CN1687267A - 纳米水性天然真石乳胶漆 - Google Patents

纳米水性天然真石乳胶漆 Download PDF

Info

Publication number
CN1687267A
CN1687267A CN 200510020870 CN200510020870A CN1687267A CN 1687267 A CN1687267 A CN 1687267A CN 200510020870 CN200510020870 CN 200510020870 CN 200510020870 A CN200510020870 A CN 200510020870A CN 1687267 A CN1687267 A CN 1687267A
Authority
CN
China
Prior art keywords
portions
agent
powder
particle diameter
paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510020870
Other languages
English (en)
Inventor
杨世相
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200510020870 priority Critical patent/CN1687267A/zh
Publication of CN1687267A publication Critical patent/CN1687267A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种乳胶漆，尤其是一种纳米水性天然真石乳胶漆，其特征在于其组成成分及重量比为：粒径为10～40纳米的SiO2 4～15，粒径为10～40纳米的TiO2 6～20，粒径为20～50微米的白色和/或彩色天然石粉总量320～380，改性丙烯酸乳液250～550，水100～300，分散剂1～9，润湿剂1～5，成膜助剂2～5.5，防腐剂0.1～0.5，流变性改进剂1～1.5。本发明产品属优质的内外墙真石乳胶漆，使用时便于施工，其漆膜的硬度高、粘结力强、疏水、自洁、恒久不变色、使用寿命长，另外，制作原料中的天然石粉为纯天然物质，不含VOC，材料易于得到，成本低，属于真正的环保型材料。

Description

纳米水性天然真石乳胶漆
技术领域
本发明涉及一种乳胶漆，尤其是一种纳米水性天然真石乳胶漆。
背景技术
现有的乳胶漆通常由四部分组成：成膜物质、溶剂和稀释剂(分散媒)、颜料和填料、各种助剂。在现有产品中，产品的组份中一般是采用立德粉或高岭土等为填料，用化工颜料染色，其产品的性能较差，含有较高的有害物质VOC。中国发明专利ZL99114776.6号公开了一种真石涂料，该涂料以大理石粉或花岗石粉为颜料，兼作填料，以合成高分子树脂为成膜物质，添加各种助剂制成的涂料。其组成成份包括大理石(花岗石)粉、合成高分子树脂(乳液)、增稠剂、六偏磷酸钠、氨水、成膜助剂和水，大理石(花岗石)粉的细度为600～1200目。该产品可用于建筑物的内外墙面等，具有一定的优点。但是，在实际应用过程中发现，由于上述产品未对石粉的粒径进行优选，产品所形成漆膜的光滑度及平整度较差，并不具有“真石”的感觉和特性，特别易于沾染灰尘，耐污性极差，而且涂刷时不便施工，另外，该产品还未对产品组份中的成膜物质——合成高分子树脂(乳液)进行优选，这也影响了产品的整体性能，因此，有待于对上述现有产品作进一步地改进。
发明内容
本发明的目的是对上述现有产品的组成成份及其比例进行优选和改进，提供一种性能更好的纳米水性天然真石乳胶漆。
本发明的纳米水性天然真石乳胶漆的组成成份及重量比为：
粒径为10～40纳米的SiO2             4～15
粒径为10～40纳米的TiO2             6～20
粒径为20～50微米的白色和/或彩色天然石粉    总量320～380
改性丙烯酸乳液    250～550
水                100～300
分散剂                  1～9
润湿剂                  1～5
成膜助剂                2～5.5
防腐剂                  0.1～0.5
流变性改进剂            1～1.5。
在本发明中，上述改性丙烯酸乳液是一种用于配制乳胶漆的市售产品，其产品名称即为改性丙烯酸乳液，如江苏日出化工有限公司生产的TL-615D型改性丙烯酸乳液，河北新光化工有限公司出品的XG-2000型改性丙烯酸乳液等等。
上述分散剂为市售的乳胶漆用分散剂，如上海上大攀登化工科技有限公司生产的SD-Dispersion5468分散剂或SD-Dispersion5080分散剂，圣诺普科(上海)有限公司生产的SN-DISPERSANT 5027型分散剂或SN-DISPERSANT5029型分散剂，北京兴美亚化工有限公司生产的BEVALIOD 270型分散剂，北京富特斯化工有限公司生产的FX-107型分散剂等等。
上述润湿剂为市售的乳胶漆用润湿剂，如圣诺普科(上海)有限公司生产的SN-WET366型润湿剂，北京兴美亚化工有限公司生产的IGEPAL CA-630型润湿剂或IGEPAL CTA-639W型润湿剂等。
上述成膜助剂为市售的乳胶漆用成膜助剂，如圣诺普科(上海)有限公司生产的醇酯-12成膜助剂，北京兴美亚化工有限公司生产的NEXCOAT-795型成膜助剂，大连信源工贸有限公司生产的晶华醇酯-12成膜助剂，上海长风化工厂生产的醇酯-12成膜助剂等。
上述防腐剂为市售的乳胶漆用防腐剂，如圣诺普科(上海)有限公司生产的SN-CIDE135型防腐剂或SN-CIDE215型防腐剂，北京兴美亚化工有限公司生产的罐内防腐剂HF或罐内防腐剂SPX、罐内防腐剂MV等。
上述流变性改进剂为市售的乳胶漆用流变性改进剂。如圣诺普科(上海)有限公司生产的SN-THICKENER 612NC型流变性改进剂或SN-THICKENER 617型流变性改进剂等。
上述乳胶漆组份中的水可以采用去离子水或蒸馏水等洁净水，但尤以去离子水为佳。
在本发明乳胶漆的组份中，粒径为20～50微米的白色和/或彩色天然石粉的总量为320～380重量份，即粒径为20～50微米的白色天然石粉和彩色天然石粉的总用量为320～380重量份。一般情况下，可以同时使用白色天然石粉和彩色天然石粉，但也不排除仅使用白色天然石粉或仅使用彩色天然石粉的情形。在仅使用一种天然石粉(白色或彩色石粉)的情形下，另一种天然石粉的用量即为零。同时，通过增减彩色天然石粉与白色天然石粉的比例并选取彩色天然石粉的颜色，就可以决定最终乳胶漆成品的颜色。
在生产本发明的乳胶漆时，可以先将上述组份中的水、粒度为纳米级的SiO2、分散剂、湿润剂和粒度为纳米级的TiO2依次加入分散罐中，在200～300转/分的转速下分散10～20分钟，再加入粒径为20～50纳米的天然白色石粉和天然彩色石粉，在1000～1200转/分的转速下分散30～40分钟，并适量加入pH调节剂，将pH值调节至9～10。加入的pH调节剂除可以为氨水外，还可以采用美国ANGUS化学公司生产的AMP-95或AMP-96型pH调节剂。本发明推荐采用AMP-95或AMP-96型pH调节剂，因为该种调节剂既能很好地控制乳胶漆的pH值，又没有气味大、pH值易漂移等弊端。在PH值合格并砂磨一至二遍且检查细度合格后，再加入改性丙烯酸乳液、成膜助剂、防腐剂和流变性改进剂，加完上述物料后低速搅拌5～10分钟，即可包装入库。
与前述现有同类产品相比，本发明的乳胶漆中不采用任何化工颜料，最终成品的颜色完全由彩色天然石粉与白色天然石粉的比例和所选彩色天然石粉的颜色决定，同时，本发明的乳胶漆中不采用有机填料，并对作为填料的天然石粉的颗料粒径进行了优选，即选取粒径为20～50微米的天然超微细石粉作为乳胶漆的填料，并辅以粒度为纳米级的SiO2和粒度为纳米级的TiO2，且特别选取改性丙烯酸乳液为成膜物质，从而使产品具有优异的耐侯、耐洗刷、耐污、耐紫外线侵蚀的性能。在本发明中，所选用的纳米级粒度的TiO2可以增加漆膜的遮盖力和疏水性，使漆膜紧密丰满，具有更强的疏水和自洁性能，使污渍不易粘附，一擦即净，让墙体保持长久的清洁；纳米级粒度的SiO2可以显著地增加漆膜的表面硬度、提高漆膜的耐侯性和耐洗刷性。因此，本发明产品属优质的内外墙真石乳胶漆，使用时便于施工，其漆膜的硬度高、粘结力强、疏水、自洁、恒久不变色、使用寿命长，另外，制作原料中的天然石粉为纯天然物质，不含VOC，材料易于得到，成本低，属于真正的环保型材料。
本发明的内容结合以下实施例作更进一步的说明，但本发明的内容不仅限于实施例中所涉及的内容。
具体实施方式
实施例1：本实施例中的纳米水性天然真石乳胶漆的组成成份及用量为：粒径为10～40微米的SiO2 6Kg、粒径为10～40微米的TiO2 7Kg、粒径为20～50纳米的白色天然石粉340Kg、改性丙烯酸乳液320Kg、去离子水300Kg、分散剂4Kg、润湿剂3Kg、成膜助剂3.8Kg、防腐剂0.4Kg、流变性改进剂1.2Kg。在本实施例中，所采用的改性丙烯酸乳液为河北新光化工有限公司出品的XG-2000型改性丙烯酸乳液，分散剂为圣诺普科(上海)有限公司生产的SN-DISPERSANT 5027型分散剂，润湿剂为圣诺普科(上海)有限公司生产的SN-WET366型润湿剂，成膜助剂为圣诺普科(上海)有限公司生产的醇酯-12成膜助剂，防腐剂为圣诺普科(上海)有限公司生产的SN-CIDE135型防腐剂和SN-CIDE215型防腐剂(二者总量为0.4Kg)，流变性改进剂为圣诺普科(上海)有限公司生产的SN-THICKENER 612NC型流变性改进剂。
实施例2：本实施例中的纳米水性天然真石乳胶漆的组成成份及用量为：粒径为10～40纳米的SiO2 8Kg、粒径为10～40纳米的TiO2 10Kg、粒径为20～50微米的白色天然石粉200Kg、粒径为20～50微米的彩色(本例中为黄色)天然石粉150Kg、改性丙烯酸乳液410Kg、去离子水200Kg、分散剂7Kg、润湿剂5Kg、成膜助剂4.2Kg、防腐剂0.5Kg、流变性改进剂1.1Kg。在本实施例中，所采用的改性丙烯酸乳液为江苏日出化工有限公司生产的TL-615D型改性丙烯酸乳液，分散剂为圣诺普科(上海)有限公司生产的SN-DISPERSANT 5027型分散剂，润湿剂为圣诺普科(上海)有限公司生产的SN-WET366型润湿剂，成膜助剂为圣诺普科(上海)有限公司生产的醇酯-12成膜助剂，防腐剂为圣诺普科(上海)有限公司生产的SN-CIDE135型防腐剂和SN-CIDE215型防腐剂(二者总量为0.5Kg)，流变性改进剂为圣诺普科(上海)有限公司生产的SN-THICKENER 612NC型流变性改进剂。

Claims (1)

1、一种纳米水性天然真石乳胶漆，其特征在于其组成成份及重量比为：
粒径为10～40纳米的SiO2              4～15
粒径为10～40纳米的TiO2              6～20
粒径为20～50微米的白色和/或彩色天然石粉    总量320～380
改性丙烯酸乳液       250～550
水                   100～300
分散剂               1～9
润湿剂               1～5
成膜助剂             2～5.5
防腐剂               0.1～0.5
流变性改进剂         1～1.5。
CN 200510020870 2005-05-09 2005-05-09 纳米水性天然真石乳胶漆 Pending CN1687267A (zh)