CN1657243A - Thin shell structure reinforced type artificial board - Google Patents
Thin shell structure reinforced type artificial board Download PDFInfo
- Publication number
- CN1657243A CN1657243A CN 200510038522 CN200510038522A CN1657243A CN 1657243 A CN1657243 A CN 1657243A CN 200510038522 CN200510038522 CN 200510038522 CN 200510038522 A CN200510038522 A CN 200510038522A CN 1657243 A CN1657243 A CN 1657243A
- Authority
- CN
- China
- Prior art keywords
- veneer
- bamboo
- wood
- shell structure
- bamboo curtain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A thin-shell structure reinforced artificial board is composed of two composite surface layers and a sandwich layer. Its preparing process includes such steps as applying isocyanate adhesive to bamboo curtain, immersing a single wood board in phenolic resin, combining them together, hot pressing to obtain said composite surface layer, preparing sandwich layer from the quickly growing wood (poplar wood), applying adhesive, combining it with two surface layers, and hot pressing.
Description
One, technical field
The invention belongs to the glued board manufacturing technology field in the timber industry.
Two, background technology
Along with continuing of building of China and world fast-growing, high-yield woods carried out, quick growth poplar wood (as eastern cottonwood etc.) becomes a kind of relative rich in natural resources gradually and is adopted in a large number by the glued board manufacturing industry.Because the wood property characteristics of quick growth poplar wood, with the glued board of quick growth poplar wood manufacturing, its physical and mechanical property is relatively low purely.
Bamboo is the peculiar resource in China and Southeast Asia, and not only accumulation is big, physical and mechanical property is apparently higher than timber, and has fast, the normal operation of growth and advantage such as can upgrade naturally.Through research for many years, the application and development of China backroom boys and relevant enterprise, bamboo wood also is used in the wood-based plate manufacturing industry in a large number.
The poplar of having developed at present and the composite product of artificial bamboo board mainly contain:
03152841.4 1 kinds of container bottom boards of CN and manufacture method thereof
03112794.0 1 kinds of bamboo woods of CN strengthen laminated veneer lumber and manufacture method thereof
CN 92107278.3 bamboo weaving lagers stacked material making methods
CN 87100368.6 bamboo plywood manufacture methods
CN 91108203.4 improved technology for making ply-bamboo
CN 02258059.X poplar base composite plate
CN 98227629.X improved laminated bamboo-wood composite lumber or the like.
Because the surf green thin bamboo strip of bamboo and the chemical composition of the tabasheer thin bamboo strip have very big difference, therefore, the glue performance of the surf green thin bamboo strip and the tabasheer thin bamboo strip differs greatly, and general adhesive is generally very low for the bonding strength of the surf green thin bamboo strip.In the wood-based plate manufacturing industry as adhesive, the bonding strength of the surf green thin bamboo strip often can't satisfy basic performance requirement for main use Lauxite or phenolic resins.Therefore, bamboo wood in order to guarantee the bonding strength of finished product, generally all will be removed the surf green thin bamboo strip in the raw material preparatory stage in Wood-based Panel Production.This has just influenced the processing and utilization rate of bamboo wood greatly.
On the other hand, though the too late tabasheer thin bamboo strip of the glue performance of the surf green thin bamboo strip, its physical and mechanical property is much higher than the tabasheer thin bamboo strip again.Through experimental determination, its elastic modelling quantity (MOE) can reach 15000～20000MPa, and MOR (MOR) can reach 180～200MPa, is about the twice of tabasheer.If can adopt high performance isocyanates, and overcome the high problem of cost as adhesive, the surf green thin bamboo strip utilize prospect very desirable.
Isocyanate adhesive is as toluene di-isocyanate(TDI) (being called for short TDI); 4,4 '-methyl diphenylene diisocyanate (being called for short MDI); 1,6-hexamethylene diisocyanate (be called for short HDI) and triphenylmethane triisocyanate etc., directly use synthesis of polyurethane raw material---polyisocyanates uses as adhesive.Because characteristics such as its molecular weight is little, easy infiltration are suitable for gluing together the processing of farm products residue, especially as materials such as bark, bagasse, cocoanut fiber, straw, peanut shell, rice husks.Experiment showed, isocyanate adhesive is used to glue together the surf green thin bamboo strip that its glue performance is also very desirable.
But isocyanate adhesive is big except toxicity, the operation requirement of shelter higher, its price also wants high more than adhesive such as phenolic resins, Lauxites.Adopt common laminated structure and manufacture method, because consumption glue amount is bigger, the manufacturing cost of glued board is high, has become to hinder the biggest problem that it is promoted the use of.
Three, summary of the invention
The objective of the invention is to explore a kind of high-intensity wood, bamboo composite plywood manufacturing technology of effectively utilizing surf green thin bamboo strip resource, and seek to reduce the approach of manufacturing cost.
Technical solution of the present invention is: adopt secondary hot pressing manufactured thin shell structure reinforced type artificial board, the surf green thin bamboo strip is woven into bamboo curtain, timber is processed into behind the veneer dryly, it is characterized in that:
A. bamboo curtain adopts the isocyanate adhesive applying glue, and veneer impregnated phenolic resin adhesive is made high density veneer, bamboo curtain composite sheet earlier after assembly, hot pressing;
B. be surface material with high density veneer, bamboo curtain composite sheet again, common quick growth poplar wood veneer or other low-intensity wood-based plate are core material, and superficial density height (0.9～1.2g/cm is made in applying glue, hot pressing
3), the low (0.5～0.6g/cm of sandwich layer density
3) thin shell structure reinforced type artificial board.
Adopt manufacturing process provided by the invention and assembly structure, can effectively utilize the surf green resource of a large amount of preciousnesses that extensive artificial bamboo board processing enterprise discarded, improved the utilization rate of bamboo wood greatly.Because just use isocyanate adhesive at surf green, the consumption of isocyanate adhesive is little, the increase of production cost is not remarkable, and the physical and mechanical property of finished product can reach very high index.
Four, description of drawings
Fig. 1 is a kind of typical structure schematic diagram of high density veneer, bamboo curtain composite sheet.Be 3-tier architecture shown in the figure, its middle level (1) is the resin impregnating veneer of the vertical assembly of wood grain, and layer (2) is the resin impregnating veneer of the horizontal assembly of wood grain, and layer (3) is for executing the bamboo curtain splint of isocyanate adhesive, and bamboo curtain splint forms with the braiding of the surf green thin bamboo strip.
Fig. 2 is the typical structure schematic diagram of thin shell structure reinforced type artificial board.Figure mesexine (1) is the decoration veneer after impregnated phenolic resin and high temperature, the high pressure plasticizing, and layer (2) is high density veneer, bamboo curtain composite sheet, and sandwich layer (3) is multilayer quick growth poplar wood veneer or low-intensity wood-based plates such as ordinary particle board, fiberboard.
Five, the specific embodiment
Embodiment 1:
A. be raw material with mao bamboon, with the surf green thin bamboo strip of mao bamboon, make the bamboo curtain splint that thickness is 0.8～1.5mm with the cotton thread braiding separately, the adhesive applying glue is done with toluene di-isocyanate(TDI) in dry back; Quick growth poplar wood is peeled into the veneer of 0.7～1.5mm, dry back impregnated phenolic resin glue;
B. adopt the assembly structure shown in the accompanying drawing 1, with 1 layer of bamboo curtain and 2 layers of resin impregnating board using poplar board of executing isocyanate adhesive, temperature be 135～150 ℃, pressure be hot pressed into the high density board using poplar board under 3.5～4.5MPa condition, the bamboo curtain composite sheet is standby;
C. as shown in Figure 2, birch fancy veneer after top layer (1) employing impregnated phenolic resin and high temperature, the high pressure plasticizing, layer (2) is high density board using poplar board, bamboo curtain composite sheet, sandwich layer (3) adopts 9 layers of board using poplar board, using assembly after the common synvaren applying glue, is that 135～145 ℃, pressure are to be hot pressed into thin shell structure reinforced type artificial board under 0.8～1.2MPa condition in temperature.
Embodiment 2:
As shown in Figure 2, the melamine-impregnated facing paper is adopted on top layer (1), layer (2) is high density board using poplar board, bamboo curtain composite sheet, sandwich layer (3) adopts the thick particieboard of 15mm, using assembly after the common synvaren applying glue, is that 135～145 ℃, pressure are to be hot pressed into thin shell structure reinforced type artificial board under 0.8～1.2MPa condition in temperature.
All the other are with embodiment 1.
Adopt method and structure provided by the invention, the Main physical mechanical property of the thin shell structure reinforced type artificial board of making is as follows:
Density---0.6～0.75g/cm
3
Elastic feel quantity---6000～15000MPa
MOR---50～120MPa
Impact flexibility---60～100J/m
2
Realize effectively utilizing surf green thin bamboo strip resource, reduced the goal of the invention of manufacturing cost.
Claims (1)
1. thin shell structure reinforced type artificial board that adopts the secondary hot pressing method to make is woven into bamboo curtain, timber with the surf green thin bamboo strip and is processed into behind the veneer dryly, it is characterized in that:
A. bamboo curtain adopts the isocyanate adhesive applying glue, and veneer impregnated phenolic resin adhesive is made high density veneer, bamboo curtain composite sheet earlier after assembly, hot pressing;
B. be surface material with high density veneer, bamboo curtain composite sheet again, common quick growth poplar wood veneer or other low-intensity wood-based plate are core material, make thin shell structure reinforced type artificial board after applying glue, the hot pressing.