CN1655286A - Special-shaped copper-clad aluminium wire and method of production - Google Patents
Special-shaped copper-clad aluminium wire and method of production Download PDFInfo
- Publication number
- CN1655286A CN1655286A CN 200510045974 CN200510045974A CN1655286A CN 1655286 A CN1655286 A CN 1655286A CN 200510045974 CN200510045974 CN 200510045974 CN 200510045974 A CN200510045974 A CN 200510045974A CN 1655286 A CN1655286 A CN 1655286A
- Authority
- CN
- China
- Prior art keywords
- copper
- special
- shaped copper
- clad
- wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention discloses an allotype copper and aluminum wire, which comprises aluminum core and copper cover layer with non-round section. The process method comprises the following steps: processing round copper coil and aluminum compound wire; using twenty to one hundred tons of pressure to roll the wires with speed as 100-800m/min; shaping by mode pulling; match fire processing with temperature of 260-350 Deg. C.
Description
Technical field:
The present invention relates to a kind of compound wire and production method, especially a kind of abnormal shape (non-circular) copper-clad aluminum conductor and production method.
Background technology:
At present, people have developed multiple compound wire, and problem that copper resource day by day deficient bad in order to the conduction valuable, aluminum conductor that solves copper conductor is as compound wires such as copper covered steel, copper cover aluminum.Its production method all is that the Chinese invention patent application number is 98112410.0 basically; name is called " a kind of compound copper-aluminium wire and production technology " disclosed method; promptly " after copper strips (or copper pipe) after will fully annealing with wire wheel and aluminium bar surface passivation layer remove; employing cladding method wraps into copper strips with aluminium bar; and copper strips curved tubulose; seam under protective atmosphere; or with tiretube process aluminium bar is packed in the copper pipe; composite blank made; again with stretching; extruding or prick the way of (rolling) system, the composite blank machining deformation that cladding method or tiretube process are made is until final size ".Because copper is different with the physical characteristic of aluminium, the copper-clad coating is thinner in addition, so up to the present, no matter be hot working or cold working, the compound wire cross sectional shape of being processed is circle, can not satisfy the requirement of special occasions abnormal shape (non-circular) lead, to such an extent as to the still higher pure copper wire of price in the past of existing special-shaped lead.
Summary of the invention:
The present invention is in order to solve the technical problem that existing in prior technology can not satisfy special-shaped compound wire requirement, a kind of special-shaped copper-clad aluminium wire and production method to be provided.
Technical solution of the present invention is: a kind of special-shaped copper-clad aluminium wire, be composited by aluminium core and copper-clad coating, and the cross section of described recombination line is non-circular.
Described non-circular be oblate, square, rectangle, flat rhombus or ellipse.
A kind of production method of special-shaped copper-clad aluminium wire, its step is as follows:
A. make circular copper-coated aluminum complex lead;
B. with 20～100 tons pressure rolling pressure rolling compound wire, rolling speed is 100～800m/min;
C. by mould drawing typing;
D. Quenching Treatment, hardening heat is 260～350 ℃.
Described a step is for to be coated on copper strips on the aluminium bar that diameter is 8～20mm, and with the speed of 50～150m/min, 13～18% reducing rate carries out drawing, and being drawn to diameter is 3～10mm.
The drawing speed of described c step is 100～800m/min.
The present invention has overcome the prejudice of prior art, adopt the pressure and the speed that are fit to that the copper cover aluminum recombination line is carried out roll extrusion, then by mould drawing moulding, can produce multiple non-circular special-shaped line, as oblate, square, rectangle, flat rhombus or ellipse etc., to substitute the special-shaped line of existing fine copper, solved product price high-technology problem in the past, satisfy the requirement of people to special-shaped compound wire.
Embodiment:
Embodiment 1:
A. select the circular copper-coated aluminum complex lead of outsourcing for use;
B. with 20～100 tons pressure rolling pressure rolling compound wire, rolling speed is 100～800m/min, forms the flat compound wire;
C. by mould drawing typing, mold shape is the final products shape, as oblate, square, rectangle, flat rhombus or ellipse etc.;
D. Quenching Treatment, hardening heat is 260～350 ℃.
Embodiment 2:
A. copper strips is coated on the aluminium bar that diameter is 8～20mm, with the speed of 50～150m/min, 3～18% reducing rate carries out drawing, and being drawn to diameter is 3～10mm;
B. with 20～100 tons pressure rolling pressure rolling compound wire, rolling speed is 100～800m/min, forms the flat compound wire;
C. by mould drawing typing, mold shape is the final products shape, as oblate, square, rectangle, flat rhombus or ellipse etc.;
D. Quenching Treatment, hardening heat is 260～350 ℃.
Embodiment 3:
Other are as embodiment 1 or 2, and just the drawing speed by mould drawing typing is 100～800m/min.
Claims (5)
1. a special-shaped copper-clad aluminium wire is composited by aluminium core and copper-clad coating, it is characterized in that: the cross section of described recombination line is non-circular.
2. special-shaped copper-clad aluminium wire according to claim 1 is characterized in that: described non-circular be oblate, square, rectangle, flat rhombus or ellipse.
3. the production method of a special-shaped copper-clad aluminium wire, its step is as follows:
A. make circular copper-coated aluminum complex lead;
B. with 20～100 tons pressure rolling pressure rolling compound wire, rolling speed is 100～800m/min;
C. by mould drawing typing;
D. Quenching Treatment, hardening heat is 260～350 ℃.
4. the production method of special-shaped copper-clad aluminium wire according to claim 3, it is characterized in that: described a step is for to be coated on copper strips on the aluminium bar that diameter is 8～20mm, with the speed of 50～150m/min, 13～18% reducing rate carries out drawing, and being drawn to diameter is 3～10mm.
5. according to the production method of claim 3 or 4 described special-shaped copper-clad aluminium wires, it is characterized in that: the drawing speed of described c step is 100～800m/min.