CN1526681A - Brick - Google Patents
Brick Download PDFInfo
- Publication number
- CN1526681A CN1526681A CNA031468683A CN03146868A CN1526681A CN 1526681 A CN1526681 A CN 1526681A CN A031468683 A CNA031468683 A CN A031468683A CN 03146868 A CN03146868 A CN 03146868A CN 1526681 A CN1526681 A CN 1526681A
- Authority
- CN
- China
- Prior art keywords
- brick
- coal
- ceramic slurry
- ceramic
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses one kind of brick, which is produced with ceramic slurry, cinder, coal gangue, shale rock, sludge, etc. The present invention has the advantages of utilizing the waste of ceramic industry to produce useful material and protecting ecological environment.
Description
Technical field
The present invention relates to building material field, relates to a kind of brick in particular.
Background technology
At present, employed brick mainly is raw material mostly with the clay in the material of construction, and it earlier is made into adobe with brick press, then it is carried out airing, at last the adobe of airing is placed on that roasting becomes finished product to get final product in the kiln.Application number is 95104491, the applying date is May 9 nineteen ninety-five, denomination of invention is air-entrained clay brick and preparation method thereof, this disclosure of the Invention a kind of New Building Materials air-entrained clay brick and preparation method thereof, its composition contains 98.85-99.21% (weight) clay, 0.77-1.10% (weight) whipping agent, 0.02-0.05% (weight) additive, by 1: the 0.55-0.65 ratio of water to material through stirring, cast, quietly stop, cutting, oven dry, roasting form.Because the brick that adopts aforesaid method to make, it must spend a large amount of clays, goes down for a long time serious soil erosion to occur, can cause great destruction to the arable land of country, does not meet national policy to environmental protection requirement.Equally, some produce the enterprise of ceramic China, the ceramic slurry that they will produce in the process of producing ceramic mostly discards in vain as industrial waste, and they are not used, these ceramic slurry that are dropped are difficult for dry for a long time, cause destruction equally, cause the soil can't obtain for a long time utilizing, also do not meet country environmental protection requirement to ecotope.
Summary of the invention
A kind of brick that the objective of the invention is to overcome the deficiencies in the prior art and provide; it mainly replaces present with the industrial waste that is abandoned by pot bank is that main raw material is made brick with the clay; thereby avoided a large amount of soil erosions, protected national ecotope.
The present invention adopts following scheme to realize above-mentioned purpose:
A kind of brick, its main component and content are respectively:
Ceramic slurry 5%-70%
The combination 5%-70% of one or more of coal quarrel, logical powder and coal gangue
Described its main component and optimum content are respectively:
Ceramic slurry 30%-50%
The combination 30%-50% of one or more of coal quarrel, logical powder and coal gangue
Described it also can comprise Ye Yan and useless mud.
Adopted the present invention of said structure to have following advantage:
1, in the process of brickmaking, the industrial waste that main employing is discarded by pot bank is one of main raw material, a large amount of industrial wastes of pot bank can be used like this, it is turned waste into wealth, thereby played the effect of preserving the ecological environment.
2, because the industrial waste that adopts pot bank as main raw material, and has substituted clay, thereby can significantly reduce soil erosion, finally also play the effect of preserving the ecological environment.
Embodiment
A kind of brick, its main component and content are respectively:
Ceramic slurry 5%-70%
The combination 5%-70% of one or more of coal quarrel, logical powder and coal gangue
Described its main component and optimum content are respectively:
Ceramic slurry 30%-50%
The combination 30%-50% of one or more of coal quarrel, logical powder and coal gangue
Described it also can comprise Ye Yan and useless mud.
Described ceramic slurry is the industrial waste that ceramic enterprise is produced in making the ceramic product process, this industrial waste normally is dropped, but also the utmost point is not easy drying, cause the soil can't obtain for a long time utilizing, ecotope is caused very big destruction, now it is used as one of main raw material of making brick, having reached turns waste into wealth, the effect of protection environment meets country to environmental protection requirement; Described coal quarrel is that raw coal burns the remaining waste material in back; Described logical powder is the said coal ash of power plant of normal open.
It is as follows to adopt component of the present invention and content to make the technological process of brick: earlier 30% coal gangue and a kind of or its combination of coal quarrel are polished into powdery, mix with 45% ceramic slurry again and ferment, add 25% logical powder then, can add an amount of leaf rock and useless mud can not add yet yet, then make moulding through brick press, the brick that will make moulding at last dries back kiln-firing finished product and gets final product.
Claims (3)
1, a kind of brick is characterized in that: its main component and content are respectively:
Ceramic slurry 5%-70%
The combination 5%-70% of one or more of coal quarrel, logical powder and coal gangue
2, a kind of brick according to claim 1 is characterized in that: its main component and optimum content are respectively:
Ceramic slurry 30%-50%
The combination 30%-50% of one or more of coal quarrel, logical powder and coal gangue
3, a kind of brick according to claim 1 and 2 is characterized in that: it also can comprise Ye Yan and useless mud.