CN1666833A - Method for preparing copper-plated silicon carbide particle reinforced magnesium based compound material - Google Patents
Method for preparing copper-plated silicon carbide particle reinforced magnesium based compound material Download PDFInfo
- Publication number
- CN1666833A CN1666833A CN 200510024931 CN200510024931A CN1666833A CN 1666833 A CN1666833 A CN 1666833A CN 200510024931 CN200510024931 CN 200510024931 CN 200510024931 A CN200510024931 A CN 200510024931A CN 1666833 A CN1666833 A CN 1666833A
- Authority
- CN
- China
- Prior art keywords
- carbide particle
- copper
- silicon carbide
- magnesium
- based compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates the preparation method of the coppercasting silicon carbide particles reinforcing magnesium-base multiple materials. The concrete processes are as follows: select the silicon carbide particles and deposit a thin coppercasting coat on its surface through chemical coating technique; the volume content of the reinforcing particles is 5-30% and calculate the weights of the coat of silicon carbide particles and the magnesium powder needed; mix the coat of silicon carbide particles, the magnesium powder and the agate balls in the mixing machine for 2-48 hours; pour the even mixed powder into the mould and press to blocks in house temperature; agglomerate the blocks in the vacuum furnace; heat-extrude the agglomerated blocks and the area compressing ratio is 10-100:1. The invention provides a new method for the magnesium-base multiple materials integrating structure and function together.
Description
Technical field
That the present invention relates to is a kind of preparation method who is used for technical field of composite materials, specifically is a kind of preparation method of copper-plated silicon carbide particle reinforced magnesium based compound material.
Background technology
The damping capacity of material has play a part important in the vibration of control structure and noise, thereby has also prolonged cyclic loading or impacted the service life of material down.Magnesium has the highest damping capacity in all commercial metals structural materials, uses more widely yet weak mechanical performance has limited it.Therefore, improve the mechanical strength of magnesium and keep its intrinsic high damping properties to become the key problem of numerous researchs.
Through the literature search of prior art is found, (1997, people such as C.Mayencourt publish thesis on 163:357) " high damping composite material: Mg at " Phys.Status.Solidi.A "
2The research of Si/Mg ", this article proposes to prepare fibre reinforced composites Mg by directional solidification processes
2Si/Mg has the suitable hot strength of industrial cast magnesium alloy AZ63 and damping capacity has improved 10-100 doubly, and there is anisotropy in the performance of the fibrous composite that this technology obtains, and the directional solidification processes complexity, is not suitable for suitability for industrialized production.
Summary of the invention
The objective of the invention is to overcome deficiency of the prior art and defective, a kind of preparation method of copper-plated silicon carbide particle reinforced magnesium based compound material is provided, make the composite acquisition intensity of preparation and the matched well of damping capacity.This composite is to be wild phase with the carborundum of electroless copper (Cu) (SiC) particle, is the matrix phase with pure magnesium or magnesium alloy, by obtaining special boundary layer in the silicon-carbide particle Electroless copper.
The present invention is achieved by the following technical solutions, and method step is as follows:
(1) select electroless copper silicon-carbide particle and the pure magnesium powder or the compound preparation magnesium base composite material of magnesium alloy powder of different size for use, it is mixed to satisfy matrix and be the long-pending percentage 70%-95% of pure magnesium powder or magnesium alloy-powder and the percent by volume of the silicon-carbide particle 5%-30% that contains chemical plating copper layer.
(2) the described chemical plating copper layer of step (1) is by the layer of copper coating of electroless copper at the silicon-carbide particle surface deposition, the percentage by weight of copper accounts for and contains 10%～50% of chemical plating copper layer silicon-carbide particle gross weight, and the percentage by weight of silicon-carbide particle is 50%～90%.
(3) will contain chemical plating copper layer silicon-carbide particle, magnesium powder and agate ball is that 3: 1 ratio joins and mixes 2～48 hours in the batch mixer in ball material weight ratio, and wherein, the batch mixer rotating speed is 30～60r/min.
(4) powder that mixes is put into mould, briquet at room temperature, the density of pressing block is about 70%～90%.
(5) block with compacting carries out sintering in vacuum drying oven, and sintering temperature is 400 ℃～550 ℃, sintering time 1～4 hour, and vacuum is 1 * 10
-3More than the Pa.
(6) block behind the sintering is carried out hot extrusion again, extrusion temperature is 350 ℃, and area compression ratio is 10-100: 1, obtain copper-plated silicon carbide particle reinforced magnesium based compound material.
Magnesium has high intrinsic damp performance, and the interfacial effect of composite can guarantee that composite of the present invention has good damping performance in addition.The chemical plating copper layer of silicon carbide can effectively improve wetting between carborundum and the magnesium matrix, acceleration of sintering, thus improve final mechanical property, reach the structure and the function integration of high-intensity high-damping.
The raising of interface modification and correlated performance is depended in the development of high-performance composite materials system to a great extent, and the selection of boundary layer or design have played a key for optimizing the composite final properties.Regrettably, former research is not almost paid close attention to the existence of boundary layer (as the particle surface coating) to composite integral damping Effect on Performance.Because the interface of magnesium base composite material is remarkable to the influence of its mechanical property and damping capacity, adopt silicon-carbide particle copper coating method can obtain having the magnesium base composite material of particular interface layer, make it have the comprehensive of good mechanical performance and damping capacity.The preparation technology of copper-plated silicon carbide particle reinforced magnesium based compound material of the present invention has guaranteed that not only composite has high hot strength and damping capacity, and the test data favorable reproducibility, and composite has isotropic feature.
The invention has the beneficial effects as follows: utilize conventional PM technique and be aided with hot-extrusion, choose suitable coating compounds thickness, grain volume fraction, sintering temperature, sintering time, extrusion temperature and extrusion ratio and prepared wild phase even particle distribution, interface in conjunction with good, and have the magnesium base composite material of excellent mechanical performances and damping capacity concurrently, for the magnesium base composite material for preparing structure-function integration opens up a new way, further expanded its application.Be that the tensile strength of 10% copper facing SiC/Mg composite is about 208MPa with volume content for example, it is about 100% to improve the intensity of magnesium, and its room temperature damping capacity approaches 0.008 simultaneously, reaches higher damping level.
The specific embodiment
Embodiment 1
The magnesium base composite material that the copper-plated silicon carbide particle of present embodiment strengthens, the percentage by volume of SiC particle is 5%.Adopting the SiC particle of pure magnesium powder of 40 μ m and 14 μ m is the starting powder material, is 30% the chemical plating copper layer that contains in SiC particle surface chemical plating weight ratio.Then the magnesium powder of aequum and the SiC particle of plating Cu are mixed 2 hour with ratio of grinding media to material in batch mixer at 3: 1, the powder compaction that mixes is become cylinder, with being placed in the vacuum drying oven, be squeezed into bar with area extrusion ratio 10: 1 in 350 ℃ at last 400 ℃ of following sintering 1 hour.The tensile strength of this coating SiC/Mg composite that makes is about 150MPa, and it is about 50% to exceed the tensile strength of magnesium, and the room temperature damping capacity reaches 0.01 high damping.
Embodiment 2
The magnesium base composite material that the copper-plated silicon carbide particle of present embodiment strengthens, adopting the SiC particle of pure magnesium of 40 μ m and 14 μ m is the starting powder material, the percentage by volume of SiC particle is 10%.It in SiC particle surface chemical plating weight ratio 30% the chemical plating copper layer that contains.SiC particle with magnesium powder and plating Cu mixes 24 hour with ratio of grinding media to material in batch mixer at 3: 1 then, the powder compaction that mixes is become cylinder, with being placed in the vacuum drying oven, be squeezed into bar with area extrusion ratio 10: 1 in 350 ℃ at last 400 ℃ of following sintering 4 hours.This tensile strength that contains chemical plating copper layer SiC/Mg composite is about 208MPa, improves the intensity about 100% of magnesium.The room temperature damping capacity approaches 0.008.
Embodiment 3
The magnesium base composite material that the copper-plated silicon carbide particle of present embodiment strengthens, adopting the SiC particle of 40 μ m magnesium aluminum-alloy powders and 14 μ m is the starting powder material, the percentage by volume of SiC particle is 30%.It in SiC particle surface chemical plating weight ratio 30% the chemical plating copper layer that contains.Then the magnesium powder of aequum and the SiC particle of plating Cu are mixed 48 hour with ratio of grinding media to material in batch mixer at 3: 1, the powder compaction that mixes is become cylinder, with being placed in the vacuum drying oven, be squeezed into bar with area extrusion ratio 10: 1 in 350 ℃ at last 550 ℃ of following sintering 4 hours.The tensile strength of this coating SiC/Mg composite is about 265MPa, has improved the intensity about 160% of magnesium.The room temperature damping approaches 0.005, and the high temperature damping capacity has surpassed magnesium.Therefore this coating SiC/Mg composite can obtain good mechanical and damping capacity coupling.
Claims (7)
1, a kind of preparation method of copper-plated silicon carbide particle reinforced magnesium based compound material is characterized in that, concrete steps are as follows:
(1) select electroless copper silicon-carbide particle and the pure magnesium powder or the compound preparation magnesium base composite material of magnesium alloy powder of different size for use, it is mixed to satisfy matrix and be the long-pending percentage 70%-95% of pure magnesium powder or magnesium alloy-powder and the percent by volume of the silicon-carbide particle 5%-30% that contains chemical plating copper layer;
(2) the described chemical plating copper layer of step (1) is by the layer of copper coating of electroless copper at the silicon-carbide particle surface deposition, the percentage by weight of copper accounts for and contains 10%～50% of chemical plating copper layer silicon-carbide particle gross weight, and the percentage by weight of silicon-carbide particle is 50%～90%;
(3) be that 3: 1 ratio joins and mixes 2～48 hours in the batch mixer with electroless copper silicon-carbide particle, magnesium powder and agate ball in ball material weight ratio, wherein, the batch mixer rotating speed is 30～60r/min;
(4) powder that mixes is put into mould, briquet at room temperature, the density of pressing block is about 70%～90%;
(5) block with compacting carries out sintering in vacuum drying oven, and sintering temperature is 400 ℃～550 ℃, sintering time 1～4 hour, and vacuum is 1 * 10
-3More than the Pa;
(6) block behind the sintering is carried out hot extrusion again, extrusion temperature is 350 ℃, and area compression ratio is 10-100: 1, obtain copper-plated silicon carbide particle reinforced magnesium based compound material.
2, the preparation method of copper-plated silicon carbide particle reinforced magnesium based compound material according to claim 1 is characterized in that, described batch mixer, and contain chemical plating copper layer silicon-carbide particle, magnesium powder and agate ball in the batch mixer are 3: 1 ratio in ball material weight ratio.
According to the preparation method of claim 1 or 2 described copper-plated silicon carbide particle reinforced magnesium based compound materials, it is characterized in that 3, described batch mixer, rotating speed are 30～60r/min.
4, the preparation method of copper-plated silicon carbide particle reinforced magnesium based compound material according to claim 1 is characterized in that, the density of described pressing block is 70～90%.
5, the preparation method of copper-plated silicon carbide particle reinforced magnesium based compound material according to claim 1 is characterized in that, described sintering, and sintering temperature is 400～550 ℃, sintering time 1～4 hour.
6, according to the preparation method of claim 1 or 5 described copper-plated silicon carbide particle reinforced magnesium based compound materials, it is characterized in that, described sintering, vacuum is 1 * 10
-3More than the Pa.
7, according to the preparation method of claim 1 or 6 described copper-plated silicon carbide particle reinforced magnesium based compound materials, it is characterized in that, described hot extrusion, extrusion temperature is 350 ℃, area compression ratio is 10-100: 1.