CN1562548A - Micro melting soldering method of argon-shielded tungsten arc welding for thick plate of red copper without warming-up - Google Patents
Micro melting soldering method of argon-shielded tungsten arc welding for thick plate of red copper without warming-up Download PDFInfo
- Publication number
- CN1562548A CN1562548A CN 200410013687 CN200410013687A CN1562548A CN 1562548 A CN1562548 A CN 1562548A CN 200410013687 CN200410013687 CN 200410013687 CN 200410013687 A CN200410013687 A CN 200410013687A CN 1562548 A CN1562548 A CN 1562548A
- Authority
- CN
- China
- Prior art keywords
- welding
- groove
- red copper
- welding current
- tig
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A slight-smelting TIG torch-brazing method for thick red copper plate without preheating includes such steps as using electric arc to heating the bottom of groove while filling the welding wire until the height of the filled seam is 1/3 of thickness of red copper plate, heating to resmelt the filled metal while blowing the molten metal up to the top of groove for slightly smelting it, and fastly feeding the welding wire to both slopes of groove while TIG arc welding.
Description
Technical field:
The present invention relates to the improvement of thick-wall red copper plate welding method.
Background technology:
Red copper plasticity and intensity between 400-700 ℃ obviously descend, still there are some problems in the melting of red copper (as gas welding, manual metal-arc welding, TIG weldering, MIG weldering, electron beam welding etc.), soldering methods such as (gas brazing, TIG solderings etc.), as fusion welding by means of gas: relatively be suitable for the repairing of sheet copper, copper spare or the welding of inessential structure.In to the welding of thick-wall red copper spare, there are many problems: (1) preheat temperature height (600-700 ℃), and welding process should be carried out continuously.Heat time heating time is long, and the thermal capacity of input is big, and welding heat affected zone is bigger, and tissue and performance variation are bigger, and workman's condition of work is very abominable.(2) the protection effect of gas welding is bad.Airborne reducibility gas is invaded weld seam, and oxide is reduced in the copper.The low-melting-point eutectic (Cu+Cu2o) that forms 1066 ℃ is distributed in crystal boundary, has increased the tendency of fire check.(3) appearance of weld is poor, and is yielding, be prone to defectives such as pore, incomplete fusion, crackle.Gas brazing: more commonly used in factory.Welding region will adopt higher temperature (650-750 ℃) evenly to add thermal weld on the technology, and heat time heating time is long.But also to guarantee carrying out continuously of welding process.Shortcoming is: the welding temperature height, and workman's condition of work is very abominable, and heating-up temperature is difficult during manual operations grasps, and welding needs many people operation simultaneously, to workman's specification requirement height; The thermal capacity of input is big, and welding heat affected zone is bigger, and microstructure and property changes greatly; Adopt solder flux, need postwelding to clean, strength of joint is lower.Manual electric arc welding: be a kind of welding method the most frequently used in the melting welding.But the subject matter in the red copper welding is the preheat temperature height, poor welding quality.(1) welding procedure complexity: weld preheating (500-600 ℃) temperature height, and to guarantee carrying out continuously of welding process.The welding region high-temperature residence time is long, and input thermal capacity is big, and workman's condition of work is very abominable.Simultaneously big, tissue of heat affected area scope and joint performance change greatly.(2) the alloying element evaporation is serious: weld seam is hydrogeneous, oxygen amount height, and the zinc evaporation is serious, occurs defectives such as pore, crackle easily.(3) welding quality instability, appearance of weld is poor, and strength of joint is low.TIG melting welding: TIG melting welding is a kind of welding method commonly used in the red copper welding.Can not pre-thermal weld to the thin plate red copper part below the 4mm.But in the welding of the red copper part more than the 4mm, preheating (400-600 ℃) temperature height is still subject matter.Its shortcoming is embodied as: the thermal capacity of (1) input is big, and workman's condition of work is very abominable.And the heat affected area scope is big, and tissue and joint performance change greatly, and strength of joint is impaired serious, and production efficiency is low.(2) be subjected to the influence that welding current is big, speed of welding is fast, the diffusible hydrogen that dissolves in the molten bath difficulty overflows, and forms pore, crackle, incomplete fusion, defective such as lack of penetration easily.As: defectives such as pore and fire check appear in joint easily when filling T2 welding wire cooperation solder flux 301.Defectives such as crackle and pore appear in joint easily when filler wire 201.The TIG soldering: the TIG soldering set has that heat is concentrated, heat temperature raising speed is fast, argon gas can have certain cooling effect and the TIG soldering peculiar to nearly seam district " the negative electrode atomizing " phenomenon, can be broken and the characteristics such as oxide-film on cleaning brazed seam surface.For guaranteeing good soldered fitting (being that mother metal does not melt), electric arc TIG soldering requires to adopt lower heat input, should adopt less welding current in the welding process.But its strength of joint is low, weld hardness is high, plasticity, poor toughness.Advantages such as electron beam welding: electron beam welding has energy density and penetration capacity is very strong, does not generally add filler wire, and cooling rate is fast, crystal grain is thin, the heat affected area is little.Therefore thick-wall red copper being done the penetrability welding has an enormous advantage.But equally many problems can appear: because electron beam impacts splashing of deposite metal taken place when welding as thick-wall red copper, cause appearance of weld to degenerate.Especially when thick-wall red copper pipe welds, because its energy density is big especially.Test specimen is as easy as rolling off a log to be burnt, and the copper current drop down, and can not form weld seam.Electron beam welding apparatus expensive, welding requirements are carried out in a vacuum, and working environment is subjected to the restriction of vacuum chamber size.MIG weldering: the MIG soldering set has wide accommodation, the production efficiency height, and welding deformation is little, and welding process such as easily is automated at advantage.Be in the welding, the Perfected process of thick-wall red copper.But 600~700 ℃ of necessary preheatings are very sensitive to oxygen element, and when the copper of welding deoxidation deficiency, the pore of weld seam is more, and intensity is lower.Not strong to the plate sheet welding directive significance simultaneously, the poor stability in welding molten bath during thin plate, occur easily the molten bath overheated, problems of welded quality such as stay.
Summary of the invention:
The purpose of this invention is to provide a kind of thick red copper plate no-preheating TIG-micro-melting brazing method, it has welding to thick red copper plate without preheating, and welding operation is simple, and appearance of weld is attractive in appearance, the characteristics that welding quality is high.Method of the present invention is achieved in that at first leaves the joint of two thick copper plates respectively 45 ° groove, weld by three phases then, phase I adopts the TIG arc brazing to fill weld seam, bottom with electric arc heated mother metal groove, filler wire under non-oscillatory situation, the height of filling weld seam is 1/3 of a copper plate thickness, and speed of welding is 2.5-3.5mm/s, and welding current is 120-140A; Second stage heats the filling metal of remelting phase I under the situation of not sealing weld silk, and with electric arc molten metal liquid is prolonged on the side direction of groove and provoke, until the groove top, as seen the time that stops 0.5-1s have small fusing herein, electric arc moves down again, make this side form little crucible zone that solder mixes with mother metal, use the same method and make corresponding opposite side groove form little crucible zone, push ahead so repeatedly, all form little crucible zone until the whole piece weld seam, remelt speed is 2.5-3.5mm/s, and the remelting welding current is 150-170A; The quick filler wire of phase III utilization two point wire feed forms the micro-melting brazing weld seam, and speed of welding is 4-5mm/s, and welding current is 160-180A.Filler wire avoids little crucible zone of groove to have too much fusing and too much heat input that groove neighbouring mother metal crystal grain and mother metal crystal grain are had big difference fast, can clearly observe face of weld after welding finishes and present Pisces ripple shape.Filler wire of the present invention is that fusing point is a 600-800 ℃ of ternary alloy three-partalloy solder that contains Ag and P.Advantage of the present invention is: 1, can realize that with this method the thick red copper plate without preheating under the argon shield welds.2, face of weld need not specially treated, and simple to operate, joint is reliable.3, because welding temperature the end of than, generally below 1100~1200 ℃, can effectively reduce the thick degree of the width and the crystal grain of mother metal heat affected area.4, by the mother metal of fusing and the metallurgical reaction of solder on the interface of fusing, can form solid solution, play the be connected effect of base metals aspect mechanical property and the chemical composition with weld metal with certain width and thickness A g, P.5, the weld appearance shaping is attractive in appearance, does not have tangible weld defect.6, the reinforcement of weld seam height can effectively be saved wlding in the reinforcement height of melting welding.7, back-welding shape is good, is out of shape little.The index that application this method welding thick red copper plate material can reach is: joint tensile strength: 〉=95%, and angle of bend: 100 °, percentage elongation 〉=20%.
Description of drawings:
Fig. 1 is existing melting welding weld interface schematic diagram, and Fig. 2 is existing soldering weld interface schematic diagram, and Fig. 3 is little melting-soldering interface schematic diagram of the present invention, and 1 among Fig. 3 is thick red copper plate, the 2nd, and little crucible zone, the 3rd, filler wire.
The specific embodiment:
The specific embodiment one: the method for (referring to Fig. 3) present embodiment is achieved in that at first leaves the joint of two thick copper plates respectively 45 ° groove, weld by three phases then, phase I adopts the TIG arc brazing to fill weld seam, bottom with electric arc heated mother metal groove, filler wire under non-oscillatory situation, the height of filling weld seam is 1/3 of a copper plate thickness, and speed of welding is 2.5-3.5mm/S, and welding current is 120-140A; Second stage heats the filling metal of remelting phase I under the situation of not sealing weld silk, and with electric arc molten metal liquid is prolonged on the side direction of groove and provoke, until the groove top, as seen the time that stops 0.5-1s have small fusing herein, electric arc moves down again, make this side form little crucible zone that solder mixes with mother metal, use the same method and make corresponding opposite side groove form little crucible zone, push ahead so repeatedly, all form little crucible zone until the whole piece weld seam, remelt speed is 2.5-3.5mm/S, and the remelting welding current is 150-170A; The quick filler wire of phase III utilization two point wire feed forms the micro-melting brazing weld seam, and speed of welding is 4-5mm/s, and welding current is 160-180A.Filler wire avoids little crucible zone of groove to have too much fusing and too much heat input that groove neighbouring mother metal crystal grain and mother metal crystal grain are had big difference fast, can clearly observe face of weld after welding finishes and present Pisces ripple shape.Filler wire described in the present embodiment is that fusing point is a 600-800 ℃ of ternary alloy three-partalloy solder that contains Ag and P.
The specific embodiment two: the welding current of phase I is 131A in the present embodiment; The welding current of second stage is 160A; The welding current of phase III is 168A.Other process conditions and processing step are identical with the specific embodiment one.
Claims (3)
1, thick red copper plate no-preheating TIG-micro-melting brazing method, it is characterized in that at first the joint of two thick copper plates being left respectively 45 ° groove, weld by three phases then, phase I adopts the TIG arc brazing to fill weld seam, with the bottom of electric arc heated mother metal groove, filler wire under non-oscillatory situation, the height of filling weld seam is 1/3 of a copper plate thickness, speed of welding is 2.5-3.5mm/s, and welding current is 120-140A; Second stage heats the filling metal of remelting phase I under the situation of not sealing weld silk, and with electric arc molten metal liquid is prolonged on the side direction of groove and provoke, until the groove top, as seen the time that stops 0.5-1s have small fusing herein, electric arc moves down again, make this side form little crucible zone that solder mixes with mother metal, use the same method and make corresponding opposite side groove form little crucible zone, push ahead so repeatedly, all form little crucible zone until the whole piece weld seam, remelt speed is 2.5-3.5mm/s, and the remelting welding current is 150-170A; The quick filler wire of phase III utilization two point wire feed forms the micro-melting brazing weld seam, and speed of welding is 4-5mm/s, and welding current is 160-180A.
2, thick red copper plate no-preheating TIG according to claim 1-micro-melting brazing method is characterized in that described filler wire is that fusing point is a 600-800 ℃ of ternary alloy three-partalloy solder that contains Ag and P.
3, thick red copper plate no-preheating TIG according to claim 1-micro-melting brazing method, the welding current that it is characterized in that the phase I is 131A; The welding current of second stage is 160A; The welding current of phase III is 168A.