CN1569999A - Silicon resin or fluororesin curtain wall slurry - Google Patents
Silicon resin or fluororesin curtain wall slurry Download PDFInfo
- Publication number
- CN1569999A CN1569999A CN 200410022418 CN200410022418A CN1569999A CN 1569999 A CN1569999 A CN 1569999A CN 200410022418 CN200410022418 CN 200410022418 CN 200410022418 A CN200410022418 A CN 200410022418A CN 1569999 A CN1569999 A CN 1569999A
- Authority
- CN
- China
- Prior art keywords
- curtain wall
- wall slurry
- acrylic acid
- fluoro
- resin curtain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a silicon resin curtain wall slurry or fluoro-resin curtain wall slurry suitable for coating internal and external walls, which comprises (by weigh portion) crylic acid emulsion 40-60, pigment 18.8-38.0, auxiliary agent 1.9-3.9, film forming adjuvant 2.5-4.5, deflocculating agent 8.5-14.0.
Description
Technical field
The present invention relates to a kind of material of construction, particularly a kind of silicone resin curtain wall slurry or fluoro-resin curtain wall slurry of smearing interior exterior wall that be applicable to.
Background technology
For the decoration of building surface, the general at present material of construction such as stone material, sheet material, pottery, timber that adopt.Cost height such as stone material, sheet metal such as aluminium sheet, construction is difficult, and appearance luster is single, adopts timber then to be subject to the environmental protection factor, deficiency in economic performance, and wastes such as later stage transformation or repairing renovation are big, constructional difficulties.Existing curtain wall generally adopts aluminium sheet simultaneously, material therefor energy consumption height, and Mineral resources consumption is big, and production process is seriously polluted, the construction and installation complexity, the dismounting difficulty is big.Chinese patent discloses " a kind of Weak solvent composite paint with aluminum facade effect " (CN1408787A) and corresponding investment precoat (as CN1408779A).The disposable slurry of directly smearing that can reach imitative stone material, imitative minute surface, imitative aluminium sheet and imitative wood grain effect is not arranged in the disclosed technical publications as yet.
Summary of the invention
Purpose of the present invention can be directly used in the curtain wall slurry that building surface is decorated for a kind of, and this curtain wall slurry can have metallic luster or stone material or timber and all kinds of curtain wall decoration effect, and tough and tensile lasting.Strong adhesion has excellent water tolerance, alkali resistance and self-cleaning function etc., and the finishing of wall face is economical and practical in being widely used in.
Concrete technical scheme of the present invention is as follows:
A kind of silicon or fluoro-resin curtain wall slurry is characterized in that following constituent and weight percent composition:
Acrylic acid emulsion 40.0～60
Pigment 18.0～38.0
Auxiliary agent 1.9-3.9
Film coalescence aid 2.5-4.5
Thinner 8.5-14.0
Auxiliary agent of the present invention is dispersion agent or defoamer or thickening material or dispersion agent, defoamer and mixtures of thickening agents.Wherein: auxiliary agent is dispersion agent RM-1124, defoamer NXZ, thickening material RM-8W.
Thinner of the present invention is a cleaning water.
Acrylic acid emulsion of the present invention is acrylic acid or silicon modification acrylic acid or fluorine modification acrylic acid.
Film coalescence aid of the present invention is a propylene glycol.
Pigment of the present invention is titanium dioxide or metal oxide pigment or silver powder or its combination.
Curtain wall slurry of the present invention can have metallic luster or stone material or timber and all kinds of curtain wall decoration effect, and tough and tensile lasting.Strong adhesion has excellent water tolerance, alkali resistance and self-cleaning function etc., and the finishing of wall face is economical and practical in being widely used in.
Embodiment
Embodiment 1
A kind of silicon or fluoro-resin curtain wall slurry is characterized in that following constituent and weight percent composition:
Acrylic acid emulsion 40.0
Pigment 38.0
Auxiliary agent 3.9
Film coalescence aid 4.5
Thinner 13.6
Auxiliary agent of the present invention is dispersion agent or defoamer.Wherein: dispersion agent RM-1124, defoamer NXZ.Described thinner is a cleaning water.Described acrylic acid emulsion is a silicon modification acrylic acid.Described film coalescence aid is a propylene glycol.Described pigment is titanium dioxide.
Embodiment 2
A kind of silicon or fluoro-resin curtain wall slurry is characterized in that following constituent and weight percent composition:
Acrylic acid emulsion 60
Pigment 25.6
Auxiliary agent 1.9
Film coalescence aid 2.5
Thinner 10.0
Auxiliary agent of the present invention is dispersion agent, defoamer and mixtures of thickening agents.Described thinner is a cleaning water.Described acrylic acid emulsion is a fluorine modification acrylic acid.Described film coalescence aid is a propylene glycol.Described pigment is the composition of titanium dioxide, metal oxide pigment and silver powder.
Embodiment 3
A kind of silicon or fluoro-resin curtain wall slurry is characterized in that following constituent and weight percent composition:
Acrylic acid emulsion 50
Pigment 34.0
Auxiliary agent 3.0
Film coalescence aid 4.5
Thinner 8.5
Auxiliary agent of the present invention is a thickening material.Described thinner is a cleaning water.Described acrylic acid emulsion is a silicon modification acrylic acid.Described film coalescence aid is a propylene glycol.Described pigment is titanium dioxide.
Embodiment 4
The present invention mainly utilizes organosilicon crylic acid latex in the prescription, titanium dioxide, auxiliary agent, film coalescence aid etc., and the building surface after handling through the building special putty is carried out application, makes building surface reach the curtain wall decoration effect.
The present invention after testing, main quality and technical index is as follows:
Interventions Requested standard-required (acceptable end product) measured result
Time of drying, h≤2 are less than 1
Contrast ratio (white and light color) 〉=0.93 0.97
Water tolerance (168h) is no abnormal
Water tolerance (48h) is no abnormal
Abrasion resistance, inferior 〉=1000 are greater than 3000
Efflorescence ,≤1 grade of non-foaming, 1 grade of variable color, no efflorescence
Variable color ,≤2 grades do not peel off, flawless
Contamination resistance (white or light color), %≤10 3
The no abnormal cohesive strength of coating temperature-change resistance (10 circulations), Mpa
Standard＞0.5 1.20
Immersion back＞0.3 1.20
Embodiment 5
Preparation process of the present invention is as follows:
According to proportioning, after each component weighed, mix, it is even to carry out high-speed stirring through stirrer or dispersion machine, promptly obtains goods of the present invention.
Concrete construction of the present invention is as follows:
According to the construction proportioning dilution of slurry of the present invention and thinner (as cleaning water) 2.5～3: 1, look suitably regulating pondage of slurry viscosity, dilution after-filtration 200 mesh sieves spray with spray gun.Can be on metope repeatedly spraying, should thorough drying after each spraying, and carry out corresponding surface finish and handle, to coatingsurface evenly, gloss.
Claims (6)
1, a kind of silicon or fluoro-resin curtain wall slurry is characterized in that following constituent and weight percent composition:
Acrylic acid emulsion 40.0～60
Pigment 18.0～38.0
Auxiliary agent 1.9-3.9
Film coalescence aid 2.5-4.5
Thinner 8.5-14.0
2, a kind of silicon according to claim 1 or fluoro-resin curtain wall slurry is characterized in that: described auxiliary agent is dispersion agent or defoamer or thickening material or dispersion agent, defoamer and mixtures of thickening agents.
3, a kind of silicone resin curtain wall slurry according to claim 1, it is characterized in that: described thinner is a cleaning water.
4, a kind of silicon according to claim 1 or fluoro-resin curtain wall slurry is characterized in that: described acrylic acid emulsion is acrylic acid or silicon modification acrylic acid or fluorine modification acrylic acid.
5, a kind of silicon according to claim 1 or fluoro-resin curtain wall slurry, it is characterized in that: described film coalescence aid is a propylene glycol.
6, a kind of silicon according to claim 1 or fluoro-resin curtain wall slurry is characterized in that: described pigment is titanium dioxide or metal oxide pigment or silver powder or its combination.