CN1562622A - Method for fabricating composite body of optical glasses applied in polarized light - Google Patents
Method for fabricating composite body of optical glasses applied in polarized light Download PDFInfo
- Publication number
- CN1562622A CN1562622A CN 200410030780 CN200410030780A CN1562622A CN 1562622 A CN1562622 A CN 1562622A CN 200410030780 CN200410030780 CN 200410030780 CN 200410030780 A CN200410030780 A CN 200410030780A CN 1562622 A CN1562622 A CN 1562622A
- Authority
- CN
- China
- Prior art keywords
- optical lens
- polarization optical
- processing method
- lens complex
- complex according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A polarizing optical lens assembly is prepared through shaping the polarizer, preparing adhesive, adhering thermal sodidifying twice in 8 temp zones, ultrasonic cleaning sequentially in 18 bathes, hardening, strengthening, and vacuum film-plating. It features that said polarized is between two transparent optical lenses, and has high polarizing effect to filter out ultraviolet ray and strong light.
Description
Technical field
The present invention relates to a kind of processing method of polarization optical lens complex, specially refer to a kind of processing method that can process different number of degrees polarization optical lens complexs of utilizing mould shape, bonding, curing, reinforcement, cleaning, vacuum coating, belong to the optical mirror slip manufacture field.
Background technology
We know in the light that comes out in the sun has: mainly contain three kinds of visible rays, infrared ray, ultraviolet rays, UVA in its middle-ultraviolet lamp, UVB, UVC are harmful light, if tan by the sun the damage that can cause health for a long time, UVB has a strong impact on eyesight, can burn casting skin, and most canthus can absorb in the middle of this kind UVB light with skin, the eyes of ultraviolet ray meeting to human body ... .... etc., cause serious injury, so must block this kind light source.
Overcome the above problems, best bet utilizes polarized lenses exactly, allow the light of the irregular reference in the natural daylight, dazzling light and object reverberation, can effectively block, there are 300,000 straight line molecules align bodies that are invisible to the naked eye the inside of Polarizer, and be arranged in same direction, allow the light polarization obtain soft light, utilize Polarizer to see that object can more clear distinctness, otherwise when sunshine touches the water surface, ground, during plane reflection, because of so the relation difficulty of the polarisation light of straight line vibrations is seen object clearly, utilize Polarizer to filter the light source characteristic of straight line vibrations, and utilize the horizontal line of molecules align, and readjust light-absorbing direction, eliminate dry and astringent, do not know and dazzling light.
General at present coloured plate on the market has only through dyeing course, with its plate dyeing deepening, and because the dazzle in the sunshine, the object reverberation, high light is omnipresent, as vehicle glass, ripples, snowfield, when causing from the high light of sun direct projection, the dazzle on road surface disturbs human eye eyesight, make the people can't see object clearly, general coloured plate but can't be eliminated these irritating light fully, in addition since present polarization optical lens owing to be subjected to the restriction of manufacture method, the difference " Qu Guangdu " that can't satisfy myopia or " presbyopia " etc. has personalized crowd's demand, therefore demand developing a kind of new manufacture method urgently, to satisfy the needs in market.
Summary of the invention
The object of the present invention is to provide a kind of processing method of polarization optical lens complex, make the optical mirror slip of making in this way have good polarisation effect, ultraviolet ray and high light are had good filter effect.
The present invention also aims to by a kind of processing method of polarization optical lens complex is provided, so that this method can adapt to the polarization optical lens complex of processing the various different number of degrees, make these eyeglass complexs not only have the polarisation effect, also have the function of normal eyeglass.
The objective of the invention is to realize according to following technical scheme.
A kind of processing method of polarization optical lens complex comprises being arranged on optical mirror slip middle polaroid typing, the mixing of bonding raw material, the curing of polarization optical lens complex, cleaning, plated film.
Step 1, the typing of above-mentioned polaroid also further comprise:
Typing polaroid after handling is put into the cushion rubber of mould holding, between polaroid and the transparent optical eyeglass that is arranged on both sides, pour into the bright binding material of full impregnated;
Step 2, adhesives mix and further comprise;
In polymethyl methacrylate, add initator " IPP ", and mix until no bubble with vacuum mixer;
Step 3, pour into glass mold;
Step 4, curing for the first time;
To put into curing oven through the resin polarized ophthalmic lenses after the above step process heats;
Step 5, curing for the second time;
Eyeglass after solidifying is for the first time put into curing oven heats and carries out curing second time;
Step 6, ultrasonic wave clean;
Ultrasonic wave with 18 grooves cleans line, pure water 14M Ω;
Step 7, stiffened are handled;
Step 8, intensive treatment;
Eyeglass after the stiffened processing is put into the reinforcement stove to be strengthened;
Step 9, vacuum coating;
The eyeglass that intensive treatment is crossed is put into vacuum coating equipment, with pure silicon or pure titanium at the both sides of eyeglass plated film; Carry out the processing of anti-reflection film, waterproof membrane, radiation prevention film, conducting film.
The present invention can also realize with following technical scheme.
The described the best with the heater typing of above-mentioned steps 1 temperature of heating is 75 °~80 °.
Above-mentioned steps 1 described mould is formed by further being set at the concavo-convex mould of adjusting according to various different curvature that is arranged at the polaroid both sides.
" the required optimum temperature of 0.0000083% vacuum mixer that IPP accounts for total capacity is 50 degree to the described initator of step 2;
Above-mentioned steps 4 described curing ovens are heated and are made as warm areas different more than and corresponding different hardening times.
Above-mentioned steps 6 described ultrasonic waves clean and are made as an above ultrasonic cleaner.
Above-mentioned steps 7 described stiffeneds are handled and are adopted silicon bronze resin hardening liquid coating, infiltrate through the substrate top layer, make it reach 7-8H.
The optimum temperature of above-mentioned steps 8 described intensive treatment is 105 degree, and the time is 2 hours.
The method that above-mentioned steps 9 vacuum coatings can be adopted is electron gun, ion gun, looks control sputter vacuum coating that every face is at least more than 1 layer.
The material that above-mentioned radiation prevention film adopts is a Yangization Ying tin.
The present invention compared with prior art has remarkable advantages and useful effect.
Polarization optical lens complex by above method processing, the shortcoming that can only produce the zero diopter polaroid that the processing method of inciting somebody to action exists changed existing polarization optical lens complex owing to can satisfy and produce the polarization optical lens complex with various different number of degrees; Simultaneously because polaroid is arranged on the centre of two-layer transparent optical eyeglass, thereby make it more wear-resisting,, can increase anti-reflection film, waterproof membrane, radiation prevention film, conducting film as required simultaneously on the surface of transparent material.Make it have more function.
Description of drawings
Fig. 1 is a processing method flow chart of the present invention;
Fig. 2 is the structural representation with the polarization optical lens complex of this method processing;
Fig. 3 is provided with tables of data for the distribution and the parameter of this method ultrasonic cleaner;
Fig. 4 is that the recessed A mould of this method mould therefor and the parameter of protruding B mould are provided with tables of data.
The specific embodiment
The present invention is described in further detail below in conjunction with accompanying drawing and specific embodiment:
See also shown in Figure 2ly, be the structure chart of the polarization optical lens complex that processes with this method, as can be seen from the figure, the both sides of polaroid 2 are learned eyeglass 1 and 3 composition polarization optical lens complexs by CAB adhesive linkage 4 and 5 with full impregnated Mingguang City.
See also shown in Figure 1ly, be the flow chart of the polarization optical lens complex that processes with this method, the as can be seen from the figure main technique flow process of this processing method, the processing method of above-mentioned a kind of polarization optical lens complex is decomposed in detail,
Step 1, typing:
1.1, polaroid is struck out required all size;
1.2, finalize the design with heater; (heating-up temperature 75-80 degree: 30 seconds-60 seconds heat time heating time);
1.3, surface treatment; Handle with methyl alcohol with fine sandpaper hacking, polishing back;
1.4, the typing polaroid after will handling puts into the cushion rubber of mould holding, at polaroid and be arranged on the bright binding material of perfusion full impregnated between the transparent optical eyeglass of both sides.
Above-mentioned mould according to the luminosity of eyeglass required and to the curved different pieces of information that is provided with of the base of the recessed A mould of mould and protruding B mould, detailed data sees also the recessed A mould that Figure 4 shows that this method mould therefor and the parameter of protruding B mould is provided with tables of data.See also shown in Figure 2ly, the position of above-mentioned recessed A mould is arranged on the inboard of transparent glasses lens 3, and the position of above-mentioned protruding B mould is arranged on the outside of transparent glasses lens 1.Described polarization optical lens complex is arranged between recessed A mould and the protruding B mould.
Step 2, bonding raw material mix;
Adopting exposure rate is 1.56 Merlon NC-15 (97.20) or the polymethyl methacrylate " PMMA " that adopts exposure rate 1.499, add initator " IPP " (0.0000083%), mixed in 4 hours with 50 ℃ of temperature vacuum mixers, be fed into during to no bubble and put the convex surface typing well, locate emerging partially, the glass mold of sandwich of layers.
Step 3, pour into glass mold;
Step 4, curing for the first time;
To put into curing oven through the resin polarized ophthalmic lenses after the above step process and heat, all eyeglasses are through the processing of heating of 8 humidity provinces; Heating temperature curve is by microcomputerized control.Be 18.5 hours hardening time, and eyeglass is taken out in the die sinking of lowering the temperature then.Wherein are respectively described 8 humidity provinces of step 4 and corresponding hardening time:
Be 0.5 hour the hardening time during room temperature~45 °;
Be 3.5 hours the hardening time of 45 ° of constant temperature;
Be 1 hour 45 °~46 ° hardening time;
Be 2.5 hours 46 °~49 ° hardening time;
Be 6.5 hours 49 °~69 ° hardening time;
Be 3 hours 69 °~80 ° hardening time;
Be 1 hour 80 °~70 ° hardening time;
Be 0.5 hour 70 °~70 ° hardening time.
Step 5, curing for the second time;
Eyeglass after solidifying is for the first time put into curing oven heat and carry out solidifying second time, be 2 hours hardening time, and solidification temperature is 117 to spend.
Step 6, ultrasonic wave clean;
Ultrasonic wave with 18 grooves cleans line, pure water 14M Ω, and concrete data see also and Figure 3 shows that ultrasonic wave cleans the distribution table that cleans line temperature and solution with the ultrasonic wave of 18 grooves.
Step 7, stiffened are handled;
With silicon bronze resin hardening liquid coating, infiltrate through the substrate top layer, make it reach 7-8H.
Step 8, intensive treatment;
Eyeglass after the stiffened processing is put into the reinforcement stove, and intensive treatment is 2 hours under temperature 105 degree situations.
Step 9, vacuum coating;
The eyeglass that intensive treatment is crossed is put into vacuum coating equipment, and by electron gun, ion gun sputter, oxygen, argon gas are formed in both sides that silica, titanium dioxide sputters at eyeglass totally 14 layers of electron gun plated film with pure silicon and pure titanium,
Step 10, carry out the processing of anti-reflection film, waterproof membrane, radiation prevention film, conducting film; Every face is respectively 4 layers, 2 totally 8 layers, and every stove vacuumizing time is 55 minutes, and the employing method is electron gun, ion gun, look control sputter, about about the 96 secondary purple membranes of every stove, gold film, blue film, partial veil; Change color and luster with naked eyes and rete instrument oneself movingly thickness control.
Wherein the described temperature of heating with the heater typing of step 1 is 75 °~80 °.
Wherein are respectively described 8 humidity provinces of step 4 and corresponding hardening time:
Be 0.5 hour the hardening time during room temperature~45 °;
Be 3.5 hours the hardening time of 45 ° of constant temperature;
Be 1 hour 45 °~46 ° hardening time;
Be 2.5 hours 46 °~49 ° hardening time;
Be 6.5 hours 49 °~69 ° hardening time;
Be 3 hours 69 °~80 ° hardening time;
Be 1 hour 80 °~70 ° hardening time;
Be 0.5 hour 70 °~70 ° hardening time.
The material that aforesaid radiation prevention film adopts is a Yangization Ying tin.
It should be noted that at last: above embodiment only in order to the explanation the present invention and and unrestricted technical scheme described in the invention; Therefore, although this specification has been described in detail the present invention with reference to each above-mentioned embodiment,, those of ordinary skill in the art should be appreciated that still and can make amendment or be equal to replacement the present invention; And all do not break away from the technical scheme and the improvement thereof of the spirit and scope of the present invention, and it all should be encompassed in the middle of the claim scope of the present invention.
Claims (10)
1, a kind of processing method of polarization optical lens complex comprises being arranged on optical mirror slip middle polaroid typing, the mixing of bonding raw material, the curing of polarization optical lens complex, cleaning, plated film; It is characterized in that:
Step 1, the typing of above-mentioned polaroid also further comprise:
Typing polaroid after handling is put into the cushion rubber of mould holding, between polaroid and the transparent optical eyeglass that is arranged on both sides, pour into the bright binding material of full impregnated;
Step 2, adhesives mix and also comprise;
In polymethyl methacrylate, add initator " IPP ", and mix until no bubble with vacuum mixer;
Step 3, above-mentioned adhesives is poured in the glass mold;
Step 4, curing for the first time;
To put into curing oven through the resin polarized ophthalmic lenses after the above step process heats;
Step 5, curing for the second time;
Eyeglass after solidifying is for the first time put into curing oven heats and carries out curing second time;
Step 6, ultrasonic wave clean;
Ultrasonic wave with 18 grooves cleans line, pure water 10-14M Ω;
Step 7, stiffened are handled;
Step 8, intensive treatment;
Eyeglass after the stiffened processing is put into the reinforcement stove to be strengthened;
Step 9, vacuum coating;
The eyeglass that intensive treatment is crossed is put into vacuum coating equipment, use pure silicon and pure titanium at the both sides of eyeglass plated film;
Step 10, carry out the processing of anti-reflection film, waterproof membrane, radiation prevention film, conducting film.
2, the processing method of a kind of polarization optical lens complex according to claim 1 is characterized in that: wherein the described the best with heater typing of step 1 temperature of heating is 75 °~80 °.
3, the processing method of a kind of polarization optical lens complex according to claim 1 is characterized in that: wherein the described mould of step 1 is formed by further being set at punch that is arranged at the polaroid both sides and the die adjusted according to various different curvature.
4, the processing method of a kind of polarization optical lens complex according to claim 1 is characterized in that: " the required optimum temperature of 0.0000083% vacuum mixer that IPP accounts for total capacity is 50 degree to the described initator of step 2.
5, the processing method of a kind of polarization optical lens complex according to claim 1 is characterized in that: wherein the described curing oven of step 4 is heated and is made as warm areas different more than and corresponding different hardening times.
6, the processing method of a kind of polarization optical lens complex according to claim 1 is characterized in that: wherein the described ultrasonic wave of step 6 cleans and is made as an above ultrasonic cleaner.
7, the processing method of a kind of polarization optical lens complex according to claim 1 is characterized in that: wherein the described stiffened of step 7 is handled and is adopted silicon bronze resin hardening liquid coating, infiltrates through the substrate top layer, makes it reach 7-8H.
8, the processing method of a kind of polarization optical lens complex according to claim 1 is characterized in that: wherein the optimum temperature of the described intensive treatment of step 8 is 105 degree, and the time is 2 hours.
9, the processing method of a kind of polarization optical lens complex according to claim 1, it is characterized in that: wherein step 10 carry out method that the processing of anti-reflection film, waterproof membrane, radiation prevention film, conducting film adopts can be for electron gun, ion gun, look control sputter vacuum coating, every is more than 1 layer.
10, the processing method of a kind of polarization optical lens complex according to claim 1 is characterized in that: the material that described radiation prevention film adopts is a Yangization Ying tin.