CN1590482A - Heat insulating vehicle point and its production technology - Google Patents

Heat insulating vehicle point and its production technology Download PDF

Info

Publication number
CN1590482A
CN1590482A CN 03150634 CN03150634A CN1590482A CN 1590482 A CN1590482 A CN 1590482A CN 03150634 CN03150634 CN 03150634 CN 03150634 A CN03150634 A CN 03150634A CN 1590482 A CN1590482 A CN 1590482A
Authority
CN
China
Prior art keywords
heat insulation
vehicle paint
dispersion
agent
defoamer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 03150634
Other languages
Chinese (zh)
Other versions
CN100381518C (en
Inventor
潘祖峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanning Tai'an Building Material Co., Ltd.
Original Assignee
SHANGHAI SITAIAN PAINT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI SITAIAN PAINT CO Ltd filed Critical SHANGHAI SITAIAN PAINT CO Ltd
Priority to CNB031506348A priority Critical patent/CN100381518C/en
Publication of CN1590482A publication Critical patent/CN1590482A/en
Application granted granted Critical
Publication of CN100381518C publication Critical patent/CN100381518C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

An insulating paint for vehicle is prepared from acrylic resin, diluent, disperser, defoaming agent, anti-deposition agent, pigment, filler, drying agent, UV resistant, and porous ceramic microbeads for reflecting sunlight.

Description

Heat insulation vehicle paint and production technique thereof
Technical field:
The present invention relates to the technical field of coating, specifically a kind of can mainly be thermal insulating coating and the production technique thereof that is used for vehicle.
Background technology:
At present, product about heat-insulating and energy-saving commonly used mostly is the outer insulating product of exterior wall, this product is to utilize the low heat transfer coefficient of thermal baffle to realize low-yield loss, this series products can only be passive minimizing energy height between transmission, because in atmosphere, energy is that carrier transmits by light wave, when solar irradiation strong, the too high then not significantly effect of free air temperature, this series products all can increase thickness in addition, comparatively strict requirement is also arranged in construction, time-consuming bothersome, also be not used in the heat insulation coating of vehicle in the prior art.
Summary of the invention:
The object of the present invention is to provide a kind of heat insulation vehicle paint and production technique thereof, the radiation of antireflection part sunlight effectively of this heat insulation vehicle paint, thus reduce the heat energy that the coated article body receives.
To achieve these goals, technical scheme of the present invention is heat insulation vehicle paint, it is characterized in that: the weight percentages of components of described heat insulation vehicle paint is acrylic resin 40-45%, thinner 8-12%, dispersion agent 0.1-0.5%, defoamer 0.05-0.3%, anti-settling agent 0.2-0.8%, pigment 20-25%, filler 6-8%, siccative 0.05-0.1%, ultraviolet screener 0.05-0.2%, porous ceramics microballon 15-20%.
The production technique of heat insulation vehicle paint, it is characterized in that: with weight percent is that acrylic resin 40-45%, thinner 8-12%, dispersion agent 0.1-0.5%, defoamer 0.05-0.3% are fed into the low speed dispersion that the production container carried out 15 minutes, and then pigment 20-25%, filler 6-8% add produced the high speed dispersion that container carried out 40 minutes, through filtering greater than 150 purpose filtering nets, adding siccative 0.05-0.1%, ultraviolet screener 0.05-0.2%, porous ceramics microballon 15-20% again, to carry out stirring at low speed even, and packing is produced at last.
The present invention is owing to contain the porous ceramics microballon in the component of coating, reflected sunlight effectively, through testing when solar irradiation is mapped on the coating, there is the sun light wave about 85% to be reflected, and general common coating can only reflect 13%, sun light wave, promptly reduced by 72% sunlight absorption rate than common coating, thereby greatly reduced the temperature of coated article, this thermal insulating coating especially is suitable as the thermal insulating coating of vehicle, it is very easy to construct, save time and save trouble, the temperature of coated article can not raise with the sunlight acute irradiation, has heat insulation and energy-conserving action, simultaneously can save a large amount of energy, meet the long-range energy strategy plan of country.Below be noon one day 11:30 to the actual test of the relevant position of 911 tunnel (bilayer) motorbus temperature, weather condition: fine, cloudy, test sample car: adopt two No. 911 double deck buses of the same type (wherein scribbles this automobile-used thermal insulating coating spraying car load roof)
Test condition: close the doors and windows 11:30 at noon thermometric simultaneously
Test result:
The position Scribble the thermal insulating coating vehicle Do not spray the thermal insulating coating vehicle The temperature difference
The roof surface temperature 47℃ 68℃ -21℃
Temperature in the imperial 44℃ 53℃ -9℃
Temperature in the lower floor compartment 40℃ 42℃ -2℃
Description of drawings:
Fig. 1 is the temperature comparative graph of this thermal insulating coating and other material in the sun
Embodiment:
The invention will be further described below in conjunction with drawings and Examples.
The present invention is heat insulation vehicle paint, it is characterized in that: the weight percentages of components of described heat insulation vehicle paint is acrylic resin 40-45%, thinner 8-12%, dispersion agent 0.1-0.5%, defoamer 0.05-0.3%, anti-settling agent 0.2-0.8%, pigment 20-25%, filler 6-8%, siccative 0.05-0.1%, ultraviolet screener 0.05-0.2%, porous ceramics microballon 15-20%, materials in these components all can be bought on market, after above-mentioned materials is mixed with coating, is coated on the vehicle and can effectively reduces vehicle interior temperature; Thinner is the propylene glycol acetic ester in the enforcement, and dispersion agent mills the ammonium polyester polymers for poly-, and defoamer is a polysiloxane, anti-settling agent mills ammonium for poly-, and pigment is titanium dioxide, and filler is a lime carbonate, siccative is dilaurate or dibutyl tin, and ultraviolet screener is an acrylate salt; The production technique of this heat insulation vehicle paint, it is characterized in that: with weight percent is acrylic resin 40-45%, thinner propylene glycol acetic ester 8-12%, the poly-ammonium polyester polymers 0.1-0.5% that mills of dispersion agent, defoamer polysiloxane 0.05-0.3%, the poly-ammonium 0.2-0.8% that mills of anti-settling agent is fed into the low speed dispersion that the production container carried out 10-20 minute, and then with pigment titanium white 20-25%, filler-calcium carbonate 6-8% adds the high speed dispersion that the production container carried out 30-50 minute, through filtering greater than 150 purpose filtering nets, add siccative dilaurate or dibutyl tin 0.05-0.1% again, ultraviolet screener acrylate salt 0.05-0.2%, it is even that porous ceramics microballon 15-20% carries out stirring at low speed, packing is produced at last, low speed is separated into per second and is lower than 5 and changes during concrete enforcement, high speed dispersion is that per second is higher than 50 commentaries on classics, and the particle diameter of porous ceramics microballon is greater than 150 orders.Porous ceramic film material particle diameter in this thermal insulating coating is generally the 150-200 order, sneaks in the coating, and micropartical forms firm, arranged in a uniform particle and films after the coating drying, can play the purpose of reflecting light, thereby reach effect of heat insulation.
Provide specific embodiment below
Embodiment 1
With weight percent is that acrylic resin 41%, propylene glycol acetic ester 10%, the poly-poly-ammonium 0.6% that mills of ammonium polyester polymers 0.2%, defoamer polysiloxane 0.1%, anti-settling agent that mills are fed into and produce 200 rev/mins the low speed that container carried out 12 minutes and disperse, and then titanium dioxide 22%, lime carbonate 6% added produce 1000 rev/mins of high speed dispersion that container carried out 35 minutes, filter through 150 purpose filtering nets, adding dilaurate 0.05%, acrylate salt 0.05%, porous ceramics microballon 20% again, to carry out 15 rev/mins stirring at low speed even, and packing is produced at last.
Embodiment 2
With weight percent is that acrylic resin 45%, propylene glycol acetic ester 8%, the poly-poly-ammonium 0.3% that mills of ammonium polyester polymers 0.3%, defoamer polysiloxane 0.2%, anti-settling agent that mills are fed into and produce 300 rev/mins the low speed that container carried out 15 minutes and disperse, and then titanium dioxide 21%, lime carbonate 6% added produce 1200 rev/mins of high speed dispersion that container carried out 30 minutes, filter through 180 purpose filtering nets, adding dilaurate 0.1%, acrylate salt 0.1%, porous ceramics microballon 19% again, to carry out 18 rev/mins stirring at low speed even, and packing is produced at last.
Embodiment 3
With weight percent is that acrylic resin 46%, propylene glycol acetic ester 9%, the poly-poly-ammonium 0.3% that mills of ammonium polyester polymers 0.2%, defoamer polysiloxane 0.1%, anti-settling agent that mills are fed into and produce 250 rev/mins the low speed that container carried out 18 minutes and disperse, and then titanium dioxide 20%, lime carbonate 6% added produce 1000 rev/mins of high speed dispersion that container carried out 35 minutes, filter through 150 purpose filtering nets, adding dibutyl tin 0.2%, acrylate salt 0.2%, porous ceramics microballon 18% again, to carry out 15 rev/mins stirring at low speed even, and packing is produced at last.

Claims (4)

1, heat insulation vehicle paint is characterized in that: the weight percentages of components of described heat insulation vehicle paint is acrylic resin 40-48%, thinner 8-12%, dispersion agent 0.1-0.5%, defoamer 0.05-0.3%, anti-settling agent 0.2-0.8%, pigment 20-25%, filler 6-8%, siccative 0.05-0.1%, ultraviolet screener 0.05-0.2%, porous ceramics microballon 15-20%.
2, heat insulation vehicle paint according to claim 1, it is characterized in that: thinner is the propylene glycol acetic ester, dispersion agent is the poly-ammonium polyester polymers that mills, defoamer is a polysiloxane, anti-settling agent mills ammonium for poly-, and pigment is titanium dioxide, and filler is a lime carbonate, siccative is dilaurate or dibutyl tin, and ultraviolet screener is an acrylate salt.
3, the production technique of heat insulation vehicle paint, it is characterized in that: with weight percent is acrylic resin 40-48%, thinner 8-12%, dispersion agent 0.1-0.5%, defoamer 0.05-0.3%, anti-settling agent 0.2-0.8% is fed into and produces the low speed dispersion that container carried out 15 minutes, and then with pigment 20-25%, filler 6-8% adds the high speed dispersion that the production container carried out 40 minutes, through filtering greater than 150 purpose filtering nets, add siccative 0.05-0.1% again, ultraviolet screener 0.05-0.2%, it is even that porous ceramics microballon 15-20% carries out stirring at low speed, and packing is produced at last.
4, the production technique of heat insulation vehicle paint according to claim 3 is characterized in that: low speed is separated into per second and is lower than 5 commentaries on classics, and high speed dispersion is that per second is higher than 50 commentaries on classics, and the particle diameter of porous ceramics microballon is greater than 150 orders.
CNB031506348A 2003-08-25 2003-08-25 Heat insulating vehicle point and its production technology Expired - Fee Related CN100381518C (en)