CN103045034A - Algae prevention paint - Google Patents
Algae prevention paint Download PDFInfo
- Publication number
- CN103045034A CN103045034A CN2012105541781A CN201210554178A CN103045034A CN 103045034 A CN103045034 A CN 103045034A CN 2012105541781 A CN2012105541781 A CN 2012105541781A CN 201210554178 A CN201210554178 A CN 201210554178A CN 103045034 A CN103045034 A CN 103045034A
- Authority
- CN
- China
- Prior art keywords
- parts
- algae prevention
- paint
- prevention paint
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to algae prevention paint. The paint comprises the following components in part by weight: 20 to 30 parts of cuprous oxide, 10 to 15 parts of manganese oxide, 5 to 10 parts of zirconium oxide, 2 to 4 parts of inorganic silicon resin, 11 to 14 parts of acrylic latex, 3 to 7 parts of rutile titanium dioxide, 5 to 9 parts of phosphate ester acid, 1 to 5 parts of dyhydroxyl propane, 7 to 14 parts of polyacrylamide, 8 to 19 parts of polyvinylidene fluoride, 8 to 16 parts of molybdenum disulfide, 3 to 8 parts of polystyrene-acrylate copolymer and 5 to 19 parts of jade powder. The algae prevention paint has the advantages of reasonable formula, good use effect and low production cost.
Description
Technical field
The present invention relates to a kind of anti-algicide coatings.
Background technology
The high-speed development of Modern World economic jump and world industry has caused the rapid deterioration of global environment, and serious pollution threat human living space." green ", " environmental protection " are that people pay much attention to after the ecological environmental protection the coatings industry requirement, also are the developing direction of coating.Existing anti-algicide coatings, effect is undesirable, and production cost is high.For a long time, organic coating has been obtained widely application with its good diversity and cheap price ornamental, kind.But, because the main raw material(s) of organic building coating derives from the natural resource such as coal, oil, Sweet natural gas; Add and to produce a large amount of by products and volatile solvent and residual monomer man-hour; Its coating for internal and external wall generally all adopts the constructional method that an end two is coated with during construction; Not only caused environmental pollution but also wasted a large amount of resources and the energy.Simultaneously, organic coating is covered with paint, lacquer, colour wash, etc. at surface of wall, film with exterior wall formation, and the pressure that air and moisture content produce is subjected to the impact of temperature and produce motion at air-locked interior exterior wall surface, constantly act on filming of coating, after for some time, metope will be filmed hollowing, foaming even scaling occur to come off, mildew, algae spot can appear in metope simultaneously.
Summary of the invention
For these defectives of above-mentioned organic coating, be badly in need of the coating material that exploitation has good ventilation property, resistance to crocking and good synthesized environmental protection performance.The object of the present invention is to provide the good anti-algicide coatings of a kind of result of use.
Technical solution of the present invention is: a kind of anti-algicide coatings, one-tenth by following weight part is grouped into, Red copper oxide 20-30 part, manganese oxide 10-15 part, zirconium white 5-10 part, inorganic polysiloxane 2-4 part, pure-acrylic emulsion 11-14 part, golden red titanium dioxide 3-7 part, phosphoric acid fat salt 5-9 part, dihydroxypropane 1-5 part, polyacrylamide 7-14 part, polyvinylidene difluoride (PVDF) 8-19 part, molybdenumdisulphide 8-16 part, polystyrene-acrylic copolymer 3-8 part, jade powder 5-19 part.
The preparation method may further comprise the steps: at normal temperatures and pressures, and with the synthetic emulsion of the solid ingredient high speed dispersion mixing of described weight percent, sand milling, the described weight percent of adding and water concocting, filtration, packing.
The present invention fills a prescription rationally, and result of use is good, and production cost is low.
Embodiment:
Embodiment 1:
A kind of anti-algicide coatings, one-tenth by following weight part is grouped into, 20 parts in Red copper oxide, 10 parts of manganese oxide, 5 parts of zirconium whites, 2 parts of inorganic polysiloxanes, 11 parts of pure-acrylic emulsions, 3 parts of golden red titanium dioxides, 5 parts of phosphoric acid fat salt, 1 part of dihydroxypropane, 7 parts of polyacrylamides, 8 parts of polyvinylidene difluoride (PVDF), 8 parts of molybdenumdisulphide, 3 parts of polystyrene-acrylic copolymer, 5 parts in jade powder.
Embodiment 2:
A kind of anti-algicide coatings, one-tenth by following weight part is grouped into, 30 parts in Red copper oxide, 15 parts of manganese oxide, 10 parts of zirconium whites, 4 parts of inorganic polysiloxanes, 14 parts of pure-acrylic emulsions, 7 parts of golden red titanium dioxides, 9 parts of phosphoric acid fat salt, 5 parts of dihydroxypropanes, 14 parts of polyacrylamides, 19 parts of polyvinylidene difluoride (PVDF), 16 parts of molybdenumdisulphide, 8 parts of polystyrene-acrylic copolymer, 19 parts in jade powder.
Embodiment 3:
A kind of anti-algicide coatings, one-tenth by following weight part is grouped into, 25 parts in Red copper oxide, 13 parts of manganese oxide, 8 parts of zirconium whites, 3 parts of inorganic polysiloxanes, 12 parts of pure-acrylic emulsions, 5 parts of golden red titanium dioxides, 7 parts of phosphoric acid fat salt, 4 parts of dihydroxypropanes, 9 parts of polyacrylamides, 14 parts of polyvinylidene difluoride (PVDF), 13 parts of molybdenumdisulphide, 5 parts of polystyrene-acrylic copolymer, 16 parts in jade powder.
Claims (1)
1. anti-algicide coatings, it is characterized in that: the one-tenth by following weight part is grouped into, Red copper oxide 20-30 part, manganese oxide 10-15 part, zirconium white 5-10 part, inorganic polysiloxane 2-4 part, pure-acrylic emulsion 11-14 part, golden red titanium dioxide 3-7 part, phosphoric acid fat salt 5-9 part, dihydroxypropane 1-5 part, polyacrylamide 7-14 part, polyvinylidene difluoride (PVDF) 8-19 part, molybdenumdisulphide 8-16 part, polystyrene-acrylic copolymer 3-8 part, jade powder 5-19 part.