate body; Trough of belt Convenient table 5 and open-work Convenient table 2 are set respectively between two supports; Diathermanous hole 4 is evenly distributed on the load bearing board plate body.
Described is same length at the mullite polychannel tunnel kiln with the height that holds four supports 1 that are provided with respectively on the corner location that burns supporting plate 3; Being shaped as of four supports 1 being provided with respectively on the corner location that burns supporting plate 3 is cylindrical with holding at the mullite polychannel tunnel kiln, square column type or elliptical cylinder-shape; The trough of belt Convenient table 5 that is provided with between two supports therein, its end has rectangular through slot; The open-work Convenient table 2 that is provided with between two supports is the hollow setting therein; The trough of belt Convenient table 5 and the open-work Convenient table 2 that between two supports, are provided with respectively, its central axis is identical or parallel lines; Is identical size at the mullite polychannel tunnel kiln with holding the diameter that burns the diathermanous hole 4 that evenly is provided with on the supporting plate plate body.
In the use, four jiaos support 1 and trough of belt Convenient table 5 is set respectively between two supports and open-work Convenient table 2 can improve described mullite polychannel tunnel kiln with the firm performance of load bearing board, evenly be provided with the identical diathermanous hole of diameter at described mullite polychannel tunnel kiln with holding to burn on the supporting plate plate body simultaneously, capable of reducing energy consumption, improve diathermancy.
The utility model does not describe part in detail and is prior art.
Claims (7)
1. a mullite polychannel tunnel kiln load bearing board is used for the support ceramic body; It is characterized in that: described mullite polychannel tunnel kiln load bearing board comprises holding and burns supporting plate (3), support (1), diathermanous hole (4), trough of belt Convenient table (5) and open-work Convenient table (2); Be respectively arranged with four supports (1) at the four corners position that holds burning supporting plate plate body; Trough of belt Convenient table (5) and open-work Convenient table (2) are set respectively between two supports; Diathermanous hole (4) is evenly distributed on the load bearing board plate body.
2. mullite polychannel tunnel kiln load bearing board according to claim 1 is characterized in that: holding four supports (1) that are provided with respectively on the corner location that burns supporting plate (3), the height of described four supports (1) is same length.
3. mullite polychannel tunnel kiln load bearing board according to claim 1 and 2 is characterized in that: holding four supports (1) that are provided with respectively on the corner location that burns supporting plate (3), being shaped as of described four supports (1) is cylindrical, square column type or elliptical cylinder-shape.
4. mullite polychannel tunnel kiln load bearing board according to claim 1 is characterized in that: the trough of belt Convenient table (5) that is provided with between two supports therein, the end of described trough of belt Convenient table (5) has rectangular through slot.
5. mullite polychannel tunnel kiln load bearing board according to claim 1 is characterized in that: mullite polychannel tunnel kiln load bearing board, and the open-work Convenient table (2) that is provided with between two supports therein, described open-work Convenient table (2) is the hollow setting.
6. mullite polychannel tunnel kiln load bearing board according to claim 1, it is characterized in that: the trough of belt Convenient table (5) and the open-work Convenient table (2) that are provided with respectively between two supports, the central axis of described groove Convenient table (5) and open-work Convenient table (2) is identical or parallel lines.
7. mullite polychannel tunnel kiln load bearing board according to claim 1 is characterized in that: burn the diathermanous hole (4) that evenly is provided with on the supporting plate plate body at the mullite polychannel tunnel kiln with holding, the diameter in described diathermanous hole (4) is identical size.