CN1580139A - Natural multi-colour mineral decorative coating (true-stone paint) - Google Patents
Natural multi-colour mineral decorative coating (true-stone paint) Download PDFInfo
- Publication number
- CN1580139A CN1580139A CN 03132295 CN03132295A CN1580139A CN 1580139 A CN1580139 A CN 1580139A CN 03132295 CN03132295 CN 03132295 CN 03132295 A CN03132295 A CN 03132295A CN 1580139 A CN1580139 A CN 1580139A
- Authority
- CN
- China
- Prior art keywords
- natural
- mineral
- solvent
- true
- decorative paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention refers to a kind of natural polychrome mineral decorative coating (real mineral varnish) and has two kinds, solvent type and aqua type. This invention is composed of natural mineral powder, compound acrylic ester (latex) and solvent (other infused solvents). (1)The solvent type of natural polychrome mineral decorative coating (real mineral varnish), with the optional ratio of (in amounts of weight): 500 of natural mineral, 40 of silicon acrylic ester and 450 of solvent. The manufacturing method is as follows: first, whisk the compound acrylic ester rosin in the distribution kettle, then add solvent in proportion and whisk it, add the natural ore particle in proportion and whisk, pack it and get the turnoff. (2) The component ration of aqua type of natural polychrome mineral decorative coating (real mineral varnish) (in amounts of weight) is: between 300 and 350 of compound acrylic ester (such as silicon crylic acid latex or pure crylic acid latex), 600 of natural mineral powder.
Description
Technical field
The present invention relates to the natural broken colour mineral of a kind of solvent-borne type decorative paint (true mineral varnish), especially a kind of natural broken colour mineral decorative paint (true mineral varnish) that utilizes natural mineral powder and acrylic acid synthesizing, solvent or other injectings to wait mixing manufacture to use.
Background technology
Along with China's rapid development of economy, people improve constantly the pursuit of material and cultural life, particularly the wall body decoration to buildingss such as room, office building, public places of entertainment requires more and more higher, elegant style, the other tool of style, fresh and clean, the refreshing pleasant decorative environment of the heart become a kind of fashion gradually to be pursued, and people promote just significantly to the demand of architectural decoration coating material.There are shortcomings such as fugitive color, easily aging, easily be full of cracks, nature, work-ing life be low more or less in decorative paint in the market, thereby exploitation, produces the new problem that new decorative paint has become the building materials market.
Summary of the invention
The object of the present invention is to provide a kind of natural broken colour mineral decorative paint, it have solvent-borne type and water aqua type two we.
The natural broken colour mineral of solvent-borne type decorative paint, it is by raw materials such as natural mineral powder, acrylic ester synthesizing, solvents.Wherein, acrylic ester synthesizing can be a Si acrylate, also can be pure acrylic acid ester or bezene acrylic acid; Solvent is made of 200# gasoline, 180# ether solvent and other compositions.
The natural broken colour mineral of water aqua type decorative paint, it is made of natural mineral powder, acrylic acid synthesizing emulsion, other injecting.
The composition proportioning of the natural broken colour mineral of a kind of solvent-borne type provided by the present invention decorative paints (true mineral varnish) is (parts by weight are represented):
Form proportioning
Natural mineral powder 500-515
Acrylic acid synthesizing 35-50
Solvent 450
Wherein, the composition proportioning of solvent is (parts by weight are represented):
Form proportioning
200# industrial naptha 200
180# ether solvent 200
Other solvents 50
The preferred optimum proportion of the natural broken colour mineral of a kind of solvent-borne type provided by the present invention decorative paints (true mineral varnish) is than being (parts by weight are represented):
Form proportioning
Natural mineral powder 500
Silicon acrylic resin 40
Solvent 450
The production technique of the natural broken colour mineral of a kind of solvent-borne type provided by the present invention decorative paints (true mineral varnish) is: after at first the synthesizing propylene acid resin being put into distribution tank and stirring evenly, then adding solvent in proportion dilutes and stirs, add the natural ore particle powder more in proportion and mix and stir the companion, packing is finished product at last.
The natural broken colour mineral of a kind of solvent-borne type provided by the present invention decorative paints (true mineral varnish) can be made shades of colour such as red, yellow, orchid according to the self-colored difference of natural ore particle powder or mix broken colour decorative paint (true mineral varnish).
The component ratio of components of the natural broken colour mineral of another kind of water aqua type provided by the present invention decorative paint is (parts by weight are represented): acrylic acid synthesizing fat (as silicon ACRYLIC EMULSION or pure acrylic acid emulsion etc.) 300-350, natural mineral powder 600, other injecting 50.Its manufacture craft is identical with the solvent-borne type manufacture craft.
A kind of natural broken colour mineral decorative paint provided by the present invention has made full use of natural mineral powder Natural color, have that tint retention is strong, cohesive strength is high, secondary true, the long service life of ageing-resistant, color nature, effect, characteristics such as do not chap, do not peel off, and producing apparatus and technology are simple.
Embodiment
(1) manufacture craft of the natural broken colour mineral of solvent-borne type decorative paint
Embodiment 1, after acrylic ester synthesizing (35-50) put into distribution tank and stir evenly, then add solvent (450) and dilute and stir, add red natural ore particle powder (500-515) again and mix and stir the companion, pack and be natural red mineral decorative paint (true mineral varnish).
Embodiment 2, after acrylic ester synthesizing (35-50) put into distribution tank and stir evenly, then add solvent (450) and dilute and stir, add yellow natural ore particle powder (500-515) again and mix and stir the companion, pack and be natural yellow mineral decorative paint (true mineral varnish).
Embodiment 3, after acrylic ester synthesizing (35-50) put into distribution tank and stir evenly, then add solvent (450) and dilute and stir, add natural ore particle powder of all kinds (500-515) again and mix and stir the companion, packing is natural mixing broken colour mineral decorative paint (true mineral varnish) at last.
(2) manufacture craft of the natural broken colour mineral of water aqua type decorative paint
The manufacture craft of water aqua type is identical with solvent type manufacture craft, the different composition differences that just add, water aqua type is respectively acrylic acid synthesizing emulsion, natural mineral powder and other injecting at the composition that making processes should order adds in proportion.
Claims (5)
1, a kind of natural broken colour mineral decorative paint (true mineral varnish), especially a kind of natural broken colour mineral decorative paint (true mineral varnish) that utilizes natural mineral powder and acrylic ester synthesizing or emulsion, solvent or injecting to wait to be mixed and made into.
2, the described natural broken colour mineral decorative paint of claim 1 (true mineral varnish) has two kinds of solvent-borne type and water aqua types.The former composition proportioning is (parts by weight are represented):
Form proportioning
Natural mineral powder 500-515
Acrylic acid synthesizing 35-50
Solvent 450
Wherein, the composition proportioning of solvent is (parts by weight are represented):
Form proportioning
200# industrial naptha 200
180# ether solvent 200
Other solvents 50 latter's composition proportioning is (parts by weight are represented): acrylic acid synthesizing fat (as silicon ACRYLIC EMULSION or pure acrylic acid emulsion etc.) 300-350, natural mineral powder 600, other injecting 50.
3, the preferred optimum proportion of the natural broken colour mineral of the described solvent-borne type of claim 1 decorative paint (true mineral varnish) is than being (parts by weight are represented):
Form proportioning
Natural mineral powder 500
Silicon acrylic resin 40
Solvent 450
4, the production technique of the natural broken colour mineral of the described solvent-borne type of claim 1 decorative paint (true mineral varnish) is: after at first the synthesizing propylene acid resin being put into distribution tank and stirring evenly, then adding solvent in proportion dilutes and stirs, add the natural ore particle powder more in proportion and mix and stir the companion, packing is finished product at last.
5, the production technique of the natural broken colour mineral of the described water aqua type of claim 1 decorative paint (true mineral varnish) is identical with solvent type production technique.