CN1580100A - Automobile steel-made synchronizer ring gear carbon fiber friction material and use - Google Patents
Automobile steel-made synchronizer ring gear carbon fiber friction material and use Download PDFInfo
- Publication number
- CN1580100A CN1580100A CN 200410013150 CN200410013150A CN1580100A CN 1580100 A CN1580100 A CN 1580100A CN 200410013150 CN200410013150 CN 200410013150 CN 200410013150 A CN200410013150 A CN 200410013150A CN 1580100 A CN1580100 A CN 1580100A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon fiber
- synchro converter
- converter ring
- friction material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention provides a kind of friction material on steel synchronizer of automobiles and its method of application. This friction material chooses acrylonitrile carbon fiber as the reinforcing material and the cashew nut shell oil and melamine phenol-formaldehyde resin modified as the bond and is composed of many frictional-properties-adjusting agents, such as dilatant iron dust, brass powder, synthetic graphite powder, zinc stearate, precipitated barium sulfate and molybdenum disulfide. This kind of friction material is featured by stable friction system, low wear rate and good temperature resistance. Between 100deg.C and 250deg.C, the coefficient of wear is between 0.25 and 0.38 and the wear rate is between 0.04cm3/N.m and 0.47X10 to the power -7 cm3/N.m. Compared with the denticulate ring technics of steel synchronizer, it is more simple, has a lower abrasion to the fittings, improves the frictional properties of the denticulate ring of the synchronizer and reduces the production cost.
Description
Technical field
The present invention relates to automobile synchronizer tooth ring carbon fiber friction material and using method, belong to automotive friction material technology field.
Background technology
Carbon fiber friction material has excellent frictional behaviour, has stronger shock resistance, and shear strength has stronger temperature tolerance and resistance to corrosion.In the automobile industry of developed countries such as U.S., day, be used widely.It is to substitute the favorable substitutes that asbestos automotive friction material is arranged.
Synchro converter ring is in the past all made with alloyed copper, its production cost costliness, in recent years, some producers adopt the steel synchro converter ring to replace the alloyed copper synchro converter ring, but because the frictional behaviour of steel does not have the frictional behaviour of alloyed copper good, so, synchro converter ring in conjunction with the conical surface on adopt the method for sprayed molybdenum to improve its frictional behaviour, but because the price of molybdenum is still very high, so this method does not have very big meaning yet for reducing cost.
Therefore study a kind of friction layer of using carbon fiber friction material as the steel synchro converter ring, for the frictional behaviour that improves synchro converter ring, it is significant to reduce its production cost.
Summary of the invention
The objective of the invention is to study a kind of steel synchro converter ring friction materials and using method, this friction materials does not pollute the environment, and have stable friction factor, wear rate is low, heat resistance good, mating plate wearing and tearing are little, can reduce the production cost of steel synchro converter ring.
A kind of carbon fiber friction material that is used for the steel synchro converter ring provided by the invention, it is a strongthener with the carbon fiber, is binding agent with modified resin, and adds multiple frictional property regulator and form.This friction materials is mixed with by weight by following component, 20～40 parts of acrylic carbon fibre strongtheners, 26～32 parts of cashew nut shell oil and cyanurotriamide modified phenolic resin adhesives, 9～25 parts of frictional property regulator expansion iron powders, 2～4 parts of brass powders, 5～15 parts of graphous graphite powders, 0.5～1.5 part of Zinic stearas, 10～20 parts of process whites, 0.5～1.5 part of molybdenumdisulphide.Better component parts by weight proportioning is: acrylic carbon fibre strengthens tree and refers to 20～26 parts, 28～30 parts of cashew nut shell oil and cyanurotriamide modified phenolic resin adhesives, 15～25 parts of frictional property regulator expansion iron powders, 2～4 parts of brass powders, 5～15 parts of graphous graphite powders, 1 part of Zinic stearas, 10～18 parts of process whites, 1 part of molybdenumdisulphide.
The compound method of friction materials of the present invention, undertaken by following steps in sequence:
(1) in the proportion of composing scope, takes by weighing various raw materials, mix;
(2) with the resulting compound hot-die of step (1) compressing tablet, hot pressing pressure 15MPa, 160 ℃ of temperature, the compressing tablet time determines according to friction plate thickness, 1.5～2 minutes clamping times of every 1mm thickness;
(3) with the resulting compressing tablet of step (2), be heating and curing, curing process is: heated up 1 hour to 100 ℃ from room temperature, heated up then 1 hour to 120 ℃, heated up again 1 hour to 140 ℃, and, be warmed up to 160 ℃ again 140 ℃ of insulations 2 hours, after 8 hours, reduce to room temperature 160 ℃ of insulations, come out of the stove with stove;
(4) the sheet material grinding extrados that is cured, and the cleaning extrados promptly makes automobile steel synchro converter ring carbon fiber friction material.
The usage of automobile steel synchro converter ring carbon fiber friction material of the present invention, undertaken by following step:
(1) surface treatment: the synchro converter ring intrados carries out pickling degreasing, sand papering is used in the back that dewaters, eliminates rust, and the grinding of friction plate extrados is cleaned its surperficial abrasive dust with ethanol then;
(2) gluing: automobile brake sheet glue---the Harbin BC-1 tackiness agent that adopts Harbin City's Harbin Fine Chemical Works to produce, be applied to friction plate extrados surface and synchro converter ring inner arc surface, brush first pass glue with bristle, room temperature hung 30 minutes for 25 ℃, be coated with glue again second time, hung 12 hours, close up pressurization then, pressure 0.5～0.8MPa, 5 hours clamping times; Or roller coat gluing one time, place 80 ℃ of following preheatings 30～40 minutes then, close up pressurization while hot, pressure 0.5～0.8MPa, 1 minute clamping time;
(3) solidify and release: the synchro converter ring that pressing is had a carbon fiber friction plate is 180 ℃ of isothermal curings 1～2 hour, hangs release after the room temperature with stove then;
(4) car or mill glue surperficial the getting final product of automobile steel synchro converter ring inner arc of friction plate.Its product structure such as Fig. 2,3 show institute
Starting material used among the present invention are as follows:
Title specification density g/cm
3The place of production
Acrylic carbon fibre 12K is less than long 0.5 Changzhou of 0.5m Wujin Bu Hongdamo material company
5160 resins (the above 1.3 Zhejiang strong resin companies of sea salt China of cashew nut 300 orders
Shell oil and trimeric cyanamide
Modified phenolic resins)
Above Wujin, the 4.5 Changzhou Bu Hongdamo material company of expansion iron powder 120 orders
Above Wujin, the 8.5 Changzhou Bu Hongdamo material company of brass powder 80 orders
Graphous graphite powder 300～400 orders, 2.2 Changzhou Wujin Bu Hongdamo material company
The above 3 Wuhan Han Chang Raw Materials Company of Chemical Industry of Zinic stearas 300 orders
The above 2.3 Wuhan Han Chang Raw Materials Company of Chemical Industry of process white 300 orders
Wujin, 4.9 Changzhou Bu Hongdamo material company about molybdenumdisulphide 400 orders
Automobile steel synchro converter ring carbon fiber friction material of the present invention performance test:
Wear rate and frictional coefficient are measured by standard GB-5763/1998 with DMS-150 type constant speed formula frictional testing machines.
Shock strength: measure by standard GB5766-86.
Viscose glue tensile shear strength: measure by standard GB7124-86.
Apparent hardness: measure by standard GB/T5766-1996 with XHR-150 plastics Rockwell hardometer.
The performance measurement result of carbon fiber friction material of the present invention: coefficientoffriction is 0.28～0.38 in the time of 100 ℃; Be 0.29～0.33 in the time of 150 ℃; Be 0.3～0.37 in the time of 200 ℃; Be 0.25～0.32 in the time of 250 ℃; Wear rate V (10
-7Cm
3/ Nm) be 0.04～0.21 100 ℃ the time; Be 0.05～0.21 in the time of 150 ℃; Be 0.07～0.51 in the time of 200 ℃; Be 0.38～0.47 in the time of 250 ℃; Shock strength is greater than 3.0kgfcm/cm
2The viscose glue tensile shear strength is greater than 4.0Mpa (steel and friction materials are bonding).Lip river formula apparent intensity 100～115.
Description of drawings
Fig. 1 is an automobile steel synchro converter ring carbon fiber friction layer preparation technology schema.
Fig. 2 is the automobile steel synchro converter ring structure iron that the carbon fiber friction layer is arranged.
Fig. 3 is the automobile steel synchro converter ring sectional view that the carbon fiber friction layer is arranged.
Number in the figure is represented: 1 automobile steel synchro converter ring, 2 carbon fiber friction layers
Technological process shown in Figure 1: automobile steel synchro converter ring carbon fiber friction material carries out the raw material configuration by its composition, use the mixer batch mixing, then in thermocompressor and hot pressing die in 15MPa, hot pressing is in blocks under 160 ℃ of conditions, solidified 8 hours at 160 ℃, cooling back mill outer arc, the cleaning extrados, brush or the roller coat glue paste, pickling degreasing is carried out on ring gear intrados surface, rust cleaning, after the polishing, the coating viscosity glue agent, friction plate coated face and ring gear coated face close up bonding, are pressurized to 0.5～0.8MPa, 180 ℃ of constant temperature bonding curing in 1～2 hour then, solidify the back and hang the room temperature release, the synchro converter ring car or the mill intrados of friction materials arranged, promptly obtained carbon fiber friction layer automobile steel synchro converter ring product with stove.
Embodiment
Further specify the preparation and the usage of automobile steel synchro converter ring carbon fiber friction material of the present invention below by example.
Embodiment 1～3
The preparation of automobile steel synchro converter ring carbon fiber friction material: the proportioning raw materials by table 1 takes by weighing raw material, mix with mixer, reusable heat press and hot pressing die hot pressing are in blocks, hot pressing condition is pressure 15MPa, 160 ℃ of temperature, the compressing tablet time is determined according to friction plate thickness, it is 1.5～2 minutes that the thick master of every 1mm spends clamping time, its operating procedure is that 15MPa pressure was pressed 40 seconds under 160 ℃ of temperature, 0MPa exhaust 20 seconds, and 15MPa pressure was pressed 40 seconds again, 0MPa exhaust 20 seconds, 15MPa pressure was pressed after 4 minutes again, and the 0MPa depanning must be suppressed the friction plate sample; Compressed tablet is heating and curing, curing process is: heated up 1 hour to 100 ℃ from room temperature, heated up again 1 hour to 120 ℃, heated up again 1 hour to 140 ℃, be warmed up to 160 ℃ after 2 hours 140 ℃ of insulations, be incubated 8 hours, come out of the stove after cooling to room temperature with stove then, the carbon fiber friction plate sample that must solidify, this sample carries out the grinding extrados, clean its surperficial abrasive dust with ethanol after having ground cambered surface, standby.
With steel automobile synchro converter ring intrados with the pickling oiling, dewater, eliminate rust, use sand papering then.On polish cleaned synchro converter ring and friction plate flour milling, be coated with freezing city BC-1 tackiness agent with scrub-brush, after brushing first pass glue, hung 30 minutes at 25 ℃, be coated with glue again second time, hung 12 hours, close up pressurization then, pressure 0.6MPa, 5 hours clamping times, then it was solidified at 180 ℃ of constant temperature in 1.5 hours, hang the room temperature release with stove again.Promptly obtain the automobile steel synchro converter ring product of carbon fiber friction layer.The frictional behaviour of embodiment 1,2,3 three kind of prescription is listed in table 2 after testing.
From table 2 column data as can be seen, the frictional behaviour of pressing embodiment 2 prescriptions is best, and embodiment 3 prescriptions take second place.From economic angle, the formulation cost of embodiment 3 is minimum, and the prescription of embodiment 2 takes second place.
Apparent hardness embodiment 1 is 115, and embodiment 2 is 108, and embodiment 3 is 105.Shock strength is all greater than 3.0kgfcm/cm
2
Table 1
| Title material | Each component concentration % | ||
| Embodiment 1 | Embodiment 2 | Embodiment 3 | |
| 5160 resins (cashew nut shell oil and cyanurotriamide modified resol) | ???30 | ???30 | ???28 |
| Acrylic carbon fibre | ???36 | ???26 | ???20 |
| The expansion iron powder | ???9 | ???15 | ???25 |
| Brass powder | ???2 | ???4 | ???2 |
| Graphous graphite powder | ???5 | ???5 | ???15 |
| Zinic stearas | ???1 | ???1 | ???1 |
| Process white | ???16 | ???18 | ???10 |
| Molybdenumdisulphide | ???1 | ???1 | ???1 |
Table 2: frictional behaviour contrast table
| Temperature embodiment μ v | ????????100℃ | ???????150℃ | ???????200℃ | ??????250℃ | |||||||
| ??μ | ??v | ??μ | ??v | ??μ | ??v | ??μ | ??v | ||||
| Embodiment 1 | ??0.38 | ??0.04 | ??0.33 | ??0.05 | ??0.3 | ??0.07 | ??0.25 | ??0.38 | |||
| Embodiment 2 | ??0.29 | ??0.09 | ??0.29 | ??0.21 | ??0.37 | ??0.26 | ??0.34 | ??0.38 | |||
| Embodiment 3 | ??0.28 | ??0.21 | ??0.31 | ??0.14 | ??0.32 | ??0.51 | ??0.32 | ??0.47 | |||
Annotate: the μ frictional coefficient
V wear rate (10
-7Cm
3/ Nm)
Claims (4)
1, a kind of automobile steel synchro converter ring carbon fiber friction material, it is characterized in that being mixed with by weight by following component, 20～40 parts of acrylic carbon fibre strongtheners, 26～32 parts of cashew nut shell oil and cyanurotriamide modified phenolic resin adhesives, 9～25 parts of frictional property regulator expansion iron powders, 2～4 parts of brass powders, 5～15 parts of graphous graphite powders, 0.5～1.5 part of Zinic stearas, 10～20 parts of process whites, 0.5～1.5 part of molybdenumdisulphide.
2, friction materials as claimed in claim 1, it is characterized in that by following component formulated by weight, 20～26 parts of acrylic carbon fibre strongtheners, 28～30 parts of cashew nut shell oil and cyanurotriamide modified phenolic resin adhesives, 15～25 parts of frictional property regulator expansion iron powders, 2～4 parts of brass powders, 5～15 parts of graphous graphite powders, 1 part of Zinic stearas, 10～18 parts of process whites, 1 part of molybdenumdisulphide.
3, the compound method of claim 1 or 2 described friction materialss is characterized in that being undertaken by following steps in sequence:
(1) in the proportion of composing scope, takes by weighing various raw materials, mix;
(2) with the resulting compound hot-die of step (1) compressing tablet, hot pressing pressure 15MPa, 160 ℃ of temperature, the compressing tablet time determines according to friction plate thickness, 1.5～2 minutes clamping times of every 1mm thickness;
(3) with the resulting compressing tablet of step (2), be heating and curing, curing process is: heated up 1 hour to 100 ℃ from room temperature, heated up then 1 hour to 120 ℃, heated up again 1 hour to 140 ℃, and, be warmed up to 160 ℃ again 140 ℃ of insulations 2 hours, after 8 hours, reduce to room temperature 160 ℃ of insulations, come out of the stove with stove;
(4) the sheet material grinding extrados that is cured, and the cleaning extrados promptly makes automobile steel synchro converter ring carbon fiber friction material.
4, the usage of the described automobile steel of claim 1 synchro converter ring carbon fiber friction material is characterized in that being undertaken by following step:
(1) surface treatment: the synchro converter ring intrados carries out pickling degreasing, sand papering is used in the back that dewaters, eliminates rust, and the grinding of friction plate extrados is cleaned its surperficial abrasive dust with ethanol then;
(2) gluing: automobile brake sheet glue---the Harbin BC-1 tackiness agent that adopts Harbin City's Harbin Fine Chemical Works to produce, be applied to friction plate extrados surface and synchro converter ring inner arc surface, brush first pass glue with bristle, room temperature hung 30 minutes for 25 ℃, be coated with glue again second time, hung 12 hours, close up pressurization then, pressure 0.5～0.8MPa, 5 hours clamping times; Or roller coat gluing one time, place 80 ℃ of following preheatings 30～40 minutes then, close up pressurization while hot, pressure 0.5～0.8MPa, 1 minute clamping time;
(3) solidify and release: the synchro converter ring that pressing is had a carbon fiber friction plate is 180 ℃ of isothermal curings 1～2 hour, hangs release after the room temperature with stove then;
(4) car or mill glue surperficial the getting final product of automobile steel synchro converter ring inner arc of friction plate.