CN1559746A - 钢筋电渣压力焊专用焊剂 - Google Patents

钢筋电渣压力焊专用焊剂 Download PDF

Info

Publication number
CN1559746A
CN1559746A CNA2004100228902A CN200410022890A CN1559746A CN 1559746 A CN1559746 A CN 1559746A CN A2004100228902 A CNA2004100228902 A CN A2004100228902A CN 200410022890 A CN200410022890 A CN 200410022890A CN 1559746 A CN1559746 A CN 1559746A
Authority
CN
China
Prior art keywords
welding
flux
bar
steed
reinforced
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2004100228902A
Other languages
English (en)
Other versions
CN1270866C (zh
Inventor
唐东平
叶丽珠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YONGZHOU HALIN WELDING APPARATUS CO Ltd
Original Assignee
YONGZHOU HALIN WELDING APPARATUS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YONGZHOU HALIN WELDING APPARATUS CO Ltd filed Critical YONGZHOU HALIN WELDING APPARATUS CO Ltd
Priority to CN 200410022890 priority Critical patent/CN1270866C/zh
Publication of CN1559746A publication Critical patent/CN1559746A/zh
Application granted granted Critical
Publication of CN1270866C publication Critical patent/CN1270866C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明属于一种钢筋电渣压力焊的专用焊剂,解决了现有的HJ431焊剂起弧难,焊接工艺性能难以保证,焊接III级钢筋较困难等问题,具有焊接时起弧容易,电弧和电渣过程稳定,焊接接头力学性能优良等优点。本焊剂组成成分的重量百分比是:MnO20~24.5%,SiO2 35~40%,CaF2 5~10%,MgO 5~9%,CaO 5~8%,Al2O3 9~13%,TiO2 3~4.9%,FeO<3.5%。

Description

钢筋电渣压力焊专用焊剂
(一)技术领域:
本发明涉及一种钢筋电渣压力焊专用焊剂。
(二)背景技术:
目前,国内一般采用HJ431焊剂作为钢筋电渣压力焊的焊剂,焊接时具有起弧难,电弧稳定性差,电渣过程不稳定,用于III级钢筋焊接较困难等缺点。中国专利94115069.0号公开了一种钢筋电渣压力焊熔炼型专用焊剂,属中锰中氟型焊剂,但该配方中所需锰原料品位较高,氟和钛所占比例偏高,不利于低品位锰矿资源的开发利用和产品成本的降低,焊接时电弧过程中电压调整幅度过窄,容易熄弧,焊接质量难以保证。
(三)发明内容:
本发明旨在提供一种焊接工艺性能和焊接接头力学性能优良,施工方便,成本低,并可适用于III级钢筋的焊接的中锰中硅低氟型钢筋电渣压力焊专用焊剂。
本发明的焊剂组成成份的重量百分比是:MnO20~24.5%,SiO235~40%,CaF25~10%,MgO5~9%,CaO5~8%,Al2O39~13%,TiO23~4.9%,FeO<3.5%。
本发明具有以下几个明显优点:1、焊接时起弧容易,可利用钢筋本身起弧,不需引弧球;2、电弧过程和电渣过程稳定,电压调整幅度宽,电弧过程中电压调整幅度宽为35-45V;3、渣包成型好,脱渣容易,轻敲即可全部脱落,焊包大小适中,包正、圆滑、明亮,无粘连、咬边、气孔等缺陷;4、易于施工,可使用小功率焊机焊接较大直径的钢筋;5、焊接接头的力学性能好,符合国家标准。另外,本发明属于中锰中硅低氟渣系,本发明焊剂组成成份中MnO含量低于25%,可充分利用低品位的锰矿资源,所加TiO2含量较低,既能起到改善产品性能作用,又不至于增加产品成本。
(四)具体实施例:
实施例1:MnO 24.09%,SiO2 37.64%,CaF2 8.05%,MgO 6.68%,CaO 5.34%,Al2O3 10.36%,TiO2 4.73%,FeO 3.11%;
实施例2:MnO 20.76%,SiO2 38.29%,CaF2 7.53%,MgO 7.81%,CaO 6.86%,Al2O3 10.99%,TiO2 4.41%,FeO 3.25%;
实施例3:MnO 21.88%,SiO2 38.74%,CaF2 9.80%,MgO 7.51%,CaO 5.72%,Al2O3 9.38%,TiO2 4.04%,FeO 2.93%。
使用该焊剂,用BX-600型焊机,焊接φ14-φ32mm的钢筋,按下表所示规范进行电渣压力焊接。
钢筋直径(mm)   焊接电流(A)           焊接电压(V)      焊接通电时间(S)
电弧过程 电渣过程 电弧过程 电渣过程
  φ14   200-220 35-45 22-27     12     3
  φ18   250-300     15     5
  φ20   300-350     17     5
  φ25   400-450     21     6
  φ28   500-550     24     6
  φ32   500-550     28     8
按上述规定进行钢筋电渣压力焊焊接时,焊接接头成型良好,工艺性能及拉伸试验完全符合JGJ18-2003及DB43/T153的要求,是钢筋电渣压力焊的理想焊接材料。

Claims (1)

1、一种钢筋电渣压力焊专用焊剂,其特征是,该焊剂组成成份的重量百分比是:MnO 20~24.5%,SiO2 35~40%,CaF2 5~10%,MgO 5~9%,CaO 5~8%,Al2O3 9~13%,TiO2 3~4.9%,FeO<3.5%。
CN 200410022890 2004-02-08 2004-02-08 钢筋电渣压力焊专用焊剂 Expired - Fee Related CN1270866C (zh)