CN1683590A - Aluminium alloy chromium-free chemical converting liquid and its using method - Google Patents
Aluminium alloy chromium-free chemical converting liquid and its using method Download PDFInfo
- Publication number
- CN1683590A CN1683590A CN 200410026047 CN200410026047A CN1683590A CN 1683590 A CN1683590 A CN 1683590A CN 200410026047 CN200410026047 CN 200410026047 CN 200410026047 A CN200410026047 A CN 200410026047A CN 1683590 A CN1683590 A CN 1683590A
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- chemical conversion
- solution
- concentration
- conversion solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to surface treatment of aluminum alloy, and especially a kind of chromium-free chemical aluminum alloy converting solution capable of endowing aluminum alloy surface with excellent corrosion resistance and its usage. The chromium-free chemical aluminum alloy converting solution consists of silicate, titanium salt, peroxide, fluoride, and water solution of sulfuric acid. The solution is used in 50-99 deg.c and pH 4-9 and has aluminum alloy contacting time of 2-20 min. The solution contains no hexavalent chromium and potassium ferricyanate, and has less environmental pollution, low cost, easy filming and high corrosion resistance.
Description
(1) technical field
The present invention relates to aluminium alloy surface treatment method, is a kind of metallic surface conversion fluid that does not contain chromium of giving the superior erosion resistance of aluminum alloy surface specifically, and uses the process metal surfaces method of this chemical conversion solution.
(2) background technology
Chromium plating is a kind of traditional complete processing, nearly century chromium plating is widely used in functional coating and decorative coating field with the anticorrosion and abrasion resistance properties of its brilliance, as space flight and aviation, electronics, automobile, pharmacy, printing, machinery, chemical industry, food-processing and other production, chromium plating reaches 8,000,000,000 dollars in the annual output value of the U.S..
In the past, the surface treatment method of aluminium and alloy thereof was to handle with chromate conversion liquid.The chemical conversion processing of the aluminium that uses and the chromic compound of alloy thereof has many, as A Luodingfa by the invention of american chemical pigment company, adopt the formed conversion film of chromate treating, has superior solidity to corrosion, but the hexavalent chromium polluted environment of the carcinogens that in this conversion fluid, contains deleterious potassium ferricyanate, huge poison, its production environment requires high, and wastewater treatment is numerous and diverse, expensive.In addition, owing to contain sexavalent chrome in the protective membrane that forms, so consider from the angle of environment, safety, countries in the world are all being limited cancellation and are being used chromate treating technology.
At present, in order to cancel the hexavalent chromium chemistry conversion treatment process, people have proposed various chromium-free treatment methods.As at United States Patent (USP) 6,638, in 369 " the Chrome-free conversion films " announced, use and contain sodium titanate or potassium titanate, the solution of potassium ferricyanate and fluorochemical and nitric acid, the pH of solution at strong acid to the slightly acidic scope.
For United States Patent (USP) 6,638, in 369 " the Chrome-free conversion films " announced, its treatment solution has not chromyl advantage, and has added fluorochemical with existing sexavalent chrome conversion process same range as amount at treatment solution, but because sodium titanate or the solubleness of potassium titanate in water used in this technology are extremely low, so it is low effectively to dissolve titanium ion concentration, can not guarantee the quality of film in the continuous flow procedure, can't realize industrial continuous production requirement, and contain virulent potassium ferricyanate.
For aldural, owing to dissolve many metal ions in the conversion reaction process, as Cu
2+, Zn
2+Deng, the treatment solution of this patent does not contain the composition of removing these ion interference, therefore, is difficult to obtain the uniform protective membrane of color and luster for this method of this type of aluminium alloy.
(3) summary of the invention
The object of the present invention is to provide and a kind ofly do not contain six chromium valencys and potassium ferricyanate, dissolving titanium ion concentration height, can remove metal ion and disturb and be easy to film forming aluminium alloy non-chromium chemical conversion solution.
Another object of the present invention is to provide a kind of use Chrome-free chemical conversion solution to handle the aluminum alloy surface method, it is superior to make its surface be easy to form corrosion resisting property, and color and luster evenly waits the conversion film of advantageous property.
For achieving the above object, the technical solution used in the present invention is:
A kind of aluminium alloy non-chromium chemical conversion solution, its special character is: the prescription of above-mentioned chemical conversion solution is to contain in every liter of solution:
The concentration of silicate silicate is at 0.1mg/L～2000mg/L
The titanium salt titanium ion concentration is at 0.1mg/L～2000mg/L
The concentration of superoxide hydrogen peroxide is at 0.1mg/L～10000mg/L
The concentration of fluorochemical fluorion is at 1000mg/L～4000mg/L
The pH of irreducibility acid-conditioning solution is in 4～9 scopes
Preferred version in every liter of solution of the prescription of above-mentioned chemical conversion solution is:
The concentration of silicate silicate is at 0.5mg/L～500mg/L
The titanium salt titanium ion concentration is at 0.5mg/L～500mg/L
The concentration of superoxide hydrogen peroxide is at 0.5mg/L～5000mg/L
The fluorochemical fluorinion concentration is at 1500mg/L～3000mg/L
The pH of irreducibility acid-conditioning solution is in 5～7 scopes
Above-mentioned silicate adopts at least a in silicic acid, water glass, the potassium silicate.
Above-mentioned titanium salt adopts at least a in titanium chloride, titanium sulfate, titanyl sulfate, titanyl nitrate, sodium titanate, potassium titanate, the titanium dioxide.
Above-mentioned superoxide adopts at least a in sodium peroxide, Potassium peroxide, the hydrogen peroxide.
Above-mentioned fluorochemical adopts at least a in Neutral ammonium fluoride, ammonium acid fluoride, Sodium Fluoride, Potassium monofluoride, the sodium hydrogen fluoride.
Above-mentioned irreducibility acid is one or both in sulfuric acid or the nitric acid.
A kind of using method of aluminium alloy non-chromium chemical conversion solution, its step is as follows:
(1), earlier the aluminum alloy surface grease is removed;
(2), again with aluminum alloy surface alkali cleaning, deoxidation activation;
(3), use the aluminium alloy non-chromium chemical conversion solution, carry out conversion processing, this molten night, temperature was controlled at 50～99 ℃ in use, pH is 4～9, with duration of contact of aluminium alloy be 2～20 minutes;
(4), again after Al alloy parts being washed with water, seasoning gets final product.
Above-mentioned step (2) comprised for two steps:
(1), alkali cleaning, adopt 1～3% sodium hydroxide solution, after handling 1～5 minute under 40～60 ℃ of temperature by rinsed with deionized water;
(2), deoxidation activation, adopt 1～10% nitric acid at room temperature to handle after 1～10 minute by rinsed with deionized water.
The present invention is with respect to prior art, and its advantage is as follows:
Conversion fluid of the present invention does not contain potassium ferricyanate owing to do not contain six chromium valencys (chromic salt), and not only the pollution to environment alleviates greatly, and cost significantly reduces.
Conversion fluid of the present invention as titanium sulfate, titanyl sulfate, titanyl nitrate etc., so the titanium ion concentration in the conversion fluid greatly increases, can satisfy the requirement that realizes industrial continuous production owing to contain more diffluent titanium salt.
The superoxide that conversion fluid of the present invention contains can change into the titanic ion-oxygen in the solution in weak acid and neutral solution and to make sexivalent titanium oxide ion (Ti
2O
5 2+).This high price titanium oxide ion can be generated quaternary titanium dioxide conversion film by aluminium reducing when aluminum alloy surface generation redox reaction.
Conversion fluid of the present invention is owing to contain silicate, and in certain concentration range, silicate ion can not only be removed the interference of metal ion, and is easy to film forming.
The protective membrane that the present invention generated has been owing to utilized both advantages of silicate and titanium salt, thereby is easy to form conversion film, and the conversion film of generation not only corrosion resisting property is superior, and because color and luster is even, has good surface quality.
(4) specific embodiment
Aluminium alloy non-chromium chemical conversion solution of the present invention is made by containing silicate, titanium salt, superoxide, fluorochemical, irreducibility aqueous acid.
1, silicate
Adopt silicic acid or potassium silicate, concentration is at 0.1mg/L to 2000mg/L.Be preferably 0.5mg/L to 500mg/L.Silicate concentration is too high, can make the aluminum alloy surface conversion reaction be difficult to take place; And silicate concentration is too low, the silicon-dioxide (SiO that produces under reaction conditions
2) concentration is too low, it is electrical to be difficult to change aluminum alloy surface.Under reaction conditions, aluminium surface positively charged, and the electronegative property of silicon dioxide granule, because the electrostatic attraction effect, coated with silica makes the electronegative property of aluminum alloy surface in aluminum alloy surface, makes the titanium oxide ion (Ti of positively charged
2O
5 2+) easily at aluminum alloy surface generation film formation reaction.
2, titanium salt
As titanium salt, for example can enumerate titanium oxide (TiCl
4), titanium sulfate (Ti (SO
4)
2), titanyl sulfate (TiOSO
4), titanyl nitrate (TiO (NO
3)
2), sodium titanate (Na
2TiO
3), potassium titanate (K
2TiO
3), titanium dioxide (TiO
2) wait at least a.The concentration of pressing metal titanium conversion titanium ion is preferably in 0.5mg/L～500mg/L at 0.1mg/L～2000mg/L.When the concentration of titanium salt titanium ion in treatment solution is too low, almost can not be formed with the conversion film of imitating antiseptic property.On the other hand, in treatment solution, even add titanium, effect does not increase, and therefore, calculates titanium concentration by metal titanium concentration and is advisable with interior at 2000mg/L.
3, superoxide
As superoxide, for example can enumerate at least a in sodium peroxide, Potassium peroxide, the hydrogen peroxide.Added concentration of hydrogen peroxide is at 0.1mg/L～10000mg/L in the treatment solution, preferably 0.5mg/L～5000mg/L.In the solution concentration of hydrogen peroxide can not be too low can not be too high.Too low can not guarantee certain oxidisability that solution has and make titanium with the high price--sexivalent titanium oxide ion (Ti
2O
5 2+) exist, this ionic concn is too low, is not enough to form effective protective membrane; The concentration of hydrogen peroxide is too high to be unfavorable for making film formation reaction to take place on passivation aluminum metal surface.
4, fluorochemical
As fluorochemical, for example can enumerate Neutral ammonium fluoride (NH
4F), ammonium acid fluoride (NH
4HF
2), Sodium Fluoride (NaF), Potassium monofluoride (KF), sodium hydrogen fluoride (NaHF
2) etc.In the treatment solution of this way of example, the fluorine of adding is wherein a kind of of above-mentioned fluorochemical, and the amount of adding is preferably 1500mg/L to 3000mg/L for to change 1000mg/L to 4000mg/L by fluorine.Fluorine concentration is lower than 1000mg/L or is higher than 3000mg/L, and the aluminum metal surface conversion coating all is difficult to form.
5, irreducibility acid
The pH value of sulfuric acid or nitric acid regulator solution is adopted in irreducibility acid, and the pH that makes solution is in 4～9 scopes.
Below, will use the step of the process metal surfaces method of this chemical conversion solution to be listed below:
(1), earlier the aluminum alloy surface grease is removed;
(2), again with aluminum alloy surface alkali cleaning, deoxidation activation; Alkali cleaning is for adopting 1～3% sodium hydroxide solution, after handling 1～5 minute under 40～60 ℃ of temperature by rinsed with deionized water; The deoxidation activation is at room temperature handled after 1～10 minute by rinsed with deionized water for adopting 1～10% nitric acid;
(3), use the aluminium alloy non-chromium chemical conversion solution, carry out conversion processing, this molten night, temperature was controlled at 50～99 ℃ in use, pH is 4～9, with duration of contact of aluminium alloy be 2～20 minutes;
(4), again after Al alloy parts being washed with water, seasoning gets final product.
Specific embodiment 1: aluminium alloy LC4CS surface is cleaned with gasoline, immerse 3～5% the sodium hydroxide solution of temperature under 40～60 ℃ then and carried out skimming treatment in 3 minutes, after the washing this alloy at room temperature immersed in 1～10% the salpeter solution about 1 to 10 minute, and after rinsed with deionized water, immersed chemical conversion solution again and handle.The chemical conversion solution composition is water glass 0.10g/L, titanyl sulfate 3g/L, sodium titanate 5g/L, hydrogen peroxide 1.0g/L, Sodium Fluoride 5g/L.It is 4.5～8.5 that sulfuric acid is regulated conversion fluid pH, and temperature is 80～90 ℃, reacts and after 10 minutes alloy is taken out the after washing drying.Institute's film forming has been passed through 336 hours neutral salt spray test (ASTM B117) test.
Specific embodiment 2: aluminium alloy LD2CS immerses this alloy and contains the 0.05g/L water glass after the pre-treatment identical with embodiment 1, the titanyl sulfate of 2g/L, and hydrogen peroxidase 10 .5g/L, in the conversion fluid of Sodium Fluoride 4.5g/L, the pH value of sulfuric acid regulation solution.Reaction conditions is with embodiment 1.The rete that has formed one deck white through the aluminium alloy LD2CS surface of above-mentioned processing is tested still non-corrosive through 336 hours neutral salt spray (ASTM B117).
Claims (9)
1, a kind of aluminium alloy non-chromium chemical conversion solution is characterized in that: the prescription of above-mentioned chemical conversion solution is to contain in every liter of solution:
The concentration of silicate silicate is at 0.1mg/L～2000mg/L
The titanium salt titanium ion concentration is at 0.1mg/L～2000mg/L
The concentration of superoxide hydrogen peroxide is at 0.1mg/L～10000mg/L
The concentration of fluorochemical fluorion is at 1000mg/L～4000mg/L
The pH of irreducibility acid-conditioning solution is in 4～9 scopes
2, aluminium alloy non-chromium chemical conversion solution according to claim 1 is characterized in that: contain in every liter of solution of the prescription of above-mentioned chemical conversion solution:
The concentration of silicate silicate is at 0.5mg/L～500mg/L
The titanium salt titanium ion concentration is at 0.5mg/L～500mg/L
The concentration of superoxide hydrogen peroxide is at 0.5mg/L～5000mg/L
The fluorochemical fluorinion concentration is at 1500mg/L～3000mg/L
The pH of irreducibility acid-conditioning solution is in 5～7 scopes
3, aluminium alloy non-chromium chemical conversion solution according to claim 1 and 2 is characterized in that: described silicate adopts at least a in silicic acid, water glass, the potassium silicate.
4, aluminium alloy non-chromium chemical conversion solution according to claim 1 and 2 is characterized in that: described titanium salt adopts at least a in titanium chloride, titanium sulfate, titanyl sulfate, titanyl nitrate, sodium titanate, potassium titanate, the titanium dioxide.
5, aluminium alloy non-chromium chemical conversion solution according to claim 1 and 2 is characterized in that: described superoxide adopts at least a in sodium peroxide, Potassium peroxide, the hydrogen peroxide.
6, aluminium alloy non-chromium chemical conversion solution according to claim 1 and 2 is characterized in that: described fluorochemical adopts at least a in Neutral ammonium fluoride, ammonium acid fluoride, Sodium Fluoride, Potassium monofluoride, the sodium hydrogen fluoride.
7, aluminium alloy non-chromium chemical conversion solution according to claim 1 and 2 is characterized in that: described irreducibility acid is one or both in sulfuric acid or the nitric acid.
8, a kind of using method of aluminium alloy non-chromium chemical conversion solution, its step is as follows:
(1), earlier the aluminum alloy surface grease is removed;
(2), again with aluminum alloy surface alkali cleaning, deoxidation activation;
(3), use the aluminium alloy non-chromium chemical conversion solution, carry out conversion processing, this molten night, temperature was controlled at 50～99 ℃ in use, pH is 4～9, with duration of contact of aluminium alloy be 2～20 minutes;
(4), again after Al alloy parts being washed with water, seasoning gets final product.
9, the using method of aluminium alloy non-chromium chemical conversion solution according to claim 7 is characterized in that:
Described step (2) comprised for two steps:
(1), alkali cleaning, adopt 1～3% sodium hydroxide solution, after handling 1～5 minute under 40～60 ℃ of temperature by rinsed with deionized water;
(2), deoxidation activation, adopt 1～10% nitric acid at room temperature to handle after 1～10 minute by rinsed with deionized water.