CN1584237A - Mineral wool sound-absorbing board and preparing method thereof - Google Patents
Mineral wool sound-absorbing board and preparing method thereof Download PDFInfo
- Publication number
- CN1584237A CN1584237A CN 03153762 CN03153762A CN1584237A CN 1584237 A CN1584237 A CN 1584237A CN 03153762 CN03153762 CN 03153762 CN 03153762 A CN03153762 A CN 03153762A CN 1584237 A CN1584237 A CN 1584237A
- Authority
- CN
- China
- Prior art keywords
- mineral wool
- weight portion
- sound absorption
- modified fibre
- absorption board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a mineral wood sound-absorbing plate, and its preparation method. Its raw material is formed from (by weight portion) 75-85 portions of granulated wool, 1-7 portions of starch, 6-12 portions of attapulgite, 1-5 portions of modified fibre and 1-5 portions of auxiliary material, in which the modified fibre is substituted for conventional waste newspapers, so that the process for grinding waste newspapers can be saved, therefore it can greatly save energy source and can reduce cost, at the same time it can obtain identical performance.
Description
Technical field
The present invention relates to a kind of mineral wool sound absorption board and preparation method thereof.
Background technology
Mineral wool sound absorption board is a kind of house decorative material that widely uses, its light weight, sound-absorbing, fire prevention, heat insulation and environmental protection.The main component of this class sheet material is granulated wool, starch, attapulgite clay, disregard message paper and auxiliary material.Wherein, the use of disregard message paper is one of key of this mineral wool sound absorption board production technology, increases the intensity and the distortion of minimizing under wet environment of mineral wool board with utilization short fiber wherein.
Though the disregard message paper that uses in making mineral wool sound absorption board only accounts for 1～5wt% of total material, not very high, but because the requirement of process equipment, used disregard message paper must be very clean, so can only use without stock's newspaper of selling, rather than the old newspaper that reclaims arbitrarily, cost is increased; Before using disregard message paper, need in mill, it to be milled to the fine fibre shape, could add slurrying use in the mixing machinery together with other raw material, so will consume a large amount of electric energy and manpower and materials; Depositing also of disregard message paper need take big quantity space, and get damp summer easily; In addition, because disregard message paper belongs to organic matter, can influence the fireproof performance of mineral wool board when being used for mineral wool board.
Summary of the invention
The objective of the invention is to overcome mineral wool sound absorption board that prior art produces and make the cost of production defective of increase that increases, consume energy, thereby provide a kind of low production cost, few mineral wool sound absorption board consumes energy because of containing disregard message paper.
Another object of the present invention is to provide the production technology of described mineral wool sound absorption board.
The objective of the invention is to realize by the following technical solutions:
The invention provides a kind of mineral wool sound absorption board, its composition comprises:
Granulated wool 75～85 weight portions
Starch 1～7 weight portion
Attapulgite clay 6～12 weight portions
Modified fibre 1～5 weight portion
Auxiliary material 1～5 weight portion.
The rich magnesium silicate clay ore deposit modification of serving as reasons of described modified fibre obtains, and its each component and content are:
SiO
2?1.5-10wt％；
MgO?59-70wt％；
Al
2O
3?0.1-0.8wt％；
Fe
2O
3?0.2-1.6wt％；
FeO?1-8wt％；
CaO?0.01～0.6wt％；
H
2CO
3+H
2O?12-22wt％
The present invention also provides a kind of preparation technology of above-mentioned mineral wool sound absorption board, comprises the steps:
1) each component of raw material is pressed granulated wool 75～85 weight portions, starch 1～7 weight portion, attapulgite clay 6～12 weight portions, modified fibre 1～5 weight portion, auxiliary material 1～5 weight portion weighing;
2) attapulgite clay is carried out defibrination;
3) the alleged raw material of step 1) is placed on mixed pulp in the mixing machinery;
4) adopt conventional wet method, dry method or semidry process making sheet;
5) at the made plate of step 4) behind moulding and drying technology, carry out conventional following process and surfacing again and obtain finished product.
Wherein, the rich magnesium silicate clay ore deposit modification of serving as reasons of the modified fibre of described step 1) obtains.
The invention has the advantages that: the present invention uses a kind of modified fibre to replace disregard message paper, can be directly used in the system oar and need not to mill in advance, so can save operation, reduces cost, and reduces energy consumption; In addition, this modified fibre is an inorganic mineral, thereby can improve the fireproof performance of sheet material.
The specific embodiment
Embodiment 1
Each component of raw material is pressed granulated wool 85 weight portions, starch 4 weight portions, attapulgite clay 6 weight portions, modified fibre (SiO
21.5wt%; MgO 70wt%; Al
2O
30.1wt%; Fe
2O
31.1wt%; FeO 5.29wt%; CaO 0.01wt%; H
2CO
3+ H
2O 22wt%) the auxiliary material 1 weight portion weighing that 4 weight portions, and aluminum sulfate, polyacrylamide and emulsified wax are formed;
Attapulgite clay is carried out defibrination; Generally under the certain condition of pulper revolution and the mill number of teeth, the control time, make final viscosity greater than 1500 pascal seconds (PaS), down with;
With above-mentioned raw materials mixture mixed pulp in mixing machinery, after being about to all raw materials and auxiliary material and all dropping into material-compound tank,, form homogeneous, stable slip system through the abundant stirring of certain hour, can finish; Adopt dry method making sheet; After the molding substrate drying, carry out conventional following process and surfacing, make mineral wool sound absorption board 1.
The manufacturing process of corresponding prior art is as described below:
Each component of raw material is pressed granulated wool 85 weight portions, starch 4 weight portions, attapulgite clay 6 weight portions, disregard message paper 4 weight portions, reached the auxiliary material 1 weight portion weighing that aluminum sulfate, polyacrylamide and emulsified wax are formed; Disregard message paper is milled into fibrous, and attapulgite clay is carried out defibrination; With above-mentioned raw materials mixture mixed pulp in mixing machinery; Adopt dry method making sheet; After the molding substrate drying, carry out conventional following process and surfacing, make mineral wool sound absorption board P1.
Embodiment 2
Each component of raw material is pressed granulated wool 75 weight portions, starch 7 weight portions, attapulgite clay 8 weight portions, modified fibre (SiO
210wt%; MgO 70wt%; Al
2O
30.8wt%; Fe
2O
31.6wt%; FeO 1wt%; CaO 0.6wt%; H
2CO
3+ H
2O 16wt%) 5 weight portions, and the auxiliary material 5 weight portion weighings of emulsified wax, aluminum sulfate and polyvinyl alcohol composition;
Attapulgite clay is carried out defibrination;
With above-mentioned raw materials mixture mixed pulp in mixing machinery; Adopt semidry method making sheet; After the molding substrate drying, carry out conventional following process and surfacing, make mineral wool sound absorption board 2.
The manufacturing process of corresponding prior art is as described below:
Each component of raw material is pressed granulated wool 75 weight portions, starch 7 weight portions, attapulgite clay 8 weight portions, disregard message paper 5 weight portions, reached the auxiliary material 5 weight portion weighings that emulsified wax, aluminum sulfate and polyvinyl alcohol are formed; Disregard message paper is milled into fibrous, and attapulgite clay is carried out defibrination; With above-mentioned raw materials mixture mixed pulp in mixing machinery; Adopt semidry method making sheet; After the molding substrate drying, carry out conventional following process and surfacing, make mineral wool sound absorption board P2.
Embodiment 3
Each component of raw material is pressed granulated wool 83 weight portions, starch 1 weight portion, attapulgite clay 12 weight portions, modified fibre (SiO
210wt%; MgO 59wt%; Al
2O
30.2wt%; Fe
2O
30.2wt%; FeO 8wt%; CaO 0.6wt%; H
2CO
3+ H
2O 22wt%) 1 weight portion, and the auxiliary material 3 weight portion weighings of polyacrylamide, emulsified wax and alchlor composition;
Attapulgite clay is carried out defibrination;
With above-mentioned raw materials mixture mixed pulp in mixing machinery; Adopt slurry flowing process making sheet; After the molding substrate drying, carry out conventional following process and surfacing, make mineral wool sound absorption board 3.
The manufacturing process of corresponding prior art is as described below:
Each component of raw material is pressed granulated wool 83 weight portions, starch 1 weight portion, attapulgite clay 12 weight portions, disregard message paper 1 weight portion, reached the auxiliary material 3 weight portion weighings that polyacrylamide, emulsified wax and alchlor are formed; Disregard message paper is milled into fibrous, and attapulgite clay is carried out defibrination; With above-mentioned raw materials mixture mixed pulp in mixing machinery; Adopt slurry flowing process (belonging to a kind of of wet method) making sheet; After the molding substrate drying, carry out conventional following process and surfacing, make mineral wool sound absorption board P3.
As from the foregoing, adopt modified fibre of the present invention to replace disregard message paper after, can save disregard message paper is milled into fibrous operation, save a large amount of energy and manpower and materials.Simultaneously, other step still can adopt existing conventional technology, adopts very convenient.
The modified fibre of above-mentioned three embodiment is to be obtained by rich magnesium silicate clay ore deposit modification, and its each component and content obtain by detection.The present invention also can with in magnesium silicate clay ore deposit replace rich magnesium silicate clay ore deposit.
The radioassay result that mineral wool sound absorption board 1,2,3 carries out is shown in national building materials industry radioactivity and hazardous substances supervision and inspection center the detected value of its internal radiation index is 0.1; The detected value of external exposure index is 0.1, and does not contain asbestos.It meets the category-A finishing material requirement of GB6566-2001 " the radioactive material nucleic is limited the quantity of " standard code.
Table 1 is according to industry standard " mineral wool decoration acoustic absorption " JC670-1997 bending failure load and the hygroscopic deformation that the mineral wool board (15mm) of above-mentioned three embodiment (1,2,3) and comparative example (P1, P2, P3) carries out to be detected the test data that obtains.
| Mineral wool sound absorption board | Bending failure load (N) | Hygroscopic deformation (mm) | ||||
| Vertical | Horizontal | Before the distortion | After the distortion | Deflection | The average deformation amount | |
| ????P1 | ????310 | ????198 | ??24 | ??25.4 | ????1.4 | ????1.3 |
| ????P2 | ????308 | ????200 | ??24 | ??25.1 | ????1.1 | |
| ????P3 | ????312 | ????196 | ??24.2 | ??25.5 | ????1.3 | |
| ????1 | ????250 | ????230 | ??25.0 | ??26.8 | ????1.8 | ????1.5 |
| ????2 | ????252 | ????228 | ??24.2 | ??26.0 | ????1.8 | |
| ????3 | ????248 | ????232 | ??24.5 | ??25.5 | ????1.0 | |
As seen from the above table, behind the employing modified fibre, the intensity detection data of the mineral wool board of producing belong to same level for the intensity detection data with the mineral wool board that adopts the production of disregard message paper.The average level of the hygroscopic deformation of the 15mm mineral wool board behind the employing modified fibre is 1.5mm, and the average level of the hygroscopic deformation of the 15mm mineral wool board of employing disregard message paper production is 1.3mm, and both also belong to same level.Therefore, after the employing modified fibre was replaced disregard message paper, the intensity of mineral wool board and hygroscopic deformation index all kept peer-level.
Claims (5)
1, a kind of mineral wool sound absorption board, its composition comprises:
Granulated wool 75～85 weight portions
Starch 1～7 weight portion
Attapulgite clay 6～12 weight portions
Modified fibre 1～5 weight portion
Auxiliary material 1～5 weight portion.
2, mineral wool sound absorption board as claimed in claim 1 is characterized in that, the rich magnesium silicate clay ore deposit modification of serving as reasons of described modified fibre obtains.
3, mineral wool sound absorption board as claimed in claim 2 is characterized in that, described modified fibre component and content are:
SiO
2?1.5-10wt％；
MgO?59-70wt％；
Al
2O
3?0.1-0.8wt％；
Fe
2O
3?0.2-1.6wt％；
FeO?1-8wt％；
CaO?0.01～0.6wt％；
H
2CO
3+H
2O?12-22wt％
4, a kind of preparation technology of mineral wool sound absorption board as claimed in claim 1 comprises the steps:
(a) each component of raw material is pressed granulated wool 75～85 weight portions, starch 1～7 weight portion, attapulgite clay 6～12 weight portions, modified fibre 1～5 weight portion, auxiliary material 1～5 weight portion weighing;
(b) attapulgite clay is carried out defibrination;
(c) the alleged raw material of step (a) is placed on mixed pulp in the mixing machinery;
(d) adopt conventional wet method, dry method or semidry process making sheet;
(e) at the made plate of step (d) behind moulding and drying technology, carry out conventional following process and surfacing again and obtain finished product.
5, the preparation technology of mineral wool sound absorption board as claimed in claim 4 is characterized in that, the rich magnesium silicate clay ore deposit modification of serving as reasons of the modified fibre of described step (a) obtains, and its each component and content are:
SiO
2?1.5-10wt％；
MgO?59-70wt％；
Al
2O
3?0.1-0.8wt％；
Fe
2O
3?0.2-1.6wt％；
FeO?1-8wt％；
CaO?0.01～0.6wt％；
H
2CO
3+H
2O?12-22wt％