CN1693264A - 抗盐渍系列混凝土外加剂 - Google Patents

抗盐渍系列混凝土外加剂 Download PDF

Info

Publication number
CN1693264A
CN1693264A CNA2005100206503A CN200510020650A CN1693264A CN 1693264 A CN1693264 A CN 1693264A CN A2005100206503 A CNA2005100206503 A CN A2005100206503A CN 200510020650 A CN200510020650 A CN 200510020650A CN 1693264 A CN1693264 A CN 1693264A
Authority
CN
China
Prior art keywords
sodium
sodium sulfate
additive
saltresistance
admixture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2005100206503A
Other languages
English (en)
Other versions
CN1328203C (zh
Inventor
刘连新
黄梓平
王潘劳
张伟勤
戴大虎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qinghai University
Original Assignee
Qinghai University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qinghai University filed Critical Qinghai University
Priority to CNB2005100206503A priority Critical patent/CN1328203C/zh
Publication of CN1693264A publication Critical patent/CN1693264A/zh
Application granted granted Critical
Publication of CN1328203C publication Critical patent/CN1328203C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种添加剂，特别是涉及一种用于配制抗盐渍腐蚀混凝土的外加剂。本发明抗盐渍系列混凝土外加剂由下述重量百分含量原料制成：β基萘磺酸钠甲醛缩聚物75～92％；硫酸钠4～15％；松香热聚物0.5～3.5％；镁粉1～2％；烷基苯磺酸盐0.5～3.5％；氟硅酸钠1～3.5％；三乙醇胺1～2％；硅酮0.5～3.5％；消泡剂0.9～1.1％；氯化钙0.9～1.1％；亚硝酸钠+硫酸钠0.9～1.1％；羟基羧酸类1.5～2.5％。本发明与现有技术相比较有如下有益效果：本产品对提高混凝土的抗冻能力、抗渗能力、抗腐蚀能力、延长工程结构使用寿命均有良好的效果。本发明产品原料充足，配制简便，可广泛应用于盐湖地区和盐渍土地区一切工程结构建设中。

Description

抗盐渍系列混凝土外加剂
                        技术领域
本发明涉及一种添加剂，特别是涉及一种用于配制抗盐渍腐蚀混凝土的外加剂。
                        背景技术
众所周知，盐湖资源的开发与利用是21世纪西部开发的重点之一，混凝土已广泛应用于盐湖地区和盐渍土地区铁路和公路的桥梁、隧洞、生产厂房及办公楼等的工程结构之中。而盐湖地区各种盐类对混凝土的腐蚀之严重，已引起了工程界的极大关注。如何采用抗腐蚀外加剂、矿物掺和料配制具备高抗腐蚀性能的混凝土，对工程结构的高耐久性、安全性和延长使用寿命具有重要意义。目前国内混凝土外加剂的种类和品种很多，但专门针对盐湖地区和盐渍土地区混凝土结构工程的防腐蚀外加剂产品，还未见记载。
                      发明内容
本发明要解决的技术问题是克服现有技术存在的不足，提供一种具有减水、抗冻和抗盐渍腐蚀性能的混凝土外加剂。
本发明的技术方案是，本发明抗盐渍系列混凝土外加剂由下述重量百分含量原料制成：β基萘磺酸钠甲醛缩聚物75～92％；硫酸钠4～15％；松香热聚物0.5～3.5％；镁粉1～2％；烷基苯磺酸盐0.5～3.5％；氟硅酸钠1～3.5％；三乙醇胺1～2％；硅酮0.5～3.5％；消泡剂0.9～1.1％；氯化钙0.9～1.1％；亚硝酸钠+硫酸钠0.9～1.1％；羟基羧酸类1.5～2.5％。
本发明与现有技术相比较有如下有益效果：由于本发明是专门针对盐湖地区和盐渍土地区混凝土而研制的抗腐蚀高性能混凝土所用抗盐渍浸蚀混凝土外加剂，本产品对提高混凝土的抗冻能力、抗腐蚀能力、延长工程结构使用寿命均有良好的效果。本发明抗盐渍系列混凝土外加剂可根据高海拔、高寒盐湖地区不同卤水和土质配制原料，取得减水、收缩小、防止裂纹、抗冻和抗盐渍腐蚀性能的混凝土外加剂。本发明产品原料充足，配制简便，可广泛应用于盐湖地区和盐渍土地区一切工程结构建设中。
                      具体实施方式
下面结合实施例对本发明作进一步描述。本发明抗盐渍系列混凝土外加剂由下述重量百分含量原料制成：β基萘磺酸钠甲醛缩聚物75～92％；硫酸钠4～15％；松香热聚物0.5～3.5％；镁粉1～2％；烷基苯磺酸盐0.5～3.5％；氟硅酸钠1～3.5％；三乙醇胺1～2％；硅酮0.5～3.5％；消泡剂0.9～1.1％；氯化钙0.9～1.1％；亚硝酸钠+硫酸钠0.9～1.1％；羟基羧酸类1.5～2.5％。
实施例1。
由下述重量百分含量原料制成抗盐渍、防止混凝土裂纹早强的防腐减水I型抗盐渍混凝土外加剂：β基萘磺酸钠甲醛缩聚物80％；硫酸钠12.5％；松香热聚物2.0％；氟硅酸钠1.5％；硅酮2.0％；消泡剂1.0％；亚硝酸钠+硫酸钠1.0％。
实施例2。
由下述重量百分含量原料制成缓凝、防腐减水II型抗盐渍混凝土外加剂：β基萘磺酸钠甲醛缩聚物87.5％；镁粉1.5％；烷基苯磺酸盐2.0％；氟硅酸钠2.5％；三乙醇胺1.5％；硅酮1.0％；消泡剂1.0％；亚硝酸钠+硫酸钠1.0％；羟基羧酸类2.0％。
实施例3。
由下述重量百分含量原料制成防冻、抗渗、抗盐渍腐蚀III型抗盐渍混凝土外加剂：β基萘磺酸钠甲醛缩聚物85％；硫酸钠5.5％；松香热聚物1.5％；烷基苯磺酸盐1.5％；氟硅酸钠1.5％；硅酮2.0％；消泡剂1.0％；氯化钙1.0％；亚硝酸钠+硫酸钠1.0％。

Claims (4)

1、一种抗盐渍系列混凝土外加剂，其特征在于：所述的外加剂由下述重量百分含量原料制成：β基萘磺酸钠甲醛缩聚物75～92％；硫酸钠4～15％；松香热聚物0.5～3.5％；镁粉1～2％；烷基苯磺酸盐0.5～3.5％；氟硅酸钠1～3.5％；三乙醇胺1～2％；硅酮0.5～3.5％；消泡剂0.9～1.1％；氯化钙0.9～1.1％；亚硝酸钠+硫酸钠0.9～1.1％；羟基羧酸类1.5～2.5％。
2、如权利要求1所述的抗盐渍系列混凝土外加剂，其特征在于：所述的外加剂由下述重量百分含量原料制成抗盐渍、早强的防腐减水型外加剂：β基萘磺酸钠甲醛缩聚物75～85％；硫酸钠11.5～14％；松香热聚物0.5～3.5％；氟硅酸钠1～2％；硅酮1.5～2.5％；消泡剂0.9～1.1％；亚硝酸钠+硫酸钠0.9～1.1％。
3、如权利要求1所述的抗盐渍系列混凝土外加剂，其特征在于：所述的外加剂由下述重量百分含量原料制成缓凝防腐减水型外加剂：β基萘磺酸钠甲醛缩聚物82～92％；镁粉1～2％；烷基苯磺酸盐1.5～2.5％；氟硅酸钠2～3％；三乙醇胺1～2％；硅酮0.5～1.5％；消泡剂0.9～1.1％；亚硝酸钠+硫酸钠0.9～1.1％；羟基羧酸类1.5～2.5％。
4、如权利要求1所述的抗盐渍系列混凝土外加剂，其特征在于：所述的外加剂由下述重量百分含量原料制成防冻、抗渗、抗盐渍腐蚀型外加剂：β基萘磺酸钠甲醛缩聚物80～90％；硫酸钠4～7％；松香热聚物0.5～3％；烷基苯磺酸盐0.5～3％；氟硅酸钠0.5～3％；硅酮1.5～2.5％；消泡剂0.9～1.1％；氯化钙0.9～1.1％；亚硝酸钠+硫酸钠0.9～1.1％。
CNB2005100206503A 2005-03-30 2005-03-30 抗盐渍系列混凝土外加剂 Expired - Fee Related CN1328203C (zh)