CN1709718B - Method for manufacturing vitriol-plastic handicraft - Google Patents
Method for manufacturing vitriol-plastic handicraft Download PDFInfo
- Publication number
- CN1709718B CN1709718B CN 200510027427 CN200510027427A CN1709718B CN 1709718 B CN1709718 B CN 1709718B CN 200510027427 CN200510027427 CN 200510027427 CN 200510027427 A CN200510027427 A CN 200510027427A CN 1709718 B CN1709718 B CN 1709718B
- Authority
- CN
- China
- Prior art keywords
- alum
- model
- crystallization
- preparation
- vitriol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to alumina artware technical field. That is a method of the alumina molded artware. Its technical steps are (1)coiling the lines,(2) pricking the model,(3) confecting the alumia liquor,(4) riming,(5)confecting the laundered liquor,(6)washing,(7)getting the finished product. Compared with the prior art, it makes use of the principle of the physical crystal get the alumina. It can achieve the more physical artistic effect and make the production more vivid. It has the enjoyable value and the marketable value.
Description
[technical field]
The present invention relates to the handicraft manufacture technology field, specifically a kind of preparation method of vitriol-plastic handicraft.
[background technology]
With producing by indigenous method existing more than the 300 year history of alum, alum local method production principle is that ore is placed on temperature lower calcination about 700 ℃, makes it remove crystallization moisture, and with nature weathering way, after the pulverizing, uses water extraction, behind condensing crystallizing, makes alum.And unexpected discovery of people is dipped in the crystallization that can produce beauty in the alum solution with some object in the production process of alum, and be beautiful more naturally through chiseling and carving crystal product compared with some, so people have invented the preparation method of vitriol-plastic handicraft.
[summary of the invention]
The preparation method of a kind of vitriol-plastic handicraft that the objective of the invention is to utilize the alum crystallization principle and invent.
For achieving the above object, design a kind of preparation method of vitriol-plastic handicraft, its manufacturing process steps is: preparation, (4) crystallization, the preparation of (5) cleaning fluid, (6) cleaning, (7) that model, (3) alum solution are pricked in (1) coiling, (2) get finished product.
The preparing process of described alum solution is: alum and water are put into container, be heated to 72 ℃-75 ℃, be mixed with the alum solution that concentration is 23-25g/L.
Described crystallization processes is: model is put into temperature soaked 80-90 minute at 30 ℃ alum solution.
The alum solution that water is mixed with 2g/L is put into alum in being formulated as of cleaning fluid at normal temperatures.Clean to the model after the crystallization is placed on and soak in the cleaning fluid 2-5 second.
The present invention compares with prior art, and it is the handicraft that utilizes the spontaneous nucleation principle to obtain, and can reach more natural artistic effect, makes works more lively, is rich in ornamental value, has market value.
[description of drawings]
Fig. 1 is a process chart of the present invention.
Appointment Fig. 1 is a Figure of abstract.
Referring to Fig. 1,1 is coiling; 2 for pricking model; 3 is the preparation of alum solution; 4 are crystallization; 5 are the cleaning fluid preparation; 6 for cleaning; 7 be finished product.
[specific embodiment]
The present invention is further illustrated below in conjunction with accompanying drawing, and the present invention is still more clearly concerning those skilled in the art.
Copper wire one end is also tied a knot around last yarn, then the copper wire other end being placed on 2 wants in the middle of the brick, and a woodbox is fixed, arrest the end of copper wire knotting on the other hand, another hand is arrested another piece woodbox, utilizing the friction of 2 woodboxs to drive copper wire rotates and makes yarn equably on the copper wire, till copper wire is put on the spot fully, then according to different moulding needs, utilize tweezers around the copper wire of last yarn according to certain size, lace becomes as birds and flowers, Chinese caterpillar fungus, the booth platform, moulding such as building are carried out integral layout with this model according to design again, and utilize yarn or copper wire to be fixed; Alum and water are put into container, be heated to 72 ℃-75 ℃, be mixed with the alum solution that concentration is 23-25g/L; The model of moulding put in the alum solution of temperature about 30 ℃ soaked 80-90 minute, make it crystallization; Prepare the alum solution of 2g/L then at normal temperatures as cleaning fluid, alum handicraft after the crystallization is placed in the cleaning fluid for preparing soaks 2-5 and take out after second, removed surperficial unnecessary impurity, made the handicraft of crystallization more glittering and translucent, just obtained alum and moulded handicraft.
Claims (2)
1. the preparation method of a vitriol-plastic handicraft is characterized in that its manufacturing process steps is: (1) on the copper wire equably around on yarn; (2) will be bundled into model around the copper wire of last yarn; (3) preparation of alum solution: alum and water are put into container, be heated to 72 ℃-75 ℃, be mixed with the alum solution that concentration is 23-25g/L; (4) crystallization: model is put into temperature soaked 80-90 minute, form crystallization at model surface at 30 ℃ alum solution; (5) cleaning fluid preparation: at normal temperatures alum is put into the alum solution that water is mixed with 2g/L; (6) clean: the model of crystallization is put into cleaning fluid clean; (7) get finished product.
2. the preparation method of a kind of vitriol-plastic handicraft as claimed in claim 1 is characterized in that: clean to the model after the crystallization is placed on and soak in the cleaning fluid 2-5 second.