CN1090339A - Multifunctional pickling agent for stainless steel - Google Patents
Multifunctional pickling agent for stainless steel Download PDFInfo
- Publication number
- CN1090339A CN1090339A CN 93108942 CN93108942A CN1090339A CN 1090339 A CN1090339 A CN 1090339A CN 93108942 CN93108942 CN 93108942 CN 93108942 A CN93108942 A CN 93108942A CN 1090339 A CN1090339 A CN 1090339A
- Authority
- CN
- China
- Prior art keywords
- component
- stainless steel
- acid
- pickling agent
- pickling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Multifunctional pickling agent for stainless steel, first, second two components are arranged, the first component contains sulfuric acid 60-80% and nitric acid 20-40%, and the second component contains hydrochloric acid 70-90% and LK type inhibiter 10-30%, and the weight proportion of first component and second component is: first 90-98%, second 2-10%.Because multifunctional pickling agent for stainless steel of the present invention adopts ternary nitration mixture and special corrosion inhibitor, make this pickling agent can significantly improve the pickled surface quality when cleaning stainless steel, shorten the pickling time, simplify acid cleaning process, alleviating environmental pollution also can be general with the continuous pickling of band steel for single groove acid Xian.
Description
The invention belongs to Stainless Steel Cleaner, be specifically related to multifunctional pickling agent for stainless steel.
The cleaning of stainless steel surface iron scale and surface passivation are handled improving the stainless steel use properties significant, are one of important procedures in the producing stainless steel process.Stainless steel surface cleans and comprises and give processings (mechanical, chemistry and electrochemistry de-scaling) and pickling twice master operation in present known technology.General acid washing method has two kinds at present, a kind of is single groove pickling, remove iron scale with sulfuric acid (or hydrochloric acid) earlier, using the nitration mixture that is made into by sulfuric acid, SODIUMNITRATE, hydrochloric acid to carry out albefaction again handles, its pickling program be sulfuric acid wash-wash-alkaline bath-water is quick-fried-sulfuric acid washes-wash-albefaction-water logging-hot water wash-flushing, through ten procedures, pickling was for up to 40-60 minute altogether.This acid cleaning process operation is many, the pickling time is long, efficient is low, pickling installation is complicated, and floor space is big.Another kind is continuous pickling, generally uses nitric acid and the pickling of hydrofluoric acid nitration mixture, and its pickling program is: and shot-peening (alkaline bath)-nitric acid hydrofluoric acid washes-water scrubs-nitric acid hydrofluoric acid washes-and water scrubs-dries.The subject matter that this technology exists is that hydrofluoric acid and nitric acid toxicity are big, and environmental pollution is serious, acid solution cost height, and pickling time long (hot rolled strip needs 9-12 minute) and pickled surface are of poor quality.
The purpose of this invention is to provide and a kind ofly can improve the pickled surface quality, simplify pickling process, shorten the pickling time, alleviate the environmental pollution that pickling causes, reduce the pickling cost and can be single groove and the general multifunctional pickling agent for stainless steel of continuous pickling.
For achieving the above object, multifunctional pickling agent for stainless steel of the present invention has first, second two components, and (1) first component has sulfuric acid and nitric acid, and its weight proportion is: sulfuric acid 60-80%, nitric acid 20-40%; (2) component B has hydrochloric acid and LK type inhibiter, and its weight proportion is: hydrochloric acid 70-90%, LK type inhibiter 10-30%; (3) weight proportion of first, second two components is: first: 90-98%, second 2-10%.
Multifunctional pickling agent for stainless steel of the present invention, also have first, second two component weight and ethanol or the phosphoric acid of 0.2-1.2%.
Multifunctional pickling agent for stainless steel of the present invention, its vitriolic concentration is preferably 92-94%.(weight meter)
Multifunctional pickling agent for stainless steel of the present invention, the concentration of its nitric acid is preferably 96-98%.(weight meter)
Multifunctional pickling agent for stainless steel of the present invention, the concentration of its hydrochloric acid is preferably 28-32%.(weight meter)
Multifunctional pickling agent for stainless steel of the present invention, concentration of ethanol (weight) is 95%, concentration of phosphoric acid is a 85%(weight).
Multifunctional pickling agent for stainless steel compound method of the present invention is: the first component, sulfuric acid and nitric acid stir by said ratio is mixed.Component B, hydrochloric acid and LK type inhibiter stir by said ratio is mixed, and first, second two components store respectively.
Multifunctional pickling agent for stainless steel using method of the present invention is that first, second two components add respectively in the entry by proportioning, stir and heated solution to 50-75 ℃, the volume ratio of pickling agent and water is 1: 2-15.Its optimum volume ratio is a pickling agent: water=1: 4-8.
The using method of multifunctional pickling agent for stainless steel of the present invention can also adopt the various compositions that will form pickling agent to add separately respectively by said ratio and make the homogeneous solution application in the entry.The volume ratio of pickling agent and water is 2-15, and optimum volume ratio is 4-8.
Because multifunctional pickling agent for stainless steel of the present invention has been used ternary nitration mixture (sulfuric acid, nitric acid and hydrochloric acid) and has been added special corrosion inhibitor, sulfuric acid is the corrosion iron scale not only, and produce hydrogen with steel reaction iron scale is had the effect of peeling off, hydrochloric acid at high temperature has the intensive corrosion to iron scale, nitric acid iron scale not only capable of washing but also stainless steel surface produced passivation, LK type inhibiter both can alleviate nitration mixture to corrosion of metal, reduce the acid consumption, suppress acid mist, pollution abatement, and can make stainless steel obtain the surface attractive in appearance of silvery white light with the nitration mixture mating reaction.Therefore, multifunctional acid lotion of the present invention has following advantage:
1, because it has excellent cleansing power to the stainless steel surface iron scale, not only capable of washing through giving the stainless steel of processing, and can clean the stainless steel of band iron scale after the hot-work, and both can be used for single groove pickling, also can be used to be with the steel continuous pickling.
2, owing to multifunctional pickling agent for stainless steel of the present invention can be finished one step of acid wash passivation, so can simplify acid cleaning process and equipment.
3, owing to multifunctional pickling agent for stainless steel ternary nitration mixture of the present invention and LK type Synergism of Inhibitors: a, make stainless steel obtain the surface attractive in appearance of silvery white light, forms good passive film, the surface quality of raising pickling; B, strengthening the cleansing power of this pickling agent to the stainless steel oxidation iron sheet, contracted scavenging period sour, only is the 10-30% of prior art pickling time.
4, because hydrofluoric acid containing not contains nitric acid less, and adopted high-efficient corrosion inhibitor,, particularly solved the NO that the stainless steel continuous pickling exists for a long time so alleviated the pollution of pickling to air and waste water
XSevere contamination problem with HF.
5, the raw materials used price of multifunctional pickling agent for stainless steel of the present invention is low, compares with hydrofluoric acid with expensive nitric acid, and cost reduces more than one times, is a kind of pickling agent for stainless steel of cheapness.
Embodiment one,
The weight proportion of the each component of multifunctional pickling agent for stainless steel of the present invention is:
(1) first component sulfuric acid 60% nitric acid 40%
(2) component B hydrochloric acid 70% LK type inhibiter 30%
(3) first component 90% component B 10%
When cleaning, presses pickling agent of the present invention first component+component B: H
2O=1: the 3(volume ratio) convert water and use.
Embodiment two,
The weight proportion of the each component of multifunctional pickling agent for stainless steel of the present invention is:
The weight proportion of the each component of multifunctional pickling agent for stainless steel of the present invention is:
(1) first component sulfuric acid 70% nitric acid 30%
(2) component B hydrochloric acid 75% LK type inhibiter 25%
(3) first component 96% component B 4%
When cleaning, presses pickling agent of the present invention first component+component B: H
2O=1: the 5(volume ratio) convert water and use.
Embodiment three,
The weight proportion of the each component of multifunctional pickling agent for stainless steel of the present invention is:
(1) first component sulfuric acid 80% nitric acid 20%
(2) component B hydrochloric acid 90% LK-45 type inhibiter 10%
(3) first component 98% component B 2%
When cleaning, presses pickling agent of the present invention first component+component B: H
2O=1: the 7(volume ratio) convert water and use.
Embodiment four,
The weight proportion of the each component of multifunctional pickling agent for stainless steel of the present invention is:
(1) first component sulfuric acid 60% nitric acid 40%
(2) component B hydrochloric acid 60% LK type inhibiter 40%
(3) first component 91% component B 9%
(4) first component+component B 99.8% ethanol 0.2%
When cleaning, presses pickling agent of the present invention first component+component B+ethanol: H
2O=1: the 8(volume ratio) convert water and use.
Embodiment five,
The weight proportion of the each component of multifunctional pickling agent for stainless steel of the present invention is:
(1) first component sulfuric acid 70% nitric acid 30%
(2) component B hydrochloric acid 75% LK-45 type inhibiter 25%
(3) first component 96% component B 4%
(4) first component+component B 99.4% ethanol 0.6%
When cleaning, presses pickling agent of the present invention first component+component B+ethanol: H
2O=1: the 13(volume ratio) convert water and use.
Embodiment six,
The weight proportion of the each component of multifunctional pickling agent for stainless steel of the present invention is:
(1) first component sulfuric acid 80% nitric acid 20%
(2) component B hydrochloric acid 90% LK-45 type inhibiter 10%
(3) first component 98% component B 2%
(4) first component+component B 98.8% ethanol 1.2%
When pickling agent of the present invention cleans by first component+component B+ethanol: water=1: the 6(volume ratio) convert the water use.
Embodiment seven,
The weight proportion of the each component of multifunctional pickling agent for stainless steel of the present invention is:
(1) first component sulfuric acid 70% nitric acid 30%
(2) component B hydrochloric acid 75% LK-45 type inhibiter 25%
(3) first component 96% component B 4%
(4) first component+component B 99.4% ethanol 0.6%
When pickling agent of the present invention cleans by first component+component B+ethanol: water=1: the 9(volume ratio) convert the water use.
Claims (5)
1, multifunctional pickling agent for stainless steel has first component and component B, it is characterized in that: (1) first component has sulfuric acid and nitric acid, and its weight proportion is: sulfuric acid 60-80%, nitric acid 20-40%; (2) component B has hydrochloric acid and LK type inhibiter, and its weight proportion is: hydrochloric acid 70-90%, LK type inhibiter 10-30%; (3) weight proportion of first component and component B is: first component 90-98%, component B 2-10%.
2, multifunctional pickling agent for stainless steel according to claim 1 is characterized in that: have in the described multifunctional pickling agent for stainless steel first, second two component weight and ethanol or the phosphoric acid of 0.2-1.2%.
3, multifunctional pickling agent for stainless steel according to claim 1 is characterized in that: described LK type inhibiter is a LK-45 type inhibiter.
4, the multifunctional pickling agent for stainless steel one of described according to claim 1-3, it is characterized in that: described multifunctional pickling agent for stainless steel is 1 with the volume dilution ratio of water: 2-15.
5, multifunctional pickling agent for stainless steel according to claim 4 is characterized in that: described multifunctional pickling agent for stainless steel is 1 with the volume dilution ratio of water: 4-8.