CN1526675A - 制造高标号水泥的超细矿物粉添加剂 - Google Patents
制造高标号水泥的超细矿物粉添加剂 Download PDFInfo
- Publication number
- CN1526675A CN1526675A CNA03158263XA CN03158263A CN1526675A CN 1526675 A CN1526675 A CN 1526675A CN A03158263X A CNA03158263X A CN A03158263XA CN 03158263 A CN03158263 A CN 03158263A CN 1526675 A CN1526675 A CN 1526675A
- Authority
- CN
- China
- Prior art keywords
- slag
- cement
- flyash
- additive agent
- zeolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种制造高标号水泥的超细矿物粉添加剂，该添加剂由矿渣或矿渣和石灰石、沸石、粉煤灰、煤矸石、钢渣至少一种混合组成；其中矿渣的重量百分比为50％－100％，石灰石、沸石、粉煤灰、煤矸石、钢渣或其任意混合物的重量百分比为0－50％；上述矿渣或矿渣和石灰石、沸石、粉煤灰、煤矸石、钢渣至少一种混合物的中位径为0.5－3.0微米。使用该添加剂可以在不改变现有的生产工艺，不降低水泥的性能，不增加水泥成本的条件下提高水泥标号。
Description
技术领域：
本发明涉及一种水泥中使用的添加剂，具体地说是制造高标号水泥的超细矿物粉添加剂。
背景技术：
立窑水泥厂要生产高标号水泥有相当大的难度。目前通常采用三种方法来提高水泥标号，一是利用外加剂技术，但外加剂的掺入受到水泥国家标准的限制，而且由于某些外加剂与水泥在化学性能上不兼容，往往对水泥的某些性能产生不良影响，例如一些碱性外加剂虽能明显改善凝结和早期强度，但对后期强度发展不利，同时增加了发生混凝土碱集料破坏反应的潜在危险。二是提高水泥产品的细度，但另一方面由于细度提高到一定程度后需水量增大会抵消其增强效果，另一方面由于细度提高时粉磨电耗大幅度上升，增加水泥生产成本。三是改变生产工艺和设备，比如由立窑生产改为旋窑生产，这将大大增加投资成本和生产成本。
发明内容：
本发明所要解决的技术问题是提供一种在不改变现有的生产工艺，不降低水泥的性能，不增加水泥的成本条件下制造高标号水泥的超细矿物粉添加剂。
本发明的技术解决方案是：
一种制造高标号水泥的超细矿物粉添加剂，其特征是：由矿渣或矿渣和石灰石、沸石、粉煤灰、煤矸石、钢渣至少一种混合组成；其中矿渣的重量百分比为50％-100％，石灰石、沸石、粉煤灰、煤矸石、钢渣或其任意混合物的重量百分比为0-50％；上述矿渣或矿渣和石灰石、沸石、粉煤灰、煤矸石、钢渣至少一种混合物的中位径为0.5-3.0微米。
所述矿渣含量重量百分比为80％-100％。
所述的矿渣或矿渣和石灰石、沸石、粉煤灰、煤矸石、钢渣至少一种混合物的中位径为0.8-2.0微米。
本发明的有益效果为：使用该添加剂可以在不改变现有的生产工艺，不降低水泥的性能，不增加水泥的成本的条件下提高水泥标号，在普通水泥中加入8-20％的该添加剂，原水泥标号可提高一个等级，例如，在32.5号水泥中加入该添加剂后，水泥标号达42.5。该添加剂原料广泛，使用方便，制备方法简单。
具体实施方式：
实施例一：将矿渣100Kg用烘干机烘干后，入球磨机或振动磨机粉磨并经超细分级机分级，所得粗粉重新进入磨机粉磨，超细矿渣粉料中位径为D50＝1.5um，即为超细矿物粉添加剂。将该超细矿物粉添加剂13kg和42.5号通用水泥87kg，经机械或空气搅抖混合均匀后制成52.5号通用水泥。
实施例二：将矿渣100Kg用烘干机烘干后，入球磨机或振动磨机粉磨并经超细分级机分级，所得粗粉重新进入磨机粉磨，超细矿渣粉料中位径为D50＝0.5um，即为超细矿物粉添加剂。将该超细矿物粉添加剂8kg和32.5号通用水泥92kg，经机械或空气搅抖混合均匀后制成42.5号通用水泥。
实施例三：将矿渣和石灰石各50kg用烘干机烘干后，入球磨机或振动磨机粉磨并经超细分级机分级，所得粗粉重新进入磨机粉磨，超细粉料中位径为D50＝3.0um，即为超细矿物粉添加剂。将该超细矿物粉添加剂20kg和32.5号通用水泥80kg，经机械或空气搅抖混合均匀后制成42.5号通用水泥。
实施例四：将矿渣和粉煤灰各50kg用烘干机烘干后，入球磨机或振动磨机粉磨并经超细分级机分级，所得粗粉重新进入磨机粉磨，超细粉料中位径为D50＝1.5um，即为超细矿物粉添加剂。将该超细矿物粉添加剂13kg和32.5号通用水泥87kg，经机械或空气搅抖混合均匀后制成42.5号通用水泥。
实施例五：将矿渣和粉煤灰各50kg用烘干机烘干后，入球磨机或振动磨机粉磨并经超细分级机分级，所得粗粉重新进入磨机粉磨，超细粉料中位径为D50＝0.8um，即为超细矿物粉添加剂。将该超细矿物粉添加剂10kg和32.5号通用水泥90kg，经机械或空气搅抖混合均匀后制成42.5号通用水泥。
实施例六：将矿渣70kg，粉煤灰20kg，沸石10kg，用烘干机烘干后，入球磨机或振动磨机粉磨并经超细分级机分级，所得粗粉重新进入磨机粉磨，超细矿渣粉料中位径为D50＝2.0um，即为超细矿物粉添加剂。将该超细矿物粉添加剂15kg和32.5号通用水泥85kg，经机械或空气搅抖混合均匀后制成42.5号通用水泥。
实施例七：将矿渣70kg，粉煤灰20kg，煤矸石10kg，用烘干机烘干后，入球磨机或振动磨机粉磨并经超细分级机分级，所得粗粉重新进入磨机粉磨，超细矿渣粉料中位径为D50＝2.0um，即为超细矿物粉添加剂。将该超细矿物粉添加剂15kg和32.5号通用水泥85kg，经机械或空气搅抖混合均匀后制成42.5号通用水泥。
实施例八：将矿渣70kg，粉煤灰20kg，钢渣10kg，用烘干机烘干后，入球磨机或振动磨机粉磨并经超细分级机分级，所得粗粉重新进入磨机粉磨，超细矿渣粉料中位径为D50＝2.0um，即为超细矿物粉添加剂。将该超细矿物粉添加剂15kg和32.5号通用水泥85kg，经机械或空气搅抖混合均匀后制成42.5号通用水泥。
Claims (3)
1、一种制造高标号水泥的超细矿物粉添加剂，其特征是：由矿渣或矿渣和石灰石、沸石、粉煤灰、煤矸石、钢渣至少一种混合组成；其中矿渣的重量百分比为50％-100％，石灰石、沸石、粉煤灰、煤矸石、钢渣或其任意混合物的重量百分比为0-50％；上述矿渣或矿渣和石灰石、沸石、粉煤灰、煤矸石、钢渣至少一种混合物的中位径为0.5-3.0微米。
2、根据权利要求1所述的超细矿物粉添加剂，其特征是：所述矿渣含量重量百分比为80％-100％。
3、根据权利要求1所述的超细矿物粉添加剂，其特征是：所述的矿渣或矿渣和石灰石、沸石、粉煤灰、煤矸石、钢渣至少一种混合物的中位径为0.8-2.0微米。