CN1557128A - Production method of vegetable stem made pot - Google Patents
Production method of vegetable stem made pot Download PDFInfo
- Publication number
- CN1557128A CN1557128A CNA2004100139665A CN200410013966A CN1557128A CN 1557128 A CN1557128 A CN 1557128A CN A2004100139665 A CNA2004100139665 A CN A2004100139665A CN 200410013966 A CN200410013966 A CN 200410013966A CN 1557128 A CN1557128 A CN 1557128A
- Authority
- CN
- China
- Prior art keywords
- straw
- alms bowl
- basin alms
- manufacturing according
- acid solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The plant stalk pot making process has simple apparatus used, less investment and low cost, and the plant stalk pot is used in cultivating and transplanting seedling and becomes fertilizer for the plant after degradation. The making process includes adopting plant stalk as main material, adding alkali solution to raise pH value to over 9, stocking for softening, crushing, adding acid solution to regulate pH to neutral, mixing with additive, molding, demolding, and drying. The weight ratio among plant stalk, alkali solution, acid solution and additive is 1 to 0.2-0.6 to 0.06-0.2 to 0.02-0.08. The present invention is suitable for cultivating seedling and pot cultivation.
Description
Technical field:
The present invention relates to a kind of manufacture method of plant cultivation pot alms bowl, be adapted to the training of container nursery and basin pot culture, belong to the process that stalk resource utilization and plant cultivation pot alms bowl are made.
Background technology:
Straw is as a kind of regenerated resources, the annual whole nation only agricultural crop straw generation reaches 600,000,000 tons, in the age of rural energy resources short supply, stalk is utilized consumption mainly as fuel, yet, in recent years along with the rural novel energy, as: application such as biogas, coal gas, natural gas, the raising of agricultural crop straw output in addition, stalk occur excessive, and to burn or arbitrarily abandon the phenomenon that environment such as giving air, water body, rural area pollute more and more serious because of stalk the edge of a field.Therefore, it is very important to seek new technology, new way that stalk disposes.
In cultivation of plants methods such as vegetables, cotton, forest, flowers, container nursery has that root system is complete, and the four seasons can transplant, survival rate height, series of advantages such as strong stress resistance.It is significant to seek to satisfy new material and the new technology of making the container for plant growth requirement.
In floriculture, particularly in the showy flowers of herbaceous plants cultivation, can use repeatedly or the basin alms bowl of regeneration, not only cost-saved, and can reduce because of broken basin alms bowl and dispose expense or the environmental pressure that causes.
Chinese patent publication number (CN101816C) has been introduced a kind of manufacture method of straw container for plant growth, this method comprises that with the comminuted plants stalk be raw material, drying, pulverizing, classification, heating extrusion forming step is characterized by in the mould, and the grinding particle size of straw is between the 0.4-0.5mm when hot-forming, raw material water content＜15%, the heating-up temperature of mould is 170 °-210 ℃, and pressure is 10-15kg/cm, mould tapering 1: 1.8-1: 2.4.The shortcoming that exists is: 1, the smashing fineness requirement of stalk requirement is high, power consumption is big; 2, need heating in the container formation process, need firing equipment and power consumption; 3, do not consider that container nursery is transplanted after, to the influence of seedling growth, particularly do not consider the influence that chamber wall interts to the root of plant.
Chinese patent publication number (CN1087587C) has been introduced container for plant growth and method and specific purpose tool thereof, this patent provides a kind of corn container for plant growth and method and has transplanted seedlings technology and special instrument, its container is made up of with farmyard manure agricultural crop straw such as corn stalk or sunflower etc., and the tool specific purpose tool is a tubular article.The shortcoming that exists: 1, the straw of Li Yonging is more single, only is corn and sunflower straw; 2, the container manufacture technology is manual operations, is not suitable for mass industrialized production; 3, do not consider that container nursery is transplanted after, to the influence of seedling growth, particularly do not consider the influence that chamber wall interts to the root of plant.
Summary of the invention:
The present invention is directed to the shortcoming that stalk processing and fabricating container for plant growth exists, a kind of manufacture method of straw basin alms bowl is provided, the equipment that this method is used is simple, small investment, production cost are low, the stalk pot of producing is as growing seedlings or sapling transplanting use, being easy to root system of plant interts, and after the disintegration, become the high-quality fertilizer, be beneficial to growth and development of plant.
The objective of the invention is to realize by following measure:
The method that a kind of straw basin alms bowl is made, it is characterized in that with the straw being primary raw material, adding alkaline solution rises to more than 9 raw material pH value, pulverize after composting is softening, pulverize the back and add acid solution adjusting pH value to neutral range, add to add again and expect to mix, repressed moulding, demoulding drying process are made, and the weight ratio of its consumption is a straw: alkaline solution: acid solution: add material=1: (0.2～0.6): (0.06～0.2): (0.02～0.08).
The present invention utilizes straw to produce the plant cultivation pot alms bowl, and Fig. 1 is seen in its technological process.
The present invention has distinguishing feature compared to existing technology:
1, need not heating, the compression moulding of just can pressurizeing at normal temperatures, therefore, equipment is simple, and power consumption reduces;
2, can reduce the required pressure of basin alms bowl compression moulding by adding binding agent, and can strengthen the intensity of basin body, add plant nutrient substance, can make the seedling-growing container alms bowl in decay process, constantly provide nutrient for plant, can guarantee that by adding absorbent material imbibition makes the disintegration of basin alms bowl under the saturation water condition, after guaranteeing that the seedling-growing container alms bowl is transplanted the land for growing field crops, back, can not influence interting of root system of plant.And as the flower basin alms bowl time,, can significantly reduce the number of times that waters because of having added absorbent material.
3, the periphery wall of mould therefor loose tool is distributed with projection, makes the alms bowl body thickness of compacting be inhomogeneous shape, so neither influences the intensity of alms bowl body, and the interspersed passage that provides of root system of plant is provided again, also helps transplanting the disintegration of back seedling-growing container alms bowl simultaneously.
4, technology provided by the invention by mold exchange more, just can make to produce the basin alms bowl of growing seedlings or cultivating that adapts to different plants.
In a word, the manufacture method of straw basin alms bowl of the present invention, its process equipment is simple, small investment, go up detective, production cost is low, the stalk pot of producing is beneficial to growth and development of plant, because the alms bowl body of basin alms bowl leaves thin part as growing seedlings or sapling transplanting use, root system of plant is easy to intert, or after transplanting fully suction, because the abundant imbibition of water absorbing agent makes the disintegration of alms bowl body become the high-quality fertilizer, therefore, need not to remove the basin alms bowl during transplanting; As showy flowers of herbaceous plants basin alms bowl, after flower withers, plant residue, culture matrix together with alms bowl body composting, can be reused as matrix.
Description of drawings:
Fig. 1 is a process flow diagram of the present invention.
Embodiment:
Example 1
Take by weighing straw 1000kg, spray into concentration and be 10% lime water 300kg, straw is all drenched, covered with plastic film drenches in case rain; Stack and soften, when composting, every heap 1-3 rice was stacked 5-7 days summer, and spring and autumn was stacked 10-15 days, stacked turning midway 1-2 time winter 15-20 days.Be crushed to softening straw fibrous at normal temperatures.Be crushed to length fibrous at 5-15mm with the chain type cracker, place batch mixer, spray into concentration and be 10% the about 100kg of sulfur waste acid, pH is about 6 in adjusting.Add 80kg Water Quenching Slag ball milling powder, in the 2kg amino acid, trace element chelated salt, 1kg powdery high hydroscopic resin stirs.The material of mixing places mould compression moulding, and the mould of use is outward a master mold, and interior is loose tool, is distributed with several kicks on the loose tool periphery wall, and the height of projection is less than the wall thickness of basin alms bowl alms bowl body.Can adopt hydraulic press, hydraulic press or screw extruder compacting, suppress back oven dry or natural air drying and promptly can be finished product.
Example 2
Take by weighing water wheat straw stalk 1000kg, spray into the alkali lye 600kg of 2% potassium hydroxide, water wheat straw stalk is all drenched, covered with plastic film drenches in case rain; Stack and soften, when composting, every heap 1-3 rice was stacked 5-7 days summer, and spring and autumn was stacked 10-15 days, stacked turning midway 3 times winter 15-20 days.Be crushed to softening straw fibrous at normal temperatures.Be crushed to length fibrous at 5-15mm with the chain type cracker, place batch mixer, spray into concentration and be 15% the about 200kg of phosphoric acid, regulate pH about 6, add 50kg Water Quenching Slag ball milling powder, 1kg powdery high hydroscopic resin stirs.Place mould compression moulding, can adopt hydraulic press, hydraulic press or screw extruder compacting, suppress back oven dry or natural air drying and promptly can be finished product.
Example 3
Take by weighing straw 1000kg, the lime white concentration that sprays into 400kg 5% is, straw is all drenched, and covered with plastic film drenches in case rain; Stack and soften, when composting, every heap 10-3 rice was stacked 5-7 days summer, and spring and autumn was stacked 10-15 days, stacked turning midway 2 times winter 15-20 days.Be crushed to softening straw fibrous at normal temperatures.Be crushed to length fibrous at 5-15mm with the chain type cracker, place batch mixer, spray into the sulfur waste acid of 130kg 10%, regulate pH about 6, add 80kg Water Quenching Slag ball milling powder, in the 2kg amino acid, trace element chelated salt, Lauxite 1.5kg, 1kg powdered polypropylene acid amides stirs.Place mould compression moulding, can adopt hydraulic press, hydraulic press or screw extruder, suppress back oven dry or natural air drying and promptly can be finished product.
Example 4
Take by weighing straw, each 500kg of wheat straw, spray into 6% sodium carbonate liquor 450kg, straw, wheat straw are all drenched, covered with plastic film drenches in case rain; Stack and soften, when composting, every heap 1-2 rice was stacked 5-7 days summer, and spring and autumn was stacked 10-15 days, stacked turning midway 1-3 time winter 15-20 days.Be crushed to softening straw fibrous at normal temperatures.Be crushed to length fibrous at 5-15mm with the chain type cracker, place batch mixer, spray into concentration and be 15% the about 100kg of phosphoric acid, regulate pH about 7, add the 50kg manure of livestock and poultry that becomes thoroughly decomposed, trace element chelated salt in the 1kg amino acid, 1kg powdery high hydroscopic resin stirs.Place mould compression moulding, can adopt hydraulic press, hydraulic press or screw extruder, suppress back oven dry or natural air drying and promptly can be finished product.
Example 5
Take by weighing corn, each 500kg of rape straw, spray into 5% sodium hydroxide 350kg, corn, rape straw are all drenched, covered with plastic film drenches in case rain; Stack and soften, when composting, every heap 1-2 rice was stacked 5-7 days summer, and spring and autumn was stacked 10-15 days, stacked turning midway 1-2 time winter 15-20 days.At normal temperatures softening straw is crushed to length fibrous at 5-15mm with the chain type cracker, place batch mixer, spray into concentration and be 15% the about 120kg of phosphoric acid, regulate pH about 7, add the waste residue of discharging in the 50kg Chinese herbal and crude drugs preparations industrial production, trace element chelated salt in the 1kg amino acid, 1kg powdery high hydroscopic resin stirs.Place mould compression moulding, can adopt hydraulic press, hydraulic press or screw extruder, suppress back oven dry or natural air drying and promptly can be finished product.
More than the used various plant nutrient agents of each embodiment as: the feces of livestock and poultry of handling by fermentation, municipal sludge, house refuse, organic industry waste residue and inorganic industrial residue, its contained heavy metal and hygiene index must meet the index of defined in the country " the agricultural control criterion GB8172-87 of townm refuse ".
Claims (9)
1, a kind of method of straw basin alms bowl manufacturing, it is characterized in that with the straw being primary raw material, adding alkaline solution rises to more than 9 raw material pH value, pulverize after composting is softening, pulverize the back and add acid solution adjusting pH value to neutral range, add to add again and expect to mix, repressed moulding, demoulding drying process are made, and the weight ratio of its consumption is a straw: alkaline solution: acid solution: add material=1: (0.2～0.6): (0.06～0.2): (0.02～0.08).
2, the method made of straw basin alms bowl according to claim 1 is characterized in that the described alkali lye solution that adds is that concentration is 1～5% potassium hydroxide or 5～15% limewash or carbonate solution.
3, the method for straw basin alms bowl manufacturing according to claim 1 is characterized in that described acid solution is waste sulfuric acid solution or phosphoric acid solution.
4, the method for straw basin alms bowl manufacturing according to claim 1 is characterized in that the described material that adds is binding agent, water absorbing agent or plant nutrient agent, or any combination of three.
5, the method for straw basin alms bowl manufacturing according to claim 4 is characterized in that described adhesive is amylum adhesive, industrial gelatine, Lauxite or polyvinyl alcohol.
6, the method for straw basin alms bowl manufacturing according to claim 4 is characterized in that described water absorbing agent is hydroscopic high-molecular resin or polyacrylamide.
7, the method for straw basin alms bowl manufacturing according to claim 4, it is characterized in that feces of livestock and poultry, municipal sludge, house refuse, organic industry waste residue and the inorganic industrial residue of described plant nutrient agent for handling by fermentation, its contained heavy metal and hygiene index must meet the index of defined in the country " the agricultural control criterion GB 8172-87 of townm refuse ".
8, the method for straw basin alms bowl manufacturing according to claim 7, it is characterized in that described organic industry waste residue is the waste residue of discharging in various antibiotic, enzyme preparation, alcohol, citric acid, monosodium glutamate, sugaring, the Chinese herbal and crude drugs preparations industrial production, described inorganic industrial residue is an ardealite, during the Water Quenching Slag of iron-smelter, flyash etc. contain, the trace element waste residue.
9, the method for straw basin alms bowl manufacturing according to claim 1 is characterized in that the periphery wall of the loose tool of mould therefor in the described pressing process is distributed with projection, and the height of projection is less than the wall thickness of basin alms bowl alms bowl body.