CN1673168A - 废石膏改性粉煤灰三渣混合料 - Google Patents
废石膏改性粉煤灰三渣混合料 Download PDFInfo
- Publication number
- CN1673168A CN1673168A CNA2004100172004A CN200410017200A CN1673168A CN 1673168 A CN1673168 A CN 1673168A CN A2004100172004 A CNA2004100172004 A CN A2004100172004A CN 200410017200 A CN200410017200 A CN 200410017200A CN 1673168 A CN1673168 A CN 1673168A
- Authority
- CN
- China
- Prior art keywords
- waste gypsum
- mixed material
- flyash
- content
- slag mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种废石膏改性粉煤灰三渣混合料,由下列组成物及重量百分比组成:粉煤灰5%-30%,消石灰5%-15%,碎石60%-84%,早强剂0.5%-1%,废石膏0.5%-7.5%,再加上述重量30%的水混合后使用。早强剂由高钙灰与废碱液按2∶1混合而成。消石灰中活性氧化钙及氧化镁的含量至少30%。粉煤灰中的二氧化硅和三氧化二铝的总含量至少70%。废石膏中的三氧化硫的含量至少36%。本发明的优点是能使三渣路基混合料在施工七天后的强度满足路面基层的要求,铺设后无膨胀,其抗冻性、耐干湿循环性及抗硫酸盐侵蚀性好于普通的三渣路基混合料。
Description
技术领域
本发明涉及一种废石膏改性粉煤灰三渣混合料。
背景技术
目前城市建设规模越来越大,其中道路的建设是一个城市发展的先锋,由于构筑道路需要大量的路面基础材料,而另一方面燃煤的锅炉所产出的粉煤灰又是一个需要处理的废弃物,早在上世纪六十年代就有采用粉煤灰石灰作为路面的基础材料,具有成本底、来源广,有良好的水稳定性及一定的抗冻性,适合于城市的道路建设,但是它的早期强度较低,施工后的养护周期长,造成基层铺筑后无法进行最后的沥青路面摊铺,无法开放交通,为了解决上述问题,现有的方法是掺加化学添加剂或水泥,然而带来了成本上升无法推广应用。
发明内容
本发明的目的是解决现有技术中使用采用粉煤灰石灰作为路面的基础材料所存在的问题,提供一种在施工七天后的强度满足路面基层的要求,铺设后无膨胀,其抗冻性、耐干湿循环性及抗硫酸盐侵蚀性好的废石膏改性粉煤灰三渣混合料。本发明设计废石膏改性粉煤灰三渣混合料,由下列组成物及重量百分比组成:粉煤灰5%-30%,消石灰5%-15%,碎石60%-84%,早强剂0.5%-1%,废石膏0.5%-7.5%,再加上述重量30%的水混合后使用。早强剂由高钙灰与废碱液按2∶1混合而成。消石灰中活性氧化钙及氧化镁的含量至少30%。粉煤灰中的二氧化硅和三氧化二铝的总含量至少70%。废石膏中的三氧化硫的含量至少36%。本发明的优点是能使三渣路基混合料在施工七天后的强度满足路面基层的要求,铺设后无膨胀,其抗冻性、耐干湿循环性及抗硫酸盐侵蚀性好于普通的三渣路基混合料。
下面结合实施例对本发明作详细说明,
具体实施方式
实施例1:取碎石65吨,粉煤灰18吨,废石膏6吨,消石灰10吨,碎石的粒径40-70MM,将上述三种干料搅拌,再加上1吨的早强剂(高钙粉煤灰与氢氧化钙废溶液按2∶1混合而成)和水30吨搅拌混合,含水在27%待用。
实施例2:取碎石73吨,粉煤灰14吨,消石灰8吨,废石膏4吨,碎石的粒径5-30MM,将上述三种干料搅拌,再加上1吨的早强剂(高钙粉煤灰与氢氧化钠废溶液按2∶1混合而成)和水30吨搅拌混合,含水在30%待用。
上述三渣路基材料搅拌后应控制含水率不超过标准的5个百分点,在暑热天控制含水率不超过标准的8个百分点,以保证在施工碾压时接近最佳含水率,在工地上应尽可能摊铺均匀,一般为15-25CM厚,采用轮胎压路机或振动压路机进行压实。在放置七天后能满足道路铺设沥青路面的要求,可以开放路面交通。
Claims (5)
1、废石膏改性粉煤灰三渣混合料,由下列组成物及重量百分比组成:
粉煤灰 5%——30%,
消石灰 5%——15%,
碎石 60%——84%,
早强剂 0.5%——1%,
废石膏 0.5%——7.5%,
再加上述重量30%的水混合后使用。
2、按权利要求1所述的废石膏改性粉煤灰三渣混合料,其特征在于:早强剂由高钙灰与废碱液按2∶1组成。
3、按权利要求1所述的废石膏改性粉煤灰三渣混合料,其特征在于:消石灰中活性氧化钙及氧化镁的含量至少30%。
4、按权利要求1所述的废石膏改性粉煤灰三渣混合料,其特征在于:粉煤灰中的二氧化硅和三氧化二铝的总含量至少70%。
5、按权利要求1所述的废石膏改性粉煤灰三渣混合料,其特征在于:废石膏中的三氧化硫的含量至少36%。