CN1654578A - 含有星形嵌段共聚物的弹性连接粘合剂 - Google Patents
含有星形嵌段共聚物的弹性连接粘合剂 Download PDFInfo
- Publication number
- CN1654578A CN1654578A CNA2005100518702A CN200510051870A CN1654578A CN 1654578 A CN1654578 A CN 1654578A CN A2005100518702 A CNA2005100518702 A CN A2005100518702A CN 200510051870 A CN200510051870 A CN 200510051870A CN 1654578 A CN1654578 A CN 1654578A
- Authority
- CN
- China
- Prior art keywords
- block copolymer
- tackiness agent
- vinylbenzene
- substrate
- contain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
包含星形聚苯乙烯—聚异戊二烯/聚丁二烯嵌段共聚物的热熔粘合剂组合物和在一次性吸湿弹性制品的制造过程中作为弹性连接粘合剂的应用。
Description
发明领域
本发明涉及粘合剂组合物，特别涉及一种适于作为弹性连接粘合剂的含有星形嵌段共聚物的热熔粘合剂组合物以及由该组合物制成的弹性制品。
背景技术
热熔粘合剂在其熔融状态时被涂覆到基底上，然后冷却固化成粘合层。这种粘合剂被广泛地应用在商业和工业中，如产品装配和包装中，并已经广泛地应用在无纺工业，用于制备婴儿尿布和成人失禁制品。在上述应用中，粘合剂被涂覆到至少一层聚烯烃无纺基底、至少一层弹性体，如斯潘德克斯弹性纤维和/或至少一层聚烯烃膜上，使基底粘合在一起。
热熔粘合剂常规应用于无纺工业，同时还需要一种配制成用于更有效的粘合用于特定终用途的产品的特定类型的基底上的粘合剂。本发明即致力于这种需要。
发明概述
已经发现含有约15wt％到约35wt％的一种(PS-PI-PB)nX星形嵌段共聚物，其中PS-PI-PB臂的数量n等于或大于3，最高约20wt％的一种线性嵌段共聚物如SBS、SEBS、SEPS、 SIBS及其混合物，和约30wt％至70wt％的一种黏性树脂的热熔粘合剂特别适于作为弹性连接粘合剂。
本发明的一个实施方案指向含有约15wt％到约35wt％的(PS-PI-PB)nX星形嵌段共聚物的粘合剂组合物。这种粘合剂在用作含有弹性部分的制品的弹性连接粘合剂时显示了良好的蠕变性，例如在包含一个或多个定位的用以接触穿用者的腿或腰的弹性翻边的一次性吸湿服中存在的。
本发明的另一个实施方式指向含有粘合剂的制品，这种粘合剂包括约15wt％到约35wt％的一种(PS-PI-PB)nX星形嵌段共聚物，其中PS-PI-PB臂的数量n等于或大于3，最高约20wt％的一种线性嵌段共聚物如SBS、SEBS、SEPS、SIBS及其混合物，约30wt％至70wt％的一种黏性树脂。制品将包括至少一个弹性基底。本发明还包括一次性吸湿制品，特别是一次性弹性制品，包括一次性吸湿服装。
本发明的另一个实施方式指向将基底粘合到相似或不相似的基底上的方法，包括至少在第一层基底上涂覆热熔粘合剂组合物，至少把第二层基底放到第一层基底的粘合剂上，将两层基底粘合在一起。在本发明的实施过程中，所述的第一和/或第二基底中的至少一个是弹性聚氨酯纤维(斯潘德克斯)。在该方法中使用的粘合剂包括约15wt％到约35wt％的一种(PS-PI-PB)nX星形嵌段共聚物，其中n等于或大于3，最高约20wt％的一种线性嵌段共聚物如SBS、SEBS、SEPS、SIBS及其混合物，约30wt％至70wt％的一种黏性树脂。
本发明的详细描述
在本发明中引用的所有文献作为参考内容被引入。
本发明提供了一种热熔粘合剂组合物。在本发明的组合物配方中共聚物的含量较少并且显示了优良的粘合力，导致了高效的粘合体系。
弹性连接中最重要的特性之一是蠕变性。这样，需要具有优良的韧性的粘合剂。本发明的粘合剂满足了弹性连接应用及其它应用的严格要求。
因此这种粘合剂特别适用于弹性的无纺制品和婴儿尿布、训练裤、成人失禁三角裤或内衣等的制备。
本发明使用的星形嵌段共聚物是具有(PS-PI-PB)nX结构的聚苯乙烯-聚异戊二烯/聚丁二烯嵌段共聚物，其中PS是聚苯乙烯，PI是聚异戊二烯，PB是聚丁二烯，X是在星形嵌段聚合物的制备中使用的多官能团偶联剂的残基，n代表链接到X上的PS-PI-PB臂的数量，它等于或大于3。N的值在3到10之间变化，优选3到7，更优选3.5到4。优选苯乙烯-异戊二烯-丁二烯星形嵌段共聚物中含有的二嵌段百分比少于共聚物重量的25％(偶联效率大于75％)，更优选少于共聚物重量的约20％(偶联效率大于80％)，每一臂的数均分子量约在30,000至95,000之间，嵌段共聚物的总的数均分子量少于约380,000。优选星形嵌段共聚物中苯乙烯嵌段组分约为共聚物重量的25％至50％。本发明的星形嵌段共聚物的完整的用途和制备方法参见美国专利US5,372,870。
更详细地说，本发明的粘合剂包含约15wt％至35wt％的至少一种热塑性星形嵌段共聚物，特别是(苯乙烯-异戊二烯-丁二烯)nX。在本发明中，n大于或等于3，通常为3到10，更通常是3-6。
星形聚合物(PS-PI-PB)nX的每一臂的结构，即苯乙烯-异戊二烯-丁二烯嵌段共聚物的结构如下定义：PS的数均分子量约为10,000至25,000。PI+PB的数均分子量约为20,000至70,000。这就使星形嵌段共聚物的每一臂的数均分子量约为30,000至95,000。所有星形嵌段共聚物的总的数均分子量约为90,000至380,000，并且PS组分的存在量至少约为共聚物重量的25％至50％。
本发明的粘合剂包含至少一种具有通式A-B-A的线性嵌段共聚物，其中聚合物的端嵌段A是非弹性的聚合物嵌段，作为均聚物，其玻璃化转变温度约高于20℃，弹性聚合物的中间嵌段B衍生自异戊二烯、丁二烯或异丁烯，它们可以是部分或基本上氢化的或其混合物。
非弹性的端嵌段A包括乙烯基单体如乙烯基芳烃、乙烯基吡啶、乙烯基卤化物和乙烯基羧化物以及丙烯酸单体如丙烯腈、甲基丙烯腈、丙烯酸酯等的均聚物或共聚物。单乙烯基芳香烃特别地包括苯系如苯乙烯、乙烯基甲苯、乙烯基二甲苯，和乙基乙烯基苯以及双环单乙烯基化合物如乙烯基萘等。其它非弹性的聚合物嵌段可以衍生自α烯烃、烯化氧、乙缩醛、尿烷等。优选苯乙烯。
弹性的中间嵌段B组分构成了热塑性弹性共聚物的其余部分，它衍生自异戊二烯或丁二烯，异戊二烯或丁二烯可以如美国专利US 3 700 633中教导的那样被氢化。丁二烯的氢化可以是部分的也可以基本上是完全的。氢化弹性丁二烯嵌段要在不会改性乙烯基芳烃聚合物的条件下进行。也可以选择其它条件来基本上均匀地沿着聚合物链进行氢化，使弹性和非弹性嵌段都被氢化到实际上相同的程度，氢化程度既可以部分的也可以完全的。氢化的聚合物优选在加工过程中最小化降解，加工过程中的降解对于较高分子量的聚合物来说是一个更严重的问题。
本发明的粘合剂组合物通常包含约1wt％至20wt％的A-B-A嵌段共聚物。具体的例子包括苯乙烯-异戊二烯-苯乙烯(SIS)、苯乙烯-丁二烯-苯乙烯(SBS)、苯乙烯-异丁烯苯乙烯(SIBS)、苯乙烯-b-乙烯/丁烯-b-苯乙烯(SEBS)，和/或苯乙烯-b-乙烯/丙烯-b-苯乙烯(SEPS)。
本发明的粘合剂通常还包括约30％至70％重量的黏性树脂，优选约40wt％至70wt％，更优选约40wt％至45wt％的与热塑性弹性体的中嵌段相容的增粘剂。优选增粘剂的球环软化点高于约25℃。合适的增粘剂包括任何相容的树脂或其混合物，如(1)天然或改性的树脂，如松香、木松香、浮油松香、馏出松香、氢化松香、二聚松香和多聚松香；(2)天然或改性松香的丙三醇和季戊四醇酯，例如，灰木松香的丙三醇酯、氢化松香的丙三醇酯、多聚松香的丙三醇酯、氢化松香的季戊四醇酯和松香的苯酚改性的季戊四醇酯；(3)天然萜烯的共聚物和三聚物，如苯乙烯/萜烯和α甲基苯乙烯/萜烯；(4)用ASTM方法E28，58T测得的软化点为约80℃至150℃的多萜(烯)；后面的萜烯通常是由萜烯烃在Friedel-crafts催化剂的存在下在合适的低温下聚合得到的，如双环单萜烯即公知的松萜；还包括氢化的多萜(烯)；(5)苯酚改性的萜烯树脂以及氢化的衍生物例如，双环萜烯和苯酚在酸性介质中缩聚的树脂产物；(6)球环软化点为约70℃至135℃的脂肪石油烃树脂；后者树脂是由主要由烯烃和二烯烃组成的单体聚合得到的；还包括氢化的脂肪石油烃树脂；(7)脂肪族的石油烃树脂及其氢化的衍生物；(8)脂肪/芳香或脂环族/芳香族共聚物和它们的氢化衍生物。
优选用于本发明的增粘剂包括三联苯、脂肪树脂、脂环族树脂和脂肪/芳香或脂环族/芳香。更优选脂肪和脂环族树脂。例子包括Goodyear的Wingtack95，Estman Chemical Company的Eastotac H100R和ExxonMobilChemical Company的ESCOREZ 5600。对于特定的粘合剂的选择取决于所用的弹性嵌段共聚物。
另外，往粘合剂中引入最多约30wt％的端嵌段增黏剂树脂端基是理想的。粘合剂冷却后端嵌段树脂主要驻留在热塑性弹性体的非弹性嵌段中。这些树脂的代表主要是基于混合的C9石油蒸馏流芳族树脂，如购自Eastman ChemicalCompany的材料，或基于纯净的或混合的芳香族单体的单体流，如乙烯基甲苯、α-甲基苯乙烯、香豆酮或茚的均聚物或共聚物。优选基于购自EastmanChemical Company的商品名为Plastolyn的α-甲基苯乙烯。如果存在的话，端基嵌段树脂的用量通常在约1至30wt％，优选少于约20wt％。
粘合剂组合物优选包括约40wt％至70wt％的黏性树脂，黏性树脂与嵌段共聚物的中段相容，并且约5wt％至30wt％的热塑性烃增粘剂与嵌段共聚物的端嵌段相容。
本发明的粘合剂中还可以含有油或其它稀释剂，它们主要是脂肪性的并且与热塑性弹性体的中段相容。本发明的组合物通常包含液体增塑剂，其含量少于约20wt％。本发明的组合物通常包含至少约1wt％，更通常为至少5wt％的液体增塑剂。增塑剂的例子包括如链烷烃和环烷烃的石油，高度提纯的不含芳香族烃的链烷烃和环烷烃的食物和工业级的白色石油矿物油，以及液体增粘剂如聚丁烯、聚丙烯、聚萜烯等的合成液态低聚物。合成系列加工油是高粘度的低聚物，它们是具有中高分子量的永久地流动的液态烯烃单体、异链烷烃或链烷。液态增塑剂或增黏稀释剂包括聚萜烯如Goodyear公司的Wingtack 10和Exxon Chemical公司的基于C5原料流的Escorez 2520。其它的液态稀释剂包括Kuraray公司的聚异戊二烯LIR 50，和Amoco’s公司的聚丁烯Indopol。最优选Escorez 2520和聚合的C5原料流混合的链烷油。
还可以存在如聚乙烯蜡之类的蜡。在使用的情况下，蜡的存在量通常为至少约2wt％，最高约5wt％。
最后，在本发明的橡胶基压敏粘合剂中使用的抗氧剂的存在量通常为最高达约3wt％。可在这里使用的稳定剂或抗氧剂包括高分子量的受阻苯酚和多官能团苯酚如含硫和磷的苯酚。受阻酚是本领域技术人员熟知的，其特征在于在邻近酚羟基的地方含有空间大体积基团。特别是，叔丁基通常取代苯环上酚羟基的至少一个邻位。受阻酚的代表包括：1，3，5-三甲基2，4，6-三(3，5-二叔丁基-4-羟基苯)苯；四-3(3，5-二-叔丁基-4-羟基笨)-丙酸季戊四醇酯，4，4’-亚甲基二(2，2-叔丁基苯酚)；4，4’-硫代二(6-叔丁基-邻甲苯酚)；2，6-二-叔丁基苯酚；6-(4-羟基苯氧基)-2，4-二(正辛基硫)-1，2，5-三嗪；膦酸-二-正十八烷基3，5-二-叔丁基-4-羟基苄基酯；3，5-二-叔丁基-4-羟基苯甲酸2-(n-辛基硫)乙基酯；以及六[3-(3，5-二-叔丁基-4-羟基苯基)-丙酸山梨糖醇酯]。
本发明的热熔粘合剂组合物可以用工业上公知的技术配制。一个典型的方法包括将约20％的油或液态稀释剂以及所有的热塑性聚合物和稳定剂放入带夹套的混合锅中，优选带夹套的带转子的重载锅中，然后升温至最高大约190℃。在混合物熔融后，降温至约150℃至约165℃。继续混合并加热直至得到光华均匀的物质，然后加入黏性树脂、蜡以及剩余的稀释剂再搅拌均匀。
可以用本领域已知方法将粘合剂涂覆到基底上，包括但不限于辊涂、涂抹、干刷、浸涂喷涂、槽涂、漩涂、印刷(如墨水喷射印刷)、凸版印刷、挤出、雾化喷涂、凹版印刷(图形转印)、静电印刷、气相沉积、纤维化和/或筛网印刷。
本发明的粘合剂可以用作定位粘合剂、核心粘合剂或弹性粘合剂，并且特别适于用于制品的生产，包括但不限于一次性吸湿制品如尿布、成人失禁制品、床垫；卫生巾及其它吸湿制品如围涎、创伤敷料和外科披肩或窗帘，它们被用来吸收液体如水和盐水，以及体液如尿、经血和血液。使用本粘合剂将无纺布或织物粘到其它基底或元件上去。第二层基底可以是其它无纺布、织物或不相关的材料。通常在约290°F至约325°F的温度下把本发明的粘合剂涂覆到基底上。
如上所述，吸湿结构通常包括无纺织物。无纺织物的定义是具有柔软性、多孔性特征的连锁的纤维网络。用于组成无纺布的单个的纤维可以是合成的、天然的或两者的混合。单个的纤维可以通过机械的、化学的或加热方式来彼此连接。无纺布在商业上有广泛的用途包括绝缘、包装(例如食物如肉)、家用抹布、外科斗篷、医用服以及一次性制品如尿布、成人失禁制品和卫生棉。织物是紧密相关的材料，其中单个的纤维相互之间通过化学不通过化学方式连接。
可以使用粘合剂连接面材和背材。可选地，也可以用粘合剂将一次性吸湿制品的面材或背材与其它部分如织物层、侧翼、固定端、带或薄片或其它本领域公知的构成一次性吸湿制品的部分粘合在一起。
本领域人员公知哪些材料适于作面材和背材。适于作面材的材料是液体可透过材料如纺丝粘合的聚丙烯或聚乙烯，其基重约为每平方米15-20克。常用于一次性吸湿材料的背材通常是由液体不透过材料制成的，它的功能是保持如水、尿、经血和血之类的液体，它置于一次性吸湿制品的吸湿芯内从而防止床或/和外层衣服不被浸湿。一次性吸湿制品中用作背材的材料通常不透水但是透气。不透液体的材料的例子包括如聚烯烃膜，如聚丙烯和聚乙烯，透气材料如多孔聚烯烃膜，有时指可透气的膜。
本发明的粘合剂特别适用于弹性连接粘合剂。需要具有优良的延展性和弹性的材料来制作各种一次性和耐用物品如失禁垫、一次性尿布、训练裤、衣服、内衣、运动服、汽车装饰、挡风雨条、垫圈和家具装饰。拉伸性和弹性是性能特征，对衣物是否合身或贴合物品的框架具有很大的作用。虽然很多材料在室温下都显示了良好的弹性和应力应变性，然而经常需要弹性材料在重复使用，在高温如体温或夏天汽车内部温度下伸缩时，弹性材料仍能提供一致或可靠的吻合。本发明的粘合剂特别适合在无纺领域如婴儿尿布或成人失禁制品中使用。除了无纺市场，本发明的这种热熔性粘合剂还可用于包装、折叠和装订市场，此处要求降低应用温度，同时保持粘合剂的韧性和强度。
一次性弹性制品通常是从聚合物膜、弹性纤维、无纺片材和/或吸收材料通过制造技术的组合制成的复合材料。弹性纤维可用已知方法如熔融和溶液纺丝和卷绕制备。无纺片材可用纺时粘合、熔体吹塑、水缠结、机械缠结等方法制备。膜和片材的成形方法包括挤出和共挤出技术，如吹膜、铸膜、异形压出、注射模塑，挤出涂覆以及挤出成片。聚合物膜优选液体不透过材料如聚烯烃膜，例如聚丙烯和聚乙烯，以及透气材料如微孔聚烯烃膜，有时指可透气的膜。
耐用弹性制品如汽车门和窗框、衣服的腰带线或条，和建筑的挡风雨条可以用已知的成形、热成形和异形成形技术制造。
当在施加偏向力后材料被表征为具有高的弹性回复百分比(即低百分比的永久变形)时，材料被看作是弹性的。理想地，弹性材料用三个不依赖温度的性能的组合表征，即低百分比的永久变形、低应变应力或负载、低百分比的应力或负载松弛。即，在升高的使用温度下这些值要低，(1)拉伸材料时要求低的应力或负载，(2)当材料被拉伸时没有或只有低的应力松弛或无负载，和(3)在拉伸、偏置或应变中断后完全或高度地回复到原尺寸。这样，弹性聚合物通常是指没有稀释剂的树脂，其断裂伸长率超过100％，不受任何卷曲(呈纤维状时)的影响，当拉伸到两倍长度时，保持1分钟，然后松驰，在1分钟内收缩到少于原长的1.5倍。这种聚合物包括但不仅限于，天然橡胶或合成橡胶、嵌段聚氨酯(包括聚氨酯脲)，如聚醚聚氨酯和聚酯聚氨酯、聚醚酯、弹性聚乙烯和聚丙烯以及聚醚酰胺。本发明的物品包括由这些弹性聚合物以各种形状作成的基底，这样的基底可用于本发明的方法中，条件是本发明产品的益处不受不利的影响。本发明的制品可以包括粘合剂和至少一层弹性基底如至少一种弹性纤维、带、膜、条、涂层、色带和/或片材，并且包括基本上线性的乙烯聚合物和弹性基底，例如，斯潘德克斯(例如Lycra斯潘德克斯和LycraXA，在斯潘德克斯有很少或没有润滑的表涂层)。在一个实施方式中，基底包括斯潘德克斯或熔纺弹性体。在另一个实施方式中，基底包括纤维状或宽度小于10mm的带状的天然或合成橡胶。粘合剂和至少一层弹性基底可以包括制品的至少一个组件，包括腰带、腿带、腹带等，但并不局限于这些例子。
美国国际商标委员会定义斯潘德克斯是生产的纤维，其中形成纤维的物质是含有至少85％重量的嵌段聚氨酯的长链合成聚合物。Lycra斯潘德克斯是已知的具有近乎完美的不依赖于温度的弹性，从而使其适用于作衣服、运动装和泳装。
本发明进一步由以下实施例描述，但不局限于这些实施例。
实施例
在下面的实施例中，所有份以重量计，并且所有温度以华氏温度计量，除非特别说明。
粘合剂的制备.
本发明所述的配方在配有西格马桨的600g Brabender混合器中配制。将热塑性嵌段共聚物和约20％的配方中的油加入预热到约325°F的辊筒中。均匀后，加入中段增粘剂。最后加入剩下的油和末段增粘剂。混合均匀。
使用以下材料来制备粘合剂：
苯乙烯和异戊二烯和丁二烯的星形嵌段共聚物Vector DPX 589，购自ExxonMobil Chemical Company。它含有约30％的苯乙烯，熔体流动指数约为8-14，二嵌段共聚物的百分比为24％。
苯乙烯和异戊二烯的三嵌段共聚物Vector 4211，购自ExxonMobil ChemicalCompany，异戊二烯作为软的中间段。它含有约30％的苯乙烯，熔体流动指数约为10-16。
芳香烃树脂Kristalex3085，球环软化点为82℃至88℃。
氢化的烃黏性剂Eastotac H100，购自Eastman Chemical Company，软化点为95℃至105℃。
烃树脂Eastotac H130，软化点为125℃至135℃。
石油烃树脂Scorez 5400，购自Exxon，软化点100至106℃。
矿物油Calsol 5550，购自Calumet Lubricants公司。
抗氧剂IRGANOX 1010FF，购自Ciba-Geigy。
本发明用的无纺基底是Avgol的纺时粘合的聚丙烯。
本发明用的聚乙烯膜是电晕处理的TXEM-244.0压花膜，厚度为0.75mil，购自Pliant Corp。
该粘合剂接受各种模拟成功的商业应用需要的测试。测试如下描述。
热熔粘合剂的熔融粘度在Brookfield Model RVT Thermosel粘度仪上，用27号心轴进行测定。
蠕变性在最终使用温度(100°F)下，在4小时的拉伸期间，在拉伸条件下通过测量自由端弹性股收缩的多少来评估。
测量两层无纺层或无纺层与聚合物膜之间的在拉伸条件下粘合的细丝(斯潘德克斯)的长度(“起始长度”)。截断无纺层/膜与斯潘德克斯的两端，在100°F下4小时后测量所得的丝的自由端的收缩量。蠕变百分比用以下方法计算：
蠕变％＝(起始长度-最终长度)/起始长度×100
例如如果标记之间的起始长度是20cm，标记之间的最终长度是15cm，则蠕变百分比是25％。每种状态测试五个样品，将每种弹性线的测试结果平均，并记录结果。
测试的配方和得到的结果如表1所示。所用的粘合剂敷帖器是NordsonSpiral喷雾器。将三股620分特的Lycra Spandex丝粘结到含有一种15gsm纺时粘合的无纺布和一种多聚膜的基底上。在粘合剂的应用中使用连续的无覆盖的图形。三股丝的用量水平是8mg/in。
表1
| 组分 | (wt％) |
| Vector DPX 589 | 17 |
| Vector4211 | 6 |
| Kristalex3085 | 22 |
| Eastotac H100 | 12 |
| Eastotac H130 | 13 |
| Escorez 5400 | 20 |
| Calsol 5550 | 10 |
| Irgonox 1010 | 0.5 |
| 性能 | |
| 平均蠕变％ | 4.1％ |
| 在300°F时的粘度 | 7,325 |
这个实施例表明，使用多于15wt％的(苯乙烯-异戊二烯-丁二烯)n-X结合三嵌段SIS，可以制得良好的弹性粘结粘合剂。
可以在不背离本发明的精神和范围的条件下进行许多改动和变化，这对于本领域技术人员来说是显而易见的。上面描述的特定实施方式仅仅是举例而已，本发明只受所附的权利要求书的限制，以及与权利要求实质上相同的全部的等同物的范围。
Claims (14)
1.一种热熔粘合剂，包括
一种星形嵌段共聚物(PS-PI-PB)nX，其中PS是聚苯乙烯，PI是聚异戊二烯，PB是聚丁二烯，X是在星形嵌段聚合物的制备中使用的多官能团偶联剂的残基，n等于或大于3，代表链接到X上的PS-PI-PB臂的数量，
一种线性嵌段共聚物，和
一种黏性树脂，
其中基于粘合剂组合物的重量，含有约15wt％到约35wt％的星形嵌段共聚物，含有最多约20wt％的线性共聚物，含有约30wt％至70wt％的黏性树脂。
2.如权利要求1所述的粘合剂，其特征在于所述星形嵌段共聚物的每一臂的数均分子量约为30,000至95,000。
3.如权利要求2所述的粘合剂，其特征在于星形嵌段共聚物含有的二嵌段的百分比少于约25％。
4.如权利要求3所述的粘合剂，其特征在于星形嵌段共聚物含有的二嵌段的百分比少于约20％。
5.如权利要求2所述的粘合剂，其特征在于星形嵌段共聚物中苯乙烯的含量为约25wt％至约50wt％。
6.如权利要求1所述的粘合剂，其特征在于所述的线性嵌段共聚物为苯乙烯一异戊二烯-苯乙烯、苯乙烯-丁二烯-苯乙烯、苯乙烯-异丁烯苯乙烯、苯乙烯-b-乙烯/丁烯-b-苯乙烯，和/或苯乙烯-b-乙烯/丙烯-b-苯乙烯。
7.如权利要求1所述的粘合剂，其特征在于n值约为3至6。
8.如权利要求1所述的粘合剂，还含有蜡，所述蜡的含量少于约5wt％。
9.如权利要求1所述的粘合剂，还含有液体增塑剂，所述液体增塑剂的含量少于约20％。
10.一种含有热熔粘合剂及基底的制品，其中所述的热熔粘合剂包括
一种星形嵌段共聚物(PS-PI-PB)nX，其中PS是聚苯乙烯，PI是聚异戊二烯，PB是聚丁二烯，X是在星形嵌段聚合物的制备中使用的多官能团偶联剂的残基，n等于或大于3，代表链接到X上的PS-PI-PB臂的数量，
一种线性嵌段共聚物，和
一种黏性树脂，
其中，基于粘合剂组合物的重量，含有约15wt％到约35wt％的星形嵌段共聚物，含有最多约20wt％的线性共聚物，含有约30wt％至70wt％的黏性树脂，以及
所述基底包含弹性纤维。
11.如权利要求10所述的制品，它是一次性弹性制品。
12.如权利要求11所述的制品，它是尿布。
13.一种粘结第一层基底与第二层基底的方法，包括至少将热熔粘合剂涂到第一层基底上，至少把第二层基底与存在于第一层基底上的粘合剂接触，从而使所述的第一和第二层基底粘合在一起，其中至少所述的第一和或第二基底中的一层是弹性聚氨酯纤维，并且其中的热熔粘合剂包括
一种星形嵌段共聚物(PS-PI-PB)nX，其中PS是聚苯乙烯，PI是聚异戊二烯，PB是聚丁二烯，X是在星形嵌段聚合物的制备中使用的多官能团偶联剂的残基，n等于或大于3，代表链接到X上的PS-PI-PB臂的数量，
一种线性嵌段共聚物，和
一种黏性树脂，
以及任选的液体增塑剂和/或蜡，
其中，基于粘合剂组合物的重量，含有约15wt％到约35wt％的星形嵌段共聚物，含有最多约20wt％的线性共聚物，含有约30wt％至70wt％的黏性树脂，液体增塑剂的量为0到少于20wt％，和蜡的量为0到少于约5wt％。
14.如权利要求13所述的方法，其中至少一层基底是无纺基底。