CN1519279A - Waterproofing agent of Nano coating material - Google Patents
Waterproofing agent of Nano coating material Download PDFInfo
- Publication number
- CN1519279A CN1519279A CNA031149812A CN03114981A CN1519279A CN 1519279 A CN1519279 A CN 1519279A CN A031149812 A CNA031149812 A CN A031149812A CN 03114981 A CN03114981 A CN 03114981A CN 1519279 A CN1519279 A CN 1519279A
- Authority
- CN
- China
- Prior art keywords
- kilograms
- kilogram
- pure
- agent
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A nano-class water-proof paint for internal and external walls and roof of building contains pure acrylate emulsion, filler (rutile-type titanium oxide powder, aluminium silicate, wollastonite and nano calcium), phosphate as emulsifier and disperser, dihydroxy propane as filming agent, polyacrylamide as levelling agent, and penta sodium as bactericide. Its advantages are high rubbing resistance, weatherability, dispersity and glossiness, good hardness and toughness of its film, and better self-cleaning nature.
Description
Technical field
The present invention relates to architectural waterproof material, be used for the interior exterior wall of all kinds of buildings and the water-proof decorative and the anti-leakage of roofing, specifically is a kind of nano waterproof agent coating.
Background technology
Use traditional petroleum pitch water-proof material in the prior art, high temperature is easily trickling down, and easy embrittlement under the low temperature is trickled easily, chaps, rotted and seepage the waterproof effect instability.The water-proof material that also has various asphalt modifications, as emulsified bitumen, waterproof paint such as rubber asphalt and tung oil pitch or waterproofing unction etc., but price height need heat construction and are difficult to promote, simultaneously can not be as the decorative paint of interior exterior wall.
Summary of the invention
The objective of the invention is at above-mentioned weak point of the prior art, propose a kind of anti-algae of mildew-resistant that has, hardness of paint film height and flexible, anti-dust and anti-booty adhere to, and be easily self-cleaning and remove contamination easy working nano waterproof agent coating easily.
Technical solution of the present invention is: nano waterproof agent coating of the present invention is water-soluble material, contain pure-acrylic emulsion, wherein, golden red titanium dioxide, pure aluminium silicate and wollastonite powder etc. are made filler, and phosphoric acid fat salt is made emulsifying agent and dispersion agent, and dihydroxypropane is made the film forming auxiliary agent, polyacrylamide increases levelling property, sodium pentachlorophenate is made sterilant, also contains Namigai in the filler, they consist of: contain in every double centner water:
180 kilograms of pure-acrylic emulsions---250 kilograms
60 kilograms of golden red titanium dioxides---80 kilograms
15 kilograms of pure aluminium silicate---25 kilograms
15 kilograms of wollastonite powder---25 kilograms
3 kilograms of phosphoric acid fat salt---8 kilograms
8 kilograms of dihydroxypropanes---12 kilograms
1 kilogram of polyacrylamide---3 kilograms
0.2 kilogram of sodium pentachlorophenate---0.8 kilogram
20 kilograms of Namigai---30 kilograms
Can also add in the above-mentioned batching: mica powder and talcum powder as filler, potassium silicate are made auxiliary agent increases water-fast and resistance to acids and bases, and sodium hydroxide is made catalyzer, polysiloxane increases levelling property, sodium polyacrylate is made wetting agent, and benzimidazole carboxylamine formicester is made mould inhibitor, and poly-methyl silicon ether is made defoamer.The amount that can add by said ratio is:
15 kilograms of mica powders---30 kilograms
10 kilograms of talcum powder---20 kilograms
3 kilograms of potassium silicates---8 kilograms
(20%) 8 kilogram in sodium hydroxide---12 kilograms
1 kilogram of polysiloxane---2 kilograms
0.3 kilogram of polyacrylic acid sodium salt---0.8 kilogram
0.3 kilogram of benzimidazole carboxylamine formicester---0.7 kilogram
0.3 kilogram in poly-methyl silicon ether---0.8 kilogram
Nano waterproof agent coating of the present invention is applicable to the interior exterior wall of all kinds of buildings and the water-proof decorative and the anti-leakage of roofing.Owing to add Namigai, improved scrub resistance, weather resisteant, dispersiveness and the glossiness of coating, and played anti-precipitating action.Have the anti-algae of mildew-resistant, hardness of paint film height and flexible, anti-dust and anti-booty adhere to, and be easily self-cleaning and remove contamination easy working characteristics easily.
Embodiment
The present invention is further illustrated below in conjunction with embodiment: nano waterproof agent coating of the present invention is water-soluble material, and its composition is to contain in every double centner water:
220 kilograms of pure-acrylic emulsions
70 kilograms of golden red titanium dioxides
17 kilograms of pure aluminium silicate
18 kilograms of wollastonite powder
5 kilograms of phosphoric acid fat salt
9 kilograms of dihydroxypropanes
1.5 kilograms of polyacrylamides
0.5 kilogram of sodium pentachlorophenate
25 kilograms of Namigai
18 kilograms of mica powders
13 kilograms of talcum powder
5 kilograms of potassium silicates
(20%) 10 kilogram in sodium hydroxide
1.5 kilograms of polysiloxane
0.5 kilogram of polyacrylic acid sodium salt
0.5 kilogram of benzimidazole carboxylamine formicester
0.5 kilogram in poly-methyl silicon ether
Claims (2)
1, a kind of nano waterproof agent coating is water-soluble material, contain pure-acrylic emulsion, wherein, golden red titanium dioxide, pure aluminium silicate and wollastonite powder etc. are made filler, and phosphoric acid fat salt is made emulsifying agent and dispersion agent, and dihydroxypropane is made the film forming auxiliary agent, polyacrylamide increases levelling property, sodium pentachlorophenate is made sterilant, it is characterized in that also containing in the filler Namigai, they consist of: contain in every double centner water:
180 kilograms of pure-acrylic emulsions---250 kilograms
60 kilograms of golden red titanium dioxides---80 kilograms
15 kilograms of pure aluminium silicate---25 kilograms
15 kilograms of wollastonite powder---25 kilograms
3 kilograms of phosphoric acid fat salt---8 kilograms
8 kilograms of dihydroxypropanes---12 kilograms
1 kilogram of polyacrylamide---3 kilograms
0.2 kilogram of sodium pentachlorophenate---0.8 kilogram
20 kilograms of Namigai---30 kilograms
2, a kind of nano waterproof agent coating according to claim 1 is characterized in that also comprising in the above-mentioned batching:
15 kilograms of mica powders---30 kilograms
10 kilograms of talcum powder---20 kilograms
3 kilograms of potassium silicates---8 kilograms
(20%) 8 kilogram in sodium hydroxide---12 kilograms
1 kilogram of polysiloxane---2 kilograms
0.3 kilogram of polyacrylic acid sodium salt---0.8 kilogram
0.3 kilogram of benzimidazole carboxylamine formicester---0.7 kilogram
0.3 kilogram in poly-methyl silicon ether---0.8 kilogram