CN1710287A - Method for manufacturing anticorrosive wear-resistant titaniumalloy impeller for centrifugal blower - Google Patents
Method for manufacturing anticorrosive wear-resistant titaniumalloy impeller for centrifugal blower Download PDFInfo
- Publication number
- CN1710287A CN1710287A CN 200510017763 CN200510017763A CN1710287A CN 1710287 A CN1710287 A CN 1710287A CN 200510017763 CN200510017763 CN 200510017763 CN 200510017763 A CN200510017763 A CN 200510017763A CN 1710287 A CN1710287 A CN 1710287A
- Authority
- CN
- China
- Prior art keywords
- impeller
- blade
- titanium alloy
- manufacture method
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
One kind corrosion-resisting, the wear-resisting titanium alloy centrifugal air blower impeller manufacture method, its characteristic lies in: the method for making impeller of the air blower, use machine-made graphite model to cast titanium alloy air blower impeller casting in the vacuum foundry furnace; According to design request to machine-process the impeller. First chose polygon alundum wheel of 60-180 mesh to carry on coarse processing; then use basic hydroxide 50%-70%, chelating agent 10-30% and trihydroxy benzene 15-20%, three kind of surfactants mixture hot solution to make activation processing to the titanium alloy impeller blade ; Finally sprays WC series metal ceramic powder onto the blade of the said impeller by using supersonic spraying method. At the same time in the spraying process the inert gas protection is carried out to the part around the blade to the contamination by gas to the impeller.
Description
Technical field:
The present invention relates to the applied technical field of titanium-based alloy material, particularly a kind of manufacture method of anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel.
Background technique:
Centrifugal blower fan blade wheel is that pneumatic steelmaking waste gas reclaims the core component in the blower fan apparatus, and its effect is to pump by the negative pressure of blower fan import to compile back filtration processing again, carries out waste gas and is recycled.Its working environment is: water drenches acid wet environment, the washing away of the coal gas dust hybrid particles that occurs in the convertor steelmaking process, and the dust granule degree is 40 μ m, and dust content of gas is at 150mg/l, and its main component is a dust; CO:50～80%, N
2, CO
2, SO
2: 12～19%.
Former draught fan impeller front and rear cover plate is the 35MoV material, and blade is the 15MnV material; The centrifugal blower fan blade wheel material adopts 35CrMoV, and successively adopts stainless steel, A3 steel, the 45# steel body material as impeller; Adopting plating or spraying method to carry out surface abrasion resistance handles, using effect is all not obvious, add that former steel centrifugal blower fan blade wheel manufacturing process is a welded structure, the weld joint is uneven causes reasons such as dust stratification and raw material are perishable, has comprehensively caused the draught fan impeller critical component life-span to reduce and the frequent result that rolls off the production line.
After using former draught fan impeller, impeller inlet place vane thickness is thinned to 1mm by 7mm half a year as a result, and draught fan impeller structural strength deficiency loses original dynamic equilibrium state and impeller life is shortened greatly.Impeller original material centrifugal blower fan blade wheel is the longest onlinely adhered to two months, caused that this draught fan impeller service cycle is too short, user cost high.Reason be moist sour environment with the impeller material in the react compound of generation stripped shape Fe of Fe; large particle dust granule impact high speed rotation blade surface; cause the Fe compound to come off and be deposited on the blade suction surface place; and cause the impeller outlet place to narrow down; impeller pressure side place is subjected to the erosion corrosion thing and comes off; and making the impeller blade attenuate, the corrosion of impeller blade as a result aggravates.
The rotor blade of domestic water power station large-scale water turbine overcurrent blade, thermal power station adopts steel material and corresponding with it pyrolytic coating technology at present, but the abominable sour environment of metallurgy industry and wash away environment, to adopting the above-mentioned steel material and the draught fan impeller of the wear-proof technique manufacturing of correspondence not to get a desired effect, use titanium alloy material and titanium alloy Wear-resistant Treatment technology and make the draught fan impeller critical component, also do not have bibliographical information at present both at home and abroad.
Summary of the invention:
For solve present steel draught fan impeller life-span short, the problem that the cycle is frequent, can't satisfy the pneumatic steelmaking gas recovery system rolls off the production line, the manufacture method that the purpose of this invention is to provide a kind of anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel, improve the wear-resisting property of draught fan impeller, to improve the working life of draught fan impeller, reduce maintenance frequency, reduce maintenance expenses, increase economic efficiency.
For achieving the above object, the present invention adopts following technological scheme:
The manufacture method of described anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel, the employing machine adds the graphite model, waters to cast out titanium alloy draught fan impeller foundry goods in the vacuum casting stove; By designing requirement impeller casting is carried out machining; Adopt two kinds of methods to carry out surface treatment to blade then; Adopting spraying method at blade surface at last is WC that the ceramet abrasive powders carries out supersonic spray coating, will carry out inert gas shielding to position around the spraying blade simultaneously in spraying process, to reduce the pollution of gas to the titanium alloy impeller body.
The manufacture method of described anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel, to adopt the blower fan of ZTC4 titanium alloy material Integratively casting forming after machining, blade surface is handled, at first selected many ribs type 60-180 order emergy to carry out rough surface and handle.
The manufacture method of described anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel, to adopt the blower fan of ZTC4 titanium alloy material Integratively casting forming after machining, blade surface is handled, adopt alkaline hydrated oxide 50-70% again, chelating agent 10-30%, trihydroxy benzene 15-20%, the hot solution of three kinds of surface active agent compositions is carried out activation processing to the surface, titanium alloy impeller blade position after processing, and makes titanium alloy impeller blade matrix surface generate the active layer of the good one deck porous of adhesion.
The manufacture method of described anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel, and then to handle through rough surface and surface activation treatment after blade, carrying out 3-6 Mach supersonic spray coating WC is ceramet; 200～380 μ m size WC that sintering is pulverized is a ceramet, its main component: WC 7～12, and Co 2～6, and Cr 1, and metal ceramic powder makes abrasive material be deposited as wear resistant coating as high-abrasive material on the impeller blade position by special-purpose spray gun.
Owing to adopted as above technological scheme, the present invention has following good effect:
The present invention has played critical effect to the operational reliability and the stability of blower fan apparatus, greatly reduce the labor intensity and the maintenance expenses of draught fan impeller maintenance process simultaneously, titanium alloy draught fan impeller critical component of the present invention is compared with existing steel draught fan impeller, and the intensity of titanium alloy, plasticity and toughness are suitable with impeller material with present blower fan.
After the titanium alloy fan impeller blade is covered and is coated with processing, coating wear resistance: weigh surface hardness HV 〉=1000 with the surface hardness index; And untreated HV=300 is more than 3 times of untreated hardness.
Supersonic spray coating WC-Co Bond Strength of Coating σ
b〉=60Mpa.
Both acid-and base-resisting environmental corrosion of titanium alloy draught fan impeller after spraying, anti-again erosion corrosion, the life-span can be improved 4～5 times.
The invention of this technology; overcome the shortcoming of original material; having solved present steel works at first adopts water to drench dedusting; this acid, alkali condition and granulate mixture have just produced acid and alkali corrosion and erosive wear problem to impeller of high-speed fan; and the online cycle of former draught fan impeller is short, and the shortcoming that rolls off the production line and stop work diminishes because impeller weight is reduced to the 256kg motor load by 421kg; save electric energy 1/3, have broad application prospects at metallurgy industry.
AI850 draught fan impeller critical component in the diameter of phi 1540 of certain steel works, once reach the standard grade by the titanium alloy draught fan impeller of above-mentioned vacuum integral casting method and the manufacturing of Wear-resistant Treatment technology and to have reached 3 months, titanium draught fan impeller thickness when 2 years of operation test have also kept designing does not need repair welding.
Embodiment one:
The employing machine adds the graphite model, waters to cast out titanium alloy draught fan impeller foundry goods in the vacuum casting stove; By designing requirement impeller casting is carried out machining; Titanium fan impeller blade after vacuum casting surface with 60 order emergy pretreatment, is carried out the thermal spraying of supersonic speed 3-6 Mach to the wear-resistant material of 200 μ m sizes behind the sintering at blade surface, and the abrasive components weight ratio is: WC 7, Co 2, Cr 0.5.
Embodiment two:
The employing machine adds the graphite model, waters to cast out titanium alloy draught fan impeller foundry goods in the vacuum casting stove; By designing requirement impeller casting is carried out machining; Titanium fan impeller blade after vacuum casting surface with 80 order emergy pretreatment, is carried out the thermal spraying of supersonic speed 3-6 Mach to the wear-resistant material of 310 μ m sizes behind the sintering at blade surface, and the abrasive components weight ratio is: WC 8, Co 3, Cr 1.
Embodiment three:
The employing machine adds the graphite model, waters to cast out titanium alloy draught fan impeller foundry goods in the vacuum casting stove; By designing requirement impeller casting is carried out machining; Titanium fan impeller blade after vacuum casting surface with 180 order emergy pretreatment, is carried out the thermal spraying of supersonic speed 3-6 Mach to the wear-resistant material of 400 μ m sizes behind the sintering at blade surface, and the abrasive components weight ratio is: WC 12, Co 6, Cr 1.5.
Embodiment's performance index
| Test piece number (Test pc No.) | Surface hardness (HV) | Abrasive material combination force (Mpa) |
| ??1# | ??1030 | ??60.5 |
| ??2# | ??1100 | ??62 |
| ??3# | ??1006 | ??65 |
| Mean value | ??1045.3 | ??62.5 |
Claims (7)
1, a kind of manufacture method of anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel is characterized in that: the manufacture method of described draught fan impeller, and the employing machine adds the graphite model, waters to cast out titanium alloy draught fan impeller foundry goods in the vacuum casting stove; By designing requirement impeller casting is carried out machining; Adopt two kinds of methods to carry out surface treatment to blade then; Adopting spraying method at blade surface at last is WC that the ceramet abrasive powders carries out supersonic spray coating, will carry out inert gas shielding to position around the spraying blade simultaneously in spraying process, to reduce the pollution of gas to the titanium alloy impeller body.
2, the manufacture method of anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel as claimed in claim 1, it is characterized in that: the manufacture method of described draught fan impeller, to adopt the blower fan of ZTC4 titanium alloy material Integratively casting forming after machining, blade surface is handled, at first selected many ribs type 60-180 order emergy to carry out rough surface and handle.
3, as claimed in claim 1 anti-corrosion, the manufacture method of abrasion-resistant titanium alloy centrifugal blower fan blade wheel, it is characterized in that: the manufacture method of described draught fan impeller, to adopt the blower fan of ZTC4 titanium alloy material Integratively casting forming after machining, after the coarse processing of blade surface, adopt alkaline hydrated oxide 50-70% again, chelating agent 10-30%, trihydroxy benzene 15-20%, the hot solution of three kinds of surface active agent compositions is carried out activation processing to the surface, titanium alloy impeller blade position after processing, and makes titanium alloy impeller blade matrix surface generate the active layer of the good one deck porous of adhesion.
4, the manufacture method of anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel as claimed in claim 1, it is characterized in that: the manufacture method of described draught fan impeller, and then to the blade after processing of process rough surface and the surface activation treatment, carrying out 3-6 Mach supersonic spray coating WC is ceramet; 200～380 μ m size WC that sintering is pulverized is a ceramet, its main component: WC 7～12, and Co 2～6, and Cr 1, and metal ceramic powder makes abrasive material be deposited as wear resistant coating as high-abrasive material on the impeller blade position by special-purpose spray gun.
5, the manufacture method of anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel as claimed in claim 1 is characterized in that: the manufacture method of described draught fan impeller, and the employing machine adds the graphite model, waters to cast out titanium alloy draught fan impeller foundry goods in the vacuum casting stove; By designing requirement impeller casting is carried out machining; Titanium fan impeller blade after vacuum casting surface with 60 order emergy pretreatment, is carried out the thermal spraying of supersonic speed 3-6 Mach to the wear-resistant material of 200 μ m sizes behind the sintering at blade surface, and the abrasive components weight ratio is: WC 7, Co 2, Cr 0.5.
6, the manufacture method of anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel as claimed in claim 1 is characterized in that: the manufacture method of described draught fan impeller, and the employing machine adds the graphite model, waters to cast out titanium alloy draught fan impeller foundry goods in the vacuum casting stove; By designing requirement impeller casting is carried out machining; Titanium fan impeller blade after vacuum casting surface with 80 order emergy pretreatment, is carried out the thermal spraying of supersonic speed 3-6 Mach to the wear-resistant material of 310 μ m sizes behind the sintering at blade surface, and the abrasive components weight ratio is: WC 8, Co 3, Cr 1.
7, the manufacture method of anti-corrosion, abrasion-resistant titanium alloy centrifugal blower fan blade wheel as claimed in claim 1 is characterized in that: the manufacture method of described draught fan impeller, and the employing machine adds the graphite model, waters to cast out titanium alloy draught fan impeller foundry goods in the vacuum casting stove; By designing requirement impeller casting is carried out machining; Titanium fan impeller blade after vacuum casting surface with 180 order emergy pretreatment, is carried out the thermal spraying of supersonic speed 3-6 Mach to the wear-resistant material of 400 μ m sizes behind the sintering at blade surface, and the abrasive components weight ratio is: WC 12, Co 6, Cr 1.5.