CN1709612A

CN1709612A - Superthin-wall aluminium-alloy high-speed pressure casting method

Info

Publication number: CN1709612A
Application number: CNA2004100499285A
Authority: CN
Inventors: 张宗贵; 张杨宁
Original assignee: GALAXY TOP-QUALITY INDUSTRIAL Co Ltd
Current assignee: GALAXY TOP-QUALITY INDUSTRIAL Co Ltd
Priority date: 2004-06-17
Filing date: 2004-06-17
Publication date: 2005-12-21
Anticipated expiration: 2024-06-17
Also published as: CN1310725C

Abstract

This present invention relates to a method of high speed die-casting of super thin wall aluminous alloy. It comprises the steps as follow: putting a model in a die-casting machine, setting up the die-casting parameter, keeping the casting pressure at 780kg/cm2, model temperature 250Deg.c, solvent temperature 700Deg.c, then injecting the aluminous alloy into die-casting machine. Shoot up with 0.23m/sec to make cast whose wall thickness is less than 1.0mm, then take the cast out and plastic, smear, detect to satisfy international standard. This cast can be applied mainly in 3C product while the crust of computer, digital camera and mobile telephone.

Description

Ultra-thin-wall aluminium alloy high speed pressure casting method

Technical field

The present invention relates to a kind of ultra-thin-wall aluminium alloy high speed pressure casting method, relate in particular to a kind of aluminium alloy that adds copper,, and can produce the foundry goods that changes original tensile strength, make it have frivolous, short and small advantage by the setting of high-pressure forming machine parameter.

Background technology

The present scope used of industrial community thin-wall product is mainly the casing of 3C Product, as: mobile computer, digital camera, mobile phone and discman etc.Main production method is injection molding, die cast metal or pressed part, on die cast metal, adopt magnesium alloy usually, but because the die casting cost of magnesium alloy, and the surface-treated cost all is higher than aluminium alloy, under metal-like and characteristic also all will good situations than magnesium alloy, in the exploitation and the application of 3C Product, aluminium alloy replaces magnesium alloy gradually.

And the aluminium alloy of general traditional die casting, in the die casting, molten soup is quite fast in the speed of die cavity internal cooling, during the foundry goods of desire shaping sake, mold filling is difficult for and insufficient rigidity of material, and the possibility of distortion is arranged when foundry goods ejects, so the used aluminium alloy of casting forming, must adjust the composition of alloy, increase the intensity and the rigidity of material.

So when making the big foundry goods of wall sake, the slip-stick artist generally tends to wall thickness design with foundry goods between 1.5 to 2.0 millimeters (mm), even it is bigger, to avoid casting thickness too thin, metallic solution takes place pour into a mould discontented phenomenon in mould, and for present general portable 3C Product, 1.5 the casting thickness to 2.0 millimeters (mm) is still too high, still can't satisfy the demand that 3C Product uses, in view of this, how reducing the thickness that aluminium alloy compression casting is shaped, meet the demand that 3C Product uses according to this, is that the contriver wants improved place.

This case contriver because above-mentioned conventional al alloy when actual mold, disappearance that has and restriction, the long-pending individual of edge is engaged in this cause experience for many years, and studies intensively, and designs a kind of brand-new ultra-thin-wall aluminium alloy high speed pressure casting method finally.

Summary of the invention

Main purpose of the present invention is to provide a kind of ultra-thin-wall aluminium alloy high speed pressure casting method, is the die casting parameter of high speed pressure die-casting machine will be done an adjustment, allows foundry goods when casting forming, can obtain optimized setting, cooperates the making of foundry goods.

Secondary objective of the present invention is to provide a kind of ultra-thin-wall aluminium alloy high speed pressure casting method, is the composition of aluminium material alloy will be done a change, makes it increase tensile strength, and the reduction casting section thickness is to meet the design requirement of 3C Product.

For achieving the above object, the present invention is placed in a mould in the high speed pressure die-casting machine, sets the die casting parameter, uses fixedly 780kg/cm ²Casting pressure, to keep the mould temperature be 700 ℃ in 250 ℃, molten soup temperature, again aluminium material alloy is injected mould, use the 0.23m/sec injection molding, produce wall thickness 1.0 millimeters (mm) according to this with interior foundry goods, this foundry goods can have preferable tensile strength, again foundry goods is taken out and impose shaping and dress is coated with operation, cooperate product to detect and make it meet international norm; The scope system that this foundry goods is used is based on 3C Product, and collocation is used for the shell of mobile computer, digital camera and mobile phone etc.

Thereby the present invention has following improvement in design:

The die casting parameter that high speed pressure die-casting machine of the present invention sets is with 780kg/cm ²250 ℃ of casting pressure, mould temperature, molten soup temperature be 700 ℃, and, can form best process conditions with the issuing velocity of 0.23m/sec.

Aluminium material alloy ingredient of the present invention is because include magnesium, 0.17% manganese, 0.79% zinc, 10.87% silicon, 0.05% nickel, 0.79% iron and 0.03% the titanium and 0.5～1.8% the copper of aluminium, weight 0.22%.So can be when making foundry goods, tensile strength, yield strength and unit elongation that performance is best.

Description of drawings

Fig. 1 is the schematic flow sheet of pressure casting method of the present invention.

Among the figure

1 design and fabrication mould

2 installation molds are in pressure die-casting machine

3 set the pressure die-casting machine parameters

4 with aluminium material alloy input pressure die-casting machine

5 form foundry goods

6 foundry goods shaping and applications

7 foundry goods detect

Embodiment

Now be described in detail as follows with a preferable possible embodiments and a conjunction with figs.:

See also shown in the figure, be the schematic flow sheet of pressure casting method of the present invention.

On the invention process,, at first be a selected target casing as step 1, first portion's scheme of stipulating of rule rule of thumb.Utilize three-dimensional space casting Computer Simulation software Pro CAST to carry out three-dimensional space mould stream and the Computer Simulation of heat biography, carry out the preceding of Computer Simulation must be with I-DEARS3D software, set up the founding method of casing, make mould according to computer artificial result again, then carry out step 2, make mould according to computer artificial result, mould is installed on the board, the vertical high-pressure casting machine of described board use nine CT-250 of great-grand father department of system (or claiming molten soup swaging machine), then carry out step 3, allow the casting pressure of pressure die-casting machine be set at 780kg/cm ²The mould temperature remains on 250 ℃, molten soup temperature is 700 ℃, then carry out step 4, ADC12 has aluminium with code name, the magnesium of weight 0.22%, 0.17% manganese, 0.79% zinc, 10.87% silicon, 0.05% nickel, the aluminium material alloy of the copper of 0.79% iron and 0.03% titanium and 0.5～1.8% drops in the board, the issuing velocity that uses is 0.23m/sec, allow speed keep fixing switching low speed and high speed setting, just can be shaped as step 5 wall thickness 1.0 millimeters (mm) with interior foundry goods, then carry out step 6, the foundry goods that completes is taken out, foundry goods is carried out back segment to be handled, the running channel (Runner) of excision mould, progressive die mouth (Ingate), overflow well (Overflow) and stub bar runner systems such as (Biscuit), foundry goods is imposed spraying operation, then shown in step 7, the foundry goods that spraying is finished, impose and comprise X-ray, tack, hardness, solidity to corrosion, electromagnetic interference, the test of thermal conductivity coefficient and mechanical property, what make meets the international norm standard.

The scope system of its application of foundry goods that this completes is based on 3C Product, and collocation is used for the shell of mobile computer, digital camera and mobile phone etc.

The above only is in order to explain preferred embodiment of the present invention; be not that the present invention is done any pro forma restriction; thereby, all have in that identical invention spirit is following do relevant any modification of the present invention or change, all must be included in the category that the invention is intended to protect.

Claims

1. ultra-thin-wall aluminium alloy high speed pressure casting method is characterized in that:

One mould is placed in the high speed pressure die-casting machine, sets the die casting parameter, use fixedly 780kg/cm ²Casting pressure, to keep the mould temperature be 700 ℃ in 250 ℃, molten soup temperature, again aluminium material alloy injected pressure die-casting machine, uses the 0.23m/sec injection molding, produces 1.0 millimeters of wall thickness according to this with interior foundry goods.

2. ultra-thin-wall aluminium alloy high speed pressure casting method according to claim 1 is characterized in that:

This aluminium material alloy ingredient includes magnesium, 0.17% manganese, 0.79% zinc, 10.87% silicon, 0.05% nickel, 0.79% iron and 0.03% the titanium and 0.5～1.8% the copper of aluminium, weight 0.22%.