CN1583648A - Concrete reducing agent - Google Patents
Concrete reducing agent Download PDFInfo
- Publication number
- CN1583648A CN1583648A CN 200410013787 CN200410013787A CN1583648A CN 1583648 A CN1583648 A CN 1583648A CN 200410013787 CN200410013787 CN 200410013787 CN 200410013787 A CN200410013787 A CN 200410013787A CN 1583648 A CN1583648 A CN 1583648A
- Authority
- CN
- China
- Prior art keywords
- formula
- structural formula
- alkyl
- glycol ether
- weight percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Shrinkage reducing agent for concrete has weight percent of 0-50% of polyvinyl alcohol, 0-60% of fatty group glycol ether, 0-50% of hydroxide alkylamine. Polyvinyl alcohol compound structural formula is -(CH2CHOH)n-,n=1700-2200, fatty group glycol ether structural formula is RO(CH2CH2O)nH, R=C1-20, n=1-10; oxidized alkyamine structural formula is R1-NH-R2OH, R1 and R2 are the alkyls of C1-20. The shrinkage reducing agent can reduce the shrinkage of cement, sand pulp and cement paste; and has the same function to dry shrinkage and self-shrinkage, can be used to Portland cement, popular cement, allblended cement and special cement. The compound is simple, and performance is stable. It can be used in many fields. It is not limited by the environment and the cost is low. It has shrinkage to different pH value, temperature and humidity.
Description
Technical field:
The present invention relates to a kind of concrete additive, be specifically related to a kind of economization agent for concrete.
Background technology:
We know that the early stage cracking of concrete (cement+sand+stone+water+admixture) is modal quality accident in the concrete works at present, and the rimose reason is concrete contraction after all.Can be divided into dry shrinkage and self-constriction from shrinking the mechanism difference that produces.Dry shrinkage is meant that moisture loss in the concrete is in air and the contraction that produces; Self-constriction is meant that the moisture in the concrete is consumed by hydration reaction and the caused contraction of inside concrete self-desiccation that causes.The common ground of dissimilar contractions is reductions of internal moisture content.When part or all of shrinkage strain is restricted, certainly lead to tensile stress at inside concrete.When moment, tensile stress surpassed certain limit, concrete just will produce cracking.Crack on concrete is having a strong impact on concrete permeability energy, endurance quality even structure properties.Reduce concrete contraction, reduce and avoid concrete cracking significant to the work-ing life of improving concrete engineering quality, prolongation concrete structure.There are same problem in mortar (cement+sand+water+admixture) and cement paste (cement+water+admixture).From shrinking the mechanism that produces, have two kinds of methods can fundamentally reduce the amount of contraction: a kind of is the content that reduces gel pore in the concrete, and another kind is the surface tension that reduces liquid in the hole.The content of gel pore is directly proportional with the amount of hydrated product, and when guaranteeing the hydrated product amount, the hole is impossible reduce, and therefore reducing the unique feasible means of shrinking is to reduce the surface tension of water.For preventing concrete cracking, domestic life-time service swelling agent, the expansion that swelling agent produced is the contraction of compensating concrete and mortar partly or entirely, but swelling agent has stronger dependency to the extent of hydration of composition, envrionment temperature, humidity and the cement of cement, and for example one of condition of playing a role of swelling agent is to react with suff water.The concrete less to water cement ratio, inside concrete self water yield is limited.Simultaneously, because the closely knit outside moisture of structure is difficult to enter inside concrete.Therefore swelling agent usually can not play a role, even the aggravation crack on concrete.Economization agent for concrete came out in Japan in nineteen eighty-two, also succeeded in developing in the U.S. in 1985.Up to the present found that number class material can reduce concrete contraction, as alcohols, glycol, triol and the homologue thereof of comprising commonly used, but this type of boiling point substance is lower, volatile, have irritating smell simultaneously, burning-point is lower, uses very inconvenient in engineering reality; And the polymkeric substance of the bigger alcohols of molecular weight is easy to use, but will reach the required effect of reducing needs heavy dose to mix concrete, has so just increased concrete cost virtually; The another kind of material that can be used as economization agent is an ethers, as: glycol ether, polyglycol ether, polyethylene glycol alkyl ether etc., this class material is better than alcohols reducing on the effect, but most of ether is volatile and irritating smell is arranged, and is also very unfavorable to health of operators; Having the another kind of data record to reduce material is alkanolamine, and for example α, β-alkanolamine are very effective to the contraction that reduces concrete mortar and the clean oar of cement, but price is very expensive, has increased concrete cost greatly, is difficult to promote in engineering.In addition, solubility aminoresin and soap preparation also have a small amount of report as economization agent.
Summary of the invention:
The objective of the invention is to develop a kind of make up simple, dependable performance, applied widely, be not subjected to environmental restraint, production cost low, can both play the economization agent for concrete that reduces effect to different potential of hydrogen, temperature and humidity environment.Economization agent for concrete of the present invention is mixed according to weight percent by following component: polyvinyl alcohol compounds 0～50%, aliphatics glycol ether 0～60%, hydroxide alkylamine 0～50%, wherein the structural formula of polyvinyl alcohol compounds is-(CH
2CHOH)
n-, n=1700 in the formula～2200; The structural formula of aliphatics glycol ether is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; The structural formula of oxidation of alkyl amine is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.Economization agent is done in the present invention's employing wherein two or three mixture, can effectively reduce the contraction of concrete, mortar and cement paste; Effective equally to dry shrinkage and self-constriction, be applicable to silicate cement, ordinary Portland cement and all mixed cements and special cement.The present invention can also mix use with admixtures such as the water reducer of using always, hardening accelerator, retardant, swelling agents, and reinforcing bar is not had corrosion; After adding economization agent, can make the contraction of concrete, mortar and cement paste reduce by 60～80%.According to the size of blank concrete shrinkage value, the volume scope that economization agent for concrete of the present invention works is 2～7% (accounting for water weight ratio), and consumption is 3～5% usually, and it can significantly reduce the surface tension of water effectively.The present invention is with respect to traditional swelling agent, the environment that works is unrestricted, can both play the effect that reduces to shrink to different potential of hydrogen, temperature and humidity environment, guaranteeing that concrete shrinkage is reduced under 60～80% prerequisites, with respect to former alcohols economization agent, solved the excessive problem of volume, the volume 8～10% by the past is reduced to 3～5%; Economization agent with respect to other type has reduced production cost, makes it more feasible in application in engineering.At the like product high volatility, to direct labor's healthy disadvantageous problem, in the selection of prescription, taked relative measures simultaneously.Environment by related substances is carried out technical Analysis and experimental study, has been determined main component.When volume was higher, the early strength of concrete or mortar slightly reduced, but later strength is higher than the intensity that contrasts test specimen.Because economization agent itself is a tensio-active agent efficiently, the adding of economization agent can make concrete air content obviously reduce; When adding air entrapment agent, the bleed effect of air entrapment agent will be weakened to some extent, therefore air content had under the situation of requirement, should adjust the content of air entrapment agent according to test.The present invention makes up simply, dependable performance, applied widely, be not subjected to environmental restraint, production cost low, can both play different potential of hydrogen, temperature and humidity environment and to reduce effect.
Embodiment:
Embodiment one: present embodiment is mixed according to weight percent by following component: polyvinyl alcohol compounds 0～50%, aliphatics glycol ether 0～60%, hydroxide alkylamine 0～50%, wherein the structural formula of polyvinyl alcohol compounds is-(CH
2CHOH)
n-, n=1700 in the formula～2200; The structural formula of aliphatics glycol ether is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; The structural formula of oxidation of alkyl amine is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.
Embodiment two: present embodiment is mixed by polyvinyl alcohol compounds and two kinds of materials of aliphatics glycol ether, and wherein the polyvinyl alcohol compound accounts for 40～50% of component total weight percent, and its structural formula is-(CH
2CHOH)
n-, n=1700 in the formula～2200; The aliphatics glycol ether accounts for 50～60% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10.
Embodiment three: present embodiment is mixed by polyvinyl alcohol compounds and two kinds of materials of aliphatics glycol ether, and wherein the polyvinyl alcohol compound accounts for 45% of component total weight percent, and its structural formula is-(CH
2CHOH)
n-, n=1700 in the formula～2200; The aliphatics glycol ether accounts for 55% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10.It is 5% (accounting for water weight ratio) that present embodiment works the volume scope of reducing effect, behind the adding economization agent, can make the contraction of concrete, mortar and cement paste reduce by 60～80%.
Embodiment four: present embodiment is mixed by aliphatics glycol ether and two kinds of materials of oxidation of alkyl amine, and wherein the aliphatics glycol ether accounts for 50～60% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; Oxidation of alkyl amine accounts for 40～50% of component total weight percent, and its structural formula is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.
Embodiment five: present embodiment is mixed by aliphatics glycol ether and two kinds of materials of oxidation of alkyl amine, and wherein the aliphatics glycol ether accounts for 50% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R=is C in the formula
1～20Alkyl, n=1～10; Oxidation of alkyl amine accounts for 50% of component total weight percent, and its structural formula is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.It is 7% (accounting for water weight ratio) that present embodiment works the volume scope of reducing effect, behind the adding economization agent, can make the contraction of concrete, mortar and cement paste reduce by 60～80%.
Embodiment six: present embodiment is mixed by polyvinyl alcohol compounds, aliphatics glycol ether and three kinds of materials of hydroxide alkylamine, and wherein the polyvinyl alcohol compound accounts for 35～45% of component total weight percent, and its structural formula is-CH
2CHOH)
n-, n=1700 in the formula～2200; The aliphatics glycol ether accounts for 45～55% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; Oxidation of alkyl amine accounts for 5～15% of component total weight percent, and its structural formula is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.
Embodiment seven: present embodiment is mixed by polyvinyl alcohol compounds, aliphatics glycol ether and three kinds of materials of hydroxide alkylamine, and wherein the polyvinyl alcohol compound accounts for 40% of component total weight percent, and its structural formula is-CH
2CHOH)
n-, n=1700 in the formula～2200; The aliphatics glycol ether accounts for 50% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; Oxidation of alkyl amine accounts for 10% of component total weight percent, and its structural formula is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.It is 3% (accounting for water weight ratio) that the present invention works the volume scope of reducing effect, behind the adding economization agent, can make the contraction of concrete, mortar and cement paste reduce by 70～80%.
Claims (7)
1, economization agent for concrete, it is characterized in that it is mixed according to weight percent by following component: polyvinyl alcohol compounds 0～50%, aliphatics glycol ether 0～60%, hydroxide alkylamine 0～50%, wherein the structural formula of polyvinyl alcohol compounds is-(CH
2CHOH)
n-, n=1700 in the formula～2200; The structural formula of aliphatics glycol ether is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; The structural formula of oxidation of alkyl amine is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.
2, economization agent for concrete according to claim 1, it is characterized in that it is mixed by polyvinyl alcohol compounds and two kinds of materials of aliphatics glycol ether, wherein the polyvinyl alcohol compound accounts for 40～50% of component total weight percent, and its structural formula is-(CH
2CHOH)
n-, n=1700 in the formula～2200; The aliphatics glycol ether accounts for 50～60% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10.
3, economization agent for concrete according to claim 1 is characterized in that it is mixed by polyvinyl alcohol compounds and two kinds of materials of aliphatics glycol ether, and wherein the polyvinyl alcohol compound accounts for 45% of component total weight percent, and its structural formula is-(CH
2CHOH)
n-, n=1700 in the formula～2200; The aliphatics glycol ether accounts for 55% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10.
4, economization agent for concrete according to claim 1 is characterized in that it is mixed by aliphatics glycol ether and two kinds of materials of oxidation of alkyl amine, and wherein the aliphatics glycol ether accounts for 50～60% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; Oxidation of alkyl amine accounts for 40～50% of component total weight percent, and its structural formula is R
1-NH-ROH, R in the formula
1, R
2Be C
1～20Alkyl.
5, economization agent for concrete according to claim 1 is characterized in that it is mixed by aliphatics glycol ether and two kinds of materials of oxidation of alkyl amine, and wherein the aliphatics glycol ether accounts for 50% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R=is C in the formula
1～20Alkyl, n=1～10; Oxidation of alkyl amine accounts for 50% of component total weight percent, and its structural formula is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.
6, economization agent for concrete according to claim 1, it is characterized in that it is mixed by polyvinyl alcohol compounds, aliphatics glycol ether and three kinds of materials of hydroxide alkylamine, wherein the polyvinyl alcohol compound accounts for 35～45% of component total weight percent, and its structural formula is-CH
2CHOH)
n-, n=1700 in the formula～2200; The aliphatics glycol ether accounts for 45～55% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; Oxidation of alkyl amine accounts for 5～15% of component total weight percent, and its structural formula is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.
7, economization agent for concrete according to claim 1, it is characterized in that it is mixed by polyvinyl alcohol compounds, aliphatics glycol ether and three kinds of materials of hydroxide alkylamine, wherein the polyvinyl alcohol compound accounts for 40% of component total weight percent, and its structural formula is-CH
2CHOH)
n-, n=1700 in the formula～2200; The aliphatics glycol ether accounts for 50% of component total weight percent, and its structural formula is RO (CH
2CH
2O)
nH, R is C in the formula
1～20Alkyl, n=1～10; Oxidation of alkyl amine accounts for 10% of component total weight percent, and its structural formula is R
1-NH-R
2OH, R in the formula
1, R
2Be C
1～20Alkyl.