CN1629342A - 一种铝钼铌硅中间合金及其制备方法 - Google Patents
一种铝钼铌硅中间合金及其制备方法 Download PDFInfo
- Publication number
- CN1629342A CN1629342A CN 200310119079 CN200310119079A CN1629342A CN 1629342 A CN1629342 A CN 1629342A CN 200310119079 CN200310119079 CN 200310119079 CN 200310119079 A CN200310119079 A CN 200310119079A CN 1629342 A CN1629342 A CN 1629342A
- Authority
- CN
- China
- Prior art keywords
- alloy
- preparation
- raw material
- titanium alloy
- master alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
生产过程实施例 | 称取原料(kg) | 料温 | 反应状况 | 反应时间 | 分析结果(%)余量为杂质 |
实施例1 | MoO3 MoO2 Nb2O5 Al Si CaF21 1 0.4 0.95 0.012 0.415 | 45℃ | 反应挺激烈,激溅一次 | 22″ | Al Mo Nb Si O10 73.50 15.00 0.9 0.088 |
实施例2 | MoO3 MoO2 Nb2O5 Al Si CaF21 1 0.4 0.763 0.012 0.415 | 40℃ | 反应略激烈,火光较高 | 24″ | Al Mo Nb Si O8 75.14 15.34 0.92 0.090 |
实施例3 | MoO3 MoO2 Nb2O5 Al Si CaF21 1 0.43 0.95 0.012 0.415 | 41℃ | 反应较激烈,发出呼呼声 | 25″ | Al Mo Nb Si O9.88 72.63 16.00 0.89 0.076 |
实施例4 | MoO3 MoO2 Nb2O5 Al Si CaF21 1 0.373 0.95 0.012 0.415 | 42℃ | 反应激烈 | 26″ | Al Mo Nb Si O10.12 74.37 14 0.91 0.074 |
实施例5 | MoO3 MoO2 Nb2O5 Al Si CaF21 1 0.4 0.95 0.013 0.415 | 44℃ | 反应特激烈,溅点火花 | 23″ | Al Mo Nb Si O10.01 73.57 15.02 1.0 0.085 |
Claims (6)