CN1702247A - 环保节能阻燃型挤塑式聚苯乙烯保温板及其制备方法 - Google Patents
环保节能阻燃型挤塑式聚苯乙烯保温板及其制备方法 Download PDFInfo
- Publication number
- CN1702247A CN1702247A CN 200510040534 CN200510040534A CN1702247A CN 1702247 A CN1702247 A CN 1702247A CN 200510040534 CN200510040534 CN 200510040534 CN 200510040534 A CN200510040534 A CN 200510040534A CN 1702247 A CN1702247 A CN 1702247A
- Authority
- CN
- China
- Prior art keywords
- districts
- flame retardant
- thermal insulation
- environment
- polystyrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种环保节能阻燃型挤塑式聚苯乙烯保温板及其制备方法，它是由以下组分的原料组成：聚苯乙烯94～95％、色母粒0.5～0.6％、纳米滑石粉2.5～2.6％、六溴环十二烷1.8～2.4％和发泡催化剂氟里昂0.2～0.4％。其制备方法为：将聚苯乙烯加上色母粒、纳米滑石粉和六溴环十二烷阻燃剂通过混配，在200℃～220℃进行搅拌后均匀加入挤塑机内，进行加热混合同时注入发泡催化剂氟里昂，然后挤塑压出成型。本发明低容重、低吸水性、低热导系数，高抗压性和抗老化。
Description
技术领域：
本发明涉及一种建筑物或路面隔热、防冻、防潮用保温板，具体涉及一种环保节能阻燃型挤塑式聚苯乙烯保温板。属保温材料技术领域。
背景技术：
房屋建筑，特别是高寒地区的房屋建筑，建筑物中的大量热量是通过屋顶、墙体散失的。因此，其屋顶、隔墙及外墙均需铺砌保温层，用以保温隔热和节约能源。在北方地区，由于天气的寒冷，水汽、冰霜等对路面的侵蚀使许多公路、铁路、机场跑道等出现高低不平的状况，使得安全出现了一系列的隐患。因此控制路面冷胀是必不可少的事。目前，在房屋建筑或路面建设中铺砌保温层大体分为三大类：一类是将粒状保温材料如膨胀珍珠岩，轻质陶瓷等与水泥混合制成浆料，然后将其浇灌在建筑中的一定部位，以形成保温层；第二类是用某种胶凝剂如水泥等将粒状保温材料如泡沫塑料、陶粒、珍珠炭、粉煤灰等预制成保温板，施工时，将其铺砌于屋顶、隔墙、外墙或路面中，形成保温层。第三类是采用挤塑方法生产的低密度保丽龙板(EPS)。施工时将其直接铺砌于建筑隔墙或道路路面中。后二类在施工方面显然要比第一类方法简便，但无论哪一类方法，又都有这样或那样的缺点和不足，例如，有的保温材料容重过大，如加气砼块，憎水珍珠岩，水泥泡沫塑料板等，一般容重大于600～700kg/m3；有的导热系数偏高，保温效果不好，如加气砼块，陶粒灌层，珍珠炭浇灌层等，其导热系数均大于0.3w/mk；吸水率均大于2％；有的强度不够，施工中保温层容易破损。如保丽龙板吸水性和热导系数高，抗压低、密度低、抗老化性弱等。因此，建筑界仍在不断努力，研究开发性能优越的保温材料，以适应建筑市场日益增大的需求。
发明内容：
本发明的目的在于克服上述不足，提供一种低容重、低吸水性、低热导系数，高抗压性和抗老化的环保节能阻燃型挤塑式聚苯乙烯保温板。
本发明的目的是这样实现的：一种环保节能阻燃型挤塑式聚苯乙烯保温板，它是由以下组分的原料组成：聚苯乙烯、色母粒、纳米滑石粉、辅料、聚合物、六溴环十二烷阻燃剂和催化剂氟里昂；其各组分的重量百分比为：
聚苯乙烯 94～95％
色母粒 0.5～0.6％
纳米滑石粉 2.5～2.6％
六溴环十二烷 1.8～2.4％
氟里昂 0.2～0.4％
各组分的重量比总和为100％。
其制备方法为：将聚苯乙烯加上色母粒、纳米滑石粉和六溴环十二烷阻燃剂通过混配，进行搅拌后均匀加入挤塑机内，进行加热混合同时注入发泡催化剂氟里昂，然后挤塑压出成型，挤压的过程制造出拥有连续、均匀的表面及闭孔式蜂窝结构。这些蜂窝结构的互连壁有一致的厚度，完全不会出现空隙。这种闭孔蜂窝结构使本发明保温板具有传统低密度保丽龙板所没有的极低的吸水性(几乎不吸水)、低热导系数、高抗压性能及抗老化，正常使用几乎无老化分解现象。
由于聚苯乙烯原材料的分子链非常稳定，在生产过程中没有化学反应，注入氟里昂气体后，通过一系列的物理发泡工艺加上合理的温度区域(共分八个区，一区80℃±5℃，二区180℃±5℃，三区165℃±5℃，四区120℃±5℃，五区100℃±5℃，六区30℃±2℃，七区30℃±2℃，八区30℃±2℃，模头115℃±5℃)，原有性能没有受到破坏和改变，纳米滑石粉的加入使产品泡孔起到一种均匀而密集的作用。阻燃剂的合理加入，增强了保温板本身的阻燃性能，加入颜色母粒在生产工艺过程中能体现产品的整体规定颜色。抗老化也就是本身采用了整体生产工艺的一个物理反应的全部过程。因此本发明具有绝佳的隔热性、绝低的透湿系数和低容重。特别适用于建筑物的隔热、防冻、防潮工程。还可以适用于公路、铁路、机场跑道等。它可以阻止水汽、冰雹等的渗透把路基结冰情况减少至最低，有效地控制地面冷胀，延长其使用寿命。
具体实施方式：
实施例1：
将950kg聚苯乙烯加上5kg色母粒、25kg纳米滑石粉和18kg六溴环十二烷阻燃剂通过混配，在200℃～220℃下进行搅拌后均匀加入挤塑机内，加热混合同时注入2kg催化剂氟里昂，然后挤塑压出成型。其中挤塑机温度区域共分八个区，一区80℃，二区180℃，三区165℃，四区120℃，五区100℃，六区30℃，七区30℃，八区30℃，模头105℃。
实施例2：
将940kg聚苯乙烯加上6kg色母粒、26kg纳米滑石粉和24kg六溴环十二烷阻燃剂通过混配，在200℃～220℃下进行搅拌后均匀加入挤塑机内，加热混合同时注入4kg催化剂氟里昂，然后挤塑压出成型。其中挤塑机温度区域共分八个区，一区85℃，二区175℃，三区170℃，四区115℃，五区105℃，六区28℃，七区28℃，八区28℃，模头115℃。
实施例3：
将945聚苯乙烯加上5.5kg色母粒、25.5kg纳米滑石粉和21kg六溴环十二烷阻燃剂通过混配，在200℃～220℃下进行搅拌后均匀加入挤塑机内，加热混合同时注入3kg催化剂氟里昂，然后挤塑压出成型。其中挤塑机温度区域共分八个区，一区75℃，二区185℃，三区160℃，四区125℃，五区95℃，六区32℃，七区32℃，八区32℃，模头110℃。
Claims (2)
1、一种环保节能阻燃型挤塑式聚苯乙烯保温板，其特征在于它是由以下组分的原料组成：聚苯乙烯、色母粒、纳米滑石粉、六溴环十二烷阻燃剂和发泡催化剂氟里昂；其各组分重量百分比为：
聚苯乙烯94～95％
色母粒0.5～0.6％
纳米滑石粉2.5～2.6％
六溴环十二烷1.8～2.4％
氟里昂0.2～0.4％
各组分的重量比总和为100％。
2、根据权利要求1所述的一种环保节能阻燃型挤塑式聚苯乙烯保温板的制备方法，其特征在于其具体工艺步骤为：将聚苯乙烯加上色母粒、纳米滑石粉和六溴环十二烷阻燃剂通过混配，在200℃～220℃进行搅拌后均匀加入挤塑机内，进行加热混合同时注入发泡催化剂氟里昂，然后挤塑压出成型，挤塑机温度区域共分八个区，一区80℃±5℃，二区180℃±5℃，三区165℃±5℃，四区120℃±5℃，五区100℃±5℃，六区30℃±5℃，七区30℃±5℃，八区30℃±5℃，模头115℃±5℃。