CN1718865A - Method of removing oxidized skin on hot rolling nickel stainless steel material - Google Patents
Method of removing oxidized skin on hot rolling nickel stainless steel material Download PDFInfo
- Publication number
- CN1718865A CN1718865A CN 200510012652 CN200510012652A CN1718865A CN 1718865 A CN1718865 A CN 1718865A CN 200510012652 CN200510012652 CN 200510012652 CN 200510012652 A CN200510012652 A CN 200510012652A CN 1718865 A CN1718865 A CN 1718865A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- hot rolling
- steel material
- removing oxidized
- oxidized skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for removing the oxidized surface layer from the hot-rolled Ni-contained stainless steel includes such steps as preparing acid washing liquid from sulfuric acid or hydrochloric acid, inorganic S compound and water proportionally, immersing said stainless steel in it at 5-95 deg.C for 4-180 min, and ultrasonic cleaning in water.
Description
Technical field
The present invention relates to the matting of metallic surface, specifically belong to a kind of method of removing hot rolling nickel stainless steel bar and sheet material oxide skin.
Background technology
High temperature hot rolling nickel stainless steel bar and plate surface are covered with one deck compact structure and matrix bond is firm, molecular formula is NiOFe
2O
3With the black oxidation skin that the nickel spinel structure exists, it is insoluble in the acid.For removing this oxide skin, the technology that domestic and international enterprises of producing stainless steel is adopted is divided into two types, and a class is that the mixing acid pickling is carried out in electrolytic pickling again after the Shot Blasting, and another kind of is to implement the mixing acid pickling again after high-temperature molten salt alkali soaks.
Round the existing a lot of patent disclosures of the technical study of removing the stainless steel oxidation skin, the composition according to the pickle solution of these patent contents can reduce: fluorochemical pickling and floride-free pickling.The fluorochemical pickling is characterized as in the chemical pickling liquid and contains fluorion; Floride-free pickling is characterized as in the chemical pickling liquid not fluoride ion.
The fluorochemical pickling, as: the Acidwash solution of United States Patent (USP) 6554908 (April 29 2003 applying date) contains free sulfuric acid 50～200g/L, free hydrogen fluoric acid 0～60g/L, total fluorion 5～150g/L.Its pickle solution of Chinese patent (application number 93111022) of Desheng Seamless Steel Pipe Factory, Dalian's application is made up of nitric acid, hydrofluoric acid, hydrogen peroxide.The Chinese patent (application number 86101522) of Daming Steel Works, Shanghai's application, the moiety of its acid wash passivation cream is nitric acid, hydrofluoric acid, Magnesium Stearate, sodium polyphosphate.
Floride-free pickling; as consisting of of the passivating agent for acid-washing stainless steel of the Chinese patent (application number 03141908.9) of: Shanghai Hudong-Zhonghua Shipbuilding(Group) Co., Ltd. application: nitric acid 6～20%, phosphatase 11 2～35%, hydrogen peroxide 5～15%; phosphoric acid suffering 15～25%, magnesium nitrate 5～62%.The multifunctional pickling agent for stainless steel of the Chinese patent (application number 93108942) of Li Qing application then is made up of sulfuric acid, nitric acid and hydrochloric acid and inhibiter.
For Ni304, Ni304HC bar, the method that domestic enterprises of producing stainless steel adopts is that they are directly immersed in the mixing acid of nitric acid and hydrofluoric acid composition, cleans scale removal under 45～60 ℃ of conditions.Stainless steel enterprise is a large-lot producer, uses nitric acid, hydrofluoric acid scale removal in a large number, certainly leads to NO and HF gas to atmospheric pollution, and especially hydrogen fluoride can cause the disease that is difficult to cure to the poisoner.And fluorochemical in the waste pickle liquor and nitrate can not be separated them with the precipitator method, cause the pollution to surface water again.
Summary of the invention
The objective of the invention is to set up a kind of efficient, economical, do not use the method for the removal oxidized skin on hot rolling nickel stainless steel material of nitric acid, hydrofluoric acid.
A kind of method of removing oxidized skin on hot rolling nickel stainless steel material provided by the invention is characterized in that, comprises the steps: that (1) soak stainless material 180～4 minutes down at 5～95 ℃ with chemical pickling liquid; (2) will be cleaned material again places water with 5～120 seconds of ultrasonic generator supersound process.Take out airing then.
Described stainless material is stainless steel bars or sheet material.
The component of described pickle solution and weight proportion are: sulfuric acid or hydrochloric acid 5%～25%, and inorganic sulfide compound 0.5%～25%, all the other are water.Wherein, described inorganic sulfide compound is to be selected from a kind of in S-WAT, potassium sulfite, ammonium sulphite, V-Brite B, Sodium Pyrosulfite, Sulfothiorine, the ammonium thiosulfate.
Pickle solution of the present invention is removed nickel stainless steel material oxide skin in 5～95 ℃ of scopes, along with speeding up of pickle solution temperature rising scale removal.
Advantage of the present invention and effect:
Do not use nitric acid, hydrofluoric acid, reduce environmental pollution; The oxide skin that washes down is deposited in container bottom, is easy to separate; Production cost is low, is easy to realize industrialization.
Embodiment
Embodiment 1, at 1 liter of 10%H
2SO
4Dissolving 5 gram S-WATs in the aqueous solution.Each cleaning material is 100 gram Ni304 bars.
The pickle solution temperature (℃) 5 20 40 60 80 95
Material soak time (min) 180 60 35 10 64
The supersound process time (sec) 80 70 50 30 55
Treatment step:
(1) cleaning material is immersed in the pickle solution, pickle solution temperature and material soak time are as above shown listed;
(2) cleaning material is taken out from pickle solution, place water ultra-sonic generator supersound process again, the supersound process time is as above shown listed.Result: the oxide skin of material surface all comes off.
Used ultrasonic generator is the HYT miniature ultrasonic cleaning machine that Huayitong Mechanical Apparatus Co., Ltd., Xiamen produces, ultrasonic power 300W, ultrasonic frequency 28KHz.
Controlled trial:
Controlled trial 1 is with the H of 1 liter 20% of 100gNi304 bar immersion
2SO
4In the solution, 40 ℃ down with supersound process 15 minutes, fails scale removal.
Controlled trial 2 immerses 1 liter of H of 20% that contains the 5g S-WAT with the 100gNi304 bar
2SO
4In the solution, use supersound process 8 minutes down, get final product scale removal for 40 ℃.
Controlled trial result shows, at H
2SO
4In the aqueous solution, exist as no S-WAT, though to be cleaned material carry out supersound process can not scale removal.
The H that embodiment is 2,1 liter 20%
2SO
4Dissolving 50g S-WAT in the solution.Each cleaning material is Ni304HC bar 150 grams.
The pickle solution temperature (℃) 8 20 40 60 80
Material soak time (min) 130 60 30 12 6
The supersound process time (sec) 80 65 50 40 15
Treatment step, result are with embodiment 1.
The H that embodiment is 3,1 liter 25%
2SO
4Dissolving 100g S-WAT in the solution.Each cleaning material is 15 * 15cmNi304 sheet material.
The pickle solution temperature (℃) 20 40 60 80 95
Material soak time (min) 60 35 25 15 10
The supersound process time (sec) 120 90 80 70 60
Treatment step, result are with embodiment 1.
The H that embodiment is 4,1 liter 25%
2SO
4Dissolving 15g V-Brite B in the solution.Each cleaning material is 15 * 15cmNi304 sheet material.
The pickle solution temperature (℃) 20 40 60 80 95
Material soak time (min) 65 40 30 12 8
The supersound process time (sec) 120 90 80 65 60
Treatment step, result are with embodiment 1.
The H that embodiment is 5,1 liter 20%
2SO
4Dissolving 75g Sulfothiorine in the solution.Each cleaning material is 15 * 15cmNi304 sheet material.
The pickle solution temperature (℃) 20 40 60 80 95
Material soak time (min) 50 30 25 10 8
The supersound process time (sec) 120 100 80 60 60
Treatment step, result are with embodiment 1.
The H that embodiment is 6,1 liter 20%
2SO
4Dissolving 100g Sodium Pyrosulfite in the solution.Each cleaning material is 200 gram Ni304HC bars.
The pickle solution temperature (℃) 20 40 60 80 95
Material soak time (min) 70 45 30 18 15
The supersound process time (sec) 90 70 60 50 45
Treatment step, result are with embodiment 1.
The H that embodiment is 7,1 liter 20%
2SO
4Dissolving 150g ammonium thiosulfate in the solution.Each cleaning material is 200 gram Ni304HC bars.
The pickle solution temperature (℃) 70 80 95
Material soak time (min) 40 25 20
The supersound process time (sec) 30 20 10
Treatment step, result are with embodiment 1.
Dissolving 50g S-WAT in the hydrochloric acid soln that embodiment is 8,1 liter 15%.Each cleaning material is 200 gram Ni304HC bars.
The pickle solution temperature (℃) 25 40 60
Material soak time (min) 60 35 20
The supersound process time (sec) 100 70 40
Treatment step, result are with embodiment 1.
The H that embodiment is 9,1 liter 20%
2SO
4Dissolving 100g ammonium sulphite in the solution.Each cleaning material is 200 gram Ni304HC bars.
The pickle solution temperature (℃) 70 80 95
Material soak time (min) 30 20 10
The supersound process time (sec) 30 20 10
Treatment step, result are with embodiment 1.
Dissolving 50g potassium sulfite in the hydrochloric acid soln that embodiment is 10,1 liter 15%.Each cleaning material is 200 gram Ni304HC bars.
The pickle solution temperature (℃) 25 40 60
Material soak time (min) 60 35 20
The supersound process time (sec) 100 70 40
Treatment step, result are with embodiment 1.
Claims (3)
1, a kind of method of removing oxidized skin on hot rolling nickel stainless steel material is characterized in that, comprises the steps: that (1) soak stainless material 180～4 minutes down at 5～95 ℃ with chemical pickling liquid; (2) will be cleaned material again places water with 5～120 seconds of ultrasonic generator supersound process;
The component of described pickle solution and weight proportion are: sulfuric acid or hydrochloric acid 5%～25%, and inorganic sulfide compound 0.5%～15%, all the other are water.
2, according to the described a kind of method of removing oxidized skin on hot rolling nickel stainless steel material of claim 1, it is characterized in that described inorganic sulfide compound is to be selected from a kind of in S-WAT, potassium sulfite, ammonium sulphite, V-Brite B, Sodium Pyrosulfite, Sulfothiorine, the ammonium thiosulfate.
3, according to the described a kind of method of removing oxidized skin on hot rolling nickel stainless steel material of claim 1, described stainless material is stainless steel bars or sheet material.