CN1695911A

CN1695911A - Method for fabricating damp proofing and heat-resistant floorboard in solid wood structure

Info

Publication number: CN1695911A
Application number: CN 200510049802
Authority: CN
Inventors: 姚根法
Original assignee: Individual
Current assignee: Individual
Priority date: 2005-05-23
Filing date: 2005-05-23
Publication date: 2005-11-16
Anticipated expiration: 2025-05-23
Also published as: CN100337802C

Abstract

A wooden floor board resisting moisture and high temp is prepared through providing raw materia, gluing, sawing, planning, making the slot on bottom by planning, making tenons and mortises, painting, and drying.

Description

The manufacture method of damp proofing and heat-resistant floorboard in solid wood structure

Technical field

The present invention relates to a kind of manufacture method of timber floor, the manufacture method that particularly a kind of moisture resistance heat-resisting solid wood structure floor is used.

Background technology

Below the indoor floor of the many top grades in the north, be provided with thermal source, heating installation is transmitted on the floor, warm sensation is also arranged on the floor even step in winter like this.This floor generally is made up of multilayer, is that the top layer is generally thinner topmost, and material is good, and is not only attractive in appearance but also wear-resisting, and price is higher; The second layer is the table substrate; The 3rd layer is central layer, thicker, normally uses elongated timber wide, uniform thickness, and a rule is arranged in parallel and becomes to have the flat board of slit as the air guide groove, fixing with the horse nail between the elongated timber.Be base plate again, be by being arranged in parallel with a gap each other, and become cross-like with the slit of central layer with the isometric strip solid wood in floor; Four layers of plank are bonding through adhesive, into strips the floor.Around central layer, have corresponding groove and tenon again, last frosted, paint, package test warehouse-in.The floor of every strip is spliced into large-area floor by cooperatively interacting between groove around the central layer and the tenon.Make with such method that the waste of moisture resistance heat-resisting solid wood structure flooring material is many, production efficiency is low, manufacturing cost is high, quality is difficult for assurance.

Summary of the invention

The present invention has overcome the shortcoming that exists in the existing method, provides a kind of easily manufactured, the manufacture method of the damp proofing and heat-resistant floorboard in solid wood structure that production efficiency is high.

In order to address the above problem, the present invention realizes through the following steps:

(1), gets the raw materials ready

1. the manufacturing of dash board;

2., the manufacturing of table substrate;

3., the manufacturing of central layer;

4., the manufacturing of base plate;

(2), gummed

1., gluing;

2., pasting board;

3., pressurization, curing;

(3), saw plate

(4), long limit groove, tenon are driven in sliced venceer, sole plate groove, side

(5), saw end face length, drive end face groove, tenon

(6), oil surface lacquer, oven dry or airing

(7), check, packing, warehouse-in.

The central layer of processing damp proofing and heat-resistant floorboard in solid wood structure according to said method has production efficiency height, dimensional accuracy height, and quality guarantees easily, advantage of low manufacturing cost.

Description of drawings

Fig. 1 is the front view of dash board;

Fig. 2 is Fig. 1 vertical view;

Fig. 3 is the front view of table substrate;

Fig. 4 is the vertical view of Fig. 3;

Fig. 5 is the front view of base plate;

Fig. 6 is the vertical view of Fig. 5;

Fig. 7 is the front view of central layer head and the tail plate;

Fig. 8 is the vertical view of Fig. 7;

Fig. 9 is the front view of central layer intermediate plate;

Figure 10 is the vertical view of Fig. 9;

Figure 11 is the front view after dash board, table substrate, central layer and base plate are fitted;

Figure 12 is the vertical view of Figure 11;

Figure 13 is the front view of damp proofing and heat-resistant floorboard in solid wood structure blank;

Figure 14 is the vertical view of Figure 13;

Figure 15 is the bottom view that floor blank long side face is left the groove that groove, tenon and base plate mill out;

Figure 16 is the vertical view of Figure 15;

Figure 17 is the front view of finished product damp proofing and heat-resistant floorboard in solid wood structure;

Figure 18 is the right view of Figure 17;

Wherein: 1, dash board; 2, table substrate; 3, base plate; 4, central layer; 5, air guide groove; 6, central layer head and the tail plate; 7, central layer intermediate plate; 8, spacing; 9, grow the limit groove; 10, grow the limit tenon; 11, groove; 12, end face groove; 13, end face tenon.

The specific embodiment

The invention will be further described below in conjunction with the drawings and specific embodiments.

(1), gets the raw materials ready

1. the manufacturing of dash board, table substrate, base plate:, respectively log is gone out boiling behind the square stock according to the timber kind and the specification of three kinds of plates; Square stock is split into the thin slice blank; Upper surface, the lower surface of sand blank regrinded finish dash board 1 (as Fig. 1, Fig. 2), table substrate 2 (as Fig. 3, Fig. 4), and base plate 3 (as Fig. 5, Fig. 6), manufacturing procedure.

2., the manufacturing of central layer: central layer 4 is to form according to different central layer head and the tail plate 6 and the central layer intermediate plates 7 of dividing in the interval of air guide groove 5, their manufacturing goes out square stock, boiling, square stock by log and is split into thin slice, become central layer 4 blanks, the upper and lower surface of planing central layer 4 blanks, the two sides on long limit on special purpose machine tool, on central layer 4 blanks, leave air guide groove 5 according to the interval of air guide groove 5 again, frosted again, finish the processing of central layer head and the tail plates 6 (as Fig. 7, Fig. 8), the processing of central layer intermediate plate 7 (as Fig. 9, Figure 10) is also identical.

(2), gummed

1., gluing: at the faying face cementing of dash board 1, table substrate 2, central layer 4, base plate 3.

2., pasting board: dash board 1, table substrate 2, central layer 4 and base plate 3 are fitted successively, and to make both sides be central layer head and the tail plates 6, the centre is a central layer intermediate plate 7, air guide groove 5 is perpendicular with the lumber fibre direction of other plates, leaves the spacing 8 (as Figure 11, Figure 12) of making tenon and saw kerf between adjacent side by side dash board 1, the table substrate 2;

3., pressurization, curing: the glued board after will fitting is put into pressurization release after 2 hours in the press, spontaneous curing 24 hours.

(3), saw plate: along the spacing 8 sawings damp proofing and heat-resistant floorboard in solid wood structure blank (as Figure 13, Figure 14) into strips that stays between adjacent dash board 1, the table substrate 2.

(4), long limit groove, tenon are driven in sliced venceer, sole plate groove, side: the upper and lower surface of digging the damp proofing and heat-resistant floorboard in solid wood structure blank on special purpose machine tool; On the central layer 4 on its two long limits, mill out long limit groove 9 and long limit tenon 10; Special-purpose milling cutter mills out the groove 11 of base plate 3, and communicate with the air guide groove 5 of central layer 4 (as Figure 15, Figure 16).

(5), saw end face length, drive end face groove, tenon: the end face length of cutting floor blank on double-side saw; On the central layer 4 of floor blank end face, mill out the end face groove 12 and the end face tenon 13 (as Figure 17, Figure 18) of both ends of the surface together.

(6), oil surface lacquer, oven dry or airing.Become the finished product of damp proofing and heat-resistant floorboard in solid wood structure.

(7), check, packing, warehouse-in.

By above-mentioned each procedure, finish the processing of damp proofing and heat-resistant floorboard in solid wood structure.

Claims

1, a kind of manufacture method of damp proofing and heat-resistant floorboard in solid wood structure is characterized in that it comprises the following steps:

(1), gets the raw materials ready

1., the manufacturing of dash board;

2., the manufacturing of table substrate;

3., the manufacturing of central layer;

4., the manufacturing of base plate;

(2), gummed

1., gluing;

2., pasting board;

3., pressurization, curing;

(3), saw plate

(5), saw end face length, drive end face groove, tenon

(6), oil surface lacquer, oven dry or airing

(7), check, packing, warehouse-in.

2, the manufacture method of damp proofing and heat-resistant floorboard in solid wood structure according to claim 1, the manufacturing that it is characterized in that dash board, table substrate and base plate goes out square stock, boiling, square stock by log and is split into the thin slice blank, and upper surface, the lower surface of the sand blank of regrinding finished the manufacturing procedure of dash board, table substrate and base plate.

3, the manufacture method of damp proofing and heat-resistant floorboard in solid wood structure according to claim 1, the manufacturing that it is characterized in that central layer goes out square stock, boiling, square stock by log and is split into thin slice, become the central layer blank, the upper and lower surface of planing central layer blank, the two sides on long limit, on the central layer blank, leave the air guide groove according to the interval of air guide groove again, the manufacturing procedure of central layer is finished in frosted again.

4, the manufacture method of damp proofing and heat-resistant floorboard in solid wood structure according to claim 1 is characterized in that long limit groove is opened in sliced venceer, sole plate groove, side, tenon is finished in same operation.

5, the manufacture method of damp proofing and heat-resistant floorboard in solid wood structure according to claim 1 is characterized in that out that end face groove, tenon finish in same operation.