CN1519289A - 一种魔芋粘结剂及其生产工艺 - Google Patents
一种魔芋粘结剂及其生产工艺 Download PDFInfo
- Publication number
- CN1519289A CN1519289A CNA2003101035086A CN200310103508A CN1519289A CN 1519289 A CN1519289 A CN 1519289A CN A2003101035086 A CNA2003101035086 A CN A2003101035086A CN 200310103508 A CN200310103508 A CN 200310103508A CN 1519289 A CN1519289 A CN 1519289A
- Authority
- CN
- China
- Prior art keywords
- binding agent
- konjak
- konjaku powder
- water
- follows
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于粘接剂制造技术领域,具体涉及利用魔芋精粉和/或飞粉生产环保型粘接剂技术领域。本发明的特点是:先将魔芋精粉或飞粉中的魔芋葡甘聚糖进行化学改性得到改性产物水溶胶,根据不同用途粘接剂的技术要求,添加合适的辅料及助剂,在本发明的工艺条件下生产出不同的粘接剂,与已有技术相比,本发明具有原料来源广泛,无环境污染,产品性能优良和生产成本较低等优点。
Description
技术领域
本发明属于粘结剂及其生产工艺技术领域,具体涉及利用魔芋精粉和飞粉生产粘结剂及其工艺技术领域。
背景技术
在本发明做出以前,粘结剂的生产主要是利用合成高分子原料以及天然高分子淀粉、纤维素、桃胶等来生产。作为胶合板或蜂窝板粘结剂一般采用脲醛树脂、酚醛树脂等合成高分子,存在极大的污染,甲醛等更成为影响环境的公害,虽然采用诸多方法降低甲醛含量,但污染还是难以完全克服,诸如专利CN881050089A、CN1040044A、CN1034417C等所述的那样,至于建筑用胶水,一般均采用聚乙烯醇作为粘结成分,单纯的聚乙烯醇溶液没有环境污染,但其使用性能很差,尤其是耐水性等完全不能达到使用要求。因此实践中往往采用甲醛缩合的方法,提高其耐水性,但随之而来的是更为广泛的环境污染,同样采取了诸多方法降低甲醛的残留,但尚不能完全达到理想的效果,类似的专利有CN1039033A,CN1031090A,CN1008528B,CN85103463A等。
采用天然高分子研制粘结剂的报道也较多,但主要集中在淀粉粘结剂方面,淀粉通过氧化、交联等处理,可以最终形成具有一定粘结强度的粘结剂,主要应用在饲料、型煤、铸造、纺织、纸箱等方面,有关利用魔芋精粉、魔芋飞粉等制造粘结剂、尤其是胶合板、蜂窝板、建筑胶水等方面尚无文献报道。
发明内容
本发明在于克服已有技术之不足,以魔芋精粉和飞粉为原料生产系列环保型魔芋粘结剂,以降低生产成本,提高粘结剂的性能并应用于胶合板、蜂窝板、建筑胶水等用量大的领域。
本发明通过以下技术方案实现:
一种利用植物天然高分子生产的粘结剂,其特征在于,所述的粘结剂以魔芋精粉和/或魔芋飞粉为原料,该原料经化学双改性及物理共混处理制成涂料的半成品,其中
所述的粘结剂组分及含量如下:
以重量份数计,魔芋精粉5-40,魔芋飞粉30-200,石灰乳0-60,氢氧化钠0-30,邻苯二甲酸二丁酯0-20,硅酸钠0-30,过氧化氢0.1-3,消泡剂0.1-3,聚醋酸乙烯乳液0-30。
所述的粘结剂为胶合板粘结剂,其配比如下:
以重量份数计,魔芋精粉5-20,魔芋飞粉50-200,石灰乳6-60,NaOH10-30,邻苯二甲酸二丁酯5-20,硅酸钠20-70,过氧化氢1-3,磷酸三丁酯1-6,水700。
所述的粘结剂为蜂窝板粘结剂,其配比如下:
以重量份数计,魔芋精粉10-20,魔芋飞粉30-200,高锰酸钾1-6,邻苯二甲酸二丁酯5-20,Na2CO3 3-10,聚醋酸乙烯乳液10-30,三聚磷酸钠1-6,水700。
所述的粘结剂为建筑用胶水,其配比如下:
以重量百分比计,魔芋精粉0.3-10,过氧化氢0.02-0.2;苯并咪唑基甲酸甲酯0.1-0.3,其余是水。
所述的粘结剂的工艺,其特征在于所述的工艺步骤包括:
按配方量向反应釜中加入700公斤水,加热至50-80℃,投入魔芋精粉5-40公斤,保温10-30min,加入改性剂0.1-3公斤,反应30-100min,至粘度达到特征粘度,终止反应,出料至搅拌桶,缓慢加入其它原料,消泡后得成品。
本发明具有以下积极的效果:
魔芋粘结剂是以天然高分子魔芋葡聚甘糖为主要粘结成分的粘结剂,生产过程无环境污染,产品无挥发性溶剂,是一种绿色环保粘结剂。它同时还具有省资源,低能耗的特点。
本发明可以大量消耗魔芋精粉和飞粉,对我国山区特产作物魔芋资源的开发利用具有重要的意义。同本发明为粘结剂行业提供了一种新型粘结成分,完全符合产业发展方向。
具体实施方式
实施例1:胶合板粘结剂配方
以重量份数计,魔芋精粉20,魔芋飞粉100,石灰乳(1∶4)60,30%NaOH 10,邻苯二甲酸二丁酯6,40波尔美硅酸钠38,过氧化氢3,磷酸三丁酯5.5,水700。
实施例2:蜂窝板粘结剂配方
以重量份数计,魔芋精粉15,魔芋飞粉100,高锰酸钾3,邻苯二甲酸二丁酯5,30%Na2CO3 10,聚醋酸乙烯乳液20,水700。
本发明的实施效果:
表1:魔芋改性前后的性能比较
性能比较 | 改性前 | 改性后 |
干擦性 | 2 | 0 |
湿擦性(次) | 16 | 1540 |
附着力(%) | 13 | 100 |
遮盖力(g/m2) | 350 | 100 |
耐水性 | 异常 | 无异常 |
耐碱性 | 异常 | 无异常 |
Claims (5)
1、一种利用植物天然高分子生产的粘结剂,其特征在于,所述的粘结剂以魔芋精粉和/或魔芋飞粉为原料,该原料经化学双改性及物理共混处理制成涂料的半成品,其中
所述的剂组分及含量如下:
以重量份数计,魔芋精粉5-40,魔芋飞粉30-200,石灰乳0-60,氢氧化钠0-30,邻苯二甲酸二丁酯0-20,硅酸钠0-30,过氧化氢0.1-3,消泡剂0.1-3,聚醋酸乙烯乳液0-30。
2、根据权利要求1所述的粘结剂,其特征在于,所述的粘结剂为胶合板粘结剂,其配比如下:
以重量份数计,魔芋精粉5-20,魔芋飞粉50-200,石灰乳6-60,NaOH10-30,邻苯二甲酸二丁酯5-20,硅酸钠20-70,过氧化氢1-3,磷酸三丁酯1-6,水700。
3、根据权利要求1所述的粘结剂,其特征在于,所述的粘结剂为蜂窝板粘结剂,其配比如下:
以重量份数计,魔芋精粉10-20,魔芋飞粉30-200,高锰酸钾1-6,邻苯二甲酸二丁酯5-20,Na2CO33-10,聚醋酸乙烯乳液10-30,三聚磷酸钠1-6,水700。
4、根据权利要求1所述的粘结剂,其特征在于,所述的粘结剂为建筑用胶水,其配比如下:
以重量百分比计,魔芋精粉0.3-10,过氧化氢0.02-0.2;苯并咪唑基甲酸甲酯0.1-0.3,其余是水。
5、生产如权利要求1所述的粘结剂的工艺,其特征在于所述的工艺步骤包括:
按配方量向反应釜中加入700公斤水,加热至50-80℃,投入魔芋精粉5-40公斤,保温10-30min,加入改性剂0.1-3公斤,反应30-100min,至粘度达到特征粘度,终止反应,出料至搅拌桶,缓慢加入其它原料,消泡后得成品。